• Journal of the Korean institute of surface engineering
• /
• v.54 no.5
• /
• pp.248-259
• /
• 2021

This study examined the influence of post weld heat treatment (PWHT) conditions on corrosion behaviors of laser-welded super duplex stainless steel tube. Due to the high cooling rate of laser welding, the phase fraction of ferrite and austenite in the weld metal became unbalanced significantly. In addition, the Cr₂N particles were precipitated adjacent to the fusion line, which can be susceptible to the localized corrosion. On the other hand, the phase fraction in the weld metal was restored at a ratio of 5:5 when exposed to temperatures above 1060 ℃ during the post weld heat treatment. Nevertheless, the high beltline speed during the PWHT, leading to the insufficient cooling rate, caused a precipitation of σ phase at the interface between ferrite/austenite in both weld metal and base metal. This resulted in the severe corrosion damages and significant decrease in critical pitting temperature (CPT), which was even lower than that measured in as-welded condition. Moreover, the fraction of σ phase in the center region of post weld heat treated steel tube was obtained to be higher than in the surface region. These results suggest that the PWHT conditions for the steel tube should be optimized to ensure the high corrosion resistance by excluding the precipitation of σ phase even in center region.

• Korean Journal of Heritage: History & Science
• /
• v.35
• /
• pp.138-158
• /
• 2002

To compare and analyze technical system related to manufacturing of ironware during the period of the Three Kingdoms, an analysis was conducted on the minute system of metalwork, as study objects, of the remains of the Mt. Wolpyeong fortress wall in Daejeon in the period of capital during the era of the Three Kingdoms in the 5th century, the Sanwol-ri remains in the 6th century in Gunsan and the remains of ironware excavated from the great ancient tomb of Hwangnam of the Silla dynasty in the 5th century. The result of analysis shows that in the most of the casting products, the minute system of white cast iron were contained. While the iron part of decarbonization was in the system by casting as white cast iron in the central part, on the surface layer it was turned out that comparatively uniform 100% pearlite system of about 1~2mm degree was existing. The part of pearlite on the surface layer was caused by decarbonization, which appears in all the parts of blade front end and handle. Therefore, it was found that the iron part of decarbonization was manufactured by casting, and then was processed at the high temperature by decarbonization. For the products of forging, after processing the products on the basis of pure iron for materials, they manufactured the ironware that raises the strength by carbonizing that keeps carbon infiltrated on the necessary part, by the method of black smith welding that add pure iron to steel, or by varying the method of heat processing onto the part required of strength. Though limited, we could understand that the technical systems for manufacturing skill of ironware in the areas of Baekje and Silla were different each other. In the technical system for Hwangnam great ancient tomb in the Silla area, it is found that they had raised the strength on the necessary part by applying the steelmaking method of carbonizing in the last stage of production of products, in the meantime in Baekje area, it appears that they had produced steel in advance in the first stage of production of the products, and used the produced steel only to the necessary part.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.23 no.2
• /
• pp.111-117
• /
• 2019

An experimental study on the welding part of a heat transfer plate that constitutes the lightweight and high efficiency recuperator is presented in this paper. In particular, to find out the service life of the welded part, fatigue characteristics were determined through experiments. Experiments were carried out on two materials (STS347, AL20-25 + nb), which are selected as the material of the recuperator; further, the specimens were manufactured through the methods used for actual fabrication and the standards recommended by ASTM. To evaluate the mechanical properties of the specimens at room and high temperature, MTS-810 was used in a high-temperature furnace. The tensile test was carried out at room and high temperatures for each specimen. The fatigue test was carried out by setting the load ratio corresponding to 50%, 40%, 30%, 20%, and 10% of the tensile strength at the stress ratio of 0.1. Finally, the fatigue life characteristics obtained by the experiment were compared with the stresses owing to the load generated in the operating conditions of the recuperator, and the lifetime of the welds was evaluated to prepare for the operation time required by the UAV.

