• Korean Journal of Materials Research
• /
• v.15 no.7
• /
• pp.486-490
• /
• 2005

Thin films of tungsten oxide and nickel oxide were deposited on $Al_2O_3/Si-substrate$ by high vacuum thermal evaporation. The properties of microstructure and crystallinity were analyzed by SEM and XRD respectively. $WO_3$ films without addition of NiO showed polycrystalline structure after annealing at $500^{\circ}C$ for SO min. There were the cracks between the polycrystalline grains and the crack width was increased with the thickness of $WO_3$ films. The cracks in the $WO_3$ films could be controlled by an optimum deposition of NiO on $WO_3$ films and either less or more than the optimum addition fails to suppress the cracks. A process mechanism to suppress the crack has been discussed.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1508-1510
• /
• 1999

스퍼터 퇴적 $WO_3$ 박막에 대해 열처리에 따른 전기적특성 및 구조적특성을 각각 4탐침법 및 AFM 관측에 의해 조사해 보고, 또한 스퍼터링시의 산소가스 유량비에 따른 $WO_3$ 박막의 막질을 ESCA에 의해 평가하였다 실험 결과 열처리에 의해 $WO_3$ 박막 표면의 평균거칠기가 $2.45\AA$에서 $152\AA$으로 크게 증가함을 알 수 있었다 또한 스퍼터시 산소유량비에 따른 효과를 ESCA로 관측한 결과, 열처리전에는 주피크가 34eV에서 나타남에 비해 열처리 후에는 36eV전후에서 나타났다.

• Journal of the Korean Vacuum Society
• /
• v.8 no.2
• /
• pp.136-140
• /
• 1999

The stability and response time of $WO_3$ thin films for EC device are critical problems being solved. Those are affected by the species of electrolyte, preparation conditions and fabricating methods of specimen. In this paper, we compared the stabilities of three kinds of tungsten oxide film in electrolyte. Each of three films was prepared by different manufacturing conditions, that is, one is a thermal oxidation film of tungsten metal deposited on pure glass substrate, another is a $WO_3$ film made on ITO glass directly, the other is a thermally oxidized film on tungsten plate. It was observed that thermally oxidized $WO_3$ films has a remarkable stability (the lifetime was above $10^6$ cycle). From these results, we found that the stability was closely related to the stoichiometric bonding between tungsten and oxygen atoms in addition to crystallinity and density of film.

• Current Photovoltaic Research
• /
• v.4 no.2
• /
• pp.42-47
• /
• 2016

Increasing the efficiency of dye-sensitized solar cells (DSSCs) by the fabrication of new photoelectrodes (PEs) is an important challenge. This study examined the photovoltaic parameters of DSSCs composed of a $TiO_2$ PE with $WO_3$ nanoparticles (NPs). A number of PEs with the same thickness but different concentrations of $WO_3$ NPs in the $TiO_2PE$ were prepared. The morphology and structural properties of the prepared PEs were examined by field-emission scanning electron microscopy and X-ray diffraction, respectively. The effects of the $WO_3$ NPs mixing concentration on the efficiency of DSSCs were investigated under simulated solar light irradiation.

• Journal of the Korean Ceramic Society
• /
• v.34 no.4
• /
• pp.387-393
• /
• 1997

In order to apply WO3 thin films to the semiconducting NOx gas sensors as a sensing material, which have been expected to show good electrical properties, such as large sensitivity, rapid responsibility, and high selectivity, the fabrication method and their sensing characteristics were studied. The variations of surface morphologies, crystallographic orientations and crystallinity with the WO3 thin film growing methods thermal evaporation and DC sputtering methods were investigated by using scanning electron microscopy (SEM) and X-ray diffraction(XRD) analysis. As a result of sensitivity (Rgas/Rair) measurements for the 5 ppm NO2 test gas, the sensitivity values were 113 for the sputtered films and 93 for the evaporated films. It was also observed that the recovery rate of a sensing signal after measuring sensitivity was faster in the sputtered films than in the evaporated films.

