• Journal of Korea Foundry Society
• /
• v.28 no.1
• /
• pp.31-36
• /
• 2008

Ti-Ni-Cu alloys are very attractive shape memory alloys for applications as actuators because of a large transformation elongation and a small transformation hysteresis. Rapidly solidified Ti-Ni alloy ribbons have been known to have the shape memory effect and superelasticity superior to the alloy ingots fabricated by conventional casting. In this study, solidification structures and shape memory characteristics of $Ti-Ni_{30}-Cu_{20}$ alloy ribbons prepared by melt spinning were investigated by means of DSC and XRD. Operating parameters to fabricate the amorphous ribbons were the wheel velocity of 55 m/s and the melt spinning temperature of $1500^{\circ}C$. The crystallization temperature was measured to be $440^{\circ}C$. The crystallized ribbons exhibited very fine microstructure after annealing at $440^{\circ}C$ for 10 minutes and $460^{\circ}C$ for 5 minutes and was deformed up to about 6.8% and 6.23% in ductile manner, respectively. Stress-strain curve of the ribbon exhibited a flat stress-plateau at 64 MPa and this is associated with the stress-induced a B2-B19 martensitic transformation. During cycle deformation with the applied stress of 220 MPa, transformation hysteresis and elongation associated with the B2-B19 transformation were observed to be $4.3^{\circ}C$ and 3.6%.

• Journal of Powder Materials
• /
• v.7 no.2
• /
• pp.85-92
• /
• 2000

The Cu55Ti45 system was effectively mechanically-alloyed using a pulverizer. Noncrystallinities of the powders were characterized by TEM, X-ray and DSC. The amorphous powders were consolidated without losing their noncrystallinities. The consolidating conditions keeping a non-crystalline were obtained by building a TTT diagram of the amorphous powders. The microhardness of the crystallite and bulk amorphous alloys are also compared.

• Journal of the Korean Ceramic Society
• /
• v.35 no.1
• /
• pp.55-65
• /
• 1998

The oxidation behavior of Ag-36.8a%Cu-7.4at%Ti alloy brazed on Si3N4 substrate was investigated at 400, 500 and 600$^{\circ}C$ in air. Under this experimental condition Si3N4 and Ag were not oxidized whereas Cu and Ti among the brazing alloy components were oxidizied obeying the parabolic oxidation rate law. The activation energy of oxidation was found to be 80kj/ mol which was smaller than that of pure Cu owing to the presence of oxygen active element of Ti. The outer oxide scale formed from the initial oxidation state was always composed of Cu oxides which were known to be growing by the outward diffusion of Cu ions. As the oxidation progressed the concentration gradient occurred due to the continuous consumption of Cu as Cu oxides and consequently build-up of an Ag-enriched layer below the Cu oxides resulted in the formation of multiple oxide scales composed of Cu oxide (CuO) /Ag-enriched layer/Cu oxide (Cu2O) /Ag-enriched layer. Also the inward diffusing of oxygen through Cu oxide and Ag-enriched layers led to the formation of internal oxides of TiO2.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.1
• /
• pp.20-29
• /
• 1997

Pure copper is widely used for base material for electrical and electronic parts because of its good electrical conductivity. However, it has such a low strength that various alloying elements are added to copper to increase its strength. Nevertheless, alloying elements which exist as solid solution elements in copper matrix severely reduce the electrical conductivity. The reduction of electrical conductivity can be minimized and the strengthening can be maximized by TMT(Thermo-Mechanical Treatment) in copper alloys. In this research, the effects of TMT on mechanical and electrical properties of Cu-Ni-Al-Si-P, Cu-Ni-Al-Si-P-Zr and Cu-Ni-Si-P-Ti alloys aged at various temperatures were investigated. The Cu alloy with Ti showed the hardness of Hv 225, electrical conductivity of 59.8%IACS, tensile strength of 572MPa and elongation of 6.4%.

