• Progress in Superconductivity
• /
• 제8권2호
• /
• pp.169-174
• /
• 2007

We measured the field profiles, H(x)'s of coated conductors by using scanning Hall probe method when various magnetic fields, $H{_\alpha}'s$ or currents, I's were applied. From the measured field profiles, we calculated the current profiles, J(x)'s by the inversion method. The calculated J(x)'s of coated conductors show some different properties from the standard critical state model. $J{_c}'s$ are inhomogeneous varying with the positions and are not constant when $H_{\alpha}$ or I changes. And when I decreases the features of current reversion are remarkably different from the model.

• 한국초전도ㆍ저온공학회논문지
• /
• 제21권1호
• /
• pp.15-17
• /
• 2019

We present terahertz optical properties of $GdBa_2Cu_3O_{7-x}$ (GdBCO) superconducting thin films. GdBCO films with a thickness of about 105 nm were grown on a $LaAlO_3$ (LAO) single crystal substrate using a conventional pulsed laser deposition (PLD) technique. Using an Ar ion milling system, the thickness of the GdBCO film was reduced to 58 nm, and its surface was also smoothened. Terahertz (THz) transmission spectra through two different GdBCO films are measured over the range between 0.2 and 1.5 THz using THz time domain spectroscopy. Interestingly, the THz transmission of the thinner GdBCO film has been increased to six times larger than that of the thicker one, while the thinner film is still maintaining its superconducting property at below 90 K.

• 한국초전도ㆍ저온공학회논문지
• /
• 제24권4호
• /
• pp.29-35
• /
• 2022

We fabricated MHOS (multi-HTS layers on one substrate) high-temperature superconducting (HTS) REBCO conductors using HTS REBCO coated conductor (CC) A-specimen, which induces an artificial magnetic flux pinning effect, and HTS REBCO CC B-specimen, that does not induce this effect. The superconducting magnetic properties of the fabricated MHOS conductors were examined by measuring their magnetic moment m(H) curves using a physical property measurement system (QD PPMS-14). The critical current density (J_c) characteristics of our four-layered MHOS HTS REBCO conductor specimens such as BAAB, BBBB, and AAAA were lower than those of their two-layered and three-layered counterparts. At a temperature T of 30 K the magnetic flux pinning physical indicator δ values (obtained from the relationship J_c ∝ H^-δ) of the three-layer ABA (δ = 0.35) and two-layer AB (δ = 0.43) specimens were found to be significantly lower than those of the four-layer ABBA (δ = 0.51), BAAB (δ = 0.60), AAAA (δ = 0.78) and BBBB (δ = 0.81) structures.

• 한국초전도ㆍ저온공학회논문지
• /
• 제10권3호
• /
• pp.1-4
• /
• 2008

For the effective evaluation of superconducting properties of a coated conductor, with a long length, a non destructive characterization technique including a reel-to-reel (R2R) Hall measuring system have been developed. A non-contact R2R Hall sensor array system was particularly designed to measure the superconducting property of coated conductors. The superconducting properties of long length coated conductors were measured by using this device. It was demonstrated that this system was convenient to measure the intensity and distribution of the magnet field applied perpendicular to the surfaces of the coated conductors. Using this device, the defect and low critical current density(Jc) area of coated conductors could be detected in real-time measurement.

• 한국초전도ㆍ저온공학회논문지
• /
• 제14권4호
• /
• pp.16-19
• /
• 2012

In power cables as one of the important power applications adopting HTS tapes, a good insulation should be kept at its optimum performance. As an insulation material for superconducting device applications, polypropylene laminated paper (PPLP) is now widely used instead of the conventional Kraft paper. In addition to its dielectric property, the insulation material should also possess superior mechanical property at cryogenic temperatures and operability that is necessary for the insulation winding process. This study aims to evaluate the mechanical property of the PPLP material at ambient and cryogenic temperatures. At cryogenic temperature, the failure stress of PPLP increased significantly as compared with that at ambient temperature. The failure stress at both temperatures depended upon the sample orientation to the load application.