• Korean Journal of Metals and Materials
• /
• v.46 no.5
• /
• pp.321-327
• /
• 2008

Cu based amorphous ($Cu_{54}Zr_{22}Ti_{18}Ni_6$) coating was produced by cold spraying as a new fabrication process. The microstructure and macroscopic properties of amorphous coating layer was investigated and compared with those of cold sprayed pure Cu coating. Amorphous powders were prepared by gas atomization and Al 6061 was used as the substrate plate. X-ray diffraction results showed that Cu based amorphous powder could be successfully deposited by cold spraying without any crystallization. The Cu based amorphous coating layer ($300{\sim}400{\mu}m$ thickness) contained 4.87% porosity. The hardness of Cu based amorphous coating represented $412.8H_v$, which was correspond to 68% of the hardness of injection casted bulk amorphous material. The wear resistance of Cu based amorphous coating was found to be three times higher than that of pure Cu coating. The 3-point bending test results showed that the adhesion strength of Cu based amorphous coating layer was higher than that pure Cu coating. It was also observed that hard Cu base amorphous particle could easily deform soft substrate by particle collisions and thus generated strong adhesion between coating and substrate. However, the amorphous coating layer unexpectedly represented lower corrosion resistance than pure Cu coating, which might be resulted from the higher content of porosity in the cold sprayed amorphous coating.

• Korean Journal of Metals and Materials
• /
• v.46 no.10
• /
• pp.672-682
• /
• 2008

The resistance spot welding of TRIP590 steels was investigated to enhance understanding of weld fracture during tensile-shear strength (TSS) test. The main failure modes for spot welds of TRIP590 steels were nugget pullout and interfacial fracture. The peak load to cause a weld interfacial failure was found to be related to fracture toughness of the weld and the weld diameter. Although interfacial fracture occurred in the samples, the load carrying capacity of the weld was high and not significantly affected by the fracture mode. Substantial part of the weld exhibits the characteristic dimple (or elongated dimple) fractures on interfacial fractured surface, in spite of the high hardness values associated with the martensite microstructures. The high load-bearing ability of the weld is directly associated with the area of ductile fracture occurred in weld. Therefore, the judgment of the quality of resistance spot welds in TRIP590 steels, the load carrying capacity of the weld should be considered as an important factor than fracture mode.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.3
• /
• pp.102-111
• /
• 2021

The corrosion behaviors of laser-welded super duplex stainless steel tubes with post-weld heat treatment(PWHT) conditions(950, 1000, 1050, 1100 ℃ for 5 and 30 min) were evaluated by electrochemical potentiodynamic polarization and critical pitting temperature measurements. This study showed that the critical metallurgical factors affecting the degradation of corrosion resistance of a steel tube in as-welded condition were the unbalanced phase fraction(ferrite:austenite = 94:4), Cr₂N precipitation, and phase transformation from the austenite phase to ɛ-martensite(via stress-induced phase transformation). The improvement in the corrosion resistance of the welded specimen depends greatly on the PWHT conditions. The specimens after PWHT conducted below 1000 ℃ showed inferior corrosion resistance, caused by precipitation of the sigma phase enriched with Cr and Mo. At 1100 ℃ for a longer duration in PWHT, the ferrite phase grows, and its fraction increases, leading to an unbalanced phase fraction in the microstructure. As a result, pitting can be initiated primarily at the interface between the ferrite/austenite phase, particularly in base metal.

• Fashion & Textile Research Journal
• /
• v.23 no.1
• /
• pp.129-141
• /
• 2021

This study investigated fabrics, washing and cares, design, pattern, subsidiary materials, and sewing methods with a focus on the functional outers using moisture-permeable waterproof fabric as a shell; in addition, each element was analyzed for differences depending on fabric type. The characteristics of 34 outers were investigated through labels, online product introductions, visual inspection, observations from two experts with more than 30 years experience and wear tests. Moisture-permeable waterproof fabrics used for the outer were classified into two types; in addition, the shell of the high-density fabric and the 2 & 3-layer fabrics had different characteristics. Various fabrics, detailed designs, and three-dimensional patterns suitable for each part of the human body were used to improve functionality. In addition, various subsidiary materials and sewing methods were used to form an organic relationship. The same washing and cares, patterns and subsidiary materials were used regardless of fabric type; however, the fabric type influenced the detailed design and sewing. The outers with high-density fabric had a loose fit, short placket, e-banded cuffs, lock-stitch, and lock-stitch+binding. However, the outer with 2 & 3 layer fabric had a slim fit, hood width adjustment, zippered pockets, cuffs with tab, seamless adhesive sewing such as laminating, lock-stitch+ seam-sealing, and welding.

