The Korean Journal of Ceramics

The Korean Ceramic Society (한국세라믹학회)
권호 표지

Strength Degradation from Contact Fatigue in Self-toughened Glass-ceramics

  • Lee, Kee Sung (Energy Materials Research Team, Korea Institute of Energy Research) ;
  • Kim, Do Kyung (Dept. of Mat. Sci. and Eng., Korea Advanced Institute of Science and Technology) ;
  • Woo, Sang Kuk (Energy Materials Research Team, Korea Institute of Energy Research) ;
  • Han, Moon Hee (Energy Materials Research Team, Korea Institute of Energy Research)
  • Published : 2001.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

We investigated strength degradations from cyclic contact fatigue in self-toughened glass-ceramics. Hertzian indentation was used to induce cyclic contact load. Dynamic fatigue was also performed with changing stress rates from 0.01 to 10000 MPa/sec. After that, strength data and fracture origins were analysed. As the number of contact cycles increased or stressing rate decreased, severe strength degradation occurred by as much as 50% because of radial cracks developed from microcrack coalescence.

Keywords

References

  1. Fracture of Brittle Solids(ed.2) B.R. Lawn
  2. Phil. Mag. Lett. v.64 no.4 Flaw-insensitive Ceramics S.J. Bennison;N.P. Padture;J.L. Runyan;B.R. Lawn
  3. J. Am. Ceram. Soc. v.82 no.12 Effect of Initial α-phase Content on Microstructure and Mechanical Properties of Sintered Silicon Carbide Y.W. Kim;M. Mitomo;H. Emoto;J.G. Lee
  4. J. Am. Ceram. Soc. v.80 no.9 Role of Microstructure in Hertzian Contact Damage in Silicon Nitride: I. Mechanical Characterization S.K. Lee;S. Wuttiphan;B.R. Lawn
  5. J. of Kor. Powd. Metall. Inst. v.5 no.1 A Study on the Mechanical Properties and Contact Damage of Silicon Nitrides: I. Effect of α/β Phase Fraction S.K. Lee;K.S. Lee;S.W. Lee;J.H. Kim;D.K. Kim
  6. J. of Kor. Powd. Metall. Inst. v.5 no.2 Effect of Seeding on Microstructure Development of Silicon Nitride Ceramics C.J. Lee;D.J. Kim
  7. J. Kor. Ceram. Soc. v.36 no.10 Microstructures and Mechanical Properties of SiC Containing SiC-platelet Seeds of Various Size M.J. Choi;C. Park;D.S. Park;H.D. Kim
  8. J. Am. Ceram. Soc. v.75 no.7 Improved Flaw Tolerance in Alumina Containing 1 vol% Anorthite via Crystallization of the Intergranular Glass N.P. Padture;H.M. Chan
  9. J. Am. Ceram. Soc. v.78 no.1 Enhanced Machinability of Silicon Carbide via Microstructural Design N.P. Padture;C.J. Evans;H.H.K. Xu;B.R. Lawn
  10. J. Am. Ceram. Soc. v.79 no.12 Short-crack Toughness and Abrasive Machining of Silicon Nitride H.H.K. Xu;S. Jahanmir;L.K. Ives;L.S. Job;K.T. Ritchie
  11. J. Dent. Res. v.77 no.4 Mechanical Characterization of Dental Ceramics Using Hertzian Contacts I.M. Peterson;A. Pajares;B.R. Lawn;V.P. Thompson;E.D. Rekow
  12. Bull. of the Kor. Ceram. Soc. v.10 no.5 Ceramic Materials for Dental Restoration D.J. Kim;J.S. Han
  13. Mater. Sci. Eng. v.A103 Mechanism of Fatigue Crack Propagation in Metals, Ceramics, Composites: Role of Crack-tip Shielding R.O. Ritchie
  14. J. Mater. Sci. v.26 no.12 Cyclic Fatigue of Ceramics F. Guiu;M. Reece;D.A.J. Vaughan
  15. Int. J. Fract Mechanisms of Fatigue-crack Propagation in Ductile and Brittle Solids R.O. Ritchie
  16. Acta. Mater. v.46 no.2 On the Quantification of Bridging Tractions During Subcritical Crack Growth Under Monotonic and Cyclic Fatigue Loading in a Grain-bridging Silicon Carbide Ceramic C.J. Gilbert;R.O. Ritchie
  17. J. Kor. Ceram. Soc. v.34 no.10 Dynamic Fatigue Behavior of Alumina Ceramics H.L. Lee;K.H. Lee;S.E. Park
  18. Philos. Mag. v.A68 no.5 Indentation Fatigue: A Simple Cyclic Hertzian Test for Measuring Damage Accumulation in Polycrystalline Ceramics F. Guiberteau;N.P. Padture;H. Cai;B.R. Lawn
  19. J. Am. Ceram. Soc. v.78 no.6 Contact Fatigue of a Silicon Carbide with a Heterogeneous Grain Structure N.P. Padture;B.R. Lawn
  20. Acta. Mater. v.47 no.18 Cyclic Fatigue of Intrinsically Brittle Ceramics in Contact with Spheres D.K. Kim;Y.G. Jung;I.M. Peterson;B.R. Lawn
  21. J. Am. Ceram. Soc. v.83 no.9 Model for Cyclic Fatigue of Quasiplastic Ceramics in Contact with Spheres K.S. Lee;Y.G. Jung;I.M. Peterson;B.R. Lawn;D.K. Kim;S.K. Lee
  22. J. Am. Ceram. Soc. v.83 no.6 Role of Microstructure in Dynamic Fatigue of Glass-ceramics after Contact with Spheres J.G. Yeo;K.S. Lee;B.R. Lawn
  23. J. Dental Res. v.79 no.2 Lifetime-limiting Strength Degradation from Contact Fatigue in Dental Ceramics Y.G. Jung;I.M. Peterson;D.K. Kim;B.R. Lawn
  24. J. Am. Ceram. Soc. v.81 no.8 Indentation of Ceramics with Spheres: A Century after Hertz B.R. Lawn
  25. J. Kor. Ceram. Soc. v.35 no.5 Contact Damage and Strength Degradation of Yittria Doped Tetragonal Zirconia Polycrystal Y.G. Jung;S.C. Choi
  26. J. Mater. Res. v.9 no.3 Deformation and Fracture of Mica-containing Glass-ceramics in Hertzian Contacts H. Cai;M.A.S. Kalceff;B.R. Lawn
  27. J. Am. Ceram. Soc. v.81 no.6 Model of Strength Degradation from Hertzian Contact Damage in Tough Ceramics B.R. Lawn;S.K. Lee;I.M. Peterson;S. Wuttiphan
  28. J. Am. Ceram. Soc. v.66 no.5 Theory of Fatigue for Brittle Flaws Originating from Residual Stress Concentrations E.R. Fuller;B.R. Lawn;R.F. Cook
  29. J. Mater. Sci. v.17 Fatigue Analysis of Brittle Materials Using Indentation Flaws: II. Case Study on a Glass Ceramic R.F. Cook;B.R. Lawn;G.R. Anstis