To improve the interfacial bonding of carbon fiber-nylon 6 composite, carbon fiber(CF) were oxidized by nitric acid treatment, and two types of graft polymer(GP) of nylon 6-g-polyacrylamide (PAAm) -water dispersable GP(WDGP) and m-cresol solu ble GP(CSGP) were treated as coupling agents. Introduction of polar groups such as -COOH, -OH, etc, on the surface of the oxidized CF was confirmed by IR spectra. The stem polymer of nylon 6 in the coupling agent (GP) could be compatible with'matrix nylon 5, and the grafted branch of PAAm on GP could react to the polar groups on the oxidized CF in composite. The interfacial strength was measured by the transverse tensile test to the fiber direction for single CF embedded nylon 6 film especially prepared and by the pull-out test method. The interfacial strength of the composite reinforced with oxidized CF is greater than that reinforced with unoxidized CF. The interfacial strength of the composite was increased by treatment of coupling agents(GPs) considerably, and the increasing tendency by the WDGP is greater than that by the CSGP. The optimum conditions of coupling agent treatment are as follows: the concentration, adsorption tlme of GP, and curing temperature are 2%, 20 minutes, and $170^{\circ}$, respectively.
Adhesive bonding is one of the most promising joining methods which may substitute for conventional metallurgical joining processes, such as welding, brazing and soldering. Curing behavior and mechanical properties of adhesive joint are largely dependent on the curing agent including hardener and catalyst. In this study, effects of curing system on the curing behavior and single-lap shear strength of epoxy adhesive joint are investigated. Dihydrazide, anhydride and dicyandiamide(DICY) were chosen as hardener and imidazole and triphenylphosphine(TPP) were chosen as catalyst. In curing behavior, TPP showed the delay of the curing rate for DICY and ADH at $160^{\circ}C$, compared to imidazole catalyst due to the high curing onset/peak temperature. DICY seemed to be most beneficial in the joint strength for both steel and Al adherends, although the type of adherends affected the shear strength of epoxy adhesive joint.
One of the principal problems encountered in the use of fiber reinforced composites is to establish an active fiber surface to achieve maximum adhesion between resin and fiber surface. In order to improve the interface bonding, the surface of glass fiber should be treated with silane coupling agent in ordinary composite manufacturing processes. However, the price of the coupling agent is very high and in the treating process voids are formed, which decreasees electrical and mechanical strength. We want to develope new process that will overcome the disadvantage of the coupling agent and achieve maximum adhesion at the interface between resin and fiber by active plasma treatment on the glass fiber surface. In this study, we investigate the improvement of contact angle on the glass plate surface as the first step in developing new GFRP.
치면열구전색은 수 십년간 교합면 우식의 예방에 가장 효과적인 방법 중 한가지로 알려져 왔다. 하지만 치면열구전색제의 마모와 파절 때문에 치면열구전색제의 재시술 또는 수리를 필요로 하게 되었다. 본 연구의 목적은 파손된 치면열구전색제를 수리할 때 치질과 잔여 전색제의 표면처리 방법에 따른 미세누출 차이를 알아보고자 하는 것이다. 120개의 영구 대구치에 치면열구전색제를 적용하고 인위적인 파손을 만든 뒤 인공타액에 4주동안 보관하였다. 4주 후 근심 또는 원심의 치면열구전색제가 완전히 파손 양상을 나타내는 치아 60개를 선택하여 각각 15개씩 4개 군으로 나누어 실험에 사용하였다. 각 군을 산부식만 시행한 경우(1군), air-abrasion만 시행한 경우(2군), 산부식 후 결합제를 적용한 경우(3군), air-abrasion 후 결합제를 적용한 경우(4군)로 나눠 각각의 치아를 표면처리한 후 치면열구전색제를 도포하였다. 고온$(55^{\circ}C)$과 저온$(5^{\circ}C)$에서 각각 30초씩 500회의 열순환을 시행한 뒤 미세누출도를 검사하여 다음과 같은 결과를 얻었다. 1. 치면열구전색제/치면열구전색제 경계면에서 미세누출도는 결합제 사용 유무에 관계없이 air-abrasion을 처리한 2군, 4군에서 산부식을 사용한 1군, 3군보다 낮은 값을 보였고(p<0.05) 1군과 2군, 3군과 4군 사이에는 통계적 유의차가 없었다(p>0.05). 2. 치면열구전색제/치아 경계면에서 미세누출도는 결합제를 사용한 3군, 4군에서 결합제를 사용하지 않은 1군, 2군보다 낮은 값을 보였고(p<0.05) 산부식을 사용한 1, 3군과 air-abrasion을 사용한 2, 4군 사이에는 통계적 유의차가 없었다(p>0.05). 3. SEM 상에서 치면열구전색제를 산부식 처리하였을 때 표면거칠기의 증가가 적었으나 air-abrasion 하였을 경우 표면거칠기가 현저하게 증가하는 것을 관찰하였다.
