• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.672-675
• /
• 2001

The Sr$\sub$0.8/Bi$\sub$2.4/Ta$_2$O$\sub$9/(SBT) thin films are deposited on Pt-coated electrode(Pt/TiO$_2$/SiO$_2$/Si) using RF magnetron sputtering method. With increasing annealing tempera ture from 600[$^{\circ}C$] to 850[$^{\circ}C$], Bi-layered perovskite phase was crystallized above 650[$^{\circ}C$]. The maximum remanent polarization and the coercive electric field is 11.60[${\mu}$C/$\textrm{cm}^2$], 48[kV/cm] respectively. The dielectric constant and leakage current density is 213, 1.01${\times}$10$\^$-8/ A/$\textrm{cm}^2$ respectively at annealing temperature of 750[$^{\circ}C$].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.565-568
• /
• 2001

We have fabricated $Bi_{3.25}La_{0.75}Ti_{3}O_{12}(BLT)$ thin(200nm) films on the $Pt/Ti/SiO_{2}/Si$ substrates using a MOD(Metalorganic decomposition) method with annealing temperature from $550^{\circ}C$ to $750^{\circ}C$. The structural properties of the films examined by x-ray diffraction. The layered-perovskite phase obtained above $600^{\circ}C$. Scanning electron micrographs showed uniform surface composed of rodlike grains. The grain size increased with increasing annealing temperature. The BLT thin films showed little polarization fatigue test up to $3.5{\times}10^{9}$ bipolar cycling at a 5V and 100kHz.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.565-568
• /
• 2001

We have fabricated $Bi_{3.25}$$La_{0.75}$ti$_3$O$_{12}$ (BLT) thin(200nm) films on the Pt/Ti/SiO$_2$/Si substrates using a MOD(Metalorganic decomposition) method with annealing temperature from 55$0^{\circ}C$ to 75$0^{\circ}C$. The structural properties of the films examined by x-ray diffraction. The layered-perovskite phase obtained above $600^{\circ}C$. Scanning electron micrographs showed uniform surface composed of rodlike grains. The grain size increased with increasing annealing temperature. The BLT thin films showed little polarization fatigue test up to 3.5x10$^{9}$ bipolar cycling at a 5V and 100kHz.kHz.

• Journal of the Korean Society of Safety
• /
• v.19 no.1
• /
• pp.72-76
• /
• 2004

The $Sr_{0.7}Bi_{2.6}Ta_2O_9$(SBT)thin films are deposited on pt-coated electrode(Pt/$TiO_2/SiO_2/Si$) using a RF magnetron sputtering method. The electrical properties of SBT capacitors with annealing conditions were studied. In the XRD pattern, the SBT thin films in all annealing temperatures had (105) orientation. In the SEM images, Bi-layered perovskite phase was crystallized at $750^{\circ}C$,/TEX> and grains largely grew in oxygen annealing atmosphere. The maximum renanent polarization and the coercive electric field with annealing conditions are 12.40C/$cm^2$ and 30kV/cm, respectively. The dielectric constant and leakage current density with Pt electrode is 340 and 2.13${\times}10^{-10}A/cm^2$, respectively.

• Journal of IKEEE
• /
• v.25 no.1
• /
• pp.37-41
• /
• 2021

In this paper, a low-profile and broadband bowtie antenna using multi-layer substrate for UWB sensor application is presented. A compact bowtie antenna is designed and implemented on two multi-layered substrate with total thickness of 4.5 mm. The antenna consists of bowtie radiator and planar-type balun. The designed radiator and balun are connected to each other so that it can be easily implemented in various structures. The implemented antenna provides 3 to 6 dBi of gain for whole frequency range from 6.8 to 10 GHz.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.6
• /
• pp.486-491
• /
• 2002

