• Laser Solutions
• /
• v.13 no.3
• /
• pp.1-6
• /
• 2010

The in-process monitoring of $CO_2$ welding of Zn-coated steel plates has been studied and compared with that of conventional thin plates. Relationships between weld defects and plasma emission signals were evaluated in laser lap joint of thick Zn-coated steel. According to the study, weld defects were found to increase with Zn content. As a result, measured plasma emission signals also decreased. In case of plate with $15{\mu}m$-thick Zn-coated layer, defects caused by evaporation of Zn could, therfore, controled by gap of 0.1mm, resulting in a stable emission signals. However, the amplitude of signals fluctuated very widely. Variation of amplitude sould be limited in 3-8V by FFT smoothing.

• Transactions of Materials Processing
• /
• v.28 no.2
• /
• pp.71-76
• /
• 2019

Corrosion resistance is one of the essential properties required in steel bolts. The various types of coatings are used to improve the corrosion resistance of steel bolts. But, roll formed, subsequently Zn alloy electrodeposited and top coated steel bolt easily takes place the white storage stain or white rust under high humidity condition. To investigate the corrosion resistance of roll formed and subsequently the various types of coated steel bolts, their polarization curves were measured by potentio-dynamic tester in this study. Based on the measured polarization curves, the more times of chromate and top coating on roll formed steel bolt, the higher corrosion resistance was shown. The roll formed steel bolt, which was Zn-Ni electro-deposited, two times chromated, one time inorganic top coated, one time organic top coated and annealed, showed the best corrosion resistance.

• Transactions of Materials Processing
• /
• v.21 no.5
• /
• pp.330-335
• /
• 2012

Roll formed steel bolts are electrodeposited with Zn-Ni to protect themselves from corrosion. However, white storage stain or white rust(corrosion) is found on Zn-Ni electrodeposited surface of steel bolts when they are exposed to moisture. In this paper a new process is introduced to protect Zn-Ni electrodeposited steel bolt from white storage stain or white rust for a long time under the salt spray test and high humidity test conditions. The better corrosion resistance could be gotten by the additional process of Ni-P electroless deposition and heat treatment to conventional manufacturing method of Zn-Ni coated steel bolt. The corrosion resistance of Zn-Al powder slurry coated steel bolt showed better than that of Zn-Ni electrodeposited one.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1996.10a
• /
• pp.166-173
• /
• 1996

There are kinds of materials for protective heat shield, i.e.Zn-coated steel, AI-coated steel and aluminum alloy sheets. This study compare formability, corrosion resistance, heat protectability, weight, and cost of these materials for heat protective shield. Generally aluminum alloy sheets are less formable than steel sheets, but A1100 alloy sheet shows almost same press quality of steel parts, using the press dies which producing steel parts. The heat shields using aluminum alloy sheet and steel sheet show almost same heat protectibility. It is the conclusion that Zn-coated merit, and AI-coated steel sheet and aluminum alloy sheet can be used to protect functional corrosion in severely corrosive market area. The material cost of AI-coated steel sheet and aluminum alloy sheet for a mid-size car is almost same, so aluminum alloy sheet is more recommendable in the point of weight reduction of vehicle.

• Journal of Welding and Joining
• /
• v.34 no.4
• /
• pp.48-54
• /
• 2016

The use of Zn coated steel has increased in the automotive industry due to its excellent corrosion resistance. Conventionally the BIW(body-in-white) structure and the hang-on parts have been made of Zn coated steel and more recently Zn coated steel began to be applied in the chassis parts. During gas metal arc (GMA) welding of the chassis part, lap fillet joint used to be adopted but spatter generation and porosities are most important concerns. In the industrial applications, an intentional joint gap was made to avoid the weld defects but it is not easy to control the size of joint gap. In this research, gas tungsten arc (GTA) is combined with GMA welding where GTA precedes GMA. As pulsed arc was adopted as GMA, GTA was oscillated along the longitudinal direction by pulsing GMA, but the arc oscillation did not disturb the molten droplet transfer of GMA welding. By increasing the distance between GTA and GMA, the length of weld pool increased and porosity could be reduced. Moreover porosity in the welds was fully removed when the distance between two arcs was 15 mm.

