• 한국전산구조공학회논문집
• /
• 제15권3호
• /
• pp.433-440
• /
• 2002

본 연구에서는 균일한 인장과 굽힘을 받는 반무한 평판내의 분기균열에 대하여 해석하였다. 중첩의 원리를 이용하여 인장과 굽힘을 받는 분기균열에 대하여 응력 및 모멘트 확대계수를 해석하였다. 응력확대계수는 유한요소법과 J 기저 상호매개적분을 이용하여 해석하였고, 모멘트확대계수는 균열선단의 모멘트로부터 모멘트외삽을 이용하여 계산하였다 무차원화된 응력확대계수와 모멘트확대계수에 대한 수치해석 결과는 분기균열 길이와 주균열의 비, 그리고 분기균열각의 함수로 나타내었다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2000년도 추계학술대회 논문집
• /
• pp.461-464
• /
• 2000

A branched crack in a semi-infinite plate under tension and bending moment is considered. Intensity factors of the stress and moment for the branched crack are evaluated. The stress intensity factors are obtained by using the finite element method and the J-based mutual integral. The moment intensity factors are calculated by extrapolating the values of the moment near the crack tip. Approximate expressions are also obtained as functions of the branched crack length and branching angle.

• Journal of Mechanical Science and Technology
• /
• 제16권12호
• /
• pp.1594-1603
• /
• 2002

In this paper, when the initial propagation angle of a branched crack is calculated from the maximum tangential stress criterion (MTSC) and the minimum strain energy density criterion (MSEDC), it is essential that you use stress components in which higher order terms are considered and stress components at the position in a distance 0.005㎜ from the crack tip (=r). When an interfacial crack propagates along the interface at a constant velocity, the initial propagation angles of the branched crack are similar. to the mode mixities (phase angle) and the theoretical values obtained from MTSC and MSEDC. The initial propagation angle of the branched crack depends considerably on the stress intensity factor K$_2$.

• 한국생산제조학회지
• /
• 제9권5호
• /
• pp.73-79
• /
• 2000

The applications of fracture mechanics have traditionally concentrated on cracks loaded by tensile stresses, and growing under an opening or mode I mechanism. However, many cases of failures occur from growth of cracks subjected to mixed mode loading. Several criteria have been proposed regarding the crack growth direction under mixed mode loadings. This paper is aimed at investigation of fatigue crack growth behaviour under mixed mode(I＋II) with variation of angle and pre-crack length in two dimensional branched type precrack. Especially the direction of fatigue crack propagation was predicted and effective stress intensity factor was calculated by finite element analysis(FEA. In this paper, the maximum tangential stress(MTS) criterion was used to predict crack growth direction. Not only experiment but also finite element analysis was carried out and the theoretical predictions were compared with experimental results.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 춘계학술대회논문집A
• /
• pp.182-187
• /
• 2000

The application of fracture mechanics have traditionally concentrated on cracks leaded by tensile stresses, and growing under an opening or mode I mechanism. However, many cases of failures occur from growth of cracks subjected to mixed mode loading. Several criteria have been proposed regarding the crack growth direction under mixed mode loadings. This paper is aimed at prediction of fatigue crack growth behaviour under mixed mode(I+II) in two dimensional branched type precrack. In this paper, the maximum tangential stress(MTS) criterion was used to predict crack growth direction. Not only experiment but also finite element analysis(FEA) was carried out. The theoretical predictions were compared with experimental results in this paper

• 대한기계학회논문집
• /
• 제10권2호
• /
• pp.257-264
• /
• 1986

무한평판에 묻혀진 크랙에 대한 응력확대계수를 결정하는 전위분포법을 반무한 평판에서의 표면크랙에 확장 적용하였다. 이를 위해 반평면에서의 전위응력의 기본 해가 간단한 복소수 응력함수형태로 얻어졌다. 평형을 이루는 절편적인 분포로부터 응력확대의 계수를 계산하는 새로운 방식을 제안하였으며, 수직표면 크랙과 묻혀진 경사크랙에 대한 기존해와 이 방법의 결과가 상호 비교되었다. 경사진 표면크랙에 대한 계산결과는 유한평판에서의 기존하는 Mapping Collocation 해석과 비교되어 좋은 일치를 보여 주었다. 구부러진 크랙과 대칭으로 가지친 크랙에 대해서는 표면크랙과 묻혀진 크랙사이에 상당한 차이가 있음이 나타났다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2000년도 추계학술대회 논문집
• /
• pp.473-476
• /
• 2000

