• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.366-371
• /
• 1999

The effect of VC addition on the microstructural evolution of Fe-TiC cermet has been investigated. The microstructures of the Fe-TiC varied with the amount of VC addition. The addition of 1wt% VC enhanced the instability of liquid-solid interface ; the dissolving interface showed round shape instead of facetted one which was ascribed to the increase of lattice mismatch between TiC and solid-solution carbide. in the speci-men with 10wt% VC the new set of solid-solution carbide grains of uniform and small size was formed in-side coarse TiC particles by diffusion induced recrystallizatin (DIR). With increasing the heat-treatment time fine recrystallized grains were dispersed homogeneously in the matrix and resulted in the increase in fracture strength.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.250-257
• /
• 2000

The feasibility of synthesizing SiC-AlN solid solution by field-activated combustion synthesis was demonstrated. At lower fields of 8-16.5V/cm, composites of AlN-rich and SiC-rich phases were synthesized, but at fields of 25-30 V/cm, the product was a 2H structure solid solution. Combustion synthesis of the solid solution by nitridation of aluminum with silicon carbide under a nitrogen gas pressure of 4-8 MPa was also investigated. The maximum combustion temperature and wave propagation velocity were found to be influenced by the electric field in the field-activated combustion synthesis, and by the green density and nitrogen pressure in the combustion nitridation. In both cases the formation of solid solutions is complete within seconds, considerably faster than in conventional methods which require hours.

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.223-227
• /
• 1996

The effect of ZrC and VC addition on the diffusion induced recrystallization (DIR) of TiC-Cr3C2 has been investigated. With in creasing the amount of added ZrC to Cr3C2 the DIR of TiC was suppressed at the begining and then occurred. On the contrary the DIR was accelerated with the addition of VC to Cr3C2 Because the lattice parameters of (Ti, Cr)C and (Ti,V)C are smaller and that of (Ti, Zr)C is larger than that of TiC the lattice parameter of (Ti,Cr,Zr)C is expected to be similar to that of TiC,. The results indicate that the strain energy due to lattice mismatch between TiC and solid-solution carbide is the driving force of the observed energy due to lattice mismatch between TiC and solid-solution carbide is the driving force of the observed DIR.

• International Journal of Precision Engineering and Manufacturing
• /
• v.5 no.1
• /
• pp.19-26
• /
• 2004

The growth of solid particles in TiC-XC-2vo1.% and TiC-XC-30vo1.% Ni alloys, (where X=Zr, W or Mo) was fitted to the equation of the form $d^3$-${do}^3$=Kt during the liquid phase sintering at 1,673K. Also, the grain growth behavior decreased markedly with the addition of ${MO}_2$C or WC and increased with the addition of zrC. The contiguity was greater in the alloys with a smaller growth rate constant and especially, decreased by increasing the Ni content in the TiC-${MO}_2$C-Ni alloy. In addition, the effect of the addition of carbide on the grain growth of 2 vo1.% Ni alloys was found to be similar to that of 30vo1.% Ni alloys. Consequently, the grain growth mechanism cannot be explained by the usual solution / reprecipitation process, but can be explained in terms of a new growth velocity equation, which includes the effects of contiguous carbide grain boundaries in restricting the overall grain growth, as well as the area of the solid / liquid interface in the alloy.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.355-356
• /
• 2006

WC-TiC-TaC binderless cemented carbide was oxidized under low partial pressure of oxygen (50ppm) at 873K for 1 to 20 h. Surface roughness was measured using atomic force microscope, and effect of TiC amount on oxidation behavior of the carbide was investigated. WC phase was oxidized more easily than WC-TiC-TaC solid solution phase. With an increase in TiC amount, WC-TiC-TaC phase increased and the oxidation resistance of the carbide increased.

• Clean Technology
• /
• v.19 no.2
• /
• pp.75-83
• /
• 2013

In the present paper, we review recycling and applications of titanium binary alloy scraps. The recycling techniques are to successfully prepare low oxygen content ingots using hydrogen plasma arc melting (HPAM) and to produce low oxygen content titanium alloy powders by Hydrogenation-dehydrogenation (HDH) and Deoxidation in solid state (DOSS) process. In addition, as applications of the titanium binary alloy scraps, Ti based solid-solution carbide powders, which would be used for producing Ti based solid-solution cermets with high toughness, were prepared using the titanium binary alloy scraps. These results confirmed that the titanium alloy scraps could be recycled and refined using the HPAM. The resulting oxygen content of the titanium alloy powders were below 1,000 ppm after powderizing. Finally, we had confirmed that the refined titanium alloy powders were able to be utilized as raw materials for preparing the toughened cermets.

