• The Korean Journal of Ceramics
• /
• 제7권2호
• /
• pp.63-69
• /
• 2001

We investigated strength degradations from cyclic contact fatigue in self-toughened glass-ceramics. Hertzian indentation was used to induce cyclic contact load. Dynamic fatigue was also performed with changing stress rates from 0.01 to 10000 MPa/sec. After that, strength data and fracture origins were analysed. As the number of contact cycles increased or stressing rate decreased, severe strength degradation occurred by as much as 50% because of radial cracks developed from microcrack coalescence.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 추계총회,초청강연,특별강연,연구발표회
• /
• pp.167.2-167
• /
• 2000

• 한국세라믹학회지
• /
• 제52권2호
• /
• pp.137-139
• /
• 2015

In this study, we examined the influence of molten $KNO_3$ flow on mechanical properties and their deviation when a chemical toughening process was applied to soda lime silicate glass ($Na_2O-CaO-SiO_2$). $KNO_3$ melt flow was controlled using three methods: (1) glass tray rotation, (2) impeller stirring, and (3) natural convection. DOL and hardness were found to be enhanced by tray rotation because this rotation was able to maintain the concentration around the glass surface, in contrast to other methods. However, there did not appear to be a statistically significant difference in the 3-point bending strength for the three flow conditions due to the ground edge condition.

• 한국세라믹학회지
• /
• 제44권4호
• /
• pp.189-193
• /
• 2007

Effect of additive composition on fracture toughness of in situ-toughened $SiC-Si_3N_4$ composites was investigated for five different additive compositions. The highest toughness $(6.4MPa{\cdot}m^{1/2})\;in\;SiC-Si_3N_4$ composites investigated herein was obtained when an Y-Mg-Si-Al-O-N oxynitride glass was used as a sintering additive. The improvement in fracture toughness was produced by enhanced bridging and deflection by $Si_3N_4$ grains.

• 한국재료학회지
• /
• 제9권1호
• /
• pp.35-41
• /
• 1999

In this study we investigated the effects of process variables on the bond strength, and its dependency upon the interfacial chemistry when the joined $ZrO_2$ toughened $Na\beta$"-alumina to $\alpha$-alumina using B$_2$$O_3$-$SiO_2$-Al$_2$$O_3$-CaO glass sealant. We observed that bond strength is mainly determined by the strength of the glass, which, in turn, depends on the glass composition established after joining reaction. Joining at $950^{\circ}C$ for 15min yielded the highest average bond strength of 66MPa. Different types of interfacial reaction seem to occur at each interface. After joining at $950^{\circ}C$ for 15min we found that Ca and Si diffuse much deeper(~15$\mu\textrm{m}$) into the $\beta$"-alumina composite than into the $\alpha$-alumina(<1$\mu\textrm{m}$) as a result of ion exchange reaction and more effective grain boundary diffusion. Thermal expansion coefficient of the glass was found to have changed more closely to those of the $\beta$"-alumina composite and $\alpha$-alumina, which put the glass under a slight compressive stress.ressive stress.

• 한국화재소방학회논문지
• /
• 제17권4호
• /
• pp.124-130
• /
• 2003

본 연구는 방화구획에 적용 가능한 수막형성유리벽에의 직근에 화원이 위치하는 경우 국부복사열에 의해 수막형성전 유리면이 가열된 상태에서 상부 수막분사노즐에서 분사되는 수막이 접촉함에 따른 급냉파열현상을 규명하기 위한 연구이다. 유리면 직근에서 국부복사열을 주는 실화재실험을 실시하여 분석하면 보통유리는 유리면 포면온도(가열측)가 $100^{\circ}C$를 넘는 경우에 수막을 접촉시킬 경우 파열이 발생하며, 강화유리는 유리 가열면 온도가 $250^{\circ}C$이상일 때 수막형성에 의한 급냉 파열이 발생함을 알 수 있었다. 향후 강화유리에 수막을 도포시키는 현재 방화구획에 사용되고 있는 유리의 대다수가 강화유리인 것을 감안하면 수막의 도포이전에 강화유리면의 온도가 $300^{\circ}C$이내에서는 수막을 유리면에 급속히 접촉시켜도 유리면의 급냉 파열이 일어나지 않음을 발견하였다. 따라서 일정한 공간구획 내에서 화재발생시 유리면의 직근에 화원이 위치하여 국부적으로 복사열을 가할 경우에도 화원상부 천정면에 설치된 감지시스템에 의해 한계온도이전에 수막형성시스템을 작동시켜 급냉파열현상을 발생시키지 않는다면 수막형성유리벽을 실제 방화구획의 경계벽으로 사용하는데 있어서 예측가능한 장애요인을 제거하는 데 비약적인 공헌을 한 것에 그 의미를 둔다.

• 공업화학
• /
• 제25권2호
• /
• pp.121-133
• /
• 2014

ABA형태의 삼중블록공중합체는 고무상과 유리상의 상대적 성분에 좌우되는 열가소성 탄성체와 강화 플라스틱으로써 유용하다. 이러한 물질은 다른 고분자와 혼합하여 첨가제, 강화제, 상용화제로써 기능성을 줄 수 있다. 상업적으로 유용한 대부분의 블록 공중합체는 석유로부터 유래된다. 지구상의 유한한 화석자원 공급과 석유 사용 및 채굴에 관련된 경제, 환경적 비용을 고려하면 그 대안은 매력적이다. 이러한 흐름에 더하여 미래 지속 가능한 물질의 최종 용도를 위한 설계 및 그 실행이 요구되고 있다. 본 총설에서는 재생 가능한 ABA 형태의 삼중블록 공중합체 합성과 특성을 살펴보고, 특히 공중합체의 경성부분을 위한 높은 유리 전이온도 혹은 녹는점을 지닌 식물 유래 폴리올레핀과 다당류 유래 폴리락타이드와 공중합체의 연성부분을 위한 바이오 기반, 낮은 유리 전이온도, 무결정의 탄화수소계 고분자에 대해 논의하려고 한다. 이를 위해서 다양하게 제어된 고분자 중합법은 강력한 도구임이 증명되고 있다. 이러한 혼성 고분자의 정교한 합성에 관한 연구는 재생가능성, 생분해성, 고성능을 지닌 새로운 탄성체와 강화 플라스틱의 발전을 이끌고 있다.