• 한국응용과학기술학회지
• /
• 제17권2호
• /
• pp.144-148
• /
• 2000

A modification of the sol-gel method to obtain phase pure superconducting oxides is described. The method starts from organic salts of yttrium, barium and copper, such as acetates, and avoids the sudden and uncontrollable decomposition of the organic fraction which occurs if nitrates are used as starting materials. The aqueous solution obtained with citric acid in an alkaline medium is concentrated under vacuum. The solid so prepared is decomposed at about $300^{\circ}C$ thus giving an oxide precursor containing well dispersed yttrium, barium and copper. Pyrolysis at 850 - $920^{\circ}C$ followed by oxygen annealing gives the superconducting orthorhombic 123 phase. The results of TGA/DTA of the precursor, as well as XRD, electrical and magnetic property measurements on the pyrolysis products are presented and discussed.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1996년도 하계학술대회 논문집 C
• /
• pp.1489-1491
• /
• 1996

The effect of Ag alloy sheath have been investigated in terns of critical current density and mechanical property. Nevertheless the continuous improvement of critical current density($J_c$) of Ag sheathed Bi2223 oxide superconducting wire processed with powder in tube(PIT) method, poor mechanical strength is still considered to be demerits for power application. In this study, we prepared two kinds of Ag- x wt% Cu alloy and pure Ag sheathed Bi2223 superconducting tapes. The hardness and tensile strength of prepared tapes has been measured. Their mechanical propertes were improved by Ag alloying.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1997년도 추계학술대회 논문집 학회본부
• /
• pp.288-290
• /
• 1997

Pulsed laser ablation has been used to fabricate superconducting $YBa_2Cu_3O_{7-x}$(YBCO) thin films on MgO substrates. The epitaxial YBCO thin films were grown at $750^{\circ}C$ and oxygen partial pressure of 200 mTorr. The electrical property and the characteristics of the YBCO thin films have been studied by R-T measurement. scanning electron microscopy (SEM) and X-ray diffraction (XRD). A microstrip line resonator has been fabricated using YBCO superconducting thin films by photolithography and wet-etch process. The resonator has linear microstrip line separated by a gap of 0.278 mm. We observed a fundamental resonance peak at the frequency of 10.007 GHz.

• Progress in Superconductivity
• /
• 제3권2호
• /
• pp.247-251
• /
• 2002

In general, the bubbling, generated during the fabrication of the tapes, breaks the superconducting filament, and critical current of the tapes will be decreased. Heat-treatment schemes of Bi-2223/Ag HTS tapes were modified, such as pre-annealing of multi-stacked billet, 2-step main sintering and ramp rate etc. The generation of bubbling was drastically decreased from 20 bubbles/m to 0 ~ 1 bubble/m by the modified heat-treatment. Therefore, the value of critical current of the tapes without bubbling was increased almost twice higher than that of already existing tapes. Critical current up to 42 A in 40 m length Bi-22231Ag tapes have been measured at 77K, self-field, 1$mutextrm{V}$/cm criterion. It could be confirmed that elimination of bubbling is effective to maintain the superconducting property along the tape length.

• 한국전기전자재료학회논문지
• /
• 제13권3호
• /
• pp.247-253
• /
• 2000

We evaluated the electric properties of Bi-2223 jointed tapes processed by both resistive-and superconducting-joint methods. For resistive-joint. filler materials of wood metal Pb/Sn. In and silver paste were used whereas for superconductive-joint lap joint method was used. In the resistive joint tape. critical transport property(CCR) n-value and contact resistance were observed to be in the range of 10-85% 1-8,9. and 0.71x10$\^$-6/-0.13x10$\^$-6/Ω, respectively. depending on their filler materials. Specifically it is believed that the electrical properties of resistive joint tape are significantly related to the resistivity of filler materials. On the other hand the CCR of superconductin joint type was varied 55 to 85% with uniaxial pressure probably due to the irregular microstructure in the transition region.