• The Journal of Advanced Prosthodontics
• /
• v.1 no.2
• /
• pp.107-112
• /
• 2009

STATEMENT OF PROBLEM. Macroscopic and especially microscopic properties of implant surfaces play a major role in the osseous healing of dental implants. Dental implants with modified surfaces have shown stronger osseointegration than implants which are only turned (machined). Advanced surface modification techniques such as anodic oxidation and Ca-P application have been developed to achieve faster and stronger bonding between the host bone and the implant. PURPOSE. The purpose of this study was to investigate the effect of surface treatment of titanium dental implant on implant stability after insertion using the rabbit tibia model. MATERIAL AND METHODS. Three test groups were prepared: sandblasted, large-grit and acid-etched (SLA) implants, anodic oxidized implants, and anodized implants with Ca-P immersion. The turned implants served as control. Twenty rabbits received 80 implants in the tibia. Resonance frequencies were measured at the time of implant insertion, 2 weeks and 4 weeks of healing. Removal torque values (RTV) were measured 2 and 4 weeks after insertion. RESULTS. The implant stability quotient (ISQ) values of implants for resonance frequency analysis (RFA) increased significantly (P <. 05) during 2 weeks of healing period although there were no significant differences among the test and control groups (P >. 05). The test and control implants also showed significantly higher ISQ values during 4 weeks of healing period (P < .05). No significant differences, however, were found among all the groups. All the groups showed no significant differences in ISQ values between 2 and 4 weeks after implant insertion (P >. 05). The SLA, anodized and Ca-P immersed implants showed higher RTVs at 2 and 4 weeks of healing than the machined one (P < .05). However, there was no significant difference among the experimental groups. CONCLUSION. The surface-modified implants appear to provide superior implant stability to the turned one. Under the limitation of this study, however, we suggest that neither anodic oxidation nor Ca-P immersion techniques have any advantage over the conventional SLA technique with respect to implant stability.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.32 no.3
• /
• pp.194-201
• /
• 2016

Purpose: The purpose of this study was to evaluate of Zirconium Nitride (ZrN) coating on shear bond strength with denture base resin in Co-Cr and Ti-6Al-4V alloy. Materials and Methods: Co-Cr and Ti-6Al-4V alloy disks (10 mm in diameter, 2.5 mm in thickness; each other: n = 14) were prepared and divided with 2 groups each other by ZrN coating. After primer was applied to disks surface, denture base resin with diameter 6 mm, height 5 mm was bonded on metal disk surface. After surface roughness was measured by Profiler, shear bond strength was determined with Universal testing machine and analyzed with two-way ANOVA. The specimen surfaces and failure mode were examined using a scanning electron microscope. Results: ZrN coated groups showed significantly higher rough surface than non-coated groups (P < 0.05). Irrespective of alloy materials, shear bond strength of ZrN coated groups were lower than non-coated groups (P < 0.001). The scanning electron microscope (SEM) of ZrN coated groups showed mixed and adhesive fractures. Conclusion: ZrN coating weakened bonding strength between denture base resin and Co-Cr, Ti-6Al-4V alloy.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.489-498
• /
• 2005

Recently, the deterioration of concrete structures have been increased by the damage from salt, carbonization, freezing & thawing and the others. Therefore, the measures for the deterioration of concretes have been taken. Among them, it has been often used that surface treatment which cut off the deterioration factors of durability by protecting the surface of concrete. The water proof and repair materials for concrete mainly use organic materials such as epoxy, these materials excel in intial bonding force and resistance to chemical agents. But they cause difference in the modulus of elasticity and the rate of shrinkage and expansion of concrete, and thus result in such problems as scaling and spatting in the progress of time. Therefore in this study it develop the performance Improving agent of concrete surface that can block a deterioration cause such as $CO_2$ gas, chloride ion and water from the outside and enhance waterproofing ability by reinforcing the concrete surface when applying it to concrete structures.

• Restorative Dentistry and Endodontics
• /
• v.34 no.2
• /
• pp.113-119
• /
• 2009

The purpose of this study was to compare the tensile bond strength of several self-adhesive resin cements bonded to dentin surfaces with different wet conditions. Three self-adhesive resin cements: Rely-X Unicem (3M ESPE, St. Paul, MN. USA). Embrace Wetbond (Pulpdent. Oakland. MA. USA). Maxcem (Kerr. Orange. CA. USA) were used. Extracted sixty human molars were used. Each self-adhesive resin cement was adhered to the dentin specimens (two rectangular sticks from each molar) in different wet conditions. Tensile bond strength were measured using universal testing machine (EZ Test. Shimadzu corporation. Kyoto. Japan) at a crosshead speed of 1.0mm/min. After the testing. bonding failures of specimens were observed by Operative microscope (OPMI pro, Carl Zeiss. Oberkochen, Germany). T-test was used to evaluate the effect of dentin surface wetness. One-way ANOVA test was used to evaluate the tensile bond strength of self-adhesive resin cements in the same condition. Scheffe's test was used for statistical analyzing at the 95% level of confidence. The result showed that wetness of dentin surface didn't affect tensile bond strength of self-adhesive resin cements and Maxcem showed the lowest tensile bond strength.

