• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.985-994
• /
• 1996

The initiation and growth of $\alpha$-Al2O3/metal composites by the directed oxidation of molten commercial AlZnMg-alloy at 1223-1423K were investigated. Spontaneous bulk growth did not occur on the alloy alone. but the uniform initiation and growth of the composite were obtained by putting a thin layer of SiO2 particles on the surface of the alloy. Without SiO2 the external surface of the oxide layer was convered by MgO and MgAl2O4. But with the SiO2 reaction initiate the porous ZnO layers were found on the growth surface. The higher process temperature yielded a lower metal content. The oxidation product of $\alpha$-Al2O3 was found to be oriented with c-axis parallel to th growth direction. The growth rates increased with temperature and the apparent activation energy was 111.8 kJ/mol.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.47-50
• /
• 2002

ZnO nanowires were coated conformally with aluminum oxide ($Al_{2}O_{3}$) material by atomic layer deposition (ALD). The ZnO nanowires were first synthesized on a Si (100) substrate at $1380^{\circ}C$ from ball-milled ZnO powders by a thermal evaporation procedure with an argon carrier gas without any catalysts; the length and diameter of these ZnO nanowires are $20\sim30{\mu}m$ and $50{\sim}200$ nm, respectively. $Al_{2}O_{3}$ films were then deposited on these ZnO nanowires by ALD at a substrate temperature of $300^{\circ}C$ using trimethylaluminum (TMA) and distilled water ($H_{2}O$). Transmission electron microscopy (TEM) images of the deposited ZnO nanowires revealed that 40nm-thick $Al_{2}O_{3}$ cylindrical shells surround the ZnO nanowires.

• Journal of the Korean Vacuum Society
• /
• v.20 no.2
• /
• pp.141-145
• /
• 2011

ZnO:Al thin films were deposited by RF magnetron sputtering with various base pressure, and their structural, optical, and electrical properties were studied. The influence of the base pressure on the ZnO:Al thin film was confirmed and a high-quality thin film was obtained by controlling the base pressure. In all Al-doped ZnO thin films, the preferred orientation of (002) plane was observed and light transmittance in visible region (400 nm~800 nm) had above 85%. With decreasing of base pressure, crystallinity, resistivity, and figure of merit were improved. The improvement of resistivity with base pressure was attributed to the change of grain size.

• Korean Journal of Materials Research
• /
• v.21 no.2
• /
• pp.120-124
• /
• 2011

Silicon heterojunction solar cells have been studied by many research groups. In this work, silicon heterojunction solar cells having a simple structure of Ag/ZnO:Al/n type a-Si:H/p type c-Si/Al were fabricated. Samples were fabricated to investigate the effect of transparent conductive oxide growth conditions on the interface between ZnO:Al layer and a-Si:H layer. One sample was deposited by ZnO:Al at low working pressure. The other sample was deposited by ZnO:Al at alternating high working pressure and low working pressure. Electrical properties and chemical properties were investigated by light I-V characteristics and AES method, respectively. The light I-V characteristics showed better efficiency on sample deposited by ZnO:Al by alternating high working pressure and low working pressure. Atomic concentrations and relative oxidation states of Si, O, and Zn were analyzed by AES method. For poor efficiency samples, Si was diffused into ZnO:Al layer and O was diffused at the interface of ZnO:Al and Si. Differentiated O KLL spectra, Zn LMM spectra, and Si KLL spectra were used for interface reaction and oxidation state. According to AES spectra, sample deposited by high working pressure was effective at reducing the interface reaction and the Si diffusion. Consequently, the efficiency was improved by suppressing the SiOx formation at the interface.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.66 no.10
• /
• pp.1488-1493
• /
• 2017

Boron-doped ZnO:Al films were deposited by rf magnetron sputtering. The structural and optical property variations of the films with the boron amounts were studied. ZnO nanorods were grown on $SiO_2/Si$ wafers and glass by a hydrothermal method. ~50 nm-thick boron-doped ZnO:Al films were deposited on the substrates as seed layers. The mixed solution of zinc nitrate hexahydrate and hexamethylenetetramine in DI water was used as a precursor for ZnO nanorods. The concentration of zinc nitrate hexahydrate and that of hexamethylenetetramine were 0.05 mol, respectively. ZnO nanorods were grown at $90^{\circ}C$ for 2 hours. X-ray diffraction was conducted to observe the crystallinity of ZnO nanorods. A field emission scanning electron microscope was employed to study the morphology of nanorods. Optical transmittance was measured by a UV-Vis spectrophotometer, and photoluminescence was carried out with 266 nm light. The ZnO nanorods grown on the 0.5 wt% boron-doped ZnO seed layer showed the best crystallinity.