The restorations of the severely damaged teeth by post core have been increased with the developement of endodontic procedures. But high failure rates of these procedures being reported, various restorative modifications were induced for successful treatments. Cast post-core and prefabricated post with core buildups are choice of treatment. The main causes of failure of the restorations are the fracture of post and core, root fracture, and recurrent caries due to microleakage. Recently, the acid etching technique and the use of dentin bonding agent at tooth surface to reduce the possible microleakage at the tooth-restoration interfaces were introduced. The object of this study was to measure and compare the microleakage by the types and cementation methods of post-core. For this study, forty extracted human anterior teeth were selected for specimen. After cleansing and routine endodontic procedures, anatomic crowns of each specimen were removed at the level of 2mm above the cementoenamel junction. Canals were preparated for post insertion and specimens were divided into four groups randomly. Post-cores were fabricated according to method for each group. Microleakage was measured by length of dye penetration at the tooth-restoration interfaces with measuring microscope at 50 magnification. Oneway ANOVA and t-test were performed for statistical analysis of resulting data. The following results were obtained from this study. 1. There wert significant statistical differences in degree of microleakage between each group (p<0.01). 2. Cast post-core cemented with ZPC (Group I) showed the most severe microleakage pattern$(1.5547{\pm}0.0872mm)$, and cast post-core cemented with adhesive resin cement after tooth surface treatment with dentin bonding agent (Group II) showed the least microleakage $(0.1497{\pm}0.0872mm)$. 3. Group IV revealed less dye penetrations than group III, but no statistical significance was seen between two groups.
The toxic effect of adhesive resins on the dog's pulp tissue was studied with 70 teeth from 5 dogs. The experimental materials were Clearfil, a mixture of Clearfil with calcium hydroxide powder, Panavia-EX, and a mixture of Panavia-EX with calcium hydroxide powder. As a control group, calcium hydroxide powder was used. Each material was placed on the pulpotomized tissue surface. After 3 days, 1, 2,4, and 6 weeks, the teeth and apical tissue were processed routinly and stained with hematoxylin and eosin. Pathological tissue changes due to the toxicity of adhesive resins were observed by light microscope, and the pH of Panavia-EX and the Bonding agent of Clearfil were measured. Following were the results; 1. In the group of calcium hydroxide powder, slight inflammatory change was observed in the pulpotomized surface and adjacent pulp tissue on 3 day. 1 week case showed incomplete dentin bridge. The remaining pulp tissue was normalized according to the days elapsed. 2. In the group of Clearfil, early inflammatory change revealed in the superificial portion of the remaining pulp tissue on 3 day. The inflammation spreaded over the total pulp tissue and partial necrosis was observed in 1 week and 2 week cases. Total necrosis of pulp tissue and moderate inflammatory change at the apical tissue was noticed in 4 week and 6 week cases. 3. In the group of Panavia-EX, moderate inflammatory change appeared in the superficial pulp tissue on 3 day, and severe inflammatory change over all pulp tissue found in 1 week case. Pulp necrosis was obvious in 2 week case. 4 week and 6 week cases were totally necrotized up to the periapical tissue. 4. In the groups of mixtures with calcium hydroxide powder, the pulp tissue destruction was retarded, compared with the groups of Clearfil and Panavia-EX. 5. Panavia-EX was more destructive than Clearfil. 6. The acidity of freshly mixed Bonding agent of Cleafil was pH 4.0, and that of Panavia-EX was pH 2.0.
A variety of surface pre-treatments have been advocated to prepare the dentin prior to placement of a bonding agent. The purpose of this study was to evaluate the effect of various dentin conditioners upon the degree of resin impregnation to the dentinal tubules and the shear bond strength of a new dentinal bonding agent (Scotchbond 2) used in conjunction with a visible light cured composite (Silux). The healthy eighty human molars extracted due to periodontal or orthodontic reasons were used and randomly divided into five groups. All the grinded dentin surfaces were conditioned with 3% $H_2O_2$, Cavity Cleanser (Columbus/Bayer), Dentin Conditioner (GC Inter. Corp.), Scotchprep (3M Co.) according to the manufacturer's directions. The specimens were then demineralized in 10% HCl for 20 sec. and 24 hrs. in order to observe the resin tags in Hitachi X-450 scanning electron microscope at 25KV. Also, shear strengths were obtained using an Instron Testing Machine with a cross head speed of 1 mm/min. The following results were obtained ; 1. In group treating with Dentin Conditioner and Scotchprep, the resin strings were formed on most of the surfaces and penetrated more than $50{\mu}m$ into the tubules. 2. The inner surface of resin treated with Cavity Cleanser, indicating the resin strings formed partly and penetrated about in depth of $30{\mu}m$. 3. In control and experimental group treated with 3% $H_2O_2$, the resin tags were not formed, if any, penetrated shortly. 4. Shear bond strengths in groups treating with Dentin Conditioner and Scotchprep were statistically significant increase than with 3% $H_2O_2$. (P<0.01). 5. The Scotchprep treatment group was significantly higher in shear strength than groups treated with no conditioning and Cavity Cleanser.(P<0.01) 6. Shear bond strengths evaluated were gradually increase in proportion to the tag length of resin impregnation.
