• Korean Journal of Materials Research
• /
• v.23 no.12
• /
• pp.714-721
• /
• 2013

A stoichiometric mixture of evaporating materials for $ZnAl_2Se_4$ single-crystal thin films was prepared in a horizontal electric furnace. These $ZnAl_2Se_4$ polycrystals had a defect chalcopyrite structure, and its lattice constants were $a_0=5.5563{\AA}$ and $c_0=10.8897{\AA}$.To obtain a single-crystal thin film, mixed $ZnAl_2Se_4$ crystal was deposited on the thoroughly etched semi-insulating GaAs(100) substrate by a hot wall epitaxy (HWE) system. The source and the substrate temperatures were $620^{\circ}C$ and $400^{\circ}C$, respectively. The crystalline structure of the single-crystal thin film was investigated by using a double crystal X-ray rocking curve and X-ray diffraction ${\omega}-2{\theta}$ scans. The carrier density and mobility of the $ZnAl_2Se_4$ single-crystal thin film were $8.23{\times}10^{16}cm^{-3}$ and $287m^2/vs$ at 293 K, respectively. To identify the band gap energy, the optical absorption spectra of the $ZnAl_2Se_4$ single-crystal thin film was investigated in the temperature region of 10-293 K. The temperature dependence of the direct optical energy gap is well presented by Varshni's relation: $E_g(T)=E_g(0)-({\alpha}T^2/T+{\beta})$. The constants of Varshni's equation had the values of $E_g(0)=3.5269eV$, ${\alpha}=2.03{\times}10^{-3}eV/K$ and ${\beta}=501.9K$ for the $ZnAl_2Se_4$ single-crystal thin film. The crystal field and the spin-orbit splitting energies for the valence band of the $ZnAl_2Se_4$ were estimated to be 109.5 meV and 124.6 meV, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $ZnAl_2Se_4/GaAs$ epilayer. The three photocurrent peaks observed at 10 K are ascribed to the $A_1$-, $B_1$-exciton for n = 1 and $C_{21}$-exciton peaks for n = 21.

• Journal of Sensor Science and Technology
• /
• v.24 no.6
• /
• pp.404-411
• /
• 2015

A stoichiometric mixture of evaporating materials for $BaAl_2Se_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $BaAl_2Se_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperatures were $610^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $BaAl_2Se_4$ single crystal thin films measured from Hall effect by van der Pauw method are $8.29{\times}10^{-16}cm^{-3}$ and $278cm^2/vs$ at 293 K, respectively. The temperature dependence of the energy band gap of the $BaAl_2Se_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=3.4205eV-(4.3112{\times}10^{-4}eV/K)T^2/(T+232 K)$. The crystal field and the spin-orbit splitting energies for the valence band of the $BaAl_2Se_4$ have been estimated to be 249.4 meV and 263.4 meV, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $BaAl_2Se_4/GaAs$ epilayer. The three photocurrent peaks observed at 10 K are ascribed to the $A_1$-, $B_1$-exciton for n =1 and $C_{31}$-exciton peaks for n=31.

• Journal of Sensor Science and Technology
• /
• v.16 no.1
• /
• pp.1-6
• /
• 2007

A silver indium sulfide ($AgInS_{2}$) epilayer was grown by the hot wall epitaxy method, which has not been reported in the literature. The grown $AgInS_{2}$ epilayer has found to be a chalcopyrite structure and evaluated to be high quality crystal. From the photocurrent measurement in the temperature range from 30 K to 300 K, the two peaks of A and B were only observed, whereas the three peaks of A, B, and C were seen in the PC spectrum of 10 K. These peaks are ascribed to the band-to-band transition. The valence band splitting of $AgInS_{2}$ was investigated by means of the photocurrent measurement. The crystal field splitting, ${\Delta}cr$, and the spin orbit splitting, ${\Delta}so$, have been obtained to be 0.150 eV and 0.009 eV at 10 K, respectively. And, the energy band gap at room temperature has been determined to be 1.868 eV. Also, the temperature dependence of the energy band gap, $E_{g}$(T), was determined.

• ETRI Journal
• /
• v.38 no.2
• /
• pp.265-271
• /
• 2016

We analyzed the interface characteristics of Zn-based thin-film buffer layers formed by a sulfur thermal cracker on a $Cu(In,Ga)Se_2$ (CIGS) light-absorber layer. The analyzed Zn-based thin-film buffer layers are processed by a proposed method comprising two processes - Zn-sputtering and cracker-sulfurization. The processed buffer layers are then suitable to be used in the fabrication of highly efficient CIGS solar cells. Among the various Zn-based film thicknesses, an 8 nm-thick Zn-based film shows the highest power conversion efficiency for a solar cell. The band alignment of the buffer/CIGS was investigated by measuring the band-gap energies and valence band levels across the depth direction. The conduction band difference between the near surface and interface in the buffer layer enables an efficient electron transport across the junction. We found the origin of the energy band structure by observing the chemical states. The fabricated buffer/CIGS layers have a structurally and chemically distinct interface with little elemental inter-diffusion.