• Clean Technology
• /
• v.27 no.1
• /
• pp.24-32
• /
• 2021

Unburned carbon (UC) was successfully separated from fly ash by up to 85.8% in weight via froth flotation using soybean oil as a collector. An 18 wt% yield of microceramics (CM) could be achieved by employing a hydro cyclone separator located immediately after the flotation equipment. UC and CM were tested as alternatives to weight-adding material and polymer (especially polypropylene in this study) filler, respectively. Large particles of UC were broken down into smaller ones via ball milling to have an average particle diameter of 10.2 ㎛. When crushed UC was used as an alternative to clay as a rubber weight-adding material, a somewhat lower tensile strength and elongation rate than the allowed values were unfortunately obtained. In order to satisfy the standard limits, further treatment of UC is required to enhance surface energy for more intimate bonding with rubber. CM was observed in spherical forms with an average diameter of 5 ㎛. The surface of the CM particles was modified with phenol, polyol, stearic acid, and oleic acid so that the surface modified CM could be used as a polypropylene-filling agent. The flowability was good, but due to the lack of coupling forces with polypropylene, successful impact strength and flexural strength could not be obtained. However, when mixing the surface-modified CM with 1% silane by weight, a drastic increase in both the impact strength and flexural strength were obtained.

• The korean journal of orthodontics
• /
• v.40 no.4
• /
• pp.260-266
• /
• 2010

Objective: The aim of this study was to determine whether different types of adhesive systems and enamel-protective agents will affect the tensile bond strength of lingual brackets. Methods: A total of 75 extracted mandibular incisors were randomly divided into 5 groups and lingual brackets were bonded. Group 1 specimens received Transbond XT (3M Unitek, Monrovia, CA, USA), Group 2 required the application of a fluoride-releasing resin (Ortho-coat, Pulpdent, Watertown, MA, USA) with Transbond XT, Group 3 specimens received a chlorhexidine varnish (Cervitec Plus, Ivoclar Vivadent, Schaan, Lichtenstein) with Transbond XT. In Group 4, a light-cured orthodontic adhesive (Aegis Ortho, Bosworth, Skokie, USA) was applied and in Group 5, an antimicrobial self-etching primer (Clearfil Protect Bond, Kuraray, Osaka, Japan) was used. Results: There were no significant differences in bond strength whether fluoride-releasing resin or chlorhexidine varnish were used or not. Group 5 had significantly higher bond strength and adhesive remnant index (ARI) values than other groups (p < 0.001). The application of enamel-protective products did not have an adverse affect on the bond strength of lingual brackets. Conclusions: These products might provide benefits both for the patient and the clinician, by supporting the oral hygiene during lingual orthodontic treatment. The higher ARI score may be beneficial for Clearfil Protect Bond but its excessive bond strength should be considered in clinical practice, especially where the enamel is thin.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.23-28
• /
• 2007

In order to have a superconductive connection between the wire-wound pickup coil and input coil, typically Nb terminal blocks with screw holes are used. Since this connection structure occupies large volume, large stray pickup area can be generated which can pickup external noise fields. Thus, SQUID and connection block are shielded inside a superconducting tube, and this SQUID module is located at some distance from the distal coil of the gradiometer to minimize the distortion or imbalance of uniform background field due to the superconducting module. To operate this conventional SQUID module, we need a higher liquid He level, resulting in shorter refill interval. To make the fabrication of gradiometers simpler and refill interval longer, we developed a novel method of connecting the pickup coil into the input coil. Gradiometer coil wound of 0.125-mm diameter NbTi wires were glued close to the input coil pads of SQUID. The superconductive connection was made using an ultrasonic bonding of annealed 0.025-mm diameter Nb wires, bonded directly on the surface of NbTi wires where insulation layer was stripped out. The reliability of the superconductive bonding was good enough to sustain several thermal cycling. The stray pickup area due to this connection structure is about $0.1\;mm^2$, much smaller than the typical stray pickup area using the conventional screw block method. By using this compact connection structure, the position of the SQUID sensor is only about 20-30 mm from the distal coil of the gradiometer. Based on this compact module, we fabricated a magnetocardiography system having 61 first-order axial gradiometers, and measured MCG signals. The gradiometers have a coil diameter of 20 mm, and the baseline is 70 mm. The 61 axial gradiometer bobbins were distributed in a hexagonal lattice structure with a sensor interval of 26 mm, measuring $dB_z/dz$ component of magnetocardiography signals.

