• Tribology and Lubricants
• /
• v.24 no.5
• /
• pp.255-263
• /
• 2008

Adhesion tests were conducted to investigate the adhesion characteristics between mold and thermoplastic polymer film. Coating of anti-sticking layer (ASL), a kind of polymer material, imprint pressure, and separation velocity were considered as the process conditions. A piece of fused silica without patterns on its surface was used as a mold and the thermoplastic polymer films were made on Si substrate by spin-coating the commercial polymer solution such as mr-I PMMA and mr-I 7020. The ASL was derived from (1H, 1H, 2H, 2H - perfluorooctyl) trichlorosilane($F_{13}$-OTS) and coated on the fused silica mold in vapor phase. The pull-off force was measured in various process conditions and the surfaces of the mold and the polymer film were observed after separation. It was found that the adhesion characteristics between the mold and the thermoplastic polymer film and the release performance of ASL were changed according to the process conditions. The ASL was effective to reduce the pull-off force and the damage of polymer film. In cases of the mold coated with ASL, the pull-off force did not depend on imprint pressure and separation velocity.

• Korean Chemical Engineering Research
• /
• v.47 no.3
• /
• pp.316-320
• /
• 2009

UV curable hard and color coatings were formed on polycarbonate(PC) films. The coating materials were composed of a commercially available end-capped polyester(EB830), diacrylate monomer(HDDA), silicon acrylate, photoinitiator, and organic dye as a coloring agent. The surface properties of coating films were evaluated, and the influences of the compositions of coating materials were investigated. The coating films showed high transmission and good adhesion between coating layer and PC substrate. And the coating films exhibited higher hardness than bare PC film. The coating films with various colors were obtained by wet process, and the clear and color window lenses for mobile phone were prepared successfully.

• Tribology and Lubricants
• /
• v.37 no.2
• /
• pp.54-61
• /
• 2021

The effect of the sand blasting before TiAlN coating in the manufacture of WC hard metal alloy tips have been studied. For four different tips, according to the status of processing of the sand blasting and the coating, residual stress measurement by X-ray diffraction and several tests for mechanical properties have been conducted. The results suggest that there was no difference in static mechanical properties, such as hardness, surface roughness and elastic modulus, between two coatings. Furthermore, compressive residual stress was generated equally on their surfaces. Additionally, the compressive residual stress in substrate WC was found to increase greatly when subjected to sand blasting treatment. However, the compressive residual stress decrease after coating regardless of sand blasting treatment. Nevertheless, it is confirmed that the compressive residual stress generated in the coating after sand blasting is less than that in the non-sandblasting coating. This was attributed to the plastic deformation occurring in the WC substrate during coating after sand blasting. In contrast to the scratch test results, sand blasting was assumed to have a negative effect on the adhesion between the coating and substrate. This is because there is a high possibility of microcracks due to plastic deformation in the WC substrate under the coating after sand blasting.

• Corrosion Science and Technology
• /
• v.23 no.3
• /
• pp.179-194
• /
• 2024

A layer-by-layer coating was produced using electrophoretic deposition for a HA/Al₂O₃ coating layer and a bioglass coating layer on Co-Cr-Mo alloy with a roughness of 0.5 ㎛ (400 emery paper SiC). The corrosion behaviour was analyzed by assessing the coating layers' exceptional corrosion resistance, which outperformed the substrate. Cr ion release test using AAS was carried out, indicating that factional graded coating inhibited ion release from the uncoated substrate to coated sample. The porosity was expressed as a percentage, representing the extent of imperfections on the surface of all coatings. These imperfections fell within an acceptable range of 1% to 3%. The roughness of the coated surface was measured using atomic force microscopy, which revealed an excellent roughness value of 3.32 nm. Tape test technique for adhesion revealed that the removal area of the substrate coating layer varied by 11.92%. X-ray diffraction analysis confirmed the presence of all coating material peaks and verified phases of the deposited coating layers. These findings provided evidence that the coating composition remains unaffected by the electrophoretic deposition process. The bioactivity was assessed by immersion in a simulated bodily fluid, which revealed the formation of HCA during a period of 5 days.

• Journal of the Korean Society of Safety
• /
• v.25 no.3
• /
• pp.45-52
• /
• 2010

The purpose of this study is application to flame retardant powder coating(FRPC) material consisting of ammonium polyphosphate(APP) and magnesium hydroxide($Mg(OH)_2$) as a halogen free flame retardant into thermoplastic resin(LDPE-g-MAH). For improvement of adhesion, LDPE-g-MAH was synthesized from low density polyethylene(LDPE) and maleic anhydride(MAH). The mechanical properties as melt flow index, pencil hardness, cross-hatch adhesion and impact resistance of FRPC were measured. Also, the limited oxygen index(LOI) values were measured 17.3vol%, 31.1vol% and 33.7vol% for LDPE-g-MAH, FRPC-3(APP 15wt%, $Mg(OH)_2$ 15wt%) and FRPC-5(APP 30 wt%), respectively. The thermo gravimetry/differential thermal analysis(TG/DTA) of FPRC-3 was observed endothermic peak at $340^{\circ}C$ and $450^{\circ}C$, it was confirmed predominant thermal stability though the wide temperature range by APP and $Mg(OH)_2$. It was showed V-0 grade for FRPC-3 and FRPC-4(APP 20wt%, $Mg(OH)_2$ 10wt%) that a char formation and drip suppressing effect, and combustion time reduced by UL94(vertical burning test). It was confirmed that flame retardancy was improved with the synergy effect because of char formation by APP and $Mg(OH)_2$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.45-45
• /
• 2014