• Electrical & Electronic Materials
• /
• v.10 no.1
• /
• pp.33-38
• /
• 1997

The green emitting phosphors of the Field Emission Display(FED), Al codoped ZnGa$_{2}$O$_{4}$:Mn, were synthesized and sintered at high temperature. From X-ray diffraction measurements, it was confirmed that poly crystalline ZnGa$_{2}$O$_{4}$ and ZnAI$_{2}$O$_{4}$ solid solution coexist in Al codoped ZnGa$_{2}$O$_{4}$:Mn. Photoluminescence spectra of Al codoped ZnGa$_{2}$O$_{4}$:Mn show that the main peak position is shifted from 504 nm to 513 nm with the increase of Al concentration. The brightness was improved with the amount of Al dopant. It showed the maximum value at the doping level of 0.03 mole and then, it degraded rapidly. These results are due to the superposition of emission from . ZnGa$_{2}$O$_{4}$:Mn and ZnAI$_{2}$O$_{4}$:Mn.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.2
• /
• pp.31-34
• /
• 2018

In this study, the feasibility of ZnO/Al/ZnO flexible transparent electrodes for future flexible optoelectronic devices was investigated. All depositions were performed on PET substrates. The thicknesses of the top and bottom ZnO layers were 5-70 nm and 2.5-20 nm, respectively. The highest visible light transmittance was recorded when the thicknesses of the top and bottom ZnO layers 30 nm and 2.5 nm, respectively. 62% optical transmittance (at the wavelength of 400 nm) and sheet resistance of $19{\Omega}/{\Box}$ were measured. After repetitive bending test at a curvature radius of 5 mm, the transmittance and sheet resistance did not change.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.49.2-49.2
• /
• 2009

투명전극은 디스플레이, 태양전지와 같은 광전자 소자에 필수적이며, 지금까지 개발된 재료 중에는 ITO가 가장 투명하면서 전기전도도가 높고 생산성도 좋기 때문에 투명전극의 재료로 사용하고 있다. ITO는 낮은 비저항(${\sim}10^{-4}{\Omega}cm$) 과 높은 투과율 (~85 %), 상대적으로 넓은 밴드갭 에너지 (3.5 eV) 의특성과 같이 뛰어난 전기적 광학적 특성에 반해서 높은 원자재 가격, 불안정한 공급량 등으로 인한 문제점이꾸준히 제기되고 있다. 따라서 $In_2O_3$:Sn, ZnO:Al, ZnO:Ga, ZnO:F, ZnO:B, TiN 등과 같은 물질들로대체하려는 연구가 활발하게 진행되고 있다. ZnO는 ITO보다원자재의 수급이 원활하기 때문에 원가가 낮으며, 상대적으로 낮은 온도에서도 제작이 가능하다. 또한 화학적으로 안정적이므로 ZnO에 Al, Ga 등의 3족 원소를 도핑함으로써 낮은 비저항의 박막 제작이 가능하고, ITO 박막과 비교하여 etching이 쉬우며 기판과의 접착성이 좋으며, sputtering 공정시 plasma 분위기에서의 안정성이 뛰어나고 박막증착율이 높기 때문에 투명전극으로 적합한 재료이다. 본 연구에서는 cylindrical type의 Aldoping된 ZnO single target을 사용하여 박막 증착 압력의 변화를 주어 유리기판 위에 DC sputtering을 하였다. Fieldemission scanning electron microscope (FESEM)을 통해 ZnO:Al 박막의 표면의 형상과 두께를 확인하였으며, X-ray diffraction (XRD) 분석을 통해 박막의 결정학적 특성을 관찰하였다. 투명전극용 물질로서 ZnO:Al 박막의 적합성 여부를 확인하기 위하여 Van der Pauw 방법을 이용하여 박막의 비저항, 전자 이동도, 캐리어 농도를 측정하였으며, 박막의 기계적 성질 및 표면 접착성을 확인하기 위하여 nano-indentaion 분석을 하였다. 또한 UV-vis spectrophotometer를 이용하여 ZnO:Al 박막의 투과율을 분석하여 투명전극으로의 응용 가능성을 확인하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.444-445
• /
• 2006

We prepared ZnO:Al thin films under various sputtering conditions by using facing targets sputtering (FTS) method. ZnO:Al thin films were deposited on polyethersulfon (PES) substrate which is the thickness of 200um at room temperature. the electrical, optical and crystallographic properties of ZnO:Al were investigated. From the results, prepared alll ZnO:Al thin films showed (002) diffraction peaks. ZnO:Al thin film with a resistivity of $8.4{\times}10^{-4}{\Omega}cm$ and a transmittance of over 80% in visible range was obtained.

• Journal of Sensor Science and Technology
• /
• v.8 no.2
• /
• pp.189-194
• /
• 1999

The heat treatment effects of the undoped ZnO and Al doped ZnO(AZO) transparent conductive films prepared by rf magnetron sputtering were investigated. The variations of the electrical and optical properties with heat treatment temperature and ambient were studied. The resistivity of the un doped ZnO films heat treated in air and $H_z$ plasma for 1 hour increased rapidly above $200^{\circ}C$ and $300^{\circ}C$, respectively. And that of the ZnO:Al films heat treated in air also increased rapidly above $300^{\circ}C$. On the other hand that of the ZnO:Al films heat treated in $H_z$ plasma was constant regardless of heat treatment temperature. The optical transmittance above 550nm is about 90% for all thin films regardless of impurity doping, the heat treatment temperature and ambient.