• The Journal of Korean Academy of Prosthodontics
• /
• v.30 no.1
• /
• pp.55-64
• /
• 1992

This study investigated the effect of porcelain primer on bonding of coomposite resin to porcelain surface. In order to test the bond strength between porcelain and composite resin, porcelain cylinders were embedded in acrylic resin, and polished with 240grit silicone caqrbide paper. The specimens were divided into twelve groups. All specimens were treated with three porcelain primers and bonded with five composite resins. All test groups were stored in $37^{\circ}C$ distilled water for 48hours. Shear bond strengths were measured with Instron(Model 4201) at a cross-head speed of 1mm/min. The obtained results were as follows : 1. Scotchprime/Silux II group and BISCO Porcelain Primer/Bisfill group showed significant higher bond strengths than Clearfil Porcelain Primer/photo Clearfil Bright group(p<0.05). And there was no significant differences in bond strengths between Scotchprime/Silux II group and BISCO Porcelain Primer/Bisfill group(p>0.05). 2. When composite resins were used with Scotchprime, the bond strengths were decresed Silux II$(16.68{\pm}3.35MPa)$, Bisfil$(16.23{\pm}4.54MPa)$, Poly-Fill$(14.74{\pm}4.08MPa)$, Photo Clearfil Bright$(13.75{\pm}2.89MPa)$ and Pekalux$(14.74{\pm}4.08MPa)$ in order, but there was no statistical significance(p>0.05). 3. When composite resins were used with BISCO Porcelain Primer, the bond strength were decreased Bisfil$(16.17{\pm}1.60MPa)$, Silux II$(12.13{\pm}2.37MPa)$, Poly-Fill$(10.78{\pm}1.99MPa)$, Photo Cleafil Bright $(9.91{\pm}4.59MPa)$ and Pekalux$(7.36{\pm}2.16MPa)$ in order, but there was no statistical significance(p>0.05). 4. Silux II, Photo Clearfil Bright and Poly-Fill used with Scotchprime showed significant higher bond strengths than BISCO Porcelain Primer(p>0.05).

• The Journal of Advanced Prosthodontics
• /
• v.10 no.5
• /
• pp.374-380
• /
• 2018

PURPOSE. The effect of silica-based glass-ceramic liners on the tensile bond strength between zirconia and resin-based luting agent was evaluated and compared with the effect of 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-containing primers. MATERIALS AND METHODS. Titanium abutments and zirconia crowns (n = 60) were fabricated, and the adhesive surfaces of the specimens were treated by airborne-particle abrasion. The specimens were divided into 5 groups based on surface treatment: a control group, 2 primer groups (MP: Monobond Plus; ZP: Z Prime Plus), and 2 liner groups (PL: P-containing Liner; PFL: P-free Liner). All specimens were cemented with self-adhesive resin-based luting agent. After 24-hour water storage and thermocycling (5,000 cycles, $5^{\circ}C/55^{\circ}C$), the tensile bond strength was measured using a universal testing machine. Failure mode analysis and elemental analysis on the bonding interface were performed. The data were analyzed using Kruskal-Wallis test, Dunn's post hoc test, and Fisher's exact test. RESULTS. The liner groups and primer groups showed significantly higher tensile bond strengths than that of the control group (P<.05). PFL showed a significantly higher tensile bond strength than the primer groups (P<.05). The percentage of mixed failure was higher in the primer groups than in the control group (P<.001), and all the specimens showed mixed failure in the liner groups (P<.001). A chemical reaction area was observed at the bonding interface between zirconia and liner. CONCLUSION. The application of liner significantly increased the tensile bond strength between zirconia and resin-based luting agent. PFL was more effective than MDP-containing primers in improving the tensile bond strength with the resin-based luting agent.

• Journal of Korean Society of Forest Science
• /
• v.63 no.1
• /
• pp.12-20
• /
• 1984

This research was performed to estimate the properties of particleboard based on the press time and temperature which was made of chip of larch that grows in Korea. The results in this study were as follows: 1) Even though the chips, 1:1-35 ratio between length and thickness, are relatively bad condition, the surface smoothness that can easily spread the adhesive evenly and thoroughly and bonding ability of chips can give proper physical properties. 2) It shows more mechanical properties at the press time of 10 min. in MOR (Modulus of Rupture), MOE (Modulus of Elasticity) and SHA (Screw Holding Ability). 3) It is not significant according to the press time 20 min. in MOR, IBS (Internal Bonding Strength) and SHA, for the reciprocal actions between the accelerating aging effect of chip and the softening effect of adhesion are occured. 4) IBS is rising according to the increasing temp at the press time of 10 min. Because it needs to transfer the plate heat to make the proper hardening temp. In the layer. 5) The heat treatment effects have greatly influenced the stahility of dimension by falling the absorption, anisotropy and inhomegenity. As a result of these the values of thickness and linear expansion ratio were respectively dropped by the increase of press temp and the time and so did absorption.