• 한국표면공학회지
• /
• 제35권4호
• /
• pp.199-205
• /
• 2002

TiN and TiAlN films were deposited on SKD 11 steel substrates by an arc ion plating (AIP) technique. The crystallinity and morphology for the deposited films were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The mechanical properties of both films were investigated through the indentation, impact, and wear test. Those films fairly adherent to SKD 11 steel substrate, showed hardness values of 2300 $\pm$ 100kg/$\textrm{mm}^2$ and 3200 $\pm$ 100kg/$\textrm{mm}^2$ with a load of 25g, respectively. During impact test, TiAlN films showed much superior impact wear resistance to TiN films. It could be suggested that the TiN films was failed relatively by plastic deformation with oxidation during impact test, while TiAlN films was failed by brittle fracture and resisted the oxidation by the impact energy. The friction coefficient of TiAlN films became lower than that of TiN films at high sliding speed condition although it was higher than that of TiN films at low speed. Therefore, TiAlN films was suggested to be more advantageous than TiN films for high speed machining fields.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2003년도 춘계학술대회논문집
• /
• pp.99-104
• /
• 2003

TiN coated films show a good mechanical properties, high thermal properties and wear, erosion and corrosion resistance and are widely used as a coating materials in tools, ornaments, parts and semiconductors. In spite of these good properties, the fracture of TiN coated films occur during use. The fracture of TiN thin films is related to their microstructure. Especially, the life of TiN coated layer is related to the texture of the TiN films. One researcher suggested that the corrosion and erosion resistance of the TiN thin films is related to a uniform and dense structure of films. In this study, we studied the relationships between textures and friction coefficient, erosion and corrosion in TiN coated films. The flatness of (115) texture surface of TiN thin films is flatter than that of (111) texture surface. The friction coefficient of (115) texture surface of TiN thin films is similar with that of (111) texture surface. The wear resistance of (115) texture surface of TiN thin films is better than that of (111) texture surface. The erosion and corrosion resistance of (115) texture surface of TiN thin films is better than that of (111) torture surface. As well as texture, the wear, erosion and corrosion of TiN thin films has to consider defects such as pinholes, cracks, surface roughness and open columnar structure. The life of TiN coated products is influenced by the properties of wear, erosion, and corrosion resistance of TiN thin films and is related to texture of TiN coated films, density of pinholes and cracks, density of structure, and surface flatness.

• 한국표면공학회지
• /
• 제25권5호
• /
• pp.235-252
• /
• 1992

(Ti, Al)N films were deposited on 304 stainless steel sheet by D.C. magnetron sputtering using Al target and Ti plate. The high temperature oxidation of (T, Al)N films with the variation of composition has been investigated. The chemical composition of (Ti, Al)N films with the variation of composition has been investigated. The chemical composition of (Ti, Al)N films was similar to the sputter area ratio of titanium to aluminum target by means of EDS and AES survey. The high temperature oxidation test of (Ti, Al)N showed that (Ti, Al)N has better high temperature resistance than TiN and TiC films. TiC films were cracked at 40$0^{\circ}C$ in air TiN films quickly were oxidised at $600^{\circ}C$, were spalled more than $700^{\circ}C$. But (Ti, Al)N films are relatively stable to$ 900^{\circ}C$. The good resistance to high temperature oxida-tion of (Ti, Al)N films are due to the formation of dense Al2O3 and TiO2 oxide layer. Especially, Al2O3 oxide layer is more important. The results obtained from this study show, it is believe that the (Ti, Al)N film by D.C. magnetron sputtering is promising for the use of high temperature and wear resistance mate-rials.

• 한국진공학회지
• /
• 제11권3호
• /
• pp.159-165
• /
• 2002

본 연구에서는 $TiCl_4$과 $NH_3$을 이용하여 atomic layer deposition(ALD)법으로 TiN막을 증착한 후, 그 막의 특성에 관하여 조사하였다. 최적 공정조건에서 TiN막의 성장률은 cycle당 두께가 약 0.6 $\AA$인 것으로 나타났고, 비저항은 반응온도 구간에서 200~350 $\mu\Omega$cm 수준으로 낮게 얻어졌다. XRD분석결과 TiN-ALD온도구간에서 TiN막이 결정화되었음을 알 수 있었다. AES 분석결과 Cl불순물의 함량이 거의 없는 상태(<1 at%)로 나타났고, TiN막에서의 Ti:N비가 1:1인 것으로 보아 거의 균일하게 형성되었음을 알 수 있었다. 또한 SEM관찰로 Aspect ratio 10:1의 trench 내에 형성된 TiN막의 스텝.커버리지는 극히 우수함을 알 수 있었다.

• Transactions on Electrical and Electronic Materials
• /
• 제14권5호
• /
• pp.242-245
• /
• 2013

Sn-doped $In_2O_3$ (ITO) thin films were prepared by radio frequency magnetron sputtering without intentional substrate heating on bare glass and $TiO_2$-deposited glass substrates to investigate the effect of a $TiO_2$ buffer layer on the electrical and optical properties of ITO films. The thicknesses of $TiO_2$ and ITO films were kept constant at 5 and 100 nm, respectively. As-deposited ITO single layer films show an optical transmittance of 75.9%, while $ITO/TiO_2$ bi-layered films show a lower transmittance of 76.1%. However, as-deposited $ITO/TiO_2$ films show a lower resistivity ($9.87{\times}10^{-4}{\Omega}cm$) than that of ITO single layer films. In addition, the work function of the ITO film is affected by the $TiO_2$ buffer layer, with the $ITO/TiO_2$ films having a higher work-function (5.0 eV) than that of the ITO single layer films. The experimental results indicate that a 5-nm-thick $TiO_2$ buffer layer on the $ITO/TiO_2$ films results in better performance than conventional ITO single layer films.

