• 한국재료학회지
• /
• 제17권5호
• /
• pp.263-267
• /
• 2007

Hafnium oxide $(HfO_2)$ films were deposited on Si(100) substrates by remote plasma-enhanced atomic layer deposition (PEALD) method at $250^{\circ}C$ using TEMAH [tetrakis(ethylmethylamino)hafnium] and $O_2$ plasma. $(HfO_2)$ films showed a relatively low carbon contamination of about 3 at %. As-deposited and annealed $(HfO_2)$ films showed amorphous and randomly oriented polycrystalline structure. respectively. The interfacial layer of $(HfO_2)$ films deposited using remote PEALD was Hf silicate and its thickness increased with increasing annealing temperature. The hysteresis of $(HfO_2)$ films became lower and the flat band voltages shifted towards the positive direction after annealing. Post-annealing process significantly changed the physical, chemical, and electrical properties of $(HfO_2)$ films. $(HfO_2)$ films deposited by remote PEALD using TEMAH and $O_2$ plasma showed generally improved film qualities compare to those of the films deposited by conventional ALD.

• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2003년도 기술심포지움 논문집
• /
• pp.185-190
• /
• 2003

고유전물질인 $HfO_2$ 극박막에 사용될 TaN metal 전극에 대한 특성에 대한 연구를 하였다. 고유전물질인 $HfO_2$는 4" p-type wafer를 SCI cleaning후 ALD(atomic layer deposition)을 통해 $50\AA$를 증착하였다. Ff source는 TEMAH를 이용하였으며 Oxygen source는 $H_2O$를 이용하였다. 이렇게 증착한 $HfO_2$ 극박막에 Ta target을 이용하여 질소 가스를 Ar가스에 첨가하여 reactive sputtering을 통해서 TaN 전극을 증착하였다. TaN 박막의 증착두께는 a--step과 TEM을 통해서 확인하였으며 면저항은 four point probe를 이용하여 측정하였다. 이렇게 증착된 $HfO_2/TaN$구조에 대한 전기적 특성을 측정하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.9-10
• /
• 2007

In this paper, Thin films of $HfO_2$/Hf were deposited on p-type wafer by Atomic Layer Deposition(ALD). And we studied the electrical characterization of $HfO_2$/Hf/Si MOS capacitor depending on thickness of Hf metal layer. $HfO_2$ films were deposited using TEMAH and $O_3\;at\;350^{\circ}C$. Samples were then annealed using furnace heating to $500^{\circ}C$. The MOS capacitor of round-type was fabricated on Si substrates. Through TEM(Transmission Electron Microscope), XRD(X-ray Diffraction), capacitance-voltage(C-V) and current-voltage(I-V) analysis, the role of thin Hf metal layer for the better $HfO_2$/Si interface property was investigated.

• 한국전기전자재료학회논문지
• /
• 제22권2호
• /
• pp.101-106
• /
• 2009

In this paper, Thin films of $HfO_2$/Hf were deposited on p-type wafer by Atomic Layer Deposition (ALD). We studied the electrical and material characteristics of $HfO_2$/Hf/Si MOS capacitor depending on thickness of Hf metal layer. $HfO_2$ films were deposited using TEMAH and $O_3$ at $350^{\circ}C$. Samples were then annealed using furnace heating to $500^{\circ}C$. Round-type MOS capacitors have been fabricated on Si substrates with $2000\;{\AA}$-thick Pt top electrodes. The composition rate of the dielectric material was analyzed using TEM (Transmission Electron Microscopy), XRD (X-ray Diffraction) and XPS (X-ray Photoelectron Spectroscopy). Also the capacitance-voltage (C-V), conductance-voltage (G-V), and current-voltage (I-V) characteristics were measured. We calculated the density of oxide trap charges and interface trap charges in our MOS device. At the interface between $HfO_2$ and Si, both Hf-Si and Hf-Si-O bonds were observed, instead of Si-O bond. The sandwiched Hf metal layer suppressed the growing of $SiO_x$ layer so that $HfSi_xO_y$ layer was achieved. And finally, the generation of both oxide trap charge and interface trap charge in $HfO_2$ film was reduced effectively by using Hf metal layer.

• 대한전자공학회논문지SD
• /
• 제44권5호
• /
• pp.8-14
• /
• 2007

본 논문에서는 MOS 소자의 게이트 유전체로 사용될 고유전 박막으로 $HfO_2$/Hf 박막을 제조하여 그 전기적 특성을 관찰하였다. $HfO_2$박막은 TEMAH와 $O_3$ 전구체를 사용한 ALD 방법으로 p-type (100) 실리콘 웨이퍼 위에 증착하였다. $HfO_2$막을 증착시키기 전에 중간층으로써 Hf 금속 층을 증착하였다. Round-type의 MOS 커패시터 제작을 위해, 상부 전극은 Al 또는 Pt을 이용하여 약 2000 ${\AA}$ 두께의 전극을 형성하였다. $HfO_2$ 박막은 화학정량적 특성을 보였으며, $HfO_2$/Si 계면에서 Si-O 결합 대신 Hf-Si 결합과 Hf-Si-O 결합이 관찰되었다. $HfO_2$와 Si 사이의 Hf 중간층은 $SiO_x$의 성장이 억제되었고, $HfSi_xO_y$으로 변형되었다. 이러한 결과로 $HfO_2$/Hf/Si 구조에서 Hf 중간층이 있음으로 게이트 유전체의 고유전율이 유지되면서 계면 특성이 개선됨을 확인하였다.