• Journal of the Korean Society of Clothing and Textiles
• /
• v.15 no.2 s.38
• /
• pp.199-209
• /
• 1991

In this paper, the fabrics for Korean folk clothes(KFC) undergoes repeated laundering under given condition. After this cyclic laundering was applied, the mechanical properties of the specimen were measured using KES-F system in order to evaluated the end-use performance of fabrics for KFC. And also, the crease recovery of fabrics for KFC were measured by shirley crease recovery tester. 78 different kinds of commercial silk fabrics and polyester fabrics for KFC were used for this study. The experimental results were analysed statistically to relate the mechanical properties and the crease recovery of fabrics for KFC. Furthermore, these changes in dimensional stability, mechanical properties and handle of fabrics for KFC were discussed in comparison with those values for silk fabrics and polyester fabrics. The results obtained are as follows. 1. Regardless of materials, remarkable increase are observed in shrinkage of the fabrics for KFC about repeated laundering, but dull increase are observed in shrinkage after 10 cycles of the repeated laundering. On the other hand, slack extend are observed in dimensions after 20 cycles of the repeated laundering. The shrinkage of fabrics for KFC after 10 cycles of the lundering showed that the silk fabrics are $1.74{\pm}0.33\%$ (warp direction) and $1.35{\pm}0.23\%$ (weft direction) and the polyester fabrics are $1.45{\pm}0.22\%$ (warp direction) and $1.25{\pm}0.23\%$ (weft direction). 2. Except for tensile property, these changes in mechanical properties of fabrics for KFC by laundering have $\pm$ 16 range of bending, shearing, compression, surface, thickness & weight as compared with before laundering. Particularly, the LT and RT about $1\~3$ cycles of the repeated laundering showed remarkable decrease. And SMD, WC, T & W of fabrics for KFC by the laundering were more increased than one for original fabrics. But B, 2HB, G, 2HG, 2HGS were decreased more than one for original fabrics. 3. 'Stiffness', 'Anti-drape', 'Crispness' and 'Scroop' hand values decrease and'Fullness & softness', 'Flexibility & softness' hand values increase with repeated laundering. 4. Remarkable decrease are observed in crease recoveries about $1\~5$ cycles of the repeated lundering, but slack decrease are observed in crease recoveries after 5 cycles of repeated laundering. The crease recovery of fabrics for KFC have negative(-) correlation with LT, RT, G, RC and MMD, This fact implies that the smaller these values, the larger the crease recovery. The crease recovery of fabrics for KFC has a high degree of correlation with the mechanical properties such as shearing, compression, surface property. And also, the crease recovery are expected by measuring the mechanical properties such as G, 2HG, 2HGS, RC, WC, LC, MIU, MMD and SMD, according to the obtained regression equation.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.119-124
• /
• 2011

Objectives: The purpose of this experiment was to evaluate four different polishing systems of their polishability and polishing time. Materials and Methods: 4 mm diameter and 2 mm thickness Teflon mold was made. Z-250 (3M ESPE) hybrid composite resin was slightly overfilled and pressed with slide glass and cured with Optilux 501 for 40 sec each side. Then the surface roughness (glass pressed: control group) was measured with profilometer. One surface of the specimen was roughened by #320 grit sand paper and polished with one of the following polishing systems; Sof-Lex (3M ESPE), Jiffy (Ultradent), Enhance (Dentsply/Caulk), or Pogo (Dentsply/Caulk). The surface roughness and the total polishing time were measured. The results were analyzed with one-way ANOVA and Duncan's multiple range test. Results: The surface roughness was lowest in Pogo, and highest in Sof-Lex. Polishing times were shortest with Pogo, and followed by the Sof-Lex, Enhance and Jiffy. Conclusions: One-step polishing system (Pogo) is very effective to get the smooth surface in a short time, therefore it can be recommended for final polishing system of the restoration.

• Resources Recycling
• /
• v.7 no.4
• /
• pp.22-26
• /
• 1998

The purpose of this experimenL is to investigate the magnetic anisotropy and microwave absorbing properties in M-type Bat territe (${BaFe}_{12-2X}{A}_{X}{Me}_{X}{O}_{19}$), where $Fe_{3+}$ is substituted by $Ti_{4+}$ in A site and $Co_{2+}$ in Me site. The saturation magnetization (Ms) is linearly decreased with the substitution rate(x) and the coerciviLy (He) is rapidly decreased in accordance with the reduction in t the magnetocrystalline anisotropy For the specimen with x=0.8 and thickness of 2 mm, the reflection loss calculated from the n material constants is less than -10 dB (90% absorption) in the frequency range of 10~16 GHz. The absorption loss is pre이.ctcd t to be more than 20 dElern in the frequency range of 12-16 GHz. The results demonstrate that the Ti-Co substituted M-type Ba-ferrite can be effectively used as a microwave absorber at high frequency range.