• 한국세라믹학회지
• /
• 제49권6호
• /
• pp.642-647
• /
• 2012

$TiO_2$ thin films for a pulse power capacitor were deposited by RF magnetron sputtering. The effects of the deposition gas ratio and thickness on the crystallization and electrical properties of the $TiO_2$ films were investigated. The crystal structure of $TiO_2$ films deposited on Si substrates at room temperature changed to the anatase from the rutile phase with an increase in the oxygen partial pressure. Also, the crystallinity of the $TiO_2$ films was enhanced with an increase in the thickness of the films. However, $TiO_2$ films deposited on a PET substrate showed an amorphous structure, unlike those deposited on a Si substrate. An X-ray photoelectron spectroscopy(XPS) analysis revealed the formation of chemically stable $TiO_2$ films. The dielectric constant of the $TiO_2$ films as a function of the frequency was significantly changed with the thickness of the films. The films showed a dielectric constant of 100~110 at 1 kHz. However, the dissipation factors of the films were relatively high. Films with a thickness of about 1000nm showed a breakdown strength that exceeded 1000 kV/cm.

• 한국표면공학회지
• /
• 제41권6호
• /
• pp.264-268
• /
• 2008

Interaction between human osteoblast and TiN films was conducted in vitro. TiN films were produced by cathodic arc plasma deposition. The surface was characterized by atomic force microscopy (AFM). TiN films, glass substrates and Ti films were cultured with human osteoblasts for 48 and 72 h hours. Actin stress fiber patterns and microtubules of osteoblasts were found slightly more organized and distributed on TiN films compared to those on the Ti films and the glass substrates. Human osteoblasts also showed slightly higher cell attachment, proliferation, and focal contact adhesion on TiN films compared to those on Ti films and glass substrates. Our results demonstrated that TiN films showed slightly better cellular adhesion of osteoblasts than Ti films and glass substrates in a short-time culture period.

• 전기학회논문지
• /
• 제62권2호
• /
• pp.284-287
• /
• 2013

In this work, we have fabricated TiC films by using unbalanced magnetron sputtering method with graphite and Ti targets for contact strip application of electric railway. TiC films were deposited with various substrate temperatures. We investigated various properties of TiC films prepared with various substrate temperatures, such as the hardness, surface roughness, friction coefficient, resistivity, FESEM (Field Emission Scanning Electron Microscopy), HRTEM (High Resolution Transmission Electron Microscopy) and XPS (X-ray Photoelectron Spectroscopy). The hardness and friction coefficient properties of TiC films were improved with increasing substrate temperature. These results indicate that the improvement of hardness and resistivity is related to the increase of sp2 clusters in TiC films. And also, the resistivity value of TiC films were decreased with increasing substrate temperature.

• 마이크로전자및패키징학회지
• /
• 제7권2호
• /
• pp.37-42
• /
• 2000

저유전상수 폴리머와 $SiO_2$위에 형성된 Al/Ti박막의 우선방위에 대해 비교하였다. DC 마그네트론 스퍼터를 이용하여 50 nm 두께의 Ti과 500 nm의 Al-1%Si-0.5%Cu(wt%) 합금 박막을 저유전상수 폴리머와 $SiO_2$기판위에 증착하였다. Al의 우선방위는 XRD $\theta$-2$\theta$와 rocking curve로 측정하였고, Al/Ti박막의 미세조직은 투과전자현미경 (TEM)으로 관찰하였다. 저 유전상수 폴리머 위에 증착된 Al/Ti박막은 $SiO_2$위에 증착된 것보다 낮은 우선방위를 가졌다. 단면 TEM으로 Ti을 관찰한 결과, $SiO_2$위의 Ti의 결정립은 기판에 수직하게 성장하였으나 저유전상수 폴리머 위의 Ti 결정립은 등축정으로 성장하였으며, 저유전상수 폴리머위의 Al/Ti박막이 낮은 우선방위를 갖는 이유는 Ti 미세조직 때문이었다.

• Journal of Ceramic Processing Research
• /
• 제13권spc1호
• /
• pp.149-153
• /
• 2012

Ti2AlN MAX-phase films were synthesized through the post-annealing process of as-deposited Ti-Al-N films. Near amorphous or quasi-crystalline ternary Ti-Al-N films were deposited on Si and Al2O3 substrates by sputtering a Ti2AlN MAX-phase target at room temperature, 300 ℃ and 450 ℃, respectively. A vacuum annealing of those films at 800 ℃ for 1 hour changed those films to crystalline Ti2AlN MAX-phase. The polycrystalline Ti2AlN MAX-phase films exhibited very excellent oxidation resistance due to its characteristics microstructure (nanolaminates), which has potential applications for high-temperature protective coatings. The microstructure and composition of Ti2AlN MAX-phase films were investigated using with a variety of characterization tools.