• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.202.1-202.1
• /
• 2013

ZnO nanostructure was fabricated on a Si substrate using two-step growth. The seed layer was grown on the Si substrate by a sol-gel spin-coating. In the first step, ZnO nanorods were grown by a hydrothermal method at $140^{\circ}C$ for 5 min. In the second step, a ZnO thin film was grown on the ZnO nanorods by spin-coating. After growth, these films were annealed at $800^{\circ}C$ for 10 min. Electrical and optical properties of ZnO nanostructures have modified by plasma-assisted molecular beam epitaxy (PA-MBE) regrowth. The carrier concentration and resistivity increased by PA-MBE regrowth. In the photoluminescence, the full width at half maximum and intensity were decreased and increased, respectively, by PA-MBE regrowth.

• Korean Journal of Materials Research
• /
• v.22 no.10
• /
• pp.526-530
• /
• 2012

Silica-based ceramic-matrix composites have shown promise as advanced materials for many applications such as chemical catalysts, ceramics, pharmaceuticals, and electronics. $SiO_2$-CuO-$CeO_2$ multi-component powders and their thin film, using an oxalic acid template as a chelating agent, have larger surface areas and more uniform pore size distribution than those of inorganic acid catalysts. $SiO_2$-CuO-$CeO_2$ composite powders were synthesized using tetraethylorthosilicate, copper (II) nitrate hemi (pentahydrate), and cerium (III) nitrate hexahydrate with oxalic acid as template or pore-forming agent. The process of thermal evolution, the phase composition, and the surface morphology of these powders were monitored by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffractometry (XRD), field-emission scanning electron microscopy (FE-SEM), and energy dispersive X-ray spectrometry (EDXS). The mesoporous property of the powders was observed by Brunner-Emmett-Teller surface (BET) analysis. The improved surface area of this powder template with oxalic acid was $371.4m^2/g$. This multi-component thin film on stainless-steel was prepared by sol-gel dip coating with no cracks.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.28 no.1
• /
• pp.214-224
• /
• 2002

High concentrated $TiO_2$ nano colloids were synthesized by sol-gel method. Reactions were performed in $TiCl_4$/HCl/$H_2O$ aqueous solution and the conditions of particles such as shape, size and aggregation, etc. were controlled by polymerization and adsorption of acrylamide in surface of $TiO_2$ nano particles. And also, aminopropyltriethoxysilane was added instead of acrylamide and compared each other. The prepared colloids were well dispersed and showed the strong absorption peaks at 350nm-370nm which is blue shifted to 20-30nm, compared to macro particles. The obtained techniques from $TiO_2$ nato colloids synthesis were utilized in coating on boron nitride powders which are nonpolar and isoelectronic materials of carbon. Their surface morphology, structure, thermal stability and U. V absorption chracteristics were examined by SEM(Scanning Electron Microscopy), XRD(X-ray diffraction), TG/DTA(Thermogravimetric and Differential Thermal Analysis), UV-VIS(Ultraviolet-Visible Spectroscopy).

• Journal of Ceramic Processing Research
• /
• v.20 no.6
• /
• pp.603-608
• /
• 2019

In this study, the multilayered thin films of (Ba,Sr)TiO3/K(Ta,Nb)O3 were fabricated by the sol-gel and spin coating methods, and their structural and electrical properties were investigated. The specimen showed polycrystalline X-ray diffraction (XRD) characteristics with a tetragonal structure. The average grain size and film thickness for one coating were about 30~40nm and 60nm, respectively. The phase transition temperature of specimen was lower than 10 ℃. The dielectric constant and loss at 20 ℃ of the specimen coated six times were 1,231 and 0.69, respectively. The rate of change in dielectric constant at an applied direct current (DC) voltage of the six times coated thin films was 17.3%/V. The electrocaloric effect was the highest around the temperature at which the remanent polarization rapidly changed. When an electric field of 660kV/cm was applied to the triply coated thin films, the highest electrocaloric property of 4.41 ℃ was observed.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.3
• /
• pp.37-40
• /
• 2006

Oxide buffer layers for YBCO coated conductors were fabricated using MOD processing and development of microstructure and texture were investigated. A $CeO_2$ buffer layers were formed on RABiTS tape. Acetate-based precursor solution was employed to synthesize the precursor solution. Subsequently, the precursor solution was stabilized and modified with triethanolamine. $CeO_2$ precursor gel film was coated and annealed in $Ar/H_2$ atmosphere at high temperature. An annealed $CeO_2$ film shows mixed orientation with high (001) texturing. It was shown that (111) texture of $CeO_2$ layers were enhanced by multiple coating. This degradation was attributed to development of microcracks in the multiply coated $CeO_2$ films. Also discussed are the synthesis and the characterization of $La_2Zr_2O_7$ (LZO) buffer layers on RABiTS tape. A biaxially textured LZO buffer layer was fabricated with MOD processing method using metal alkoxide based precursor solution. It was shown that the LZO film were epitaxially grown on RABiTS tape and crack-free & uniform surface was obtained after annealing in $Ar/H_2$ atmosphere.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.3
• /
• pp.99-105
• /
• 2014