• Journal of Welding and Joining
• /
• v.18 no.1
• /
• pp.91-96
• /
• 2000

Characteristics of the weld defect, such as a blowhole and a pit in lap-jointed fillet Co₂ welds of Zn-coated steel sheet were studied in order to make clear the sequence of the blowhole formation during welding. Main conclusions obtained are as follows: 1) Blowhole, wormhole and pit were found in fillet welds, although the optimum welding condition of 200A-23V-100cm/min was applied. 2) Zn was only detected at the solidification boundary at the early stage of the blowhole formation. 3) Most of the blowholes was started to form at lap-joint by the Zn vapor. With increasing of the Zn vapor and its pressure, the blowhole was develope to th bed surface until the completion of weld solidification. 4) The behavior of the blowhole in growth was similar to that of the columnar dendrite during welding.

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.29-36
• /
• 2012

The resistance spot welding of high strength steel degrades the weldability because of its high strength with rich chemical composition and coating layer to protect from corrosion. During the each resistance welding process the electrodes tip reacts with coating layer, then subsequently deteriorates and shorten electrode life. In this study, the Al-coated HPF (Hot Press Forming) steels and Zn-coated TRIP steels were used to investigate the electrode life for resistance spot welding. Experimental results show that the reactivity of Al-coating on HPF steels to electrode tip surface behaviors different from the conventional Zn-coated high strength steels. The electrode tip diameter and nugget size in electrode life test of Al-coated HPF steels are observed to be constant with respect to weld numbers. For Al-coated HPF steels, the hard aluminum oxide layer being formed during high temperature heat treatment process reduces reactivity with copper electrode during the resistance welding process. Eventually, the electrode life in resistance spot welding of Al-coated HPF steels has the advantage over the galvanized steel sheets.

• Laser Solutions
• /
• v.1 no.1
• /
• pp.4-10
• /
• 1998

A basic research for tailored blank welding between mild steel and Zn-coated steel was carried out with $CO_2$ laser beam. The materials used in this work were low carbon steel sheet with a thickness of 1.2mm and Zn-coated steel sheet with the same thickness and 6.3$\mu$m Zn coating. Experiments were carried out by applying the Taguchi method in order to obtain optimized conditions for the application of tailored blank laser welding method in practical manufacturing process. Optical microscopy, XRD, SEM and TEM analysis were performed to observe microstructures and to determine the solidification mode of welded zone. Also mechanical properties were measured by microhardness test tensile test and Erichsen test in order to evaluate the formability of welded specimen. There was no trapped Zn in the fusion zone, and the phases in this region consisted of polygonal ferrite, quasi-polygonal ferrite, banitic ferrite and martensite. The elongation value of welded specimen was more than 80% of that value in the substrate and LDH value was more than 90% of that value in the substrate metal.

• Korean Journal of Materials Research
• /
• v.31 no.12
• /
• pp.704-709
• /
• 2021

In the flux used in the batch galvanizing process, the effect of the component ratio of NH₄Cl to ZnCl₂ on the microstructure, coating adhesion, and corrosion resistance of Zn-Mg-Al ternary alloy-coated steel is evaluated. Many defects such as cracks and bare spots are formed inside the Zn-Mg-Al coating layer during treatment with the flux composition generally used for Zn coating. Deterioration of the coating property is due to the formation of AlCl_x mixture generated by the reaction of Al element and chloride in the flux. The coatability of the Zn-Mg-Al alloy coating is improved by increasing the content of ZnCl₂ in the flux to reduce the amount of chlorine reacting with Al while maintaining the flux effect and the coating adhesion is improved as the component ratio of NH₄Cl to ZnCl₂ decreases. Zn-Mg-Al alloy-coated steel products treated with the optimized flux composition of NH₄Cl·3ZnCl₂ show superior corrosion resistance compared to Zn-coated steel products, even with a coating weight of 60 %.

• Transactions of Materials Processing
• /
• v.28 no.2
• /
• pp.77-82
• /
• 2019

Corrosion occurs well on surface of roll formed and Zn alloy subsequently electro-deposited on steel bolt under wet condition. In this study, variations in corrosion resistance were investigated through the measurement of polarization curves on steel bolts which were roll formed and subsequently coated with various types of coating methods. According to the measured polarization curve, Ni-P electroless deposits on roll formed steel increased the resistance to corrosion. The corrosion resistance of Zn alloy powder coated steel bolt was found to be better than that of Zn-Ni electro-deposited sample.