• Journal of the Korean Wood Science and Technology
• /
• v.40 no.6
• /
• pp.418-423
• /
• 2012

In order to develop the end use of cylindrical laminated veneer lumber (LVL) such as wooden crafts, the water proof-bonding strength, the resistance to abrasion and the surface hardness by painting the surface of LVL were investigated. The study results were as follows; The water proof-bonding strength through 5 cyclic test by boiling in water immersion and drying were favorable without delamination of glue line. Then the formulation of glue was resorcinol resin (100) to hardener of paraformaldehyde (5) by mixed weight percentage. The resistance to abrasion was relatively higher at cross section than tangential section. When tangential section of LVL was painted by UV protection oil, the resistance to abrasion was improved. In case of an cross section of LVL, the higher surface hardness appeared at larch core than radiata pine LVL. Also, in case of an tangential section of LVL, the higher surface hardness appeared at glue line than veneer side.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.275.2-275.2
• /
• 2014

현재 자동차 분야에서 차량 경량화의 한 수단으로 자동차용 유리를 고강도 투명 플라스틱 소재인 Polycarbonate(PC)로 대체하고자 하는 연구가 이루어지고 있다. 하지만, PC의 낮은 내마모 특성과 자외선에 의한 열화 및 변색 현상은 해결하여야 할 문제점으로 지적되고 있으며, 에너지 소비 저감을 위하여 적외선 영역 반사율(reflectance)이 높은 저방사(low emissivity) 특성이 요구되고 있다. 본 연구에서는, ICP-assisted reactive magnetron sputtering 장비를 이용하여 투과율(transmittance)이 확보되고, 고경도 특성을 갖는 Al-Si-N와 300 nm 파장 이하의 자외선 차단 특성이 있는 SiN:H 그리고 저방사 특성을 위해 Al을 증착하였고, 박막의 증착 순서는 SiN:H 박막을 가장 아래에 증착하고 그 위에 Al/Al-Si-N 박막을 다층으로 형성하였다. 박막의 chemical state와 crystallinity를 확인하기 위하여 XPS(X-ray Photoelectron Spectroscopy), XRD (X-ray Diffraction)를 이용하여 분석하였다. Knoop ${\mu}$-hardness tester와 Taber tester를 이용하여 경도 및 내마모 특성을 분석하였다. 제작된 샘플의 Al-Si-N 박막 경도는 Si 비율에 따라 다른 경도 특성을 갖는데, 실제 Si/(Al+Si) 비율이 24%에서 최대 31 GPa의 경도 값을 갖는 것을 확인하였다. UV-Vis Spectrometer를 이용하여 250 nm~700 nm 파장의 투과율을 측정하였고, 자외선 영역의 경우 SiN:H 박막에 의해 300 nm 이하의 파장에서 2% 이하의 투과율을 확인하였다. 그리고 FT-IR(Fourier Transform Infrared Spectroscopy)를 이용하여 $2.5{\mu}m{\sim}15{\mu}m$ 파장의 반사율을 이용하여 방사율을 측정하였는데, 3*(Al/Al-Si-N) 구조의 다층 박막의 경우 방사율은 0.27로 측정되었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.121-121
• /
• 2017