• Journal of the Korean Geotechnical Society
• /
• v.33 no.5
• /
• pp.5-13
• /
• 2017

The sand layer deposited in clay is called a sand seam, which is formed by inflow of sands due to river flooding or slope failure in the middle of sinking and sediment of clay. When the sand seam exists in clay layer, the drainage direction changes from one way to both ways, and the time of consolidation may be reduced. However, it is not clearly proved due to lack of studies of sand seam and currently is not reflected in the design of soft soil improvement. As a fundamental study about sand seam, the oedometer tests and constant rate of strain tests with Rowe cell were conducted on clay specimens with sand seam. For tests, a frozen method was specially designed for making the sand seam. It was concluded that the test results showed the sand seam affects the coefficient of consolidation of clay. If the thickness of sand seam exceeds 0.05 times of specimen height, the sand seam works as drainage layer of pore water horizontally as well as vertically, and consequently the consolidation is accelerated.

• Journal of the Korea Convergence Society
• /
• v.12 no.12
• /
• pp.145-151
• /
• 2021

This study aimed to investigate the efficient conduct of HA coating on Ti Gr4 for the practical use of medical device. Ti Gr4 alloy specimens measuring 𝜱 25mm × 1mm were sprayed with hydroxyapatite using thermal spray according to ASTM F1185-88. The surface was evaluated at #120, #400, #1,000 sandpaper and barrel finishing. Each coating properties was analyzed using SEM, UTS 20,000psi cap. and in vitro cytotoxicity. Surface morphology consists of well molten particles with very little resolidified or unmolten areas. The average Ca/P ratio is 1.74 which is in good agreement with theoretical value of 1.67. The average roughness Ra is very representative of roughness of specimen. The coatings are dense and well adhered to the substrate. The average bond strength was 61.74 MPa with a standard deviation of 4.06 which indicates fairly reliable results for ASTM 633 type tests. Variations in results from jig design, epoxy used, crosshead speeds etc. in vitro cytotoxicity result had a Grade 3. The results of the study are expected to be helpful in osseointegration and plasma-spray HA coated Ti Gr4 are more satisfactory in HA coating thickness elevation which is preferable to any other system.

• Journal of dental hygiene science
• /
• v.18 no.6
• /
• pp.367-373
• /
• 2018

The consumption of beverages among children is rising. The purpose of this study was to examine the effect of kid's drink on dental resin-based pit and fissure sealant. Pororo, I-kicker, Sunkist kids were included in the experimental groups, and Samdasu was included in the control group. A conventional dental sealant material ($Clinpro^{TM}Sealant^{(R)}$) was selected for this study. Resin specimens (8 mm in diameter and 1 mm in thickness) were prepared according to manufacturers' instructions and the initial roughness (Ra) was then measured. The pH of all the four groups was measured using a pH meter. The specimens were individually immersed in 5 ml of the experimental solutions and stored at $37^{\circ}C$ for 72 hours. Following this, the surface roughness of the resin specimens was measured by Surftest. The concentration of residual monomer released was determined by high performance liquid chromatography (HPLC). The surface morphology of the resin specimen was evaluated before and after storage by scanning electron microscopy (SEM). Data were statistically analyzed using Kruskal-Wallis and Duncan's test. The results showed that all the children's beverages examined in this study contained citric acid. The pH of I-kicker was the lowest ($3.03{\pm}0.01$), followed by that of Sunkist kids ($3.26{\pm}0.02$) and Pororo ($3.47{\pm}0.02$). We observed an increase in the surface roughness of resin specimens after 72 h of immersion in all the beverages tested (p<0.05). There was matrix degradation after immersion, visualized on SEM image, in all the beverage groups. Bisphenol-A-glycidyl methacrylate was not detected after 72 hours, but triethylene glycol dimethacrylate levels were increased in all the beverages tested during the 72 hours by HPLC. These results suggest that intake of beverages containing acid can cause degradation of the resin-based pit and fissure sealants in children.