• Journal of the Korean Chemical Society
• /
• v.60 no.6
• /
• pp.402-409
• /
• 2016

Thin films of lead sulfide colloidal quantum dots (CQDs) of 2.8 nm in diameter are fabricated and their surfaces are passivated by 3-mercaptopropionic acid (MPA) ligand or hybrid type ($MPA+CdCl_2$) ligand, respectively. The changes in valence band electronic structure and atomic composition of each PbS CQD film upon post-treatment such as air, N2 annealing or UV/Ozone have been studied by photoelectron spectroscopy. The air annealing makes the CQD fermi level to move toward the valence band leading to "p-type doping" regardless of ligand type. The UV/Ozone post-treatment generates $Pb(OH)_2$, $PbSO_x$ and PbO on both CQD surfaces. But the amount of the PbO has been reduced in hybrid type ligand case, especially. That is probably because the extra Pb cations in (111) surface are additionally passivated by $Cl_2$ ligand, which limits the reaction between the Pb cation and ozone.

• Current Photovoltaic Research
• /
• v.3 no.2
• /
• pp.65-70
• /
• 2015

We applied KF on CIGS film to modify CIGS surface with a wider-bandgap surface layer. With the KF deposition the surface of CIGS film had fine particle on the CIGS surface at 350 and $300^{\circ}C$. No fine particle was detected at 500 and $250^{\circ}C$. With the KF treatment, the Ga and O content increased at the surface, while the In and Cu content decreased. The valence band maximum was lowered with KF treatment. The composition profile and band structure were positive side of applying KF on the CIGS surface. However, the efficiency decreased with the KF treatment due to high series resistance, probably due to too thick surface layer. A smaller amount of KF should be supplied and more systematic analysis is necessary to obtain a reproducible higher efficiency CIGS solar cells.

• Journal of Sensor Science and Technology
• /
• v.1 no.2
• /
• pp.165-172
• /
• 1992

To determine the effect of additions of trivalent and pentavalent ions on the electrical conductivity and sensing behaviour, indium and antimony were incorporated in tin oxide by the coprecipitation method. Antimony may be considered to enter the cassiterite structure as pentavalent ions, thermal energy could excite electrons from these ions into the conduction band. Similarly the indium ions would enter the lattice as $In^{3+}$ but could accept electrons from the valence band, thereby becoming monovalent or divalent. These phenomena, however, how the potential barrier existing $SnO_{2}$ by addition of two kinds of ions could influence on the sensing behaviour in comparison with their influence on the resistivity were observed.

• Korean Journal of Materials Research
• /
• v.4 no.6
• /
• pp.620-625
• /
• 1994

We recently showed from the neutron diffraction and extended X-ray absorption fine structure studies the structural evidence for the formation of an amorphous phase in immiscible Cu-Ta system subjected to mechanical alloying. In a system with a positive heat of mixing like Cu-Ta, we consider it necessary to confirm the formation of an amorphous phase not only from the structural studies but also from a change in the electronic properties. We show the electronic evidence for the formation of the chemical bonding between the unlike atoms Cu and Ta for the 120 h-milling sample through changes in superconducting transition temperature and X-ray photoemission spectroscopy valence band structure.

• Current Applied Physics
• /
• v.18 no.11
• /
• pp.1190-1195
• /
• 2018

By employing soft X-ray magnetic circular dichroism (XMCD), soft X-ray absorption spectroscopy (XAS), and photoemission spectroscopy (PES), we have investigated the electronic structure of the candidate zero-moment half-metallic $Mn_3Ga$. We have studied the ball-milled and annealed $Mn_3Ga$ powder samples that exhibit nearly zero magnetization. Mn 2p XAS revealed that Mn ions in $Mn_3Ga$ are nearly divalent for both of the Mn ions having the locally octahedral symmetry and those having the locally tetrahedral symmetry. The measured Mn 2p XMCD spectrum of $Mn_3Ga$ is very similar to that of ferrimagnetic $MnFe_2O_4$ having divalent Mn ions. The sum-rule analysis of the Mn 2p XMCD spectrum shows that both the spin and orbital magnetic moments of Mn ions in $Mn_3Ga$ are negligibly small, in agreement with the nearly compensated-ferrimagnetic ground state of $Mn_3Ga$. The valence-band PES spectrum of $Mn_3Ga$ agrees well with the calculated density of states, supporting the half-metallic electronic structure of $Mn_3Ga$.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.1
• /
• pp.26-29
• /
• 2006

We present the structural, magnetic, and electrical properties in the (Al,Mn)N films with various Mn concentrations grown by plasma-enhanced molecular beam epitaxy. X-ray diffraction analyses reveal that the (Al,Mn)N films have the wurtzite structure without secondary phases. All (Al,Mn)N films showed the ferromagnetic ordering. Particularly, ($Al_{1-x}Mn_{x}$)N film with x = 0.028 exhibited the highest magnetic moment per Mn atom at room temperature. Since all the films exhibit the insulating characteristics, the origin of ferromagnetism in (Al,Mn)N might be attributed to either indirect exchange interaction caused by virtual electron excitations from Mn acceptor level to the valence band within the samples or a percolation of bound magnetic polarons arisen from exchange interaction of localized carriers with magnetic impurities in a low carrier density regime.