본 연구는 비전도성 폴리머 표면을 개질하여 감광성 금속을 유전체 표면에 흡착시키고, 감광성 금속의 광화학 반응을 이용하여 귀금속 촉매를 비전도성 폴리머 표면에 선택적으로 흡착시켜 무전해 Cu 도금을 수행하여 금속패턴을 형성하였다. 기능성 유연 필름은 일반적으로 투명한 플라스틱 고분자 기판을 기반으로 전기 전자, 에너지, 자동차, 포장, 의료 등 다양한 분야에서 폭넓게 활용 되고 있으며, 본 연구에서는 습식 도금 공정을 이용하여 폴리이미드 필름상에 $10{\mu}m$ 이하의 미세패턴을 형성하기 위한 공정을 개발하고자 하였다. 비전도성 폴리머 표면에 무전해 도금을 위해서 우선 폴리머 필름의 표면을 개질하는 공정이 필요하다. 이에 KOH 또는 NaOH 알카리 용액을 이용하여 표면을 개질하였으며 개질된 표면에 감광성 금속이온의 흡착시키기 위한 감광성 금속이온은 주석을 사용하였으며, 주석 용액의 안정성 및 퍼짐성 향상을 위해 감광성 금속 용액의 제조 및 특성을 관찰하였으며, 감광성 금속화합물이 흡착된 비전도성 유전체 표면을 포토마스크를 이용하여 특정 부위, 즉 표면에 금속패턴 층을 형성하고자 하는 곳은 포토마스크를 이용하여 광원을 차단하고 그 외 부분은 주 파장이 365nm와 405nm 광원을 조사하여 선택적으로 감광성 금속화합물의 산화반응을 유도하는 광조사 공정을 수행하였다. 광원이 조사되지 않은 부분에 귀금속 등의 촉매 입자를 치환 흡착시켜 금속 패턴이 형성될 수 있는 표면을 형성하였다. 위의 활성화 공정이후에 활성화 처리된 표면을 세척하는 수세 공정을 거친 후 무전해 도금공정에 바로 적용할 경우 미세한 귀금속 입자가 패턴이 아닌 부분 즉 자외선(UV) 조사된 부분에도 남아있어 도금시 번짐 현상이 발생한다. 이에 본 연구에서는 활성화 처리 후 약 알칼리 용액에 카르복실산을 혼합하여 잔존하는 귀금속 입자를 제거한 후 무전해 Cu 도금액을 이용하여 $10{\mu}m$ 이하의 Cu 금속 패턴을 형성하였다.

• Analytical Science and Technology
• /
• v.23 no.5
• /
• pp.477-484
• /
• 2010

Personal care products are a diverse group of synthetic organic chemicals such as antimicrobial compounds, UV filters and organo-phosphate flame retardants and derived from individual usages of soaps, toothpaste and cosmetics. It has been detected in municipal sewage effluent and various environmental samples such as surface water, marine, soil, sediment and aquatic biota in many countries. The occurrence of personal care products in environmental samples could negatively impact the health of the ecosystem and humans, due to persistent, long-term chronic exposure of aquatic organisms. In this study, fifteen personal care products in aquatic environmental samples were determined by gas chromatography-mass spectrometry (GC-MS) with liquidliquid extraction (LLE). Method detection limits were in the range of $0.004\sim0.273\;{\mu}g/L$. Two compounds (TCEP, TCPP) were detected in surface waters and seven compounds (triclosan, 4-MBC, EHMC, BP-3, TCEP, TPP, TBEP) were detected in sewage treatment plants (STP) influents or effluents.

• Analytical Science and Technology
• /
• v.14 no.3
• /
• pp.259-265
• /
• 2001

Photocatalytic degradation of Congo red was performed using various semiconductors as ZnO, CdS, rutile-$TiO_2$ or mixed rutile-$TiO_2$/ZnO. The change of degradation of the dye was investigated by UV-visible spectrophotometric method. The photocatalytic action of CdS was greater than ZnO and rutile-$TiO_2$ in account of low band gap energy of CdS. The rate of photocatalytic degradation reaction increased drastically in according to increasing ratio of ZnO on mixed rutile-$TiO_2$/ZnO. These photocatalytic effect of rutile-$TiO_2$ was suppressed by more stable rutile-$TiO_2$, doping the hydrolysis product with $Zn^{2+}$ prior to calcination onto the rutile-$TiO_2$ surface.

• Polymer(Korea)
• /
• v.38 no.5
• /
• pp.632-639
• /
• 2014

2,7-Dihydroxynaphthalene bis(trimellitate anhydride) (2,7-TA) was synthesized from trimellitic anhydride chloride and 2,7-dihydroxynaphthalene. Copolyimides (Co-PI) containing ester group were synthesized from 2,7-TA, pxylylenediamine, and 2,2'-bis(trifluoromethyl)benzidine (TFB). The Co-PI films were obtained from poly(amic acid) by solution casting through thermal imidization on a glass plate. The thermal property, gas permeation, and optical transparency of the Co-PI films with various TFB monomer contents were investigated. These Co-PIs could be solution-cast into a flexible and tough film. The cast Co-PI films exhibited high optical transparency with a cut-off wavelength of 370~395 nm in UV-vis. absorption and a low yellow index value of 3.55~7.63. The thermal property of Co-PI films increased linearly with increasing TFB content. However, the oxygen permeation and optical transparency of the Co-PI films was found to worsen with increasing TFB content.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.352-352
• /
• 2013