We have fabricated $Bi_{3.25}La_{0.75}Ti_3O_12$ (BLT) thin films on the Pt/Ti/$SiO_2$/Si substrates using a metalorganic decomposition (MOD) method with annealing temperature from $550^{\circ}C$ to $750^{\circ}C$. The structural properties of BLT films examined by x-ray diffraction (XRD). From XRD analysis. BLT thin films show polycrystalline structure. The layered-perovskite phase was obtained by spin-on films at above $600^{\circ}C$ for 1h. Scanning electron microscopy (SEM) showed uniform surface composed of rodlike grains. The grain size of BLT films increased with increasing annealing temperature. The BLT film annealed at $650^{\circ}C$ was measured to have a dielectric constant of 279, dielectric loss of 1.85(%), remanent polarization of $25.66\mu C/\textrm{cm}^2$, and coercive field of 84.75 kV/cm. The BLT thin films showed little polarization fatigue test up to $3.5{\times}10^9$ bipolar cycling at 5 V and 100 kHz.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2006.10a
• /
• pp.166-169
• /
• 2006

A promising capacitor, which has conformable step coverage and good uniformity of thickness and composition, is needed to manufacture high-density non-volatile FeRAM capacitors with a stacked cell structure. In this study, ferroelectric $Bi_{3.61}Nd_{0.39}Ti_3O_{12}$ (BNT) thin films were prepared on $Pt(111)/Ti/SiO_2/Si$ substrates by the liquid delivery system MOCVD method. In these experiments, $Bi(ph)_3$, $Nd(TMHD)_3$ and $Ti(O^iPr)_2(TMHD)_2$ were used as the precursors and were dissolved in n-butyl acetate. The BNT thin films were deposited at a substrate temperature and reactor pressure of approximately $600^{\circ}C$ and 4.8 Torr, respectively. The microstructure of the layered perovskite phase was observed by XRD and SEM. The remanent polarization value (2Pr) of the BNT thin film was $31.67\;{\mu}C/cm^2$ at an applied voltage of 5 V.

• Journal of the Korean Ceramic Society
• /
• v.42 no.4
• /
• pp.219-223
• /
• 2005

A promising capacitor, which has conformable step coverage and good uniformity of thickness and composition, is needed to manufacture high-density non-volatile FeRAM capacitors with a stacked cell structure. In this study, ferroelectric $Bi_{3.61}Nd_{0.39}Ti_3O_{12}$ (BNdT) thin films were prepared on $Pt(111)/TiO_2/SiO_2/Si$ substrates by the liquid delivery system MOCVD method. In these experiments, $Bi(ph)_{3}$, $Nd(TMHD)\_{3}$ and $Ti(O^iPr)_{2}(TMHD)_{2}$ were used as the precursors and were dissolved in n-butyl acetate. The BNdT thin films were deposited at a substrate temperature and reactor pressure of approximately $600^{\circ}C$ and 4.8 Torr, respectively. The microstructure of the layered perovskite phase was observed by XRD and SEM. The remanent polarization value (2Pr) of the BNdT thin film was $31.67\;{\mu}C/cm^{2}$ at an applied voltage of 5 V.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.8
• /
• pp.476-482
• /
• 2016

Convectional PZT based piezoelectric ceramics have to sinter at high temperature about $1,200^{\circ}C$ for their suitable electrical properties. However, some issues: low temperature sintering piezoelectric ceramic composition and reliable internal electrode, have recently attracted a great deal of interest as a highly efficient multi-layered piezoelectric ceramics. In order to optimize low temperature sintering conditions of thick-film PMN-PZ-PT ceramic, it was investigated sintering and piezoelectric properties according to the change of $LiBiO_2$ contents. Thus, the superior piezoelectric properties were found at the pallet type PMN-PZ-PT optimized with low sintering processing at $925^{\circ}C$ including 7 wt% $LiBiO_2$ sintering aid. Consequentially, we successfully manufactured thick-film PMN-PZ-PT ceramics, which had superior piezoelectric and dielectric properties, with 5 wt% of $LiBiO_2$ sintering aid at temperature of $900^{\circ}C$.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.533-534
• /
• 2006

1mm-thick BLT ceramics were sintered in accordance with a bulk ceramic fabrication process. All XRD peaks detected in the sintered ceramics were indexed as the Bi-layered perovskite structure without secondary phases. Density was increased with increasing the sintering temperature up to $1050\;^{\circ}C$ and the maximum value was about 98% of the theoretical density. The remanent polarization (2Pr) value of BLT ceramic sintered at $1050\;^{\circ}C$ was approximately $6.5\;{\mu}C/cm^2$ at the applied voltage of 4.5kV. From these results, a BLT ceramic target for plused laser deposition (PLD) system was successfully fabricated.