The purpose of this study was to evaluate on the interfacial morphology between dentin and restorative materials. In this in vitro study, the cavity wall restorated with 3 different kinds of tooth colored restorative materials [resin-modified Glass Ionomer cement (Fuji II LC), composite resin (Z-100), compomer (Dyract)]. The thirty extracted human molar teeth without caries and/or restorations are used. The experimental teeth were randomly divided into three groups of ten teeth each. In each group, Wedge shaped cavities (width: 3mm, length: 2mm, depth: 1.5mm) were prepared at the cementoenamel junction on buccal and lingual surfaces. The adhesive of composite resin were mixed with rhodamine B. Primer of composite resin, Prime & Bond 2.1 of Dyract and liquid of Fuji II LC were mixed with fluorescein. In group 1, the cavity wall was treatment with dentin conditioner, and then restorated with Fuji II LC. In group 2, the cavity wall was treatment with Prime & Bond 2.1 and then restorated with Dyract. In group 3, the cavity wall was etching with 10% maleic acid, applied with primer and bonding agent and then restorated with Z-100. The interface between dentin and restorative materials was observed by fluoresence imaging with a confocal laser scanning microscope. The results were as follows : 1. In Glass ionomer group, adaptation of resin modified Glass-ionomer restoration against cavity wall is tight, but the crack formed inside of restoration were observed. 2. In Dyract group, the penetration of resin tag is shorter and the width of hybrid layer is narrower than composite resin group. 3. In Z-100 group, primer penetrated deeply through dentinal tubule. Also bonding agent was penetrated along the primer, but the penetration length is shorter than primer part, and in 3-D image, the resin tag is conical shape and lateral branch is observed.
Objective: The aim of this study was to evaluate discoloration of teeth undergoing regenerative endodontic procedures (REPs) using blood clot or platelet-rich fibrin (PRF) as the scaffolds and different calcium silicate-based materials as the intracanal coronal barriers in an ex vivo model. Materials and Methods: Forty-eight bovine incisors were prepared and disinfected using 1 mg/mL double antibiotic paste (DAP). The specimens were then randomly divided into 2 groups (n = 24) according to the scaffolds (blood or PRF). After placement of scaffolds each group was divided into 2 subgroups (n = 12) according to the intracanal coronal barriers (ProRoot MTA or Biodentine). The pulp chamber walls were sealed with dentin bonding agent before placement of DAP and before placement of scaffolds. The color changes (${\Delta}E$) were measured at different steps. The data were analyzed using 2-way analysis of variance. Results: Coronal discoloration induced by DAP was not clinically perceptible (${\Delta}E{\leq}3.3$). Regarding the type of the scaffold, coronal discoloration was significantly higher in blood groups compared with PRF groups at the end of REP and after 1 month (p < 0.05). However, no significant difference was found between PRF and blood clot after 6 months (p > 0.05). Considering the type of intracanal coronal barrier, no significant difference existed between ProRoot MTA and Biodentine (p > 0.05). Conclusions: With sealing the dentinal tubules of pulp chamber with a dentin bonding agent and application of DAP as an intracanal medicament, coronal color change of the teeth following the use of PRF and blood sealed with either ProRoot MTA or Biodentine was not different at 6-month follow-up.
To investigate the bond strength of etched porcelain, porcelain specimens were etched by 5% hydrofluoric acid during the time of 2.5 min., 5 min., 7.5 min., and 10 min. at $23^{\circ}C$ and observed by SEM. Also, electrolytically etched metal was observed by SEM. Etched porcelain specimens were treated or were not treated with Silane coupling agent and bonded to etched metals with Comspan and Panavia. The bonded specimens were stored in water at $37^{\circ}C$. 24 hours after bonding, the bond strengths were measured. There were four groups of 25 specimens each. Group 1 was bonded with Panavia. Group 2 was bonded with Panavia after treated with Silane coupling agent. Group 3 was bonded with Comspan, Group 4 was bonded with Comspan after treated with Silane coupling agent. The results were as follows: 1. he etched porcelains were obviously observed by SEM. 2. The dendritic arms were observed in etched metal by SEM. 3. The bond strength in relation to the increase of etching time increased and an analysis of variance shows significantly different at the 0.01 level in all groups. 4. The bond strength of Silane coupling agent treated groups were higher than the untreated. 5. The ratios of increase of the bond strengths of Silane coupling agent treated groups in relation to the increase of etching of etching time were lower than the untreated. 6. The bond strength of the groups used Comspan were higher than Panavia.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.