• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.4
• /
• pp.501-508
• /
• 1996

Strontium barium niobate powders were prepared by NaCl-KCl molten salt, and reaction process and morphology change of strontium barium niobate were investigated as a function of reaction temperature, time, and amount of molten salt. With increasing the reaction temperature and time, the reacted fraction was increased and the morphology of powder was changed from lumpy shape into meedle-like shape. With increasing the amount of molten salt, reacted fraction was increased rapidly, but the morphology of powder was changed from needle-like shape into spherical shape. Strontium barium niobate powder, over 90 % in fraction reacted, was obtained from the reaction conditions at $1000^{\circ}C$ for small flux ratio (=1) and at $650^{\circ}C$ for large flux ratio (=4).

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.169.1-169
• /
• 2002

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1167-1173
• /
• 2001

The tetragonal tungsten bronze type of Sr$_{x}Ba_{1-x}Nb_{2}O_{6}$(SBN) (0.3$\le$x$\ge$0.7) ceramics was synthesized by the solid state reaction method, and the dielectric properties of SBN ceramics as a function of Sr/Ba ratio were examined. With increasing Sr/Ba ratio in SBN ceramics, the Curie temperature decreased and the maximum dielectric constant at the Curie temperature increased. The relaxor behavior of the SBN ceramics as a function of Sr/Ba ratio was quantitatively evaluated. More relaxor behavior of dielectric characteristics was observed as the ratio of Sr/Ba increased. The experimental results are explained with a viewpoint of crystallography of tungsten bronze structured SBN ceramics.

• Journal of the Korean Physical Society
• /
• v.73 no.10
• /
• pp.1561-1565
• /
• 2018

The dielectric properties of the uniaxial relaxor ferroelectric $Sr_xBa_{1-x}Nb_2O_6$ with x = 0.75 were investigated along the polar [001] direction as a function of temperature. The capacitance maximum showed the frequency dispersion commonly observed in relaxors. Additional weak dielectric anomalies were observed in the paraelectric phase; they were only seen during the heating process and disappeared upon subsequent cooling. These were attributed to the existence of large polar clusters strongly pinned at defects and/or to random fields and their metastable characters. Aligning the ferroelectric domains along the polar axis at room temperature removed the high-temperature dielectric anomalies. The dependences of the capacitance and the dielectric maximum temperature on the magnitude of the poling field were investigated.

• Advances in materials Research
• /
• v.2 no.2
• /
• pp.77-91
• /
• 2013

High quality nanoparticles of neodymium barium niobium ($NdBa_2NbO_6$) perovskites have been synthesized using an auto ignition combustion technique for the first time. The nanoparticles thus obtained have been characterized by powder X-ray diffraction, thermo gravimetric analysis, differential thermal analysis, Fourier transform infrared spectroscopy, Raman spectroscopy and transmission electron microscopy. UV-Visible absorption and photoluminescence spectra of the samples are also recorded. The structural analysis shows that the nano powder is phase pure with the average particle size of 35 nm. The band gap determined for $NdBa_2NbO_6$ is 3.9 eV which corresponds to UV-radiation for optical inter band transition with a wavelength of 370nm. The nanopowder could be sintered to 96% of the theoretical density at $1325^{\circ}C$ for 2h. The ultrafine cuboidal nature of nanopowders with fewer degree of agglomeration improved the sinterability for compactness at relatively lower temperature and time. During the sintering process the wide band gap semiconducting behavior diminishes and the material turns to a high permittivity dielectric. The microstructure of the sintered surface was examined using scanning electron microscopy. The striking value of dielectric constant ${\varepsilon}_r=43$, loss factor tan ${\delta}=1.97{\times}10^{-4}$ and the observed band gap value make it suitable for many dielectric devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.1030-1035
• /
• 2001

Strontium barium niobate, (Sr$\sub$0.5/Ba$\sub$0.5/Nb$_2$O$\sub$6/), thin films of various composition were prepared by the sol-gel method. Solution derived from acetate powders and niobium ethoxide in a mixture of acetic acid, ethylene glycol and 2-methoxyehanol was spin-coated onto bare silicon, Pt-coated silicon and fused silica substrates. Processing parameters were optimized to develop stable solutions which yielded films with relatively low crystallization temperatures. It was determined that ethylene glycol was a necessary component of the solution to increase stability against precipitation and to decrease the crystallization temperature of the films as confirmed by XRD and FT-IR analyses.

• Journal of the Korean Ceramic Society
• /
• v.43 no.3 s.286
• /
• pp.173-176
• /
• 2006

${Sr_{1-x}Ba_xNb_2O_6$(SBN) have been obtained in Pt crucible by melting and cooling in air atmosphere. Some SBNs being at the bottom of the crucible are black and transparent, and the other SBNs colorless. The black SBN became to be colorless by oxidation heat treatment $1,300^{\circ}C$ for 4 h, Curie temperature is changed by colorless change of black SBN. The reason seems to be $Nb^{5+}$ oxidation of some $Nb^{4+}$ ions in SBN or effect of unknown impurities. Diffused Phase Transition (DPT) was appeared during heating and cooling process. Various sintered SBN ceramics specimen showed relaxor characteristics.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.248-249
• /
• 2005

The tungsten bronze type of strontium barium niobate(SBN) thin film was synthesized by metal organic decomposion method for SBN stock solution and the SBN thin film process were deposited by spin-coating process on Pt-deposited si-wafer(100) by magnetron sputtering system. The thickness of SBN thin film was 150$\sim$200 nm and were optimized for rpm of spin-coater system. The structural variation of SBN thin film was studied by TG-DTA and XRD. The deposited SBN stock solution on annealing at $400\sim800^{\circ}C$ a pure tungsten bronze SBN phase and the corresponding average grain size about 500$\sim$1000 nm influenced by annealing temperature.

• Korean Journal of Crystallography
• /
• v.1 no.1
• /
• pp.1-7
• /
• 1990

It is shown that the symmetry of the incommensurate phase in Ba2NaNb5O15(BSH) belongs to the four dimensional superspace group C from an analysis of the systematic extinction or the rxtra reflections due to the incommensllrate structure. The resulting superstructure is characterizetl by the space group Ima2(C3l) and the origin of the incommensurability in BSN is briefly discussed. Especially. HREM image have shown the prrscnce of discommensurations. In addition. a group-theoretical consideration of structural phase transitions in BSN is suggested.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.382-383
• /
• 2006

The tungsten bronze type of strontium barium niobate(SBN) thin film was synthesized by metal organic decomposion method for SBN stock solution and the SBN thin film process were deposited by spin-coating process on Pt-deposited si-wafer(100) by magnetron sputtering system. The thickness of SBN thin film was 150~200 nm and were optimized for rpm of spin-coater system. The structural variation of SBN thin film was studied by TG-DTA and XRD. The deposited SBN stock solution on annealing at $400{\sim}800^{\circ}C$ a pure tungsten bronze SBN phase and the corresponding. average grain size about 500~1000 nm influenced by annealing temperature. The piezoelectric properties of prepared SBN thin film, the remanent polarization value(2Pr) and coercive field was $1.2{\mu}C/cm^2$ and 2.15V/cm, respectively.