• Korean Journal of Heritage: History & Science
• /
• v.46 no.1
• /
• pp.176-187
• /
• 2013

A study has been carried out on metal materials in order to identify the quantitative relation between the concentration and damage characteristics after evaluation of the damage characteristics according to the $SO_2$ concentration. The prepared metal samples, which were categorized according to the material (silver, copper, iron, lead, brass) were exposed to 0.01, 0.12, 1, 10, 100, 1,000, and 5,000ppm of $SO_2$ for 24 hours and the optical, physical, chemical deterioration rates both before and after testing were evaluated. The results showed optical deterioration, a loss of gloss on silver specimen with $SO_2$ 100ppm, an increase of color difference on brass, iron, copper and lead specimens with $SO_2$ 5,000ppm, as well as physical changes such as an increase of thickness and corrosion rate on iron sample with $SO_2$ 5,000ppm. In the case of chemical changes such as an increase sulfate ion ($SO{_4}^{2-}$) concentration and decrease of pH on iron and brass specimens were identified. These results suggest that $SO_2$ 100ppm caused clear optical deterioration on some metals such as silver and physicochemical and optical deterioration were identified at $SO_2$ 5,000ppm regardless of metal type. Also, It was concluded that iron and brass are the most susceptible of the metal specimens to $SO_2$.

• Fire Science and Engineering
• /
• v.33 no.1
• /
• pp.76-84
• /
• 2019

Experimental studies using an open cone calorimeter were conducted to provide information on the CO and soot yields of wood combustibles required for a kitchen fire simulation of PBD. A total of eight specimens were examined for medium density fiberboard (MDF) and particle board (PB), which are used widely in kitchen furniture production, depending on the water content, surface processing method, and surface color. The thermal penetration time related to the fire spread rate in the depth direction differed significantly according to the surface processing treatment method, even for a specimen of identical thickness. The CO yield ($y_{CO}$) of the MDF and PB series did not change significantly according to the combustion mode and surface treatment process in flaming mode. On the other hand, $y_{CO}$ was approximately 10 times higher in smoldering mode than in flaming mode. The soot yield ($y_{soot}$), however, varied considerably depending on the combustion mode and surface treatment process. In particular, a higher $y_{soot}$ was found in flaming mode and in the surface-treated specimens. Finally, the $y_{CO}$ and $y_{soot}$ of MDF and PB measured for the kitchen fire simulation of PBD were applied.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.4
• /
• pp.25-37
• /
• 2020

In this study, hybridization of graphene oxide and metal was carried out by the functional groups containing oxygen and thermal treatment for reduction in order to enhance the electrical conductivity and magnetic properties of graphene materials. Graphene-metal hybrid materials were synthesized using the oxygen-containing functional groups (-OH, -COOH and so on) on the surface of graphene oxide by replacing them with metal ions via ion exchange method as well as thermal reduction. The metals used in this study were Fe, Ag, Ni, Zn, and Fe/Ag, and it was confirmed that metal particles of uniform size were well dispersed on the graphene surface through SEM, TEM, and EDS. All of the metal particles on the graphene surface had an oxide-crystalline structure. To check the electrical properties, sheet resistance of the rGO-metal hybrid sample was measured on the PET film made by the dip-coating, and the specific resistance was calculated by measuring the thickness of the specimen through SEM. As a result, the specific resistance was in the range of 2.14×10-5 and 3.5×10-3 ohm/cm.

• Journal of the Korean Society of Safety
• /
• v.38 no.4
• /
• pp.39-46
• /
• 2023

Pine trees, which account for 23% of the forested area of the Republic of Korea, are highly vulnerable to fire in comparison to broad-leaved trees due to the presence of consistent water tube sections throughout the year and resin that is composed of approximately 20% oil. In addition, the pattern of forest fires is determined by weather, topographic conditions, and fluctuation in moisture content. Therefore, when fire breaks out in pine tree forests during the dry season (January to March), it is difficult to extinguish, and it quickly spreads. In this study, the combustion characteristics of pine needles, pine cones, and pine branches in the water tube sections of living pine trees were compared and analyzed in accordance with the moisture content as per the ISO 5660-1. The monthly moisture content was analyzed from January to March, and it was found to be the lowest in March, with 53.6% for pine needles, 51.9% for pine branches, and 10.9% for pine cones. In particular, pine cones were more vulnerable to fire as compared to pine needles and pine branches because their moisture content was more than five times lower than that of pine needles and branches. The ignition time, which affects the speed of flame propagation, was the most rapid in March, and the fastest ignition time was for pine cones, at 19 seconds, followed by 34 seconds for pine needles, and 256 seconds for pine branches. The pine branches were the last to be ignited due to the effect of density, according to the thickness and specific gravity of the specimen. The peak heat release rate, which is a measurable index of fire intensity, was analyzed for pine cones and found to be 184.28 kW/m² , while the mean effective heat of combustion was 19.79 MJ/kg, and the total heat release rate was 39.7 MJ/m² , and these values were higher than those of pine branches and pine needles. Thus, we determined that the flame propagation speed and fire intensity according to the moisture content can be used to evaluate the risk of fire to the water tube section of pine trees. It is suggested that because of the combustion characteristics of the pine cone in March, that is when the forest is most vulnerable to fires.