• Journal of Welding and Joining
• /
• 제33권4호
• /
• pp.37-43
• /
• 2015

Characteristics of dissimilar metal welds between STS 316L and carbon steel ASTM A516 Gr.70 made with GTAW have been evaluated in terms of microstructure, ferrite content, chemical analysis, hardness and corrosion resistance. Three heat inputs of 9.00, 11.25, 13.00kJ/cm were employed to make joints of dissimilar metals with ER309 wire. Based on microstructural examination, the amount of vermicular type of ${\delta}$-ferrite was increased with increasing heat input due to the increase of Creq/Nieq in the second layer of welds. Based on the EDX analysis of weld metals, Cr and Ni content in the 2nd layer increased while those content in the first layer of welds decreased with heat inputs. Cellular solidification mode in the 1st layer and dendritic solidification mode in the 2nd layer due to different cooling rates were prevailed, respectively. Heat affected zone which formed hard microstructure showed higher hardness than the weld metal. The salt spray test of dissimilar metals weld joints showed that the carbon steel surfaces only corroded. The weight loss rate due to corrosion increased up to 100hours but it decreased above 100 hours. There was little difference in the weight loss caused by corrosion regardless of heat inputs.

• Journal of Welding and Joining
• /
• 제5권1호
• /
• pp.16-22
• /
• 1987

오스테나이트계 스테인레스강 용접부의 .delta.-페라이트 생성인자에 관한 위의 실험결과로부터 아래의 결론을 얻을 수 있다. (1) 오스테나이트계 스테인레스강 용접부의 .delta.-페라이트는 에너지적으로 불안정한 상으로서, 오스테나이트로의 변태가 비가역적(irreversible)이다. (2) .delta.-페라이트의 생성 및 변태에는 합금원소의 확산이 반드시 수반되며, 최종 .delta.-페라 이트 함량은 정성적으로 다음과 같이 표시된다. 페라이트함량=primary페라이트-변태한 페라이트 (3) .delta.-페라이트 생성에 일차적으로 영향을 미치는 이자는 화학조성(Cr-당량/Ni-당량)이며, primary 변태양상 및 냉각속도에도 크게 의존한다. (4) 용착부 .delta-페라이트는 대개 Vermicular와 Lathy의 혼합조직으로 존재하며, 열영향을 받 을수록 에너지적으로 안정한 Globuar 형상으로 변해간다.

• 한국정밀공학회지
• /
• 제5권1호
• /
• pp.50-62
• /
• 1988

An experimental investigation of the machining characteristics of compact vermicular cast iron whose matrix were formulated under two kinds of annealing conditions has been conducted. The various characteristics of the machinability of CA cast iron depending upon its matrix and cutting condition have been obtained from the experiment. The results are as follow. As depth of cut increases, the shear stress slightly decreases in order $P_1, \P_2, \P_3$ which are classified by ferrite matrix of CV cast iron. As depth of cut increases, the normal stress increases, and annealing effect in heavy cutting is smaller than that in light cutting. The cutting energy slightly decreases, as depth of cut increases and the effect of annealing on cutting energy in light cutting is higher than that in heavy cutting. The cutting equation in this study are as follow. $P_1\:\2{\phi}\ + \1.49({\beta} - {\alpha} )=84^{\circ}$ $P_2\:\2{\phi}\ + \1.36({\beta} - {\alpha} )=82^{\circ}$ $P_3\:\2{\phi}\ + \1.34({\beta} - {\alpha} )=79^{\circ}$ Machining constants in this study for $P_1, P_2, P_3$give $74^{\circ} , 66^{\circ}, 61^{\circ}$ Tool wear increases as depth of cut increases, and decreases as ferrit matrix increases.