Recently, many studies focus on mixed-mode fatigue-fracture characteristics of characteristics of materials. In order to reveal crack initiation and propagation mechanisms in combined -mode fatigue. This paper investigates the initiation and propagation behavior of the fatigue crack of the STS304 specimens under mixed mode loading conditions. moreover crack arrest and branch phenomena were analyzed with respect to the change do the angle of inclined loading. The relationship between the angle of inclined loading and the angle of branched crack was studied. A greate number of cycles are necessary to initiate a new crack from the initial crack. The direction of the new crack propagation is determined by MTS theory.

• 한국해양공학회지
• /
• 제6권1호
• /
• pp.96-104
• /
• 1992

Aircraft structures and engineering structures are always subject to variable amplitude loads. Variable amplitude loads include some kind of loading history; for example, constant amplitude load, single peak overload and block overload etc. Crack growth under variable amplitude loading exhibits retardation effect. In this study, the 4 point bending fatigue test was performed by hydrolic servo fatigue testing machine on 7075-T6 Al-alloy. The retardation effect of overload ratio and numbers of overload cycle was quantitatively studied. 1) Change of retardation effect against increment of overload ratio is more evident when the multiple overload is applied than single overload is done. 2) The number of overload cycle is very important factor about the crack growth retardation effect when the overload ratio is more than 1.75; that is not when the overload ratio is less than 1.75. 3) Overload affected zone size increased gradually by increment of crack growth retardation effect. 4) Crack driving force is more greatly reduced when the crack tip branched off two direction than it sloped to one direction.

• 한국정밀공학회지
• /
• 제27권12호
• /
• pp.99-106
• /
• 2010

Gas turbines operation for power generation increased rapidly since 1990 due to the high efficiency in combined cycle, relatively low construction cost and low emission. But the operation and maintenance cost for gas turbine is high because the expensive superalloy hot gas path parts should be repaired and replaced periodically This study analyzed the initiation and propagation of the crack at the gas turbine blades which are coated with MCrAIY as a bond coat and TBC as a top coat. The sample blades had been serviced at the actual gas turbines for power generation. Total 7 sets of blades were analyzed and they have different EOH(equivalent operation hour). Blades were sectioned and the cracking distribution were measured and analyzed utilizing SEM(scanning electron microscope) and optical microscope. The blades which had 52,000 EOH of operation had cracks at the substrate and the maximum depth was 0.2 mm. Most of the cracks initiated at the boundary layer between TBC and bond coat and propagated down to the bond coat. Once bond coat is cracked, the base metal is exposed to the oxidation condition and undergoes notch effect. Under this environment, the crack branched at the inter-diffusion layer and propagated to the substrate. Critical cracks affecting the blade life were analyzed as those on suction side and platform.

• Corrosion Science and Technology
• /
• 제18권2호
• /
• pp.49-54
• /
• 2019

The purpose of this paper is to present failure analysis, of the heat exchanger tube in a district heating system. SS304 stainless steel is used, as material for the heat exchanger tube. The heat exchanger operates in a soft water environment containing a small amount of chloride ions, and regularly repeats operation and standstill period. This causes concentration of chloride ions on the outer surface of the tube, as well as repeat of thermal expansion, and shrinkage of the tube. As a result of microscopic examination, cracks showed transgranular as well as branched propagation, and many pits were present, at the initiation point of each crack. Energy disperstive spectroscopy analysis showed Fe and O peak, as well as Cl peak, meaning that cracks were affected by Cl ion. Failure of the tube was caused by chloride-induced stress corrosion cracking by thermal stress, high temperature, and localized enrichment of chloride ions.