• 한국인쇄학회지
• /
• 제16권3호
• /
• pp.29-41
• /
• 1998

The ultraviolet(UV)-curable materials wildly have been used as a ink and coating materials. A according to measure UV polymerization phase separation of acryl groups 2,3,4-functional monomer, a few experiments were performed gel fraction, dynamic viscosity of alkyd resin blend system. Dependence of photoiniator concentration and various monomer, alkyd resin content investigated structural changes of films cured by UV irradiation. Curing rate measured UV irradiation under $25^{\circ}C$, cell gap 7cm and film thickness 100${\mu}{\textrm}{m}$. In results, it was through that the viscoelastic properties of films cured with increasing the ratios of monomer/alkydresin contents are network polymer in properties such as viscoelasticity.

• 한국전기전자재료학회논문지
• /
• 제22권4호
• /
• pp.297-302
• /
• 2009

We have successfully fabricated the alumina thick films using inkjet printing processes without a high temperature sintering process. Alumina suspension as dielectric ink was formulated by combining nano-sized alumina powders with an anionic polymer dispersant in formamide/water as co-solvent. The thickness of the printed alumina thick film was measured at around 5 um by field emission scanning electron microscope. The calculated packing density of 68.5 % from the printed alumina thick film was much higher than the same films fabricated by conventional casting or dip coating processes. Q factor of the dielectrics thick film infiltrated with cyanate ester resin was evaluated by impedance analyzer.

• 한국독성학회:학술대회논문집
• /
• 한국독성학회 2003년도 춘계학술대회 논문집
• /
• pp.105-106
• /
• 2003

Diisodecyl phthalate (DIDP) which has high physical flexibility, various colors, low viscosity, high stability is used as coating material in ballon, vinyl ink, tent, textile, home and cars interior design and electric cable. In rodents, DIDP is suspected to be a peroxisome proliferator, a nongenotoxic carcinogen. In this study, we performed the carcinogenicity test of DIDP. (omitted)

• 전기학회논문지P
• /
• 제65권2호
• /
• pp.142-150
• /
• 2016

This paper developed new manufacture process technology of slim type flexible flat lighting product used lower power white LED. Flexible flat lighting is applied to letter sign lighting, traffic lighting, interior wall lighting, flat lighting, aquarium back lighting, wreath light etc. Main manufacture process technology were developed drawing software for electronics circuit, inkjet electronic circuit pattern and inkjet white ink coating. For pattern printing it was utilized for piezoelectonic inkjet head printing technology. Also high vacuum pressure laminating technology was waterproofing for LED flat lighting protection. Hence, form process technology we were manufactured for flexible flat lighting product of the power 12 W, input voltage 48 V and plane size $480{\times}480mm$. It acquired a these validity from experiment results.

• 한국표면공학회지
• /
• 제26권3호
• /
• pp.109-114
• /
• 1993

Black magnetite film could be formed on Invar steel for shadows mask by iron electroplating in thickness of 0.46~0.63$\mu\textrm{m}$ on Invar steel and subsequent oxidation of iron by immersion in strongly alkaline soution for 30~60 minutes. blackness degreed of magnetite oxide film on Invar was C20BL90 in comparision of color chart of Dainippon Ink & Chemicals Inc. Co. and adhesion test showed excellent adhesion of oxide film on substrate. Magnetite oxide film grew up on iron in hot strongly alkaline solution according to 'Sato-Cohen' oxide film growth model.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 2006년도 PAN PACIFIC CONFERENCE vol.2
• /
• pp.495-497
• /
• 2006

Talc Printing mottle of coated paper is one of the most common and the most difficult problems in offset printing. For a high quality printing, development of new paper coating technologies to prevent print mottle is required. This research focused on improvement of printing mottle. Effects of ink dispersion and printing conditions such as nip conditions, printing pressure and printing speed on printing mottle were investigated with RI tester and IGT tester.

• 한국정밀공학회지
• /
• 제14권1호
• /
• pp.142-149
• /
• 1997

Ceramic-coated anilox roll for printing is resistant to corrosion and wear, and hence has enhanced life and quality. Laser engraving is used typically for machining holes to store ink in this roll. Since engraved hole size and shape are directly related to laser processing parameters, it is necessary to know the rela- tionships among these parameters. In this study, the parameters for engraving of ;oasma sprayed ceramic coatings with Nd:YAG laser were studied. Relationships between hole shape and processing parameters were analyzed. Cr$_{2}$O$_{3}$ceramic was found to be most suitable for Nd:YAG laser engraving. It was found that hole depth can be increased by using higher energy pulses. Effect of using different assistant gases was small to the final results. For better results, it was suggested to use a very stable laser with shorter pulses and higher pulse energy.

