• 한국세라믹학회지
• /
• 제34권2호
• /
• pp.123-130
• /
• 1997

본 연구에서는 유전상수가 크고, 유전체 손실이 적으며, 사용온도 범위에서 정전용량 변화율(TCC : tem-perature coefficient of capacitance)이 작고, 고압에 견딜 수 있는 재료를 개발하기 위하여 중고압용 capacitance의 기본재료로써 (Sr.Pb.Ca)TiO3-xBi2O3.3TiO2 계에서 Bi2O3.3TiO2의 mol.%를 5, 6, 7, 8, 9 mol.%로 변화시켰으며, 그 결과 고용한계 함량이 6mol.%이며, 6mol.%이상에서는 침상구조의 증가에 기인하여 유전율이 다시 감소하는 경향을 보였다. dopant로써 SiO2, Nb2O3, MnO2를 선정하여 첨가한 결과, MnO2를 첨가한 것이 유전성질이 가장 우수하였으며, MnO2의 함량이 0, 0.15, 0.3, 0.45 wt.% 증가함에 따라서 유전율의 감소와 동시에, TOC특성의 급격한 향상을 가져왔다.

• 한국재료학회지
• /
• 제31권10호
• /
• pp.552-561
• /
• 2021

For the purpose of manufacturing a high efficiency TiO₂ photocatalyst, B-doped TiO₂ photocatalysts are synthesized using a plasma electrolytic oxidation method in 0.5 M H₂SO₄ electrolyte with different concentrations of H₃BO₃ as additive. For the B doped TiO₂ layer fabricated from sulfuric electrolyte having a higher concentration of H₃BO₃ additive, the main XRD peaks of (101) and (200) anatase phase shift gradually toward the lower angle direction, indicating volume expansion of the TiO₂ anatase lattice by incorporation of boron, when compared with TiO₂ layers formed in sulfuric acid with lower concentration of additive. Moreover, XPS results indicate that the center of the binding energy peak of B1s increases from 191.45 eV to 191.98 eV, which suggests that most of boron atoms are doped interstitially in the TiO₂ layer rather than substitutionally. The B doped TiO₂ catalyst fabricated in sulfuric electrolyte with 1.0 M H₃BO₃ exhibits enhanced photocurrent response, and high efficiency and rate constant for dye degradation, which is ascribed to the synergistic effect of the new impurity energy band induced by introducing boron to the interstitial site and the improvement of charge transfer reaction.

• 한국세라믹학회지
• /
• 제35권3호
• /
• pp.287-293
• /
• 1998

The effects of B2O3 addition on the sintering behavior and th microwave dielectric properties of $(Mg_{0.93}Ca_{0.07})TiO_3$ ceramics were investigated. By addition of $B_2O_3$, increases the density of the ceramics increases and grain growth enhances, It was densified to over 94% of $(Mg_{0.93}Ca_{0.07})TiO_3$ theoretical density by the addition of 0.15-1.0wt% B2O3 and stable microwave dielectric properties observed by the addition of 0.2-0.4wt% $B_2O_3.\;(Mg_{0.93}Ca_{0.07})TiO_3$ ceramics sintered at $1200^{\circ}C$ exhibits maximum dielectric constants of 24-25 quality factor($Q{\times}f$) of more than 70000 and temperature coefficient of resonant frequency of $0\;ppm/^{\circ}C$ by adding of 0.15-0.4wt% $B_2O_3$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.381-384
• /
• 2001

The $\beta$-SiC+ZrB$_2$ and $\beta$-SiC+TiB$_2$ceramic electroconductive composites were pressureless-sintered and annealed by adding l2wt% A1$_2$ $O_3$+Y$_2$ $O_3$(6 : 4wt%) powder as a function of sintering temperature. The relative density showed highest value of 84.92% of the theoretical density for SiC-TiB$_2$ at 190$0^{\circ}C$ sintering temperature. The phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H), TiB$_2$, $Al_{5}$Y$_2$ $O_{12}$ and $\beta$-SiC(15R). Flexural strength showed the highest of 230 MPa for SiC-ZrB$_2$ composites sintered at 190$0^{\circ}C$. The vicker's hardness increased with increasing sintering temperature and showed the highest for SiC-ZrB$_2$ composites sintered at 190$0^{\circ}C$. Owing to YAG, the fracture toughness showed the highest of 6.50 MPa . m$^{1}$2/ for SiC-ZrB$_2$ composites at 190$0^{\circ}C$. The electrical resistivity was measured by the Rauw method from $25^{\circ}C$ to $700^{\circ}C$. The electrical resistivity of the composites showed the PTCR(Positive Temperature Coefficient Resistivity).).

• 한국세라믹학회지
• /
• 제32권7호
• /
• pp.817-824
• /
• 1995

TiB2 was simultaneously synthesized and densified with concurrent self-propagating high-temperature synthesis and direct contact-heating by electrcial power input and pressure. Density of TiB2 synthesized by self-propagating high-temperature synthesis and consolidated simultaneously by direct contact-heating and pressure was maximum 80% of the theoretical density (4.52g/㎤). Temperature profile was analyzed by solving heat balance equation with numerical method (FTCS method). The temperature of the sample was sufficiently raised to that temperature sufficient to be densified. It was ascertained that the density of the SHS synthesized TiB2 is exponentially proportinal to the input thermal energy per mass.

