• Transactions of Materials Processing
• /
• v.18 no.6
• /
• pp.465-470
• /
• 2009

The frictional behaviors of Cermets/Cr-Ceramics and Cu-Al coatings of piston ring were investigated. Friction tests were carried out by pin-on-disk test and materials properties of coating layer were analyzed by nano indentation tester. The effect of surface roughness of cylinder liner on the friction coefficient was analyzed. This study provided tribological data of hard and soft piston ring coatings against cylinder liner. The surface roughness does exert an influence on the average friction coefficient, with smoother surfaces generally yielding lower friction coefficients. In case of hard-coating, the scratch depth, width and pile-up height had close relationship with hardness. So the scratch width, depth and pile-up height increases with decreasing friction coefficient. But in case of soft-coating, the friction coefficients are strongly dependent on the morphological characteristics such as, scratch depth, width, pile-up height and elastic modulus.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.12
• /
• pp.4715-4720
• /
• 2010

In this study, we developed new tapered rolling type strip pressure key for the prevention of scratch in sheet metal forming line. The developed pressure key is equipped with two tapered rollers inside a conventional block pressure key. Through the scratch test, for the case of transversal movement the tapered rolling type pressure key reduces both friction and depth of scratch by the effect of tapered shape which decreases the pressure spike on edge, and for longitudinal movement the scratch on the sheet metal surface is certainly removed by the rolling contact.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.106-114
• /
• 1998

Tribological investigation of ultra thin film magnetic storage disks which have two different kinds of start/stop zone of laser textured bump disk and mechanically textured disk for before CSS test and after CSS test. To measure surface roughness, height reduction before/after CSS test and obtain accurate topographies, AFM(Atomic Force Microscope) which is most powerful recently has been used. The result of statistical analysis showed that both laser textured bump height and mechanically textured zone height have been reduced about 4~7nm after 15000 cycle CSS test. Using commercial Nano-Indenter, ramping load scratch test has been performed to investigate friction characteristic for laser textured zone and mechanically textured zone before/after CSS test.

• Transactions of the Society of Information Storage Systems
• /
• v.4 no.1
• /
• pp.13-18
• /
• 2008

Scratches are observed on a polymer cover-layer of near-field recording (NFR) media after a servo test with rotating disc. The scratches are formed by the collision of a solid immersion lens (SIL)-media. One of the possible ways to avoid the scratch problem is to coat a dielectric protective film on the polymer cover-layer which enhances the hardness of the surface. The surface with hard characteristics in the surface reduces the scratch problem in the cover-layer. Not only the mechanical properties but also the optical properties should be controlled. Specifically, the refractive index of the dielectric protective film should be matched with the polymer cover-layer not to lose light at the interface due to the difference of the refractive index. The refractive index of the dielectric film can be tailored by controlling process parameters during sputtering and matched with that of the polymer cover-layer.

• Journal of Ceramic Processing Research
• /
• v.19 no.6
• /
• pp.445-449
• /
• 2018

Chromium plating is a common surface treatment technique extensively applied in industry due its excellent properties which include substantial hardness, abrasion resistance, corrosion resistance, surface color, and luster. In this study, the effect of $MoS_2$ particles of the composite coating was investigated. To improve the lubrication of mold, $Cr-P-C/MoS_2$ composite plating was studied by varying the $MoS_2$ content. The current efficiency of the composite plating incorporated $MoS_2$ particles was increased at $MoS_2$ contents of 0.5 and 1.0 g/l due to the incorporation of fine particles. On the other hand, when the content of $MoS_2$ is 1.0 g/l or more, the current efficiency is lowered due to an increase in impact on the cathode surface. In order to evaluate the mechanical properties of Scratch test were conducted. Scratch test confirmed the lubricity and abrasion resistance characteristics revealed that the composite plating with added $MoS_2$ had relatively low surface roughness and uniform surface modification to improve its properties.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.1
• /
• pp.13-19
• /
• 2014

