• Proceedings of the KSR Conference
• /
• 2008.06a
• /
• pp.2185-2190
• /
• 2008

In a high speed train, multi-layered panels for floor, side wall and roof are important sound insulating part. As these multi-layered panels require high bending strength vs. weight, corrugated steels or aluminium honeycomb panel are generally used. However, with some inevitable factors, these panels show lower sound insulation performance than that of the plate with the same weight. Transmission loss(TL) often severely decreases in a particular frequency range because of the decrease of the critical frequency, occurrence of local resonance modes and cavity resonance modes, which are not shown in a plate. In this study, frequency range and cause of the TL drop are investigated on the corrugated and honeycomb panels.

• Composites Research
• /
• v.29 no.3
• /
• pp.117-124
• /
• 2016

The failure strength of composite single-lap joint repaired using scarf patch was investigated by test and finite element method. A total of 45 specimens were tested changing scarf ratio, stacking pattern, and defect size to study the failure strength and mode. Except for one case, all repaired specimens showed the equal or higher strength than the sound specimens and the effect of considered repair parameters was not remarkable. It was found through the failure mode inspection that the surface treatment for bonding was not enough in the case which failed at the lower load than the sound specimen. Three-dimensional finite element analysis was conducted to verify the test results. It was confirmed that the considered repair parameters do not significantly affect the stress distribution of the specimens. It was also observed that the applied tensile load is relieved passing through the overlapped region thickness of which is almost double. From this study, it is concluded that if the bonding procedure for adherends and patch including surface treatment for fabric layer is thoroughly followed, the strength of repaired single-lap joint can be restored up to the strength of sound one.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2012.04a
• /
• pp.348-353
• /
• 2012

This paper presents the HRTF based experimental approach to figure out why the human auditory perception on the interior noise source including the directional tonal components does not well match with the dominant features extracted from recorded acoustic signals in terms of psycho-acoustics. Since the general objective evaluation models for tonalness among various sound attributes are a function of width, frequency, excessive level of tonal components respectively, the directional tonal components cannot be properly evaluated without considering the effects of head-related transfer function on the binaural auditory perception. Thus, the directivity of source is additionally considered to prevent the erroneous conclusions from the same sound source in the process of source identification. The signal synthesis technique is used to solve a little difficulty in measuring all of desired acoustic signals for jury evaluation. The sound attributes of synthetic acoustics signals are analyzed to roughly predict the results of jury evaluation in advance by using sound quality factors such as loudness, sharpness, roughness, fluctuation strength and tonality. The jury evaluation is carefully conducted based on the recommended guideline suggested by N. Ottoet al. Each sound is respectively evaluated by selecting a value between -2 and 2 in intervals of 0.2 point. Through above procedure, based on the results of jury evaluation, it is confirmed that serious problems can be caused in the process of analyzing the dominant sound attributes in terms of psycho-acoustics according to the type of a microphone and a playback system.

• Transactions of the Korean Society for Noise and Vibration Engineering
• /
• v.26 no.5
• /
• pp.536-545
• /
• 2016

Household refrigerator radiates noise of which the pattern is dependent on the operating condition of its parts, such as compressor, flow fans, etc. Thus the refrigerator noise has a variety of frequency characteristics. Therefore, it is required to consider the noise characteristics for evaluating the noise quality and eventually developing the sound quality index of the refrigerator noise. In this study, five units of household refrigerator were selected to measure their noises that were used to generate sound sources for jury test of the study. The measured noises of five refrigerators were divided into ten kinds of sound source by considering operating condition and frequency characteristics. Additionally, the ten sources were each edited to have the same SPL of 30 dBA. Totally twenty kinds of sound sources (10-original SPL, 10-edited SPL 30 dBA) were evaluated by twenty-two subjects, and compared with their sound quality metrics. It was found that only the loudness of the metrics was meaningfully correlated with the subjective evaluation. The rests, sharpness, roughness and fluctuation strength, were not related. The conclusion of this study is that a new sophisticated index is necessary to be developed to qualitatively evaluate the household refrigerator noise.

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.273-278
• /
• 2003

The effects of content and particle size of sewage sludge slag on the sound absorption was investigated and the physical$.$mechanical properties of porous ceramics for sound absorbent material was studied. The physical$.$mechanical properties of specimens have depended on sintering temperature and slag content without particle size effect of slag. As water glass content increase and particle size of slag decrease at the same slag content, physical$.$mechanical properties of them have been improved. The bulk density and compressive strength of specimens with the batch composition of 77∼89 wt% of slag content and particles with 1∼3 mm, and sintered at 1,050$^{\circ}C$ for 2 h were 1.48∼1.71 and 86∼163 kgf/$\textrm{cm}^2$, respectively. The specimens with 1∼3 mm and <1 mm of particles size showed good sound absorption property at low frequency and high frequency region. With increasing thickness of specimens, sound absorption properties at low frequency region were increased.

