• 공업화학
• /
• 제7권3호
• /
• pp.536-542
• /
• 1996

본 연구에서는 유화중합을 통해 water jet loom용 경사 호제인 비용제형 수용성 아크릴 호제(GSW-7000)를 합성하였다. 이 호제는 아크릴계 호제의 암모늄염 형태로 제조되어 weaving force에 대한 저항력과 water jet loom 사용에 있어 물에 대한 저항력이 우수하였다. 제조한 GSW-7000은 sizing에 적당한 점도를 가지고 있고, 신도와 접착력, 용해성, 침투성 및 호부착성이 우수하였다. 또한 본 호제로 처리된 호부사는 접착강도가 높아 기존 용제형 아크릴 호제에 비하여 sizing시 호제 소모량을 70~80% 수준으로 저하시켜도 우수한 집속성 및 포합력을 나타내었으며, 호피막이 유연하며 평활성 및 내마모성이 우수하여 호부시 유제 및 대전 방지제를 사용하지 않아도 sizing 및 제직이 가능하였다.

• 구강회복응용과학지
• /
• 제16권1호
• /
• pp.27-36
• /
• 2000

One of the methods to improve the softness and comfortness of denture base is the use of soft denture liners. In this study, specimens were made by 2 kinds of acrylic based soft lining materials and 2 kinds of silicone based soft lining materials, and bonded to acrylic resin(Lucitone $199^{(R)}$). Then they were tested the differences of tensile bond strengths according to the materials, thickness, surface treatment and failure mode. 1. Tensile bond strength according to soft lining materials was increased in order of Coe-$soft^{(R)}$, $Mollosil^{(R)}$, $Trusoft^{(R)}$, Ufi-Gel $C^{(R)}$. The differences between groups were statistically significant at level of 0.05. 2. Tensile bond strength according to thickness of soft lining materials was increased in order of 3mm, 2mm, 1mm. The differences between groups were not statistically significant. 3. Tensile bond strength of treated surface showed higher bond strength than nontreated surface. The difference between groups was not statistically significant. 4. The failure mode of Coe-$soft^{(R)}$, $Trusoft^{(R)}$, $Mollosil^{(R)}$ were mainly cohesive failure, and that of Ufi-Gel $C^{(R)}$ were mainly adhesive failure.

• 접착 및 계면
• /
• 제5권4호
• /
• pp.1-8
• /
• 2004

다이싱 테이프에 사용되는 UV경화형 점착제를 아크릴 공중합체를 butyl acrylate, acrylic acid, methyl methacrylate를 용액 중합을 통해 중합한 뒤, trimethylolpropane triacrylate를 블렌딩하여 제조하였다. 제조된 점착제는 UV 조사량에 따라 접착력, 유리전이온도 ($T_g$)를 측정하였는데 UV 조사량이 증가할수록 접착력은 급격하게 감소하였고 $T_g$도 증가하였다. 웨이퍼 표면에 점착 샘플을 부착하여 UV 조사 후 박리하여 표면을 관찰한 결과 점착잔류물을 남기지 않았다.

• 접착 및 계면
• /
• 제4권4호
• /
• pp.7-14
• /
• 2003

택(tack)은 아주 가벼운 힘으로 단시간에 피착체와 점착하는 능력이다. 택의 측정기기 중 프로브택(probe tack)은 실험적인 영향인자를 설정할 수 있기에 택의 이론적 고찰이 유리하다. SIS계 핫멜트형 점착제(SIS-based hotmelt PSA)와 수분산성 아크릴 점착제(Water-borne acrylic PSA)를 사용하여 probe가 점착제 표면에 다가가는 속도가 택에 미치는 영향을 살펴보았다.

• 보존과학연구
• /
• 통권29호
• /
• pp.183-197
• /
• 2008

Paraloid B-72 of acrylic resins has been widely used as consolidant for bronze artifacts conservation. In previous study, xylene was appropriate for paraloid B-72 when bronze artifacts consolidated. In this study, we compared the coating properties of paraloid B-72 in various concentration levels. The surface before and after coating were observed by optical microscope and AFM. Thickness and adhesive strength of films were tested. For testing coating stability, we performed yellowing test and EIS. After these experiments, we concluded 15wt% paraloid B-72 was adequate concentration for bronze artifacts conservation when paraloid B-72 used in xylene as solvent. Because 15wt% paraloid B-72 has the lowest polarity and high hydrophobic.

