• Journal of the Korean Solar Energy Society
• /
• v.30 no.3
• /
• pp.90-97
• /
• 2010

$TiO_2$ thin films for solar energy utilization were prepared on ITO coated glass by r.f magnetron sputtering with variations of working pressure, oxygen flow rate and annealing temperature. Ion insertion and extraction reaction, and ion storage properties of films were investigated by using a cyclic voltammetry. Transmittance of thin films in as-prepared, colored and bleached states was measured by UV-VIS spectrophotometer. The samples deposited in our sputtering conditions showed poor electrochromic properties. Improvement in ion storage properties of $TiO_2$ thin film was observed after annealing at temperature of $400^{\circ}C$ in air for 2 hours. It was found that $TiO_2$ thin film in electrochromic device could be used as a passive counter-electrode.

• Journal of the Korean Ceramic Society
• /
• v.34 no.4
• /
• pp.373-379
• /
• 1997

A study on the deposition and characterization of BaTiO3 thin films on MgO-buffered Si(100) substrates by sputtering was conducted. The MgO buffer layers were investigated as a function of deposition temperature. At lower substrate temperature, the MgO layers were not fully crystalline, but a crystallized MgO layer with (001) preferred orientation was obtained at the substrate temperature of $700^{\circ}C$. Partially (00ι) or (h00) textured BaTiO3 films were obtained on Si(100) with the MgO buffer layer grown at 700ι. While, randomly oriented BaTiO3 films with large-scale cracks on the surface were made without the MgO layer. The crystallographic orientation, morphology and electrical properties between the BaTiO3 films on Si with and without the MgO layer were compared using the BaTiO3 film on MgO(100) single crystal substrate as a reference system. Also the favorable role of the MgO layer as a buffer for growing of oriented BaTiO3 films on Si substrates was confirmed.

• Journal of Powder Materials
• /
• v.31 no.3
• /
• pp.255-262
• /
• 2024

Nano-oxide dispersion-strengthened (ODS) superalloys have attracted attention because of their outstanding mechanical reinforcement mechanism. Dispersed oxides increase the material's strength by preventing grain growth and recrystallization, as well as increasing creep resistance. In this research, atomic layer deposition (ALD) was applied to synthesize an ODS alloy. It is useful to coat conformal thin films even on complex matrix shapes, such as nanorods or powders. We coated an Nb-Si-based superalloy with TiO₂ thin film by using rotary-reactor type thermal ALD. TiO₂ was grown by controlling the deposition recipe, reactor temperature, N₂ flow rate, and rotor speed. We could confirm the formation of uniform TiO₂ film on the surface of the superalloy. This process was successfully applied to the synthesis of an ODS alloy, which could be a new field of ALD applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.649-652
• /
• 1999

The (Ba, Sr)TiO$_3$(BST) thin films were fabricated on Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with substrate temperature by XRD, SEM, EDS and AES depth profils. Increasing the substrate temperature, barium multi titanate phases were decreased. The BST thin film had a structure of perovskite type, and had peaks of (100), (200) at the substrate temperature of 50$0^{\circ}C$. When the BST thin films were deposited at the substrate temperature of 50$0^{\circ}C$, the composition ratio of Ba/sr was 52/48.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.197-197
• /
• 2008

There are fast growing demands for new dielectric materials for passive capacitors of RF-ICs and other wireless applications. One of the bulk microwave dielectric materials which have superior properties is $ZrTiO_4$ due to its large dielectric constant and high quality factor. Therefore, $ZrTiO_4$ is worth studying as a form of thin film to be applied for passive capacitors of integrated circuits. In this study, we fabricated metal-insulator-metal type capacitors with $ZrTiO_4$ dielectric thin film, and evaluated their capacitor properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.104-107
• /
• 2001

The fabricated La-modified lead titanate (PLT) thin flim without paling treatment was investigated for modulation frequency dependence of pyroelectric properties by the dynamic method. $Pb_{1-x}La_{x}Ti_{1-x/4}O_{3}$ PLT (x=0.1) thin film having 10 mol% La content was deposited on a $Pt/TiO_{x}/SiO_{2}/Si$ substrate by sol-gel method. The PLT(10) thin film exhibits a relatively excellent dielectric property. The pyroelectric coefficient (p) of the PLT(10) thin film is $6.6{\times}10^{-9}C/cm_{2}\cdot K$ without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are $1.03{\times}10^{-11}C\cdot cm/J$ and $1.46\times 10^{-9}C\cdot cm/J$, respectively. The PLT(10) thin film has voltage responsivity (Rv) of 5.15 V/W at 8 Hz. Noise equivalent power (NEP) and specific detectivity (D*) of the PLT(10) thin film are$9.93{\times}10^{-8}W/Hz^{1/2}$ and $1.81\times 10^{6}cmHz^{1/2}/W$ at the same frequency of 100 Hz, respectively. The results means that PLT thin film having 10 mol % La content is suitable for the sensing materials of pyroelectric IR sensors.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.104-107
• /
• 2001