• Journal of Welding and Joining
• /
• 제34권3호
• /
• pp.69-76
• /
• 2016

Characteristics of dissimilar metal welds between ASTM Type 316L and carbon steel ASTM A516 Gr.70 made with FCAW were evaluated in terms of microstructure, ferrite content, EDS analysis, hardness, tensile strength, impact toughness and corrosion resistance. Three heat inputs of 10.4, 16.9, 23.4kJ/cm were employed to make joints of dissimilar metals with E309LMoT1-1 wire. Microstructure of dissimilar weld metals consisted of mostly vermicular type of ${\delta}$-ferrite and some lathy type of ${\delta}$-ferrite, and ${\delta}$-ferrite was transformed into globular type in reheated zone. In all conditions, weld metals were solidified on FA solidification mode. Based on the EDS analysis of weld metals, All Creq/Nieq values were in the range of FA solidification mode, and it was decreased with increasing heat inputs whereas it was increased with increasing layers. The amount of ${\delta}$-ferrite was decreased with increasing heat input due to the difference of cooling rate, and it was increased with increasing layers. Accordingly, hardness and tensile strength of dissimilar metals weld joints was decreased with increasing heat input while impact energy was increased with increasing heat input. Corrosion test of dissimilar metals weld joints showed that weight gain rate of heat input 10.4kJ/cm was the greatest, and that of three heat inputs became constant after certain time.

• 열처리공학회지
• /
• 제9권1호
• /
• pp.34-44
• /
• 1996

Austenite stainless steel was produced by arc welding with current 650A, voltage 50V and welding speed 10cm/min. It was post-welded and then heat treated at $1,050^{\circ}C$ for 120min. And then it was immersed in water or in air. The microstructural changes, ferrite contents, mechanical properties, and stress corrosion cracking(SCC) were investigated. The SCC was studied in 42wt% boiling $MgCl_2$($140^{\circ}C$) under the constant stress using SCC elongation curve. The results showed that; 1. The as-welded spedimen seemed to increase ${\delta}$-ferrite content largely, and revealed continuous network of lathy and vermicular type. The post-welded heat treatment changed the morphologies of ferrite from continuous type to island type. 2. The as-welded, air and water quenched specimens had the ${\delta}$-ferrite content 9.7%, 3.2% and 2.1% respectively. We also showed that ${\delta}$-ferrite was Cr-rich and Ni-poor by EPMA. 3. The time of failure on the SCC was measured and it was used for corrosion elongation curve. The condition of SCC was investigated under $35kgf/mm^2$ load and the results were as follows; 4. The intergranullar cracking by stress corrosion was most distinct in weld metal while the transgranular cracking occurred in the air cooled specimen.

• Journal of Welding and Joining
• /
• 제32권2호
• /
• pp.29-36
• /
• 2014

Recently, in order to enhance the function and usefulness of products, cladding of dissimilar materials that maximizes the performance of the material is being widely used in all areas of industry as an important process. Clad steel plate, produced by cladding stainless steel plate, an anticorrosive material, on carbon steel plate, is being used to produce pressure vessels. Stainless steel plate has good corrosion resistance, and carbon steel plate has good rigidity and strength; clad steel can satisfy all of these qualities at once. This study aims to find the ${\delta}$-ferrite behavior, mechanical properties, structure change, integrity and reliability of clad steel weld on hot rolled steel plates. For this purpose, multi-layer welding, repair welding and post weld heat treatment were implemented according to welding procedure specifications (WPS). In order to observe the mechanical properties and toughness of clad steel weld zone, post weld heat treatment was carried out according to ASME Sec. VIII Div.1 UW-40 procedure for post weld heat treatment. With heat treatment at $625^{\circ}C$, the hold time was used as the process variable, increased by intervals that were doubled each time, from 80 to 1,280 min. The structure of weld part was typical cast structure; localized primary austenite areas appeared near central vermicular ferrite and fusion line. The heat affected zone showed rough austenite structure created by the weld heat input. Due to annealing effects of heat treatment, the mechanical properties (tensile strength, hardness, impact value) of the heat affected area tended to decrease. From the results of this study, it is possible to conclude the integrity of clad steel welds is not affected much in field welding, repair welding, multi-layer welding, post weld heat treatment, etc.