• 한국섬유공학회:학술대회논문집
• /
• 한국섬유공학회 1994년도 추계 학술발표회
• /
• pp.137-138
• /
• 1994

Anionic water dispersible copolyesters were synthesized and characterized. Viscosity of the copolyester is lower than that of routine acrylic water dispersible polymers. Adhesive force of the copolyester was much higher than that of water dispersible acrylic polymers. Particle size of the copolyesters in water decreased with the increase of DMS or DEG feed ratio. With the conclusive study of the data of particle size and potential, it was found that the dispersion stability of copolyesters in water increased with the increase of DMS or DEG feed ratio. Judging from the results of potential and particle size of copolyesters, there seems to be competition between two dispersion stability factors, i.e. electrostatic stabilization and steric stabilization and as a result, morphological change of particles occurrs. Tg decreased with the increase of DEG molar feed ratio or oil contents.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2000년도 가을 학술발표회 논문집(II)
• /
• pp.1121-1126
• /
• 2000

The purpose of this study is to clarify chemical resistance of polymer-cement slurry coated reinforcing bars. Polymer cement slurry coated reinforcing bars were showed the good state to the bending resistance, impact resistance, adhesive strength, but exact data of the chemical resistance do not exist. Through the experimental, it is to certify chemical resistance of polymer cement slurry coated reinforcing bars. In this study, polymer cement slurry coated reinforcing bars are prepared with two types of polymer, polymer-cement ratios of 50%, 100%, 150%, coating thickness, curing periods of 3, 7, 28days, and tested for chemical resistance as KS(Korea Standard). From the test results, chemical resistance of polymer cement slurry coated reinforcing bars used by acrylic and St/BA emulsion were showed excellent without concerned polymer-cement ratios, curing period except for 1% aqueous solution $H_2SO_4$. But polymer cement coated reinforcing bar used by acrylic emulsion is inferior to aqueous solution NaOH.

• 한국잠사곤충학회지
• /
• 제47권1호
• /
• pp.41-47
• /
• 2005

1. 가야금 줄의 내구성을 향상시키기 위하여 가야금 줄에 acrylic adhesive와 poly(vinyl alcohol)을 병용 처리한 결과 강려과 신도는 차이가 없었으나 하중 70%에서 절단할때까지의 반복회수는 화학가공처리 현이 무 처리한 현보다 48% 향상되었으므로 현의 내구성을 크게 향상시킬 수 있었으나 흡습율이 무처리 현보다 높았다. 2. 현의 내구성을 증대시키고 음량을 풍부하게 할 목적으로 생사와 polyester사의 혼합비율을 달리하면서 생사/폴리에스텔 복합현을 제조하고 물성을 조사한 결과 polyester사의 비율이 많아질수록 강력이 감소하였고 신도는 증가하여 가야금 줄로서 적당하지 않았으나 mono filament 사로서 강력이 우수한 polyester사를 사용하여 복합현을 만든 SSP 복합현의 경우 생사로 만든 현보다 강력이 우수하였다. 3. 새로운 현의 소재를 개발하기 위하여 생사(가잠사)와 작잠사와의 복합현을 제조하고 그 물성을 조사한 결과 가잠사/작잠사 복합현의 강력은 작잠사와 비율이 많아질수록 저하되었다.

• 보존과학회지
• /
• 제37권2호
• /
• pp.135-143
• /
• 2021

목재 문화재의 결손부 보존처리는 동일 수종의 목분, 목재를 성형 후, 천연 접착제 또는 합성수지와 혼합하여 결실 부위를 충전하는 방식으로 접착한다. 그러나 대상의 종류와 상태에 따라 사용하는 접착제 및 첨가제의 농도, 혼합비율이 다양하게 나타난다. 이에 본 연구에서는 수피가 들뜨고 분리된 상태의 국립현대미술관 소장품을 대상으로 보존처리에 적합한 충전제 조건을 알아보기 위한 평가를 진행하였다. 건조속도, 수축·팽창률, 물리적 변형 정도를 기준으로 접착제별 최적 충전 조건을 선정하고, 실제 적용성을 확인하기 위해 해당 충전제들을 목재에 적용한 후 고습 환경에 노출하여 단면을 관찰하였다. 충전제는 아교, PVAc 접착제, Acryl 접착제 순으로 안정적인 적용 결과를 보였다. 결론적으로 수피가 들뜬 목제 조각품을 보존처리 시, 적합한 충전제는 아교와 목분 1 : 2 비율의 혼합물로 확인되었다. 이번 연구 결과를 통하여 목제 조각품의 들뜨고 분리된 수피를 안정화하는 적절한 방법을 제시하고, 향후 유사한 상태의 수피부 보존처리에 도움이 될 것으로 기대한다.

• Elastomers and Composites
• /
• 제52권1호
• /
• pp.22-26
• /
• 2017

The thermal conductivity and the adhesive properties were measured, after synthesis of thermal conductive composite which was obtained as a result of mixing alumina or graphite with acrylic adhesive synthesized by UV polymerization. The adhesive properties of the composite were evaluated measuring the peel strength at 180 degrees, the retention, and the initial tack;the thermal conductivity was estimated using laser flash analysis. As the filler contents increased, a decrease in peel strength and initial tack and an increase in retention and thermal conductivity were observed. When compared to alumina, the adhesion of graphite showed a dramatic decrease, whereas the thermal conductivity was further enhanced. It was found out that the small size of graphite increased the mechanical interlocking between the polymer and the filler, and it was easier for graphite to come into contact with other graphite in the matrix.