• Journal of Korea Foundry Society
• /
• v.22 no.6
• /
• pp.288-292
• /
• 2002

Ni-base amorphous alloys were manufactured using melt-spinning and Cu-mold die casting methods. Amorphous formability, the supercooled liquid region before crystallization and mechanical properties were examined. The reduced glass transition temperature and the supercooled liquid region of $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$alloy were 0.621 and 46 K respectively. $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$ alloy was produced in the rod shape 3mm diameter using the Cu-mold die casting. Hardness, compression strength, elongation and elastic modulus of the alloy were 850 DPN, 2.75 GPa, 1.8% and 150 GPa respectively. Moreover, compression strength of 2.75 GPa was the highest value in the amorphous bulk alloy produced up to now.

• Journal of Korea Foundry Society
• /
• v.21 no.5
• /
• pp.286-289
• /
• 2001

The glass formation behavior was investigated in the melt spun Zr-Ti-Cu-Ni-X (X=B, P and Si) ribbons. The magnitude of supercooled liquid region of Zr-Ti-Cu-Ni alloy increased with an addition of alloying element. The glass transition temperature and the crystallization temperature increased and the magnitude of supercooled liquid region decreased with increasing the content of alloying elements. The largest supercooled liquid region was observed in the Si containing alloy. This is believed to be due to the dense atom packing with the optimum atomic size ratio of constituent elements.

• Journal of Powder Materials
• /
• v.9 no.6
• /
• pp.394-408
• /
• 2002

Nanostructured high strength metastable Al-, Mg- and Ti-based alloys containing different amorphous, quasicrystalline and nanocrystalline phases are synthesized by non-equilibrium processing techniques. Such alloys can be prepared by quenching from the melt or by powder metallurgy techniques. This paper focuses on one hand on mechanically alloyed and ball milled powders containing different volume fractions of amorphous or nano-(quasi)crystalline phases, consolidated bulk specimens and, on the other hand. on cast specimens containing different constituent phases with different length-scale. As one example. $Mg_{55}Y_{15}Cu_{30}$- based metallic glass matrix composites are produced by mechanical alloying of elemental powder mixtures containing up to 30 vol.% $Y_2O_3$ particles. The comparison with the particle-free metallic glass reveals that the nanosized second phase oxide particles do not significantly affect the glass-forming ability upon mechanical alloying despite some limited particle dissolution. A supercooled liquid region with an extension of about 50 K can be maintained in the presence of the oxides. The distinct viscosity decrease in the supercooled liquid regime allows to consolidate the powders into bulk samples by uniaxial hot pressing. The $Y_2O_3$ additions increase the mechanical strength of the composites compared to the $Mg_{55}Y_{15}Cu_{30}$ metallic glass. The second example deals with Al-Mn-Ce and Al-Cu-Fe composites with quasicrystalline particles as reinforcements, which are prepared by quenching from the melt and by powder metallurgy. $Al_{98-x}Mn_xCe_2$ (x =5,6,7) melt-spun ribbons containing a major quasicrystalline phase coexisting with an Al-matrix on a nanometer scale are pulverized by ball milling. The powders are consolidated by hot extrusion. Grain growth during consolidation causes the formation of a micrometer-scale microstructure. Mechanical alloying of $Al_{63}Cu_{25}Fe_{12}$ leads to single-phase quasicrystalline powders. which are blended with different volume fractions of pure Al-powder and hot extruded forming $Al_{100-x}$$(Al_{0.63}Cu_{0.25}Fe_{0.12})_x$ (x = 40,50,60,80) micrometer-scale composites. Compression test data reveal a high yield strength of ${\sigma}_y{\geq}$700 MPa and a ductility of ${\varepsilon}_{pl}{\geq}$5% for than the Al-Mn-Ce bulk samples. The strength level of the Al-Cu-Fe alloys is ${\sigma}_y{\leq}$550 MPa significantly lower. By the addition of different amounts of aluminum, the mechanical properties can be tuned to a wide range. Finally, a bulk metallic glass-forming Ti-Cu-Ni-Sn alloy with in situ formed composite microstructure prepared by both centrifugal and injection casting presents more than 6% plastic strain under compressive stress at room temperature. The in situ formed composite contains dendritic hcp Ti solid solution precipitates and a few $Ti_3Sn,\;{\beta}$-(Cu, Sn) grains dispersed in a glassy matrix. The composite micro- structure can avoid the development of the highly localized shear bands typical for the room temperature defor-mation of monolithic glasses. Instead, widely developed shear bands with evident protuberance are observed. resulting in significant yielding and homogeneous plastic deformation over the entire sample.