$LiCoO_2$ thin film have received attention as cathodes of thin-film microbatteries. In this study, $LiCoO_2$ thin films were synthesized on Au substrates by sol-gel spin coating method and electrochemical properties were investigated under annealing temperature and time. The phycochemical properties of $LiCoO_2$ thin film were investigated by X-ray diffraction, scaning electron microscopy and atomic force microscopy. The electrochemical properties were characterized using galvanostatic charging/discharging cycling tests. From X-ray diffraction, as-grown films annealed at $550^{\circ}C$ and $750^{\circ}C$ are presumed to be spinel structure and a single phase of the layered-rock-salt, respectively. The RMS roughness and grain size of the films which annealed at $750^{\circ}C$ has similar values for annealing time 10 and 30 min, while for annealing time 120 min surface roughness, grain size increase and pore appearance were observed. The first discharge capacity of $LiCoO_2$ thin films annealed at $750^{\circ}C$ for 10, 30 and 120 min is about 54.5, 56.8 and $51.87{\mu}Ah/cm^2{\mu}m$, respectively. Corresponding capacity retention at 50th cycle is 97.25, 76.69, 77.19%.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.4
• /
• pp.20-25
• /
• 2020

As nanoscience and nanotechnology advance, techniques for selective pattern growth have attracted significant attention. Silica nanoparticles (NPs) are used as a promising nanomaterials for bio-labeling, bio-imaging, and bio-sensing. In this study, silica NPs were synthesized by a sol-gel process using a modified Stöber method. In addition, the selective pattern growth of silica NPs was achieved by the surface functionalization of the substrate using a micro-contact printing technique of a hydrophobic treatment. The particle size of the as-synthesized silica NPs and morphology of selective pattern growth of silica NPs were characterized by FE-SEM. The contact angle by surface functionalization of the substrate was investigated using a contact angle analyzer. As a result, silica NPs were not observed on the hydrophobic surface of the OTS solution treatment, which was coated by spin coating. In contrast, the silica NPs were well coated on the hydrophilic surface after the KOH solution treatment. FE-SEM confirmed the selective pattern growth of silica NPs on a hydrophilic surface, which was functionalized using the micro-contact printing technique. If the characteristics of the selective pattern growth of silica NPs can be applied to dye-doped silica NPs, they will find applications in the bio imaging, and bio sensing fields.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.37 no.6
• /
• pp.583-590
• /
• 2013

Variable emittance radiators can be used in a thermal management system in space because their total emittance changes depending on the temperature of the system. When the temperature of the system decreased, the emittance also decreased so as to minimize the heat loss to the environment. In contrast, when the temperature of the system increased, the emittance also increased such that radiation cooling could occur. Thermochromic materials, whose emittance is a function of the temperature, are often used in variable emittance radiators because no additional parts are needed. In this study, we fabricated a variable-emittance coating by using a sol-gel method based on LSMO ($La_{1-x}Sr_xMnO_3$) and experimentally characterized the emittance change with respect to temperature. Furthermore, we also examined the stability of LSMO film in space environments by exposing it to extremely low pressure and temperature.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.909-915
• /
• 2003

Anodic oxide films on aluminum play an important role as a dielectrics in aluminum electrolytic capacitor. In order to obtain the high capacitance, ZrO$_2$ films were coated on aluminum foils by sol-gel method and then, the properties of anodized films were studied. The coating and drying of the films were repeated 4-10 times and annealed at 300～$600^{\circ}C$ and the triple layer of ZrO$_2$/Al-ZrO$_{x}$ /Al$_2$O$_3$ was formed onto aluminum substrates after anodizing of ZrO$_2$/Al film. The thickness of $Al_2$O$_3$ layer was decreased with increasing the annealing temperature due to the densification of ZrO$_2$ film. The ZrO$_2$ films were crystallized even at 30$0^{\circ}C$ and showed nanocrystalline structure. The. capacitance of aluminum foil annealed at low temperature was higher than that at high temperature. The increase of capacitance was due to the high capacitance of ZrO$_2$ film annealed at low temperature. The capacitance of ZrO$_2$ coated aluminum increased about 3 times compared to that without a ZrO$_2$ layer after anodizing to 400 V. From these results, the aluminum foils with composite oxide layers are found to be applicable to the aluminum electrolytic capacitor.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.2
• /
• pp.164-168
• /
• 2024

(La_0.7Sr_0.3)(Mn_1-xFe_x)O₃ (LSMFO) (x = 0.03, 0.06, 0.09, 0.12) precursor solution are prepared by sol-gel method. LSMFO thin films are fabricated by the spin-coating method on Pt/Ti/SiO₂/Si substrate, and the sintering temperature and time are 800℃ and 1 hr, respectively. The average thickness of the 6-times coated LSMFO films is about 181 to 190 nm and average grain size is about 18 to 20 nm. As the amount of Fe added in the LSMFO thin film increased, the resistivity decreased, and the TCR and B_25/65-value increased. Electrical resistivity, TCR and B_25/65-value of the (La_0.7Sr_0.3)(Mn_0.88Fe_0.12)O₃ thin film are 0.0136 mΩ-cm, 0.358%/℃, and 328 K at room temperature, respectively. The resistivity properties of LSMFO thin films matched well with Mott's VRH model.