국내 에너지 소비량의 21.6%가 건물 분야에 소비되고 있다. 창호는 벽체에 비해 8~10배 이상 낮은 단열 특성을 가지기 때문에 열 손실량이 크다. 유리는 창호를 이루는 요소 중 가장 큰 면적을 차지하고 있으며, 창호의 단열성능을 2배로 향상시키면 30% 이상 건물의 에너지 절감 효과를 가질 수 있다. 창호의 단열 성능을 향상시키기 위해서 Low-e(emissivity) 기술 연구가 진행 중이다. 이번 실험에서는 RF 마그네트론 스퍼터링 시스템을 사용하여 XG 유리기판 위에 ZnO박막을 증착하고, evaporator 장비를 사용하여 metal층인 Ag를 증착하였다. 그리고 다시 한번 ZnO박막을 증착하였다. Low-e 연구에 활용할 수 있는지를 확인하기 위해 XRD, AFM, 투과도를 측정하였다. ZnO박막의 증착 조건은 초기압력 $3.0{\times}10^{-6}$ Torr, 공정압력 $2.0{\times}10^{-2}$ Torr, RF파워 30 W, Ar gas는 50 sccm, 증착온도는 상온으로 하였다. Metal층인 Ag를 증착하기 위해 evaporator의 증착 조건은 Rotate rate 2 rpm, voltage 0.3V, 공정압력 $5.0{\times}10^{-6}$ Torr이며, 변수로 Ag두께를 3,5,7,9,11,13,15 nm로 하였다. AFM 측정결과 Ag두께가 증가할수록 RMS roughness값이 높아졌으며, 최소 0.71 nm의 거칠기를 가지는 것을 확인하였다. XRD분석결과 37도 부근의 피크가 발생하여 ZnO 박막이 결정질 구조임을 확인할 수 있었다. 그리고 UV-Visible-NIR 분광 광도계를 이용하여 광학적 투과를 측정한 결과 Ag두께가 13 nm일 때 가시광 영역의 투과도가 최대 75%, 적외선 영역의 투과도가 최소 28%로 좋은 차단 특성을 가지는 것을 확인하였다. 위 결과들로 ZnO 박막이 Low-e 기술에 활용될 수 있음을 확인하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.351-351
• /
• 2013

한국 전체 에너지 사용량 중약 24%의 에너지가 건축물 부분에 소비되고 있다. 건축물의 벽체나 유리창 등을 통해서 에너지 손실이 이루어지는데 유리창은 벽체에 비해 약 10배 이상 낮은 단열 특성을 가지고 있기 때문에 유리창을 통한 열손실량은 더 크다. 이러한 유리창 부분의 열손실 문제를 해결할 수 있는 방안으로 좋은 단열 특성 및 낮은 방사율을 가지고 있는 Low-e coating 방법을 사용하였다. 본 실험에서는 XG glass 기판 위에 IGZO/Ag/IGZO OMO 구조의 다층 박막을 증착하였다. RF magnetron sputtering방법을 이용하여 OMO 구조의 상부와 하부의 Oxide layer로 IGZO 박막을 증착하였다. 사용된 IGZO 타겟은 $In_2O_3$ (99.99%), $Ga_2O_3$ (99.99%), ZnO (99.99%)의 분말을 각각 1:1:1 mol% 조성비로 혼합하여 소결하여 제작하였다. Thermal Evaporator 장비를 이용하여 OMO 구조의 Metal layer로 Ag (99.999%)를 증착하였다. 실험 기판은 크기 $30{\times}30mm$의 0.7T XG glass를 사용하였다. OMO 구조의 산화층 IGZO 박막은 상/하층 동일 조건으로 기판 온도는 실온으로 고정하였으며, 초기 압력 $3.0{\times}10^{-6}$ Torr, 증착 압력 $3.0{\times}10^{-2}$ Torr, RF 파워 50W, Ar 유량 50 sccm로 고정시키고 증착 시간이 변화하면서 박막을 증착하였다. OMO 구조의 Metal layer로 Ag 증착 조건은 초기 진공도가 약 $6.0{\times}10^{-6}$ Torr 이하로 유지하고 기판을 2 Rpm의 속도로 회전시켰다. 이후 0.3 V로 Ag를 10분간 가열하여 충분히 녹인 후 Film Thickness Monitor로 두께를 확인하였다. OMO 다층 박막의 산화물층 변화에 따라 로이다층 박막의 구조적, 광학적 및 전기적 특성을 분석하였다. XRD 분석결과에 의하여 Bragg's 법칙을 만족하는 피크가 나타나지 않는 비정질 구조임을 확인할 수 있으며, AFM 분석결과에 통해서 최소 1.3 nm의 Roughness를 나타내었다. UV-Visible-NIR 분광광도계를 이용하여 다층 박막은 가시광선 영역에서 평균 80%의 광 투과성을 보여 IR 영역에서 평균 30% 투과하고 좋은 차단 특성을 나왔다. Low-e 특성을 갖는 유리창을 통해서 에너지 절약을 이룰 수 있는 것을 확인할 수 있었다.

