• 한국응용과학기술학회지
• /
• 제28권4호
• /
• pp.410-417
• /
• 2011

Effects of ethylene-propylene diene monomer (EPDM)/polypropylene (PP), zinc oxide, stearic acid, and clay on the combustive properties based on EDPM/PP were investigated. The EDPM/PP/clay nanocomposites was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). It was found that the specific mass loss rate (SMLR) in the nanocomposites decreased due to the fire resistance compared with unfilled EDPM/PP, while the nanocomposites showed the higher total heat release (THR), higher CO production release, and higher specific extinction area (SEA) than those of virgin EPDM/PP. The stearic acid for softening ruber increased the THR and amount of smoke by itself, combustible.

• 한국화재소방학회논문지
• /
• 제24권5호
• /
• pp.115-121
• /
• 2010

이 연구에서는 암모늄염을 처리한 리기다 소나무의 연소성을 시험하였다. 실온에서 3종류의 암모늄염 즉, 황산암모늄, 제1인산암모늄, 그리고 제2인산암모늄의 20wt% 수용액에 각각 리기다 소나무를 함침시켜 건조시킨 후 콘칼로리미터(ISO 5660-1)를 이용하여 그의 연소성을 시험하였다. 암모늄염으로 처리한 시험편은 처리하지 않은 시험편에 비하여 그의 연소성을 감소 시켰다. 이것은 연소 억제성이 순수 리기다 소나무 시험편에 처리한 암모늄염 때문에 향상된 것으로 생각된다. 또한 암모늄염으로 처리한 시험편은 처리하지 않은 시험편에 비해 낮은 최대열방출률과 낮은 총방출열량을 나타내었다.

• Journal of the Korean Wood Science and Technology
• /
• 제51권5호
• /
• pp.410-418
• /
• 2023

In this study, the combustion characteristics of the Tulip tree, which is the representative broad-leaved afforestation tree in Korea, were analyzed. The flame retardant performance of the Tulip tree was analyzed by analyzing combustion characteristics on a total of three test samples; flame retardant treated, both flame retardant and oil stain-treated, and untreated. Then the flame retardance grade was classified for each of them. According to the result, test samples showed the strongest flame retardance were in order of flame retardant treated (C), both flame retardant and oil stain-treated (B), and untreated (A). As a result of analyzing the total heat emission and maximum heat emission rates, which is the evaluation standard for interior materials of Korean domestic buildings, test samples with flame retardant treat or flame retardant and oil stain treat were qualified for the flame-retardant standard. Both flame retardant and oil stain-treated samples showed higher total heat release (THR) and heat release rate compared to flame retardant-treated samples as the oil causes combustion with oxygen. On the other hand, they didn't qualify the THR in Quasi-non-combustible standards. To determine the correlation between the physical and combustion characteristics of wood, the combustion characteristics of other diffuse porous wood species, with which the Tulip tree is affiliated were analyzed, and noticed that the characteristic correlates with the density and quantity of wood. The results of this study are expected to be used as basic information on the combustion characteristics of the Tulip tree.

• 한국안전학회지
• /
• 제32권3호
• /
• pp.28-33
• /
• 2017

In this study, the composite material of expandable graphite was made to the material development for improving such as a composite material of the sandwich panels or material properties of a fire door and was tested by the ISO 1182, ISO 5660-1(Cone calorimeter Method). For the test, the composite material of expandable graphite, what the expandable graphite ratio was increased by respectively 0g~30g, was classified A1,A2, A3, A4, and made to the test specimens. Through cone calorimeter test, peak heat release rate(HRR) and total heat release(THR), expanded thickness and expansion rate of each composite material of expandable graphite, and fire prone crack and mass loss rate after burning was measured. Thus, the effect of the addition of the expandable graphite and whether is suitable for reference as a fire retardant, was analyzed. Consequently the correlation of THR and fire retardant performance rate was confirmed.

• 한국연소학회지
• /
• 제22권4호
• /
• pp.1-8
• /
• 2017

This study was conducted to evaluate the fire retardant performance of exfoliated graphite nanoplatelets (xGnP) applied for particleboard. This work measured heat release rate(HRR), total heat release(THR) and smoke production rate(SPR) of xGnP added particleboard, using cone calorimeter to assess its fire characteristics according to the KS F ISO 5660-1 standard code. Heat release rates of all specimens treated by xGnP were less than the $200kW/m^2$ for a total experiment period of five minutes. Heat release rates of the specimens coated with xGnP were lower than those of the specimens made by mixing wood particles with xGnP directly. Meanwhile, the total heat release rates of xGnP coated specimen maintained quite lower level than the uncoated so the xGnP coating were effective in improving the fire retardant performance of particleboard. However, the smoke emission peaking problem at the initial combustion period, which was caused by adding base coating materials, should be resolved for further satisfaction as a fire retardant materials.