• Structural Engineering and Mechanics
• /
• v.83 no.5
• /
• pp.693-707
• /
• 2022

Bonded joints have proven their performance against conventional joining processes such as welding, riveting and bolting. The single-lap joint is the most widely used to characterize adhesive joints in tensile-shear loadings. However, the high stress concentrations in the adhesive joint due to the non-linearity of the applied loads generate a bending moment in the joint, resulting in high stresses at the adhesive edges. Geometric optimization of the bonded joint to reduce this high stress concentration prompted various researchers to perform geometric modifications of the adhesive and adherends at their free edges. Modifying both edges of the adhesive (spew) and the adherends (bevel) has proven to be an effective solution to reduce stresses at both edges and improve stress transfer at the inner part of the adhesive layer. The majority of research aimed at improving the geometry of the plate and adhesive edges has not considered the effect of temperature and water absorption in evaluating the strength of the joint. The objective of this work is to analyze, by the finite element method, the stress distribution in an adhesive joint between two 2024-T3 aluminum plates. The effects of the adhesive fillet and adherend bevel on the bonded joint stresses were taken into account. On the other hand, degradation of the mechanical properties of the adhesive following its exposure to moisture and temperature was found. The results clearly showed that the modification of the edges of the adhesive and of the bonding agent have an important role in the durability of the bond. Although the modification of the adhesive and bonding edges significantly improves the joint strength, the simultaneous exposure of the joint to temperature and moisture generates high stress concentrations in the adhesive joint that, in most cases, can easily reach the failure point of the material even at low applied stresses.

• Composites Research
• /
• v.19 no.2
• /
• pp.28-34
• /
• 2006

[ $Cu-TiB_2$ ] metal matrix composites with various weight fractions of $TiB_2$ were fabricated by combination of manufacturing process, SPS (self-propagating high-temperature synthesis) and SPS (spark plasma sintering). The feasibility of $Cu-TiB_2$ composites for welding electrodes and sliding contact material was investigated through experiments on the tensile properties, hardness and wear resistance. To obtain desired properties of composites, composites are designed according to reinforcement's shape, size and volume fraction. Thus proper modeling is essential to predict the effective material properties. The elastic moduli of composites obtained by FEM and tensile test were compared with effective properties from the original Eshelby model, Eshelby model with Mori-Tanaka theory and rule-of-mixture. FEM result showed almost the same value as the experimental modulus and it was found that Eshelby model with Mori-Tanaka theory predicted effective modulus the best among the models.

• Transactions of Materials Processing
• /
• v.32 no.1
• /
• pp.12-19
• /
• 2023

The armature core is a part responsible for the skeleton of the steering wheel. Currently, in the case of commercial trucks, the main parts of the parts are manufactured separately and then the product is produced through welding. In the case of this production method, quality and cost problems of the welded parts occur, and an integrated armature core made of magnesium alloy is used in passenger vehicles. However, in the case of commercial trucks, there is no application case and research is insufficient. Therefore, this study aims to develop an all-in-one armature core that simultaneously applies a magnesium alloy material and a die casting method to reduce the weight and improve the quality of the existing steel armature core. The product was modeled based on the shape of a commercial product, and finite element analysis (FEA) was performed through Ls-dyna, a general-purpose analysis program. Through digital image correlation (DIC) and uniaxial tensile test, the accurate physical properties of the material were obtained and applied to the analysis. A total of four types of compression were applied by changing the angle and ground contact area of the product according to the actual reliability test conditions. analysis was carried out. As a result of FEA, it was confirmed that damage occurred in the spoke area, and spoke thickness (t_spoke), base thickness (t_base), and rim and spoke connection (R) were designated as design variables, and the total weight and maximum equivalent stress occurring in the armature core We specify an objective function that simultaneously minimizes . A prediction function was derived using the sequential response surface method to identify design variables that minimized the objective function, and it was confirmed that it was improved by 22%.