The various surface treated conditions of Fe-3.0%Ni-0.7%Cr-1.4%Mn-X steel such as as-received, ion nitriding, DLC coated, DLC coated after nitriding for 3 hrs and 6 hrs were investigated to evaluate the beneficial effect for plastic mold steel. Micro Vickers hardness tester was used to estimate nitriding depth from the hardness profile and to measure hardness on the surface. Elastic modulus and residual stress were measured by a nanoindentator. Scratch test and SP (small ball punch test) were utilized to assess the adhesive strength of DLC coating. The depth of nitriding layer was measured as $50{\mu}m$ for the condition of 3 hrs nitriding and $90{\mu}m$ for that of 6 hrs nitriding. Hardness, elastic modulus, residual stress of DLC coating were 20.37 GPa, 162.78 GPa and -1456 MPa respectively. Residual stress on the surface of DLC coating after nitriding could increase to -3914 MPa by introducing nitriding before DLC coating. During the 'Ball-On-Disc' test ${\gamma}^{\prime}$ particles pulled out from the surface of nitrized layer tend to enhance abrasive wear mode since the fraction of ${\gamma}^{\prime}$ (Fe4N) in ion-nitrized layer is known to increases with nitriding time. Thus the specific wear rate of the nitriding layer increased. Comparing with nitriding the specific wear rate in work piece disc as well as ball decreased prominently in DLC coating due to the remarkable reduction in friction coefficient.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.691-694
• /
• 1996

Two models of scratch testers developed recently are applied to the adhesion measurement of thin coatings. In both models the critical load is determined from the frictional irregularity when coated surface is broken in the scratching process. One model is effective for coatings thicker than 1m and the other for thin coatings down to $0.1\mu\textrm{m}$. The mechanism and the measurement principle of these testers are described. High sensitivity and good reproducibility of the measurement are attained primarily by the employment of new detection devices. These testers are even more useful for the quality control and the inspection of commercial products of coatings because only a small area of specimen is required for the test.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.294-297
• /
• 2009

The frictional behaviors of Cermets/Cr-Ceramics and Cu-Al coatings of piston ring were investigated. Friction tests were carried out by pin-on-disk test and materials properties of coating layer were analyzed by nano indentation tester. Higher friction coefficient was obtained at harder coating with rougher surface. In case of hard-coating, the scratch depth, width and pile-up height had close relationship with indentation hardness. So the scratch width, depth and pile-up height increases with decreasing friction coefficient. But in case of soft-coating, the friction coefficients are strongly dependent on the morphological characteristics after nano scratching more than indentation hardness.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.141-146
• /
• 2016

In this study, electrophoretic paint (E-paint) was deposited on the knife-abraded surface of AZ31 magnesium alloy (AZ31), and its adhesion and corrosion resistance were examined by tape peel-test and salt spray test, respectively. E-paint started to deposit on AZ31 Mg alloy after an inductance time and pores were found in the E-paint layer which is ascribed to hydrogen bubbles generated on the surface during the painting process. The pores disappeared after curing for 15 min at $160^{\circ}C$. The E-paint on AZ31 exhibited good adhesion after immersion in deionized water for 500 h at $40^{\circ}C$. The E-paint sample without scratch showed no corrosion after 1500 h of salt spray test. However, on the scratched sample, blisters were visible adjacent to the scratched sites after 500 h of salt spray test.

• Journal of Korean Society for Quality Management
• /
• v.42 no.3
• /
• pp.325-338
• /
• 2014

Purpose: The purpose of this study was to explain de-painting phenomenon of KUH-1 tail blade and to propose useful solution of it by test. The proposed solution was evaluated by real flight, and then it applied to mass product to improve the paint qual ity of KUH-1 tail blade. Methods: This study investigated an adhesive ability of primer following surface sanding condition. The cross cut and scratch test were conducted to evaluate the adhesive strength. And the water flow test was designed to simulate a real flight condition under rain. Through water flow test, an optimal condition of tail blade to prevent a de-painting phenomenon was deduced. Finally, the improvement method was evaluated by real flight under rain. Results: The results of this study are as follows; The sequential polishing was most excellent method in primer painting quality. The results of test including cross cut, scratch and water flow showed that MIL-DTL-53039 paint with epoxy primer has excellent adhesive ability. To proof the effect of improvement, a real flight during a rain condition was conducted. Finally, the comparison between original and improved configuration was conducted. Conclusion: The painting quality of KUH-1 tail blade was improved through deriving an optimal painting condition. In detail, a condition of optimal sanding and a sort of primer and paint was showed. Finally, the reliability of tail blade was guaranteed through improving the quality of painting.