The fabricated La-modified lead titanate (PLT) thin flirt without poling treatment was investigated for modulation frequency dependence of pyroelectric properties by the dynamic method. $Pb_{1-x}La_{x}Ti_{1-x/4}O_3$PLT (x=0.1) thin film having 10 mol% La content was deposited on a Pt/$TiO_{x}$/$SiO_2$/Si substrate by sol-gel method. The PLT(10) thin film exhibits a relatively excellent dielectric property. The pyroelectric coefficient (p) of the PLT(10) thin film is 6.6 x $10^{-9}$C/$\textrm{cm}^2$.K without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are 1.03${\times}$$10^{-11}$/C.cm/J and 1.46 x $10^{-9}$C.cm/J, respectively. The PLT(10) thin film has voltage responsivity ($R_{V}$) of 5.15 V/W at 8 Hz. Noise equivalent power (NEP) and specific detectivity (D＊) of the PLT(10) thin film are 9.93 x $10^{-8}$W/Hz$^{1/2}$ and 1.81 x $10^{6}$ cmHz$^{1/2}$/W at the same frequency of 100 Hz, respectively. The results means that PLT thin film having 10 mol % La content is suitable for the sensing materials of pyroelectric IR sensors.

• Journal of Korean Ophthalmic Optics Society
• /
• v.13 no.1
• /
• pp.59-63
• /
• 2008

Purpose: Ti thin films were deposited on slide glass and CR-39 lenses using small magnetron sputtering apparatus to of Ti thin films. Methods: The thickness of Ti thin films were measured by cross section SEM, the transmittance and reflectance of them were obtained using spectrophotometer, the refractive index and extinction of them were obtained from VASE data. Results: The transmittances of Ti thin films with 60 nm, 120 nm, 140 nm thickness were a little change within the visual region from 400 nm to 750 nm, but were increased a little amount at near 400 nm. The transmittance of 60 nm, 120 nm, 140 nm Ti thickness in d-line was 30%, 25%, 20%, respectively. Also, it was shown that the refractive indices and extinction coefficients of the Ti thin films obtained from VASE were similar to those of Ti thin film offered macleod program. Conclusions: Ti films on CR-39 with these transmittances were available for sunglass lens. It was indicated that the refractive indices and extinction coefficients of the Ti thin films were decreased with the thickness of Ti thin film, for the thickness of Ti thin films was due to very thin.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.11
• /
• pp.526-530
• /
• 2002

The $(Sr_{0.9}Ca_{0.1})TiO_3(SCT)$ thin films were deposited on Pt-coated electrode (Pt/TiN/$SiO_2$/Si) using RF sputtering method. The composition of SCT thin film deposited on Si substrate at room temperature is close to stoichiometry(1.081 in A/B ratio). The maximum dielectric constant of SCT thin film was obtained by ammealing at $600^{\cric}C$. The temperature dependence of dielectric loss showed a value within 0.02 in temperature ranges of -80 ${\sim}$ +90$^{\circ}C$. The capacitance characteristics showed a stable value within ${\pm}$4%. The drastic decrease of dielectric constant and increase of dielectric loss in SCT thin films was observed at the frequency above 200kHz.

• Korean Journal of Materials Research
• /
• v.3 no.1
• /
• pp.19-27
• /
• 1993

Abstract The PZT thin film was deposited by usin. RF magnetron sputtering with PZT(52/48) target. The formation of perovskite structure PZT thin film started at 55$0^{\circ}C$ on Si substrate. The AES results showed an oxide layer formed at the between Si and PZT film during the annealing. And, Ti$O_2$ layer appeared at the between TiN and PZT film for the annealing. But, the perovskite phase PZT film was formed after the annealing on the Si$O_2$/Si substarte. The ratio in PZT film was constant across the asdeposited PZT film, but, Pb have diffused into the Si substrate and Si have out-diffused into PZT layer during the post annealing at 75$0^{\circ}C$. The dielectric constants of PZT film indicated about 1300( thickness: 1500$\AA$, at 10KHz) but, the cracks were appeared to surface for annealing.