• Current Photovoltaic Research
• /
• 제2권4호
• /
• pp.173-176
• /
• 2014

We have investigated the seed layer formation of front side contact using the inkjet printing process. Conductive silver ink was printed on textured Si wafers with 80 nm thick $SiN_x$ anti reflection coating (ARC) layers and thickened by light induced plating (LIP). The inkjet printable sliver inks were specifically formulated for inkjet printing on these substrates. Also, a novel method to prepare nano-sized glass frits by the sol-gel process with particle sizes around 5 nm is presented. Furthermore, dispersion stability of the formulated ink was measured using a Turbiscan. By implementing these glass frits, it was found that a continuous and uniform seed layer with a line width of $40{\mu}m$ could be formed by a inkjet printing process. We also investigated the contact resistance between the front contact and emitter using the transfer length model (TLM). On an emitter with the sheet resistance of $60{\Omega}/sq$, a specific contact resistance (${\rho}_c$) below $10m{\Omega}{\cdot}cm^2$ could be achieved at a peak firing temperature around $700^{\circ}C$. In addition, the correlation between the contact resistance and interface microstructures were studied using scanning electron microscopy (SEM). We found that the added glass particles act as a very effective fire through agent, and Ag crystallites are formed along the interface glass layer.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2010년도 춘계학술발표대회
• /
• pp.19.2-19.2
• /
• 2010

Printed electronics using printing process has broadened in all respects such as electrics (lighting, batteries, solar cells etc) as well as electronics (OLED, LCD, E-paper, transistor etc). Copper is considered to be a promising alternative to silver for printed electronics, due to very high conductivity at a low price. However, Copper is easily oxidized, and its oxide is non-conductive. This is the highest hurdle for making copper inks, since the heat and humidity that occurs during ink making and printing simply accelerates the oxidation process. A variety of chemical treatments including organic capping agents and metallic coating have been used to slow this oxidation. We have established synthetic conditions of copper nanoparticles (CuNPs) which are resistant to oxidation and average diameter of 20 to 50nm. Specific resistivity should be less than $4\;{\mu}{\Omega}{\cdot}cm$ when sintered at lower temperature than $250^{\circ}C$ to be able to apply to conductive patterns of FPCBs using ink-jet printing. Through this study, the parameters to control average diameter of CuNPs were found to be the introduction of additive agent, the feeding rate of reducing agent, and reaction temperature. The CuNPs with various average diameters (58, 40, 26, 20nm) could be synthesized by controlling these parameters. The dispersed solution of CuNPs with an average size of 20 nm was made with nonpolar solvent containing 3 wt% of binder, and then coated onto glass substrate. After sintering the coated substrates at $250^{\circ}C$ for 30 minutes in nitrogen atmosphere, metallic copper film resulted in a specific resistivity of $4.2\;{\mu}{\Omega}{\cdot}cm$.

• 펄프종이기술
• /
• 제32권4호
• /
• pp.49-57
• /
• 2000

This study was carried out to investigate the effect of the type of base papers containing rice straw-BKP on the properties and printabilities of coated papers. Also, it was intended to evaluate the effect of coated paper prepared with anionic and amphoteric latex based coating color. The results obtained from this study were as follows. The fiber length of rice straw-BKP was observed much shorter than those of the wood pulps(Sw-BKP, Hw-BKP). This has effect on physical properties. Therefore, the results of measured physical properties were much lower than those of wood pulps. Also, physical properties tended to increase slightly with the increase of the mixing ratio of Sw-BKP. Opacity of the base paper containing rice straw-BKP, was higher than that of the wood pulps. As the mixing ratio of Sw-BKP increases the opacity tended to decrease. On the other hand, smoothness and roughness to rice straw-BKP were similar with Sw-BKP and its air permeability was lower than those of wood pulps. The optical properties of coated papers containing rice straw-BKP tended to be similar to those of other base papers. The ink receptivity of coated papers containg rice straw-BKP was higher than those of wood pulps and printing gloss was similar to wood pulps. The mixing ratio of Sw-BKP, the ink receptivity and printing gloss of rice straw-BKP were showed no difference irrespective the mixing ratio of Sw-BKP. Meannwhile, amphoteric latex improved the optical properties and printability of coated papers.