• Proceedings of the KIEE Conference
• /
• 2001.11a
• /
• pp.171-173
• /
• 2001

ZnO:Al transparent conductive thin films were prepared by facing targets sputtering system with a DC power supply using ZnO target containing 2wt% of $Al_2O_3$ and Zn metal target. Sputtering was carried out at substrate temperature of R.T. and $200^{\circ}C$ with a DC current of 0.6A, $O_2$ flow rate of $0.1{\sim}0.5$ and thickness $300{\sim}900nm$. ZnO:Al films showed a resistivity as low as $10^{-4}{\Omega}-cm$ and a transmittance above 85 % at wavelength 300 and 800nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.11a
• /
• pp.302-305
• /
• 1995

ITO(indium tin oxide) that is both conductive in electricity and transparent to the visible ray is called transparent conducting thin film. Nowaday, according to the development of flat panel display such as LCD(Liquid Crystal display, EL(electolumine- scence display), PDP(plasma display panel), ECD(electrocromic display), the higher quality in the low temperature process has been asked to reduce the production cost and to have a good uniformity on a large substrate. In this study, we prepared indium tin oxide(ITO) by a cylindrical DC magnetron sputtering with Indium-tin (9:1) alloy target instead of indium-tin oxide target. To reduce the defact in ITO, the effect on ITO by varing the magnetic field intensity and the applied voltage ares studied. the resistivity of the film deposited in oxygen partial pressure of 5% and substrate temperature of 140$^{\circ}C$. is 1.6${\times}$10$\^$-1/$\Omega$$.$cm with 85% optical transmission in viaible ray.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.99-99
• /
• 2010

Recently, amorphous transparent oxide semiconductors (TOS) have been widely studied for many optoelectronic devices such as AM-OLED (active-matrix organic light emitting diodes). The TOS TFTs using a-IGZO channel layers exhibit a high electron mobility, a smooth surface, a uniform deposition at a large area, a high optical transparency, a low-temperature fabrication. In spite of many advantages of the sputtering process such as better step coverage, good uniformity over large area, small shadow effect and good adhesion, there are not enough researches about characteristics of a-IGZO thin films. In this study, therefore, we focused on the electrical properties of a-IGZO thin films as a channel layer of TFTs. TFTs with the a-IGZO channel layers and Y2O3 gate insulators were fabricated. Source and drain layers were deposited using ITO target. TFTs were deposited on unheated non-alkali glass substrates ($5cm{\times}5cm$) with a sintered ceramic IGZO disc (3 inch $\varnothing$, 5mm t), Y2O3 disc (3 inch $\varnothing$, 5mm t) and ITO disc (3 inch $\varnothing$, 5mm t) as a target by magnetron sputtering method. The O2 gas was used as the reactive gas. Deposition was carried out under various sputtering conditions to investigate the effect of sputtering process on the characteristics of a-IGZO thin films. Correlation between sputtering factors and electronic properties of the film will be discussed in detail.

• Korean Journal of Materials Research
• /
• v.14 no.5
• /
• pp.328-333
• /
• 2004

Transparent ZnO:Al conductor films for the optoelectronic devices were deposited by using the capacitively coupled DC magnetron sputtering method. The effect of Al doping concentration and discharge power on the electrical and optical properties of the films was studied. The film resistivity of $8.5${\times}$10^{-4}$ $\Omega$-cm was obtained at the discharge power of 40 W with the ZnO target doped with 2 wt% $Al_2$$_O3$. The transmittance of the 840 nm thick film was 91.7% in the visible waves. Increasing doping concentration of 3 wt% $Al_2$$O_3$ in ZnO target results in significant decrease of film resistivity, which may be due to the formation of $Al_2$$O_3$ particles in the as-deposited ZnO:Al film and the reduced ZnO grain sizes. Increasing DC power from 40 to 60 W increases deposition rate by more than 50%, but can induce high defect density in the film, resulting in higher film resistivity.

• Journal of Powder Materials
• /
• v.26 no.5
• /
• pp.375-382
• /
• 2019

Homogeneous multicomponent indium gallium zinc oxide (IGZO) ceramics for transparent electrode targets are prepared from the oxides and nitrates as the source materials, and their properties are characterized. The selected compositions were $In_2O_3:Ga_2O_3:ZnO$ = 1:1:2, 1:1:6, and 1:1:12 in mole ratio based on oxide. As revealed by X-ray diffraction analysis, calcination of the selected oxide or nitrides at $1200^{\circ}C$ results in the formation of $InGaZnO_4$, $InGaZn_3O_6$, and $InGaZn_5O_8$ phases. The 1:1:2, 1:1:6, and 1:1:12 oxide samples pressed in the form of discs exhibit relative densities of 96.9, 93.2, and 84.1%, respectively, after sintering at $1450^{\circ}C$ for 12 h. The $InGaZn_3O_6$ ceramics prepared from the oxide or nitrate batches comprise large grains and exhibit homogeneous elemental distribution. Under optimized conditions, IGZO multicomponent ceramics with controlled phases, high densities, and homogeneous microstructures (grain and elemental distribution) are obtained.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.345.2-345.2
• /
• 2016

