• Journal of the Korean Society of Propulsion Engineers
• /
• v.14 no.5
• /
• pp.45-50
• /
• 2010

Thermal analyses have been performed to study the effect of location of fuel ring and thermal barrier coatings in regenerative cooling channels in a full-scale combustor. For the effective cooling, the fuel ring has better be installed near axial location of the low expansion ratio and low heat flux, and branching of cooling channels is preferable. Also, the radiative cooled nozzle extension is thought to be reasonable for the cooling of combustor walls. Among the possible coatings, $Y_2O_3$ stabilized $ZrO_2$ coating and Ni/Cr coating have been adopted. Compared with Ni/Cr coating which has high oxidation resistance, $Y_2O_3$ stabilized $ZrO_2$ coating, one of ceramic coatings is found to be much effective to sustain the thermal survivability of combustion walls.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2010.05a
• /
• pp.145-149
• /
• 2010

Thermal analyses have been performed to study the effect of location of fuel ring and thermal barrier coatings in regenerative cooling channels in a full-scale combustor. For the effective cooling, the fuel ring has better be installed near axial location of the low expansion ratio and low heat flux, and branching of cooling channels is preferable. Also, the radiative cooled nozzle extension is thought to be reasonable for the cooling of combustion walls. Among the possible coatings, $Y_2O_3$ stabilized $ZrO_2$ coating and Ni/Cr coating have been adopted. Compared with Ni/Cr coating which has high oxidation resistance, $Y_2O_3$ stabilized $ZrO_2$ coating, one of ceramic coatings is found to be much effective to sustain the thermal survivability of combustion walls.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.10
• /
• pp.2835-2840
• /
• 2010

A series of $MoO_3/CeO_2-ZrO_2$ catalysts with different Mo content (8 - 20 wt %) were prepared by simple co-precipitation followed by impregnation method and were characterized by X-ray diffraction (XRD), infrared spectroscopy (IR), scanning electron microscopy (SEM), energy dispersive spectroscopic (EDS) techniques. The prepared materials were tested for catalytic activity by the synthesis of benzimidazole derivatives using condensation of aromatic aldehydes and o-phenylenediamine by conventional and microwave method. Obtained results reveal that the catalytic activity increases with increase in Mo wt % loading. The best catalytic activity was obtained with 20 wt % $MoO_3/CeO_2-ZrO_2$. The particle size or crystallite size was estimated using Debye-Scherrer equation. After completion of reaction, the catalyst can be recovered efficiently and reused with consistent activity.

• Korean Journal of Materials Research
• /
• v.4 no.5
• /
• pp.510-515
• /
• 1994

Yttria-stabilized zirconia(YSZ) films were prepared onto p-type (100) silicon wafer by a plasma-enhanced metallorganic chemical vapor deposition(PE MO CVD) processing involving the application of vapor mixture of tri(2.2.6.6-tetramethyl-3, 5-heptanate) yttrium$[Y(DPM)_3]$, zirconiumtriflouracethyla cetonate$(Zr(tfacac)_4$ and oxygen gas. The x-ray diffraction(XRD) and fourier transform infrared spectra(FT1R) results showed that the deposited YSZ films had a single cubic phase. $Y_2O_3$ content of YSZ film was analyzed by PIXE(partic1e induced x-ray emission). The experimental results by PIXE revealed that 12.lmol%, 20.4mol% and 31.6mol% $Y_2O_3$ could be obtained as the $Y(DPM)_3$ bubbling temperature varied at $160^{\circ}C, 165^{\circ}C$ and $170^{\circ}C$ respectively. The increase of $Y(DPM)_3$ bubbling temperature caused shifting flat band voltage to have a negative value.

• Journal of Surface Science and Engineering
• /
• v.42 no.6
• /
• pp.256-259
• /
• 2009

The wafer surface temperature is an important parameter in the etching process which influences the reaction probabilities of incident species, the vapor pressure of etch products, and the re-deposition of reaction products on feature surfaces. In this study, we investigated all of the effects of substrate temperature on the etch rate of $ZrO_2$ thin film and selectivity of $ZrO_2$ thin film over $SiO_2$ thin film in inductively coupled plasma as functions of $Cl_2$ addition in $BCl_3$/Ar plasma, RF power and dc-bias voltage based on the substrate temperature in range of $10^{\circ}C$ to $80^{\circ}C$. The elements on the surface were analyzed by x-ray photoelectron spectroscopy (XPS).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.48-49
• /
• 2008