• Nuclear Engineering and Technology
• /
• v.25 no.4
• /
• pp.507-514
• /
• 1993

Titanium tubes have recently been used in condensers of nuclear power plants since titanium has very good corrosion resistance to seawater. However, when it is connected to Cu alloys as tube sheet materials and these Cu alloys are connected to carbon steels as water box materials, it makes significant galvanic corrosion on connected materials. It is expected from electrochemical tests that the corrosion rate of carbon steel will increase when it is galvanically coupled with Ti or Cu in sea water and the corrosion rate of Cu will increase when it is coupled with Ti, if this couple is exposed to sea water for a long time. It is also expected that the surface area ratios, R$_1$(surface area of carbon steel/surface area of Ti) and R$_2$(surface area of carbon steel/surface area of Cu) are very important for the galvanic corrosion of carbon steel and that these should not be kept to low values in order to minimize the galvanic corrosion on the carbon steel of the water box. Immersed galvanic corrosion tests show that the corrosion rate of carbon steel is 4.4 mpy when the ratio of surface area of Fe/ surface area of Al Brass is 1 while it is 570 mpy when this ratio is 10$^{-2}$ . The galvanic corrosion rate of this carbon steel is increased from 4.4 mpy to 13 mpy at this area ratio, 1, when this connected galvanic specimen is galvanically coupled with a Ti tube. This can be rationalized by the combined effects of R$_1$ and R$_2$ on the polarization curve.

• Korean Journal of Materials Research
• /
• v.29 no.4
• /
• pp.258-263
• /
• 2019

Since the directly bonded interface between TiAl alloy and SCM440 includes lots of cracks and generated intermetallic compounds(IMCs) such as TiC, FeTi, and $Fe_2Ti$, the interfacial strength can be significantly reduced. Therefore, in this study, Cu is selected as an insert metal to improve the lower tensile strength of the joint between TiAl alloy and SCM440 during friction welding. As a result, newly formed IMCs, such as $Cu_2TiAl$, CuTiAl, and $TiCu_2$, are found at the interface between TiAl alloy and Cu layer and the thickness of IMCs layers is found to vary with friction time. In addition, to determine the relationship between the thickness of the IMCs and the strength of the welded interfaces, a tensile test was performed using sub-size specimens obtained from the center to the peripheral region of the friction-welded interface. The results are discussed in terms of changes in the IMCs and the underlying deformation mechanism. Finally, it is found that the friction welding process needs to be idealized because IMCs generated between TiAl alloy and Cu act to not only increase the bonding strength but also form an easy path of fracture propagation.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.6
• /
• pp.309-314
• /
• 2021

Due to the superior corrosion resistance and mechanical properties of TiAl alloy at high temperature, it has been utilized as a turbine wheel of a turbocharger. The dissimilar metallic bonding is usually applied to combine the TiAl turbine wheel with the SCM440 structural steel which is used as a driving shaft. In this study, the TiAl and SCM440 joint were fabricated by using a friction welding technique. During bonding process, to suppress the martensitic transformation and the formation of cracks, which might reduce a strength of the joints, Cu was used as an insert metal to relieve stress. As a result, the intermetallic compounds (IMCs) layer was observed at TiAl/Cu interface while no IMC formation was formed at SCM440/Cu interface. Since understanding of the IMCs effects on the mechanical performance of welded joint is also essential for ensuring the reliability and integrity of the turbocharger system, we estimated the nanohardness of welded joint region through nanoindentation. The relation between the microstructural feature and its mechanical property is discussed in detail.