• Corrosion Science and Technology
• /
• v.14 no.4
• /
• pp.161-165
• /
• 2015

This paper presents an analysis of thermal stress induced along the interface between a polymeric coating layer and a steel substrate as a result of uniform temperature change. The epoxy layer is assumed to be a linear viscoelastic material and to be theromorheologically simple. The viscoelastic boundary element method is employed to investigate the behavior of interface stresses. The numerical results exhibit relaxation of interface stresses and large stress gradients, which are observed in the vicinity of the free surface. Since the exceedingly large stresses cannot be borne by the polymeric coating layer, local cracking or delamination can occur at the interface corner.

• Tribology and Lubricants
• /
• v.13 no.3
• /
• pp.85-92
• /
• 1997

An experimental study was performed to discover the tribological behaviors of pure silver coated 52100 bearing steel. Pure silver coatings ranging from 80 nm to several micrometers were produced by a thermal evaporation coating method. Experiments using a thrust ball bearing-typed rolling test-rig were performed for the investigations of the influence of coating thickness on the tribological rolling behavior. The existence of optimum film thickness which revealed minimum rolling resistance was discovered. A careful analysis on the contact surfaces for the optimum film thickness has been performed. The contact patches produced by the transferred silver films played an important role for the rolling resistance to keep low.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.05a
• /
• pp.140-141
• /
• 2021

Arc thermal spray process is widely used to protect the steel from corrosion and abrasion. In the present study, two different coatings i.e. Al and Al-5%Mg were used to compare their corrosion resistance performance and the effect of 5% Mg addition in the properties of deposited coating. The SEM results showed the more compact and less porous morphology of Al-5%Mg coating compared to Al. The corrosion resistance performance of both deposited coatings was studied in artificial ocean water with exposure periods and results are compared. The total impedance values of Al-5%Mg at 0.01 Hz exhibited highest with exposure periods might be attributed to the coating and corrosion products nature and morphology compared to Al coating.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.1
• /
• pp.49-60
• /
• 1999

The protective oxide scales and coatings formed on high temperature materials must be preserved in high temperature atmosphere. And the thermal stresses induced by thermal cycling and the growth stresses by the formation of oxide scales can cause the loss of adherence and spalling of the oxide scales and coated layers. Among the coating processes Al diffusion coating is favored due to thermochemical stability and superior adherence in an hostile atmosphere. In this study, protective oxide forming element, Al was coated on Ni, Inconel 600 and 690 by diffusion coating process varying coating temperature and time. And the surface stability and adherence of oxide scales formed on those Al diffusion coated materials were evaluated by thermal cycling test. Al diffusion coated specimens showed superior cyclic oxidation resistance compared to bare ones and specimens coated for longer period had better cyclic oxidation resistance, due to the abundant amount of Al in the coated layer. Meanwhile Al diffusion coated Inconel 600 and 690 showed improved cyclic oxidation resistance by the effect of Al in the coated layer and Cr in the substrate. Comparing both Al diffusion coated Inconel 600 and 690, Al diffusion coated Inconel 690 maintained better adhesion between coated layer and substrate by virtue of the bridging effect resulting from the segregation of Cr in the interdiffusion zone.

• Journal of the Semiconductor & Display Technology
• /
• v.23 no.1
• /
• pp.88-91
• /
• 2024

The europium doped yttrium oxide (Y₂O₃:Eu³⁺) thin film was formed on a Si substrate by the conventional spin-coating process followed by rapid thermal annealing (RTA) treatment. The spinning profiles such as rotation speed, acceleration and holding times were controlled during the spin-coating process for the best condition of the Y₂O₃:Eu³⁺ thin film. The RTA treatment was conducted for several temperature in order to crystallize the spin coated film. The Y₂O₃:Eu³⁺ thin film presented best performance in the conditions of 4000 rpm, 30 s and 10 s of rotation speed, acceleration time and holding time, respectively, at a fixed RTA temperature of 900 ℃.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.34.2-34.2
• /
• 2009

The ceramic coatings on metallic materials have attracted by many researchers due to the chemical inertness of ceramic materials. In such aspect, SiOC is a promising material tobe used as protective coating layer on metallic materials due to its outstanding thermal stability and chemical inertness. In this research, SiOC coating was carried out onto SuS-316 substrate using Cl free preceramic polymers such aspolyphenylcarbosilane. 20% of polymethylphenylsilane in cyclohexane solution was coated onto metal surface by dip coating method. Thermal oxidation was carried out at $200^{\circ}C$ for crosslink of the preceramic polymer and the sample was pyrolysized at $800^{\circ}C$ under argon to convert the preceramic polymer to amorphous SiOCx state. The microstructure of the SiOCx film after pyrolysis was investigated using FE-SEM. Corrosion resistance of SiOC coated SuS-316 substrate has been investigated using 5% HCl solution at 25, 40, 60 and $80^{\circ}C$ for 7days. The data revealed that the corrosion resistance increased with SiOC coating on SuS-316 substrate.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1930-1932
• /
• 2005

Colloidal Silica(CS)/methyltrimethoxy silane(MTMS) and CS/MTMS/epoxy silane(Es) sol solutions were prepared in variation with synthesizing parameters such as kinds of CS, kinds of silane and reaction time. In order to understand its physical and chemical properties, sol-gel coating films on glass were fabricated. In the case of CS/MTMS sol, the coating films had high contact angle and more enhanced flat surface than those in the case of CS/MTMS/ES sol. Also, the coating films obtained from single CS had a better flat surface than those obtained from mixed CS. In the case of thermal stability, thermal dissociation of CS/MTMS and CS/MTMS/ES sol-gel coating films did not occur up to $550^{\circ}C$ and $440^{\circ}C$ respectively. The thickness of coating films obtained from CS/MTMS sol increased than those of CS/MTMS/ES sol. In addition, the coating films obtained from single CS were more thicker than those obtained from mixed CS.

• Proceedings of the KWS Conference
• /
• 1990.11a
• /
• pp.140-144
• /
• 1990

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.7
• /
• pp.2134-2140
• /
• 1996

This study was carried out to anlayze the heat-resistant characteristics of functionally gradient material(FGM) composed with ceramic and metal. The thermal fracture behavior of plasma-sprayed FGM and conventional coating material(NFGM) was exaimined by acoustic emession technique under heating and cooling. Furnace cooling and rapid cooling tests were used to examine the effect of temperature change under various conditions, respectively. At the high temperature above $800^{\circ}C$, it was shown that FGM gives higher thermal resistance compared to NFGM by AE signal and fracture surface analysis.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.2
• /
• pp.91-98
• /
• 1994

For the plasma sprayed as well as the EB-PVD thermal barrier coatings, the fracture paths within the oxidation products developed at the interface between the partially stabilized zirconia ceramic coating and NiCoCrAlY bond coat during cyclic thermal oxidation has been investigated. It was observed that the fracture in the oxidation products primarily took place within the oxide such as $Ni_{1-x}Co_3(Al_,Cr)_2O_4$ or at the interface between the oxide and $Al_2O_3$. It was found that Al2O3 developed first, followed by the Ni/Co/Cr rich oxides such as ,,$Ni_{1-x}Co_x(Al_,Cr)_2O_4$ $Cr_2O_3$and NiO at the interface between the ceramic coating and the bond coat in a cyclic high temperature environment. It was therfore concluded that the formation of the oxide containing Ni, Cr and Co was a life-limiting event for thermal barrier coatings during cyclic thermal oxidation.