• ETRI Journal
• /
• v.35 no.6
• /
• pp.1156-1159
• /
• 2013

We investigate the characteristics of $Cu_2O$ thin films deposited through the addition of $N_2$ gas. The addition of $N_2$ gas has remarkable effects on the phase changes, resulting in improved electrical and optical properties. An intermediate phase ($6CuO{\cdot}Cu_2O$) appears at a $N_2$ flow rate of 1 sccm, and a $Cu_2O$ (200) phase is then preferentially grown at a higher feeding amount of $N_2$. The optical and electrical properties of $Cu_2O$ thin films are improved with a sufficient $N_2$ flow rate of more than 15 sccm, as confirmed through various analyses. Under this condition, a high bandgap energy of 2.58 eV and a conductivity of $1.5{\times}10^{-2}$ S/cm are obtained. These high-quality $Cu_2O$ thin films are expected to be applied to $Cu_2O$-based heterojunction solar cells and optical functional films.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.30A no.10
• /
• pp.59-66
• /
• 1993

PZT thin film deposited by rf magnetron sputtering was annealed by rapid thermal process(RTP) in PbO ambient to prevent vaporing of Pb and interface reactions. Si and TiN/Ti/Si substrates were prepared to survey application of TiN/Ti layer which can prevent interface interaction with Si and crack of PZT thin films. As temperature increased. PZT thin films surface on Si substrate appeared more severe cracks which should affect electrical properties deadly. TiN/Ti(40-150${\mu}{\Omega}{\cdot}cm$) layer applied for buffer layer suppressed interface interaction and film cracking. The measured leakage current(LC) and breakdown voltage(BV) of PZT thin film on TiN/Ti/Si substrate annealed at 650$^{\circ}$C for 15 sec (thickness of 2500$\AA$) were 38 nA/cm2 and 3.5 MV/cm and dielectric constant was 310 at 1 MHz, and remanent polarization (Pr) and coercive field (Ec) were 6.4${\mu}C/cm^{2}$ and 0.2MV/cm at 60 Hz, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.362-365
• /
• 2002

Hf thin films were deposited on bottom metal using a RF magnetron sputtering method followed by oxidation and annealing in O$_2$ and N$_2$ ambient, respectively. Various top metal electrodes (i.e., Al, Au, and Cu) were deposited by evaporation, and their roles on physical and electrical properties were investigated. Using the XRD, SEM and AFM techniques, we confirmed that the grain size of HfO$_2$ thin films enlarges as a function of oxidation temperature, increasing dielectric constant. However, other electrical properties (e.g., tan) deteriorateas a consequence. The dielectric constant and tan of HfO$_2$ thin films oxidized at 500 $^{\circ}C$ were 17-25 and 3${\times}$10-3 - 2x10-2, respectively, in the frequency range of 1 Hz to 1 MHz. The leakage current density was less than 1${\times}$10-8A/cm2 up to 0.7 MV/cm. In addition, electrical properties of HfO$_2$ thin films (e.g., the dielectric constant, leakage current and tan $\delta$) depend on top metal electrode. We showed that Al top metal electrode results in the best result.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.4
• /
• pp.280-286
• /
• 2010

We have investigated the influence of rapid thermal annealing (RTA) temperature on properties of Al-doped zinc oxide (AZO) thin films deposited on glass substrate by using radio-frequency magnetron sputtering. The RTA is performed in a nitrogen ambient in the temperature range from 300 to $600^{\circ}C$ for 1 minute in a rapid thermal annealer after growing the AZO thin films. The crystallographic structure and the surface morphology of AZO thin film are measured by using X-ray diffraction, and atomic force microscopy and scanning electron microscopy, respectively. The optical transmittance of the deposited thin films is examined in the wavelength range of 300-1100 nm, where the average transmittance is above the 90% in the visible and near-infrared regions. The optical bandgap is calculated from the Tauc's model, and it shows a significant dependence on the RTA temperature. As for the electrical properties of the thin films, the AZO thin film annealed at $400^{\circ}C$ shows the lowest electrical resistivity of $8.6{\times}10^{-3}{\Omega}cm$ and the Hall mobility of $11.3cm^2$/V-sec. These results suggest that the RTA temperature is an important parameter to influence on the structural, electrical, and optical properties of AZO thin films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.8
• /
• pp.701-706
• /
• 2006

In addition to its similarity to genuine diamond film, diamond-like carbon (DLC) film has many advantages, including its wide band gap and variable refractive index. In this study, DLC films were prepared by the RF PECVD (Plasma Enhanced Chemical Vapor Deposition) method on silicon substrates using methane $(CH_4)$ and hydrogen $(H_2)$ gas. We examined the effects of the post annealing temperature on the structural variation of the DLC films. The films were annealed at temperatures ranging from 300 to $900^{\circ}C$ in steps of $200^{\circ}C$ using RTA equipment in nitrogen ambient. The thickness of the film and interface between film and substrate were observed by surface profiler, field emission scanning electron microscopy (FESEM), high resolution transmission electron microscopy (HRTEM), respectively. Raman and X-ray photoelectron spectroscopy (XPS) analysis showed that DLC films were graphitized ($I_D/I_G$, G-peak position and $sp^2/sp^3$ increased) ratio at higher annealing temperature. The variation of surface as a function of annealing treatment was verified by a AFM and contact angle method.