• Journal of Korea Foundry Society
• /
• v.9 no.4
• /
• pp.311-319
• /
• 1989

The effects of the alloying elements and cooling rates on the formation of phosphide eutectics of compacted vermicular graphite cast irons containing copper, tin, molybdenum for producing pearlitic matrix, and also containing phosphorus and boron for increasing wear resistance, were investigated. The liquidus phosphide eutectic was found to solidify as a pseudo-binary phosphide eutectic, but with increasing of the cooling rate non-equlibrium phosphide eutectic with needle type carbide could be formed. However, the liquidus phosphide eutectic containing both phosphorus and carbide-forming boron was found to solidify always as a non-equlibrium phosphide eutectic with coarse carbide, independent from the cooling rate. It was also confirmed that the tiny isolated phase observed by SEM was gamma iron solid solution with phosphorus, silicon, molybdenum and the matrix containing these tiny islands was phosphide phase containing manganese and molybdenum. The addition of copper was found to decrease the tendency of forming ledeburitic carbides in the phosphide eutectic.

• Korean Journal of Materials Research
• /
• v.19 no.11
• /
• pp.588-595
• /
• 2009

The knowledge of grain growth of carbide particles is very important for manufacturing micrograined cemented carbides. In the present study, continuous and discontinuous grain growth in WC-Co and WC-VC-Co cemented carbides is investigated using the Monte Carlo computer simulation technique. The Ostwald ripening process (solution/re-precipitation) and the grain boundary migration process are assumed in the simulation as the grain growth mechanism. The effects of liquid phase fraction, grain boundary energy and implanted coarse grain are examined. At higher liquid phase content, mass transfer via solid/liquid interfaces plays a major role in grain growth. Growth rate of the implanted grain was higher than that of the matrix grains through solution/re-precipitation and coalescence with neighboring grains. The results of these simulations qualitatively agree with experimental ones and suggest that distribution of liquid phase and carbide particle/carbide grain boundary energy as well as contamination by coarse grain are important factors controlling discontinuous grain growth in WC-Co and WC-VC-Co cemented carbides. The contamination by coarse grains must by avoided in the manufacturing process of fine grain cemented carbides, especially with low Co.

• Journal of the Korean Society for Heat Treatment
• /
• v.15 no.2
• /
• pp.70-75
• /
• 2002

The depletion of solid solution elements from matrix and the change of carbides during artificial aging of 2.25CrMo steel at $630^{\circ}C$ were investigated. The Mo and Cr elements were found to be depleted drastically in the early stage of aging. The change of carbides was confirmed by analyzing the XRD patterns of electrolytically extracted carbides. Four type of carbides, $M_{23}C_6$, $M_3C$, $M_2C$ and $M_6C$, were found to exist in the specimen before aging. The amount of $M_6C$ carbides increased with aging time, while that of $M_3C$ carbides diminished after short aging time.

• Korean Journal of Materials Research
• /
• v.30 no.12
• /
• pp.678-686
• /
• 2020

Microstructural characteristics of directionally solidified René 80 superalloy are investigated with optical microscope and scanning electron microscope; solidification velocity is found to change from 25 to 200 μm/s under the condition of constant thermal gradient (G) and constant alloy composition (Co). Based on differential scanning calorimetry (DSC) measurement, γ phase (1,322 ℃), MC carbide (1,278 ℃), γ/γ' eutectic phase (1,202 ℃), and γ' precipitate (1,136 ℃) are formed sequentially during cooling process. The size of the MC carbide and γ/γ' eutectic phases gradually decrease with increasing solidification velocity, whereas the area fractions of MC carbide and γ/γ' eutectic phase are nearly constant as a function of solidification velocity. It is estimated that the area fractions of MC carbide and γ/γ' eutectic phase are determined not by the solidification velocity but by the alloy composition. Microstructural characteristics of René 80 superalloy after solid solution heat-treatment and primary aging heat-treatment are such that the size and the area fraction of γ' precipitate are nearly constant with solidification velocity and the area fraction of γ/γ' eutectic phase decreases from 1.7 % to 0.955 %, which is also constant regardless of the solidification velocity. However, the size of carbide solely decreases with increasing solidification velocity, which influences the tensile properties at room temperature.