Alumina (Al2O3) doped zinc oxide (ZnO) films (AZO) have been prepared from 2 wt.% Al2O3 doped ZnO target by DC magnetron sputtering at a 2 mTorr (0.27 Pa) chamber pressure in (15 sccm) argon ambient. We obtained films of various opto-electronic properties by variation of target angle from 32.5o to 72.5o. At lower target angle deposited films show higher values in optical gap, mobility of charge carrier, carrier concentration, crystallite grain size, transmission range of wavelength, which are favorable characteristics of AZO as a transparent conducting oxide (TCO). At higher target angle the sheet resistance, work function, surface roughness for the AZO films increases. Measured haze ratio of the films changed lower to higher and size of characteristic surface structure of as deposited film ranges from ~40 nm to ~300 nm. By a combination of low and high target angle we obtained a textured TCO film with high conductivity.

• Journal of the Korean Vacuum Society
• /
• v.18 no.5
• /
• pp.394-401
• /
• 2009

This paper reports the structural and optical properties of ZnO/glass thin films grown by radio-frequency magnetron sputtering with a powder target. In contrast to ZnO ceramic target typically used, a ZnO raw powder target was sputtered in this study. ZnO grew with the (0002) preferred orientation along the surface normal direction. Initially, the surface of ZnO thin films was flat considerably and then it became rougher as the thickness increased. The optical transmittance was as high as 88% in the range of 400-1000 nm. The bandgap energy of 3.23 eV at the 220 nm thick sample was estimated.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1096_1097
• /
• 2009

Aluminium doped zinc oxide(ZnO:Al) thin film, which is mainly used as a transparent conducting electrode in electronic devices, has many advantages compared with conventional indium tin oxide(ITO). In this paper in order to investigate the possible application of ZnO:Al thin films as a transparent conducting electrode for flexible film-typed dye sensitized solar cell (FT-DSCs), ZnO:Al and ITO thin films were prepared on the polyethylene terephthalate (PET) substrate by r. f. magnetron sputtering method. Specially one-inched FT-DSCs using either a ZnO:Al or ITO electrode were also fabricated separately under the same manufacturing conditions. Some properties of both the FT-DSCs with ZnO:Al and ITO transparent electrodes, such as conversion efficiency, fill factor, and photocurrent were measured and compared with each other. The results showed that by doping the ZnO target with 2 wt% of $Al_2O_3$, the film deposited at discharge power of 200W resulted in the minimum resistivity of $2.2\times10^{-3}\Omega/cm$ and at ransmittance of 91.7%, which are comparable with those of commercially available ITO. Two types of FT-DSCs showed nearly the same tendency of I-V characteristics and the same value of conversion efficiencies. Efficiency of FT-DSCs using ZnO:Al electrode was around 2.6% and that of fabricated FT-DSCs using ITO was 2.5%. This means that ZnO:Al thin film can be used in FT-DSCs as a transparent conducting layer.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.3
• /
• pp.128-132
• /
• 2009

Transparent conducting thin films of indium tin oxide(ITO) co-sputtered with aluminum-doped zinc oxide(AZO) were deposited on glass substrate by dual magnetron sputtering. It was found that the electrical properties and structural characteristics of the films are significantly changed according to the sputtering power of the AZO target. The IAZTO film prepared with D.C power of ITO at 100 W and R.F power of AZO at 50 W shows an electrical resistivity of $4.6{\times}10^{-4}{\Omega}{\cdot}cm$ and a sheet resistance of $30{\Omega}/{\square}$ (for 150 nm thick). Besides of the improvement of the electrical properties, compared to the ITO films deposited at the same process conditions, the IAZTO films have very smooth surface, which is due to the amorphous nature of the films. However, the electrical conductivity of the IAZTO films was found to be deteriorated along with the crystallization in case of the high temperature deposition (above $310^{\circ}C$). In this work, high quality amorphous transparent conductive oxide layers could be obtained by mixing AZO with ITO, indicating possible use of IAZTO films as the transparent electrodes in OLED and flexible display devices.

• Proceedings of the Korean Institute of IIIuminating and Electrical Installation Engineers Conference
• /
• 2009.10a
• /
• pp.177-179
• /
• 2009

In order to investigate the possible application of ZnO films as a transparent conducting oxide (TCO) electrode, ZnO:Al films were prepared by RF magnetron sputtering method. The effects of surface treatment and doping concentration on the structural and electrical properties of ZnO films were mainly studied experimentally. Five-inch PDP cells using either a ZnO:Al or indium tin oxide (ITO) electrode were also fabricated separately under the same manufacturing conditions. The luminous properties of both the transparent conducting oxide electrode were measured and compared with each other. By doping the ZnO target with 2 wt% of Al2O3, the film deposited at a chemical surface treatment resulted in the minimum resistivity of 8.5 _ 10_4 U-cm and a transmittance of 91.7%. And DBD surface treatment resulted in the minimum resistivity of 8.5 _ 10_4 U-cm and a transmittance of 91.7%. Although the luminance and luminous efficiency of the transparent conducting oxide electrode using ZnO:AI are lower than those of the cell with the ITO electrode by about 10%, these values are sufficient enough to be considered for the normal operation of TCO.