본 실험에서는 대향 타겟식 스퍼터링 (face target sputtering, FTS) 장비를 사용하여 플렉서블 디스플레이용 poly ethylene naphthalate (PEN) 플라스틱 기판 위에 보호층으로 사용된 $ZrO_2$ 박막의 특성들에 대해 연구하였다. FTS에 의해 3 시간동안 증착된 $ZrO_2$ 박막의 기판 온도는 $69^{\circ}C$ 로 낮은 증착 온도를 나타내었으며, 이는 유리전이온도가 낮은 PEN 과 같은 플라스틱 기판위에 박막 증착시 적용하기에 적합하다. 제작된 $ZrO_2$ 박막에서 기판 중심으로부터 거리의 함수로 측정된 박막의 두께 차이는 약 4.5%로 매우 균일한 두께를 갖는 것으로 측정되었다.

• Bulletin of the Korean Chemical Society
• /
• v.17 no.3
• /
• pp.274-278
• /
• 1996

Vanadium oxide-zirconia catalysts were prepared by dry impregnation of powdered Zr(OH)4 with aqueous solution of NH4VO3. The characterization of prepared catalysts was performed using 51V solid state NMR, XRD, and DSC. The addition of vanadium oxide up to 9 mol% to zirconia shifted the phase transitions of ZrO2 from amorphous to tetragonal toward higher temperatures due to the interaction between vanadium oxide and zirconia. On the basis of results of XRD and DSC, it is concluded that the content of V2O5 monolayer covering most of the available zirconia was 9 mol%. The crystalline V2O5 was observed only with the samples containing V2O5 content exceeding the formation of complete monolayer (9 mol%) on the surface of ZrO2.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.1
• /
• pp.22-26
• /
• 2008

Red long persistent phosphors of $CaZrO_3$ : Pr was synthesized by a solid reaction method. $CaCO_3\;and\;ZrO_2$ were used as hosting materials and Pr was doped as luminescence center element, and $B_2O_3$ was used as flux. The XRD pattern confirmed crystalline phase of the phosphor, and photoluminescence investigation showed emission spectrum at $480{\sim}570nm\;and\;590{\sim}700nm$. Phosphor samples were synthesized with $B_2O_3$ flux concentration of 1, 5, 10%, and luminescent peak of maximum intensity at 494 nm was obtained for 1% $B_2O_3$. Luminescent peak of red color at 620 nm was of highest intensity for 10% $B_2O_3$.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.506-513
• /
• 2010

The composite coatings of $(ZrO_2-8Y_2O_3)$/(Ni-22Cr-10Al-1Y) were prepared by the air plasma spraying method. They consisted of (Ni,Cr)-rich regions,$(ZrO_2-Y_2O_3)$-rich regions, and $Al_2O_3$-rich regions that were formed by oxidation of Al from (Ni-22Cr-10Al-1Y) during spraying. The coatings corroded at 800 and $900^{\circ}C$ in NaCl-$Na_2SO_4$ molten salts up to 50 hr. Ni, Cr and Al oxidized to NiO, $Cr_2O_3$ and ${\alpha}-Al_2O_3$, respectively. These oxides and $(ZrO_2-Y_2O_3)$ were dissolved off into the molten salts during hot corrosion, which resulted in the ever-lasting corrosion of the composite coatings. Chromium diffused out from the (Ni,Cr)-rich regions and oxidized to $Cr_2O_3$, which was most frequently found as surface scales. Aluminum retained in the (Ni,Cr)-rich regions were similarly diffused out.

• Journal of Powder Materials
• /
• v.4 no.1
• /
• pp.9-17
• /
• 1997

The mullite-zirconia composites were prepared by the pressureless sintering with addition of 10~20 vol% ZrO$_2$(TZ3Y) in the fused mullite and sol-gel mullite matrix. The densification rate of sol-gel mullite was higher than that of fused mullite, and the addition of ZrO$_2$(TZ3Y) was effective on the densification of fused mullite. The enhancement of densification and anisotropic growth of mullite in ZrO$_2$added specimen can be explained by the solid solution effect of $Zr^{+4}$ ion in mullite. Both mechanical strength and fracture toughness of mullite-zirconia composite were enhanced compared to those of mullite. The enhancement of mechanical properties is attributed to the hinderance of grain growth and the combined toughening effects of tetra-mono phase transformation and crack deflection due to the residual stress between mullite/ZrO$_2$.