• 공업화학
• /
• 제21권4호
• /
• pp.469-474
• /
• 2010

목재는 연소성이 높은 본질적인 결함을 가지고 있다. 본 연구의 목적은 자연 건조된 굴참나무와 느티나무의 연소성질을 시험하였다. 열방출율과 CO/$CO_2$ 발생과 연기차폐와 같은 연기지수를 콘칼로리미터(ISO 5660-1)를 이용하여 측정하였다. $50kW/m^2$의 외부 열유속하에서 굴참나무의 총 방출열량, THR ($140.2MJ/m^2$)은 느티나무의 THR ($85.7MJ/m^2$) 과 비교하여 높게 나타났다. 그리고 굴참나무의 총 연기발생량, $TSP3.50m^2$는 느티나무의 $TSP0.65m^2$에 비하여 높게 나타났다. 이들 결과는 시험목의 체적밀도에 의존함을 보여준다. CO/$CO_2$ 발생비는 굴참나무와 느티나무가 각각 0.053, 0.043을 나타내었다. 또한 느티나무가 굴참나무에 비해 숯생성으로 인한 증대된 연소 억제성을 보여주었다.

• 한국안전학회지
• /
• 제30권3호
• /
• pp.38-44
• /
• 2015

For this study, fire tests were performed targeting household items (Sofa, Drawer, Refrigerator, Washing machine) using a large cone calorimeter (Large Scale Cone Calorimeter, LSC). The data were obtained focusing on the fire characteristic of the data when the actual fire occurs. The study results showed the following mean HRR of the household items; drawer 2843 KW, sofa 2939 KW, washing machine 719 KW, refrigerator 2907 KW, and THR is found in sofa 2202 MJ, drawer 1559 MJ, refrigerator 1193 MJ, washing machine 627 MJ. From the result, it could be found that the sofa can cause significant heat generation when the fire occurs, and the flashover tendency was found relatively high in compartment fire. In addition, a weight of the four our household items was reduced sharply in a similar time (20min before and after) degree after ignition. The drawer and sofa which has a high heat release can be considered to speed up the fire spread as their weight decrease rapidly and showed relatively weak to the fire compared to the refrigerator and washing machine.

• 한국화재소방학회논문지
• /
• 제25권5호
• /
• pp.69-75
• /
• 2011

수산화마그네슘을 첨가한 저밀도 폴리에틸렌-에틸렌 비닐 아세테이트 복합체의 연소성을 시험하였다. 저밀도 폴리에틸렌-에틸렌 비닐 아세테이트에 수산화마그네슘을 40~80 wt% 첨가하여 용융 혼합하고 성형 후 콘칼로리미터(ISO 5660-1)를 이용하여 연소성을 시험하였다. 수산화마그네슘을 첨가한 시편은 첨가하지 않은 시험편에 비하여 그의 플래시오버 가능성이 감소하였다. 이것은 순수한 저밀도 폴리에틸렌-에틸렌비닐 아세테이트에 첨가한 수산화마그네슘의 흡열 분해 때문에 연소 억제성이 향상된 것으로 생각된다. 수산화마그네슘을 첨가한 시험편은 첨가하지 않은 시험편에 비해 낮은 총열방출량과 낮은 CO 발생량을 나타내었고, 수산화마그네슘 함량이 증가할수록 총연기발생량과 비소화면적이 감소하였다.

• Composites Research
• /
• 제32권6호
• /
• pp.368-374
• /
• 2019

무기필러가 첨가된 현무암섬유 강화 에폭시 복합재료를 제조하여 그 특성을 평가하였다. 첨가된 무기필러는 각각 수산화마그네슘, 수산화알루미늄, 알루미나, 베마이트이며 이를 첨가제로한 에폭시 수지를 현무암섬유에 핸드레이업으로 함침시킨 후 hot pressing하여 수지 함침량이 30 wt%인 섬유복합재료를 제조하였다. LOI 평가 결과 BFRP의 LOI (28.9)는 에폭시 수지 (21.4)에 비해 향상된 것을 확인하였으며 무기필러가 첨가될 경우 그보다 더욱 향상되는 것을 확인하였다. 또한 무기필러가 첨가된 복합재료는 무기필러가 첨가되지 않은 복합재료에 비해 콘칼로리미터 시험에서 PHRR, THR, TSR 등이 감소하여 무기필러 첨가에 따른 난연 특성 향상을 확인하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제43권6호
• /
• pp.768-776
• /
• 2015

본 연구에서는 인도네시아 조림지에서 생장한 4수종의 효율적 활용방안을 마련하기 위해 콘칼로리미터법에 의해 연소특성을 조사하였다. 그 결과, 평균열방출량($HRR_{mean}$)은 비중에 비례하였으며, 총열방출량(THR) 및 연소시간(FT) 등열관련 계수도 같은 경향을 나타냈다. Albizia는 열방출 시간이 짧았고, Mindi는 4수종 중 점화시간(TTI)과 연소시간(FT)이 길어져 4수종 중 연소속도가 늦었고, 열방출 시간도 가장 길게 이어져 결국은 Mangium 수종과 비슷한 총열방출률을 나타내는 것을 확인할 수 있었다. Albizia는 공시수종 중 가장 높은 비소화면적 값을 나타내어 연기발생비율이 높았고, 반대로 Mindi는 가장 낮은 비소화면적 값을 나타내 연기발생비율이 낮았다. 초기 연기방출률은 Albizia가 높았으나 이후에는 Gmelina와 Mangium 의 연기방출률이 높아져 총연기발생량이 높게 나타났다. Gmelina는 불완전연소로 인해 연소기간 중 가장 많은 일산화탄소 연기를 생성하였고, $CO/CO_2$ 비율은 다른 수종에 비해 3배 이상 높았다.