The importance of magnesium alloys has significantly increased due to their low density, high strength/weight ratio, very good electromagnetic shielding features and good recyclability. However, unfortunately, Mg alloys are very susceptible to corrosion due to their high chemically activities (= -2.356 V vs. NHE at $25^{\circ}C$), hence, most commercial Mg alloys require corrosion protective coatings. Organic coating such as painting, powder coating and electrophoretic deposition of paint (E-paint) is typically used in the final stages of the coating process of Mg alloys. In this study, effect of pre-immersion time on the deposition of E-paint on AZ31 Mg alloy was investigated. It was found that during pre-immersion time, AZ31 Mg alloy rapidly reacts with E-paint solution and paint can be self-deposited on the AZ31 surface without applying of electric current. The pore size on the E-painted AZ31 Mg alloy increased with increasing pre-immersion time from 0 to 5 min. Both adhesion and corrosion resistance of E-painted AZ31 Mg alloy decreased with increasing pre-immersion time. The best E-paint AZ31 Mg alloy, which showed stronger adhesion after water immersion test and good corrosion resistance, was started to deposit after 5 s of pre-immersion time.

• 연구논문집
• /
• s.28
• /
• pp.219-227
• /
• 1998

In order to investigate the interfacial structure between TiN and iron nitride, an AISI 4140 steel was nitrided to form a layer of thickness 15$\mum$ by DC ion nitriding, then the surface was bombarded with Ti ions and subsequently coated a TiN film of 5$\mum$ by arc ion plating method. The interfacial microstructure between TiN and iron nitride was characterized by optical microscope, SEM and XRD. So called black layer was observed in the duplex treatment. It was resulted from the decomposition of iron nitride during the bombardment. Its thickness was increased with increasing bombardment time at high bias voltage. But the thickness was greatly decreased when the iron nitride was bombarded with a nitrogen gas or at a reduced bias voltage. The adhesion strength of the top TiN coating was decreased with increasing thickness of the black layer. Furthermore, the reduced adhesion strength in this system was discussed in view of the interfacial structural relationship between TiN and iron nitride.

• Journal of Adhesion and Interface
• /
• v.9 no.3
• /
• pp.1-6
• /
• 2008

Hard coatings were deposited on a polycarbonate plate as potential substitutes for glass in cars. In this research the copolymers of p-polyphenylene (PPH) and m-phenylene (MPH) were synthesized, and using these copolymers the coatings were conducted on a polycarbonate plate. The hardness of the coating surface was affected with the mole ratio of PPH and MPH in the copolymer. When the mole ratio of PPH : MPH in the copolymer was 20 : 80, the coating showed 2H class of pencil hardness and also showed the best abrasion resistance.

• Journal of the Korean institute of surface engineering
• /
• v.30 no.2
• /
• pp.93-103
• /
• 1997

High temperature materials used in the elevated temperature and corrosive atmosphere must have the good oxidation resistance and preserve their own mechanical properties simultaneously. For the oxidation resistance, it is very important to form a protective oxide scale such as $Al_2O_3$ or $Cr_2O_3$ on the substrate. However, the additions of protective oxide forming elements such as Cr and Al in the alloy to enhance its oxidation resistance are limited due to the deleterious effects on their mechanical properties. PECVD(P1asma Enhanced Chemical Vapor Deposition) coating processes were employed to improve the oxidation resistance at high temperature. Cr and/or A1 were coated on the substrates of Ni and Inconel 600 at various temperatures of 400, 500, $600^{\circ}C$ and at different conditions of specimen surfaces. Then, coated specimens were exposed to isothermal and cyclic oxidation conditions in air at 1000 and $1100^{\circ}C$. In order to enhance the adhesion between the substrate and coated layer, heat treatments of the coated specimens were conducted in a vacuum. At isothermal oxidation experiments, Al-coated Ni specimen showed better oxidation resistance than pure Ni. At cyclic oxidation experiments at $1000^{\circ}C$. Cr and Al-coated specimen showed better oxidation resistance. Cr-coated Inconel 600 had also showed better oxidation resistance due to Cr in the substrate. By PECVD coating process, oxidation resistance could be improved, but it was not improved as expected due to the weakness of the adhesion between the substrate and the coated layer.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.4
• /
• pp.233-238
• /
• 2019

The formation behavior of zinc phosphate conversion coating (ZPCC) on SCM430 alloy was investigated in 25 vol.% of 1M ZnO + 170 ml/L solution containing various $Fe(NO_3)_2$ concentrations, using open-circuit potential(OCP), electrochemical impedance spectroscopy(EIS), cyclic polarization(CP) curve and tape peel test. OCP of SCM430 alloy and corrosion current density increased with increasing $Fe(NO_3)_3$ concentration. Resistance of films formed on SCM430 alloy by chemical conversion treatment decreased with increasing $Fe(NO_3)_3$ concentration. Color and adhesion of chemical conversion coatings became darker and worse, respectively, with increasing $Fe(NO_3)_3$ concentration. It is concluded that addition of $Fe(NO_3)_3$ into a zinc phosphating bath leads to faster reaction to form porous surface coatings with poor adhesion and corrosion resistance.