• Journal of Welding and Joining
• /
• 제32권4호
• /
• pp.26-33
• /
• 2014

The metallurgical and mechanical characteristics, toughness and corrosion resistance of dissimilar welds between super duplex stainless steel UNS S32750 and carbon steel ASTM A516Gr.70 have been evaluated. Three heat inputs of 21.12, 24.00, 26.88kJ/cm were employed to make joints of dissimilar metals with flux cored arc welding(FCAW). Based on microstructural examination, vermicular ferrite was formed in the first layer of weld at low heat input(21.12kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.61 while acicular ferrite was formed in last layer of weld at high heat input(26.88kJ/cm) and $Cr_{eq}/Ni_{eq}$ of 1.72. Ferrite percentage in dissimilar welds was lowest in the first layer of weld regardless of heat inputs and it gradually increased in the second and third layers of weld. Heat affected zone showed higher hardness than the weld metal although reheated zone showed lower hardness than weld metal due to the formation of secondary austenite. Tensile strengths of dissimilar welds increased with heat input and there was 100MPa difference. The corrosion test by ferric chloride solution showed that carbon steel had poor corrosion resistance and pitting corrosion occurred in the first layer(root pass) of weld due to the presence of reheated zone where secondary austenite was formed. The salt spray test of carbon steel showed that the surface only corroded but the amount of weight loss was extremely low.

• 비파괴검사학회지
• /
• 제33권2호
• /
• pp.173-180
• /
• 2013

벌레 모양 흑연철로 알려진 강화흑연강(CGI)은 주철보다 더 강하고 더 가벼운 것이 요구되는 응용제품에서 인기를 얻고 있는 금속이다. 최근 강화흑연강 디젤엔진 블록에 사용되고 있다. 본 연구에서는 디젤엔진의 배기 매니폴드에 사용되는 것을 고려하여, 873~1273 K에서 1~96 시간 열처리를 실시하여 CGI340의 기계적 특성을 평가하였다. 열처리를 실시한 시험편의 인장강도는 모재에 비하여 전체적으로 낮은 인장강도를 나타내었다. 열처리 시간이 증가할수록 인장강도가 감소하였으며, 열처리 온도가 높고 시간이 길어질수록 더 많이 감소하였다. 초음파 피로시험에 의한 피로한도는 모재는 약 130 MPa, 1173 K(96 hrs) 시험편은 약 100 MPa을 나타내었다. 경도는 열처리 시간이 증가할수록 감소하였으며, 열처리 온도가 높을수록 경도의 분포가 낮아졌다. 그리고 CGI340에 분포하는 구상흑연의 평균경도는 120 Hv, 벌레 모양 흑연의 평균경도는 114 Hv로 기지조직인 페라이트보다 낮은 경도를 나타내었다. 열처리 온도 및 시간에 따라서 구상흑연 및 벌레 모양 흑연에 대한 변화는 일정하지 않지만, 열처리 시간이 길어짐에 따라 기지조직의 결정립이 커지는 것을 확인하였다.

• 한국주조공학회지
• /
• 제7권1호
• /
• pp.53-59
• /
• 1987

In order to study the infuence of Sb addition on the compacted vermicular graphite cast iron(C/V) and gray cast iron(GC), these specimen which had different Sb content(0-0, 1wt.%) were prepared. these specimen were tested for microstructure and mechanical properties. The result from this study are as follows. For C/V and GC, the microstructure of graphite appeared to be finer with increasing Sb content more than 0.06wt.% Ferrite disappeared from the matrix with addition of Sb more than 0.06wt.% in GC and more than 0.08wt.% in C/V. The size of the eutectic cell in GC was 4.5 to 7 times larger than that in C/V, but the decreasing tendancy of its size was more remarkable in GC than in C/V with increasing Sb content. The abrasion speed corresponding to the maximum amount of abrasion in the nabrasion test was found to be 1.37m/sec. GC sample weared 3.6 to 21 times faster than those of C/V did. the amount of abrasion demeased remarkably with Sb addition, and the abrasion rate was constant with Sb content over 0.04wt.%