• International journal of advanced smart convergence
• /
• v.4 no.1
• /
• pp.145-153
• /
• 2015

Friction Stir Welding (FSW) is a solid state welding that could successfully weld the difficult-to-weldmaterials such as an aluminum alloy. In this welding process, the stirrer of the welding tool is one of the important factors for producing the perfect sound joint that indicates the higher joint strength. So, this report aims to apply the friction stir welding using various stirrer geometries to weld the AA6063-T1 aluminum alloy butt joint, investigates the mechanical properties of the joint and then compares the mechanical properties with the microstructure of the joint. An experiment was started by applying the friction stir welding process to weld a 6.3 mm thickness of AA6063-T1 aluminum alloy butt joint. A study of the stirrer geometries effect such as a cylindrical geometry, a cone geometry, a left screw geometry and a right screw geometry at a rotational speed of 2000 rpm and a welding speed of 50-200 mm/min was performed. The mechanical properties such as a tensile strength and a hardness of the joint were also investigated and compared with the microstructure of the joint. The results are as follows. A variation of FSW Stirrer shape directly affected the quality AA6063-T1 aluminum alloy butt joint. A cylindrical stirrer shape and a cone stirrer shape produced the void defect at the bottom part of the weld metal and initiated the failure of the joint when the joint was subjected to the load during the tensile test. Left and right screw stirrer shapes gave the sound joint with no void defect in the weld metal and affected to increase the joint strength that was higher than that of the aluminum base metal.

• Resources Recycling
• /
• v.22 no.1
• /
• pp.20-28
• /
• 2013

Recently, as the registration of vehicles increases, the utilization of the waste tires is emerging as environmental issues. Crumb rubber reproduced by scrap tires has been reused up to 25% in the construction field. The purpose of this paper is to investigate the mechanical properties of sulfur-rubber concrete (SRC) and to suggest the optimum mix design in terms of the compressive strength. Specimens were prepared with various mixing parameters: amount of sulfur, rubber, and micro-fillers. Two casting processes were also mentioned; dry process and wet process. The results mainly showed that the compressive strength of SRC decreased with an increment of rubber content. However, adding micro-filler and adjusting sulfur contents could improve the compressive strength of SRC. Optimum values of sulfur and rubber content were selected by workability and compressive strength of SRC. SRC can be applied to road constructions where high strength of concrete is not concerned, to wall panels that require low unit weight, to construction of median in highways to resist high impact load, and in sound barriers to absorb sound waves.

• The Journal of the Acoustical Society of Korea
• /
• v.43 no.3
• /
• pp.305-313
• /
• 2024

For effective bi-static sonar operation, detection performance analysis must be performed reflecting the characteristics of sound propagation due to the ocean environment and target information. However, previous studies analyzing bistatic sonar detection performance have either not considered the ocean environment and target characteristics or have been conducted using simplified approaches. Therefore, in this study, we compared and analyzed the bistatic detection performance in Yellow sea and Ulleung basin both with and without considering target characteristics. A numerical analysis model was used to derive an accurate bistatic target strength for the submarine-shaped target, and signal excess was calculated by reflecting the simulated target strength. As a result, significant changes in detection performance were observed depending on the source and receiver locations as well as the target strength.

• Korean Journal of Environment and Ecology
• /
• v.29 no.2
• /
• pp.174-183
• /
• 2015

We have conducted a verification test of correlation between bird community indices and bird sound recording results in order to use the equipment which deals with the automatic sound collecting system, the song meter. The study areas include four sites which are Gombaeryoung and Zochimryoung in Jeombongsan Mountain and Jookryoung and Gochiryoung in Sobaeksan National Park. We collected the bird sound data five times using a sound recorder and field survey results in the same place of the study site. As a result of the sound recording from the field survey, the species recorded by three researchers of sound analyst include common resident species or species which have a relatively conspicuous call and song. On the contrary, the species recorded by only one researcher are a relatively rare or inconspicuous species or was familiar with the personal experiences of each researcher. The number of species recorded by only one researcher totaled fourteen species (36.8 %), and that of two researchers totaled twelve species (31.6 %), and that of three researchers totaled twelve species (31.6 %). The correlations of the number of species among three researchers was not significant in some results, but the sum or maximum count of the number of species was useful to estimate a significant correlation between the result of researchers and the indices of field surveys. As a result of correlation analysis by using sound recordings, the maximum number of species among the three researchers significantly correlated with the number of species, the species diversity index and the species abundance index in the field survey at the same site, however it did not correlate with the number of individuals and species evenness index. As a result of sound analysis collected from the stationary sound recording system; song meter, the number of frequencies in bird songs and calls correlated with the number of species in the field survey at the same site. The number of calls and songs decreased as time went by. Finally, we could test the active time range and change the activity strength by using a sound recording system. In particular, that sound recording system is able to collect data in same time and site, so it is expected so that the equipment not only replenish a shortage of researchers and survey periods in field research in a short term monitoring survey, but also be able to acquire statistical objectivity.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.83-87
• /
• 2002

Aerospace industries are widely using honeycomb sandwich structures that it has high specific strength and stiffness, chemical material resistance and fatigue resistance. But, in repairing process of damaged areas, one of the problems is that delamination can be occurred in the sound areas during and/or after the exposure to the elevated curing temperature in case that the repair process is repeated. Therefore, this study was conducted Flatwise tensile, Drum peel and Long beam flexural strength tests to evaluate the degree of degradation of mechanical properties of the honeycomb sandwich structures by affecting thermal aging. As the results, the decrease of mechanical strength was observed at the specific specimen which is exposed over 50hrs at $127^{\circ}C$.