Hard Coatings on Polycarbonate Plate Using Phenylene Copolymers
폴리카보네이트 판 위에 Phenylene의 공중합체들을 이용한 하드 코팅
- Shin, Min Jae (Department of Chemical and Biomolecular Engineering, KAIST) ;
- Yang, Do Hyeon (Korea Automotive Technology Institute) ;
-
Oh, Mee Hye
(Korea Automotive Technology Institute)
;
-
Yoon, Yeo Seong
(Korea Automotive Technology Institute)
;
- Shin, Jae Sup (Department of Chemistry, Chungbuk National University)
- Received : 2008.06.09
- Accepted : 2008.09.23
- Published : 2008.09.30
Abstract
Hard coatings were deposited on a polycarbonate plate as potential substitutes for glass in cars. In this research the copolymers of p-polyphenylene (PPH) and m-phenylene (MPH) were synthesized, and using these copolymers the coatings were conducted on a polycarbonate plate. The hardness of the coating surface was affected with the mole ratio of PPH and MPH in the copolymer. When the mole ratio of PPH : MPH in the copolymer was 20 : 80, the coating showed 2H class of pencil hardness and also showed the best abrasion resistance.
자동차의 유리를 폴리카보네이트로 대체하기 위하여 폴리카보네이트 판 위에 하드 코팅을 시도하였다. 본 연구에서는 p-phenylene (PPH)과 m-phenylene (MPH)의 공중합체들을 합성하여 이것들을 이용하여 폴리카보네이트 판 위에 코팅을 시도하였다. 공중합체내의 PPH와 MPH의 비율에 따라서 다양한 강도를 나타내는 코팅이 형성되었다. PPH와 MPH의 비율이 20 : 80일 경우에 연필 경도 2H를 나타내었으며, 이 때 내마모성도 매우 우수하였다.