• Journal of the Korean Chemical Society
• /
• v.37 no.6
• /
• pp.549-554
• /
• 1993

The titanium oxide thin film was prepared by air oxidation and water vapor oxidation. The photo-electrochemical properties of the electrode was studied in 1M NaOH solution. Titanium dioxide electrodes prepared at higher temperatures were found to have slightly more negative flat band potentials and slightly higher donor densities than their low temperature counterparts. The value of flat band potential ($V_{fb}$) was obtained to be -0.95 ∼ -1.1 V by the measurement of photocurrent and Motte-Schottky plots. The photocurrent of visible region was measured in terms of single crystal filter which entirely blocks the UV radiation. The photo-response of electrodes appeared good with the measument by direct current, when the slit of great resolution was used.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.59.2-59.2
• /
• 2009

화학보호복은 독성이 있는 화학물질 및 미세분진등에 대해 공기를 차단하며 완전 밀폐형으로 공기호흡기 및 에어라인 같은 호흡보호장치와 함께 착용하여 신체부위를 보호한다. 그 예로 생물/화학보호복은 유독하고 해로운 생물/화학물질로 부터 인체를 보호해준다. 이들 보호복은 다양한 환경이 노출되어 장시간 작업을 위해서 오랜시간 보호성능을 유지해야한다. 특히, 이런 원단의 구성은 플라스틱과 고무류의 다층구조로 구성되어있다. 플라스틱류(폴리에틸렌, PTFE 등)는 표면장력이 너무 낮아 접착하는데 어려운 점이 많이 대두된다. 일반적인 표면처리방법은 크게 물리화학적 방법으로 4가지로 분류한다. 화학적산화, 불꽃처리, 플라즈마처리, UV 방사법 등이 있다. 이들 중에서 가장 간단한 산화처리는 플라즈마처리다. 이처리는 상온/상압하에서 대기 중 또는 가스내에 방전에 의해 플라즈마를 형성하고 이 플라즈마가 대상물의 표면분자와 격렬히 반응하게 하여 표면의 분자구조를 변화시킴에 따라 소수성의 표면에 Carboxyl, hydroxyl과 carbonyl과 같은 친수성으로 변하여 결합능력을 증가 시켜 표면장력을 높여주는 가장 효과적인 방법이다. 플라즈마 표면처리를 하고 나면 육안으로 표면의 변화를 감지할 수 없지만 접착, 잉크, 코팅을 잘 받아들이는 결과를 가져온다. 플라즈마 표면처리의 효과는 주로 부도체의 필름이나 합성수지 계열의 인쇄성과 접착성을 향상시키고자 많이 활용되고 있는 실정이다. 특히, 화학보호복과 같은 플라스틱류인 다양한 고분자 합성수지(Polyethylene, polypropylene, nylon, vinyl, PVC, PET 등)에 적용가능하다. 본 연구에서는 플라즈마처리조건에 영향을 주는 변수들을 고려하여 실험계획법(DOE, RSM)을 이용하여 최적화된 플라즈마 공정을 향상시키고자한다.