• Journal of the Korean Ceramic Society
• /
• v.43 no.5 s.288
• /
• pp.265-269
• /
• 2006

We have deposited NiO films by RF sputtering on $Al_2O_3/SiO_2/Si$ and 100 nm-thick Gd doped $CeO_2$ covered $Al_2O_3/SiO_2/Si$ substrates at various $Ar/O_2$ ratios. The deposited films were reduced to form porous Ni thin fllms in 4% $H_2\;at\;400^{\circ}C$. For the films deposited in pure Ar, the reduction was retarded due to the thickness and the orientation of the NiO films. On the other hand, the films deposited in oxygen mixed ambient were reduced and formed porous Ni films after 20 min of reduction. We also investigated the possibility of using the films for the single chamber operation by studying the electrical property of the films in the fuel/air mixed environment. It is shown that the resistance of the Ni film increases quickly in the mixed gas environment and thus further improvements of Ni-base anodes are required for using them in the single chamber operation.

• Proceedings of the IEEK Conference
• /
• 2006.06a
• /
• pp.471-472
• /
• 2006

The passivation technology is very important, because this technology can protect a device against the influence of ambient environment, and prevent the performance reduction. In this paper, we fabricated the $0.1{\mu}m\;{\Gamma}$-gate InAlAs/InGaAs metamorphic high electron mobility transistors (MHEMTs) on GaAs substrates using the low-k benzocyclobutene (BCB) and $Si_3N_4$ as a passivation and we performed the comparisons of characteristics of the MHEMTs. After passivation, the DC and RF measurement results were decreased either the conventional Si3N4 or BCB layers. The decrement of the BCB passivation was smaller than the $Si_3N_4$ passivation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.235-238
• /
• 1998

Ferroelectric $LiNbO_3$ thin films were grown directly on Si(100) substrates by 13.55MHz RF magnetron sputtering system using a ceramic target ($Nb_2O_5/Li_2C0_3$ = 51.4/48.6). Because high temperature process have to avoided to prevent degradation of the interface (insulator/Si), $LiNbO_3$ thin films were deposited below $300^{\circ}C$. After as-deposited films were performed RTA treatments in an oxygen ambient at $600^{\circ}C$ for 60s, electrical measurements performed films before and after anneal treatment. In high field region, the leakage current density of the films after annealing was deceased about 4order and the resistivity of these was increased to about 5\times 10^{11} \Omega \cdot cm$ at 500kV/cm. In accumulation region of C-V curve, we calculated dielectric constant of thin film $LiNbO_3$ as 27.9 which is close to that of bulk value.

• Applied Science and Convergence Technology
• /
• v.26 no.2
• /
• pp.26-29
• /
• 2017

Thin films of europium-doped yttrium oxide ($Y_2O_3$:Eu) were prepared on Si (100) substrates by using a radio frequency (RF) magnetron sputtering. After the deposition, the films were annealed at $1000^{\circ}C$ in an air ambient for 1 hour. X-ray diffraction analysis revealed that the $Y_2O_3$:Eu films had a polycrystalline cubic ${\alpha}-Y_2O_3$ structure. The as-deposited films showed no photoluminescence (PL), which was due to poor crystalline quality of the films. The crystallinity of the $Y_2O_3$:Eu films was significantly improved by annealing. The strong red PL emission was observed from the annealed $Y_2O_3$:Eu films and the highest intensity peak was centered at around 613 nm. This emission peak originated from the $^5D_0{\rightarrow}^7F_2$ transition of the trivalent Eu ions occupying the $C_2$ sites in the cubic ${\alpha}-Y_2O_3$ lattice. The broad PL excitation band was observed at wavelengths below 280 nm, which was attributed to the charge transfer transition of the trivalent Eu ion.

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.38C no.9
• /
• pp.781-786
• /
• 2013

Multiplexing information over parallel data channels based on RF MIMO concept is possible to achieve considerable data rates over large transmission ranges with just a single transmitting element. Visual multiplexing MIMO techniques will send independent streams of bits using the multiple elements of the light transmitter array and recording over a group of camera pixels can further enhance the data rates. The proposed system is a combination of the reliance on computer vision algorithms for tracking and OOK cell frame modulation. LED array are controlled to transmit message in the form of digital information using ON-OFF signaling with ON-OFF pulses (ON = bit 1, OFF = bit 0). A camera captures image frames of the array which are then individually processed and sequentially decoded to retrieve data. To demodulated data transmission, a motion tracking algorithm is implemented in OpenCV (Open source Computer Vision library) to classify the transmission pattern. One of the most advantages of proposed architecture is Computer Vision (CV) based image analysis techniques which can be used to spatially separate signals and remove interferences from ambient light. It will be the future challenges and opportunities for mobile communication networking research.