• The Korean Journal of Ceramics
• /
• 제5권2호
• /
• pp.155-161
• /
• 1999

The tribological behaviour of monolithic SiC as well as SiC-TiC and SiC-TiC-$TiB_2$ particulate composite materials has been investigated in unlubricated oscillating sliding tests against $Al_2O_3$ at temperature in the range from room temperature up to $600^{\circ}C$. At temperatures below $600^{\circ}C$ the wear rate of the systems with the composite materials was up to 20 times lower than the wear of the $Al_2O_3$/SiC system and was dominated by the oxidation of the titanium phases. At $600^{\circ}C$ the oxidation rate of the TiC and -TEX>$TiB_2$ grains becomes predominant resulting in an enhanced wear rate of the composite rate of the TiC and TiB2 grains becomes predominant resulting in an enhanced wear rate of the composite materials. The coefficient of friction shows similar values for all materials of investigation, increasing from 0.25…0.3 at room temperature to 0.7…0.8 $600^{\circ}C$. The wear of the $Al_2O_3$/SiC system is mainly abrasive at temperatures above room temperature and is characterised by an enhanced wear of the alumina ball at $600^{\circ}C$.

• Current Photovoltaic Research
• /
• 제4권1호
• /
• pp.8-11
• /
• 2016

Strong deep ultraviolet emitting aniline and $TiO_2$ composite has been synthesized via hydrolysis and condensation reactions of titaniumisopropoxide ($Ti(OPr)_4$), aniline, and acetic anhydride. Three different weight ratios of aniline and $Ti(OPr)_4$ including 3:1 ($TiO_2An-A$), 2:1 ($TiO_2An-B$), and 1:1 ($TiO_2An-C$) were synthesized and characterized their optical properties. The FTIR spectra of the $TiO_2An-A$, -B, and -C showed the absorption intensities of the benzene ring stretching and bending vibrations, and benzene ring -CH stretching, bending, and deformation vibrations increased with the increase of the amount of aniline. The UV-visible absorption spectra showed that the UV region absorption was slightly increased with the increase of the amount of aniline. The photoluminescence (PL) intensities were exponentially increased with the increase the excitation wavelength from 307 to 317 nm, steadily increased from 300 to 313 nm and slowly increased from 302 to 308 nm for $TiO_2An-A$, -B, and -C, respectively and decreased thereafter. Therefore, the PL intensity is strongly dependent on the weight ratio of $Ti(OPr)_4$ and aniline.

• 한국환경과학회:학술대회논문집
• /
• 한국환경과학회 2003년도 가을 학술발표회 발표논문집
• /
• pp.295-299
• /
• 2003

1. 고정화 $TiO_2$의 경우도 분말을 이용한 것과 같이 최적 광촉매 투입량이 나타났으며, 최적 투입량은 33.8 g/L이었고, 분말 $TiO_2$를 이용한 경우보다 빠른 초기반응속도를 보였으며, 최종반응시간도 빠른 것으로 나타났다. 2. 수용액에서 빠른 초기 제거속도의 1차적인 기작은 고정화 $TiO_2$ 표면으로의 흡착 때문이었으며, 빠른 흡착으로 인해 수용액 중의 RhB 농도가 빠르게 감소하여 광 투과율이 증가하므로 전체 반옹속도가 빠른 것으로 사료되었다. 3. 고정화 $TiO_2$를 이용한 유동층 반응기의 경우 최적 공기 공급량은 의한 Rhodamine B의 초기 제거속도는 분말보다 빠르지만 전체적인 제거시간은 흡착된 Rhodamine B의 분해 때문에 분말 $TiO_2$보다 느린 것으로 나타났다.

• 한국표면공학회지
• /
• 제34권1호
• /
• pp.25-32
• /
• 2001

$TiB_2$ ceramics were oxidized at 800, 900 and $1000^{\circ}C$ in air for 40 hr, and their oxidation property was investigated using TGA, XRD, SEM and EPMA. The oxidation resistance decreased with an increase in oxidation temperature. The scale was essentially composed of $TiO_2$ only. $B_2$$O_3$ formed during oxidation escaped from the $TiO_2$ oxide scale owing to its high vapor pressure. This made the oxide scale highly porous and thick. The oxidation reaction was mainly governed by the inward transport of oxygen.$ TiO_2$ existing at the outermost scale grew into peculiarly shaped blades, as the reaction progressed.

• 한국세라믹학회지
• /
• 제33권4호
• /
• pp.464-470
• /
• 1996

Toughening mechanism of boron carbide ceramics by the addition of titanium boride was investigated. Speci-men was prepared by hot pressing of boron carbide with upto 30vol% of titanium boride particulates. Toughness of boron carbide ceramics was increased from 4.7 MPa m1/2 to 6.3 MPa m1/2 with 15 vol% TiB2 addition. But further increase of TiB2 content results in slow decrease of toughness. From microstructure evaluation and crack propagation behavior it is concluded that the major toughening mechanism is crack deflection pheno-mena.