• Proceedings of the KIEE Conference
• /
• 1998.07d
• /
• pp.1346-1348
• /
• 1998

Tungsten oxide($WO_3$) thin films were prepared by reactive magnetron sputtering in an $Ar/O_2$ atmosphere from a compressed powder $WO_3$ target and their electrochromic(EC) phenomena were investigated. PEO-$LiClO_4$-PC polymer electrolyte can easely be formed into thin films and showed high transmittance. Such electrolyte have electrochromic properties suitable for large-scale electrochromic devices. For the devices using $WO_3$ thin films of 1500, 2500, $4000{\AA}$ thickness with glass/ITO/$WO_3$/PEO-$LiClO_4$-PC/ITO/glass structure, an optical modulation of $50{\sim}60%$ were obtained at a potential range of $1{\sim}2V$. It has shown that transmittance and reflectance of light could be electrically controlled by low applied voltage.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1298-1299
• /
• 2006

In the present work, the influence of the ball-milling time, milling atmosphere and weight ratio of ball to powder on characteristics of $WO_3-CuO$ was studied. Results show that, the grain sizes of the $WO_3$ and CuO in the ball-milled powder mixture were significantly decreased with increasing the milling time. Those of each oxide ball-milled in Argon and Hexane atmosphere for 30 and 20 hour were about 98 and 84 nm, respectively. After milling of 20 hour in Hexane as PCA, the powder had a homogeneously mixed structure and the average size of $WO_3-CuO$ powders was determined to about 230nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.347-349
• /
• 1997

In order to investigate CO sensing property of a SnO$_2$-WO$_3$composite ceramic. we prepared pure SnO$_2$and WO$_3$added SnO$_2$compostie ceramics. Using XRD and SEM, a phase analysis and microstructure were investigated. The resistances as a function of gas atmosphere were measured by High Voltage Measure/source Unit. The measured 1000ppm CO gas sensitivity of SnO$_2$-WO$_3$composite ceramics were smaller than that of pure SnO$_2$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.101-101
• /
• 2015

Photoelectrochemical water splitting is considered as a promising method of transforming solar energy into chemical energy stored in the type of hydrogen. An n-type $WO_3$ semiconductor is one of the most promising photoanodes for hydrogen production from water splitting. Films annealed at lower temperatures consisted of amorphous, whereas films annealed above $500^{\circ}C$ comprised solely of monoclinic $WO_3$. In this study, we observed photoactivity of $WO_3$ as increasing thickness of $WO_3$. And it shows good photoacivity as thickness increases. Also we tried to improve photoactivity through surface modification and bulk modification by using hydrogen treatment and conducting polymer. The photocurrent was measured in potentiostatic method with the three electrode system. A Pt wire and Ag / AgCl electrode were used as the counter electrode and the reference electrode, respectively. photocurrent-time (I-T) curve was measured at a bias potential of 0.79 V.

• Clean Technology
• /
• v.23 no.2
• /
• pp.172-180
• /
• 2017

Thermodynamic evaluation indicates that nearly 100% conversion of elemental mercury to oxidized mercury can be attained by HCl of several tens of ppm level at the temperature window of SCR reaction. Cu-, Fe-, Mn-chloride loaded $V_2O_5-WO_3/TiO_2$ catalysts revealed good NO removal activity at the operating temperature window of SCR process. The catalysts with high desorption temperature indicating adsorption strength of $NH_3$ revealed higher NO removal activity. The HCl fed to the reaction gases promoted the oxidation of mercury. However, the activity for the oxidation of elemental mercury to oxidized mercury by HCl was suppressed by $NH_3$ inhibiting the adsorption of HCl to catalyst surface under SCR reaction condition containing $NH_3$ for NO removal. Metal chloride loaded $V_2O_5-WO_3/TiO_2$ catalysts showed much higher activity for mercury oxidation than $V_2O_5-WO_3/TiO_2$ catalyst without metal chloride under SCR reaction condition. This is primarily attributed to the participation of chloride in metal chloride on the catalyst surface promoting the oxidation of elemental mercury.