• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1999년도 특별강연 및 추계학술발표대회 개요집
• /
• pp.251-254
• /
• 1999

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 1999년도 특별강연 및 춘계학술발표대회 개요집
• /
• pp.61-62
• /
• 1999

• Journal of Welding and Joining
• /
• 제20권4호
• /
• pp.505-509
• /
• 2002

Pb is considered to be eliminated from solder, due to its toxicity. However, melting temperatures of most Pb-free solders are known higher than that of Sn37Pb. Therefore, there is a difficulty to apply Pb-free solders to electronic industry. Since Sn3Ag8Bi5In has relatively lower melting range as $188~200^{\circ}C$, on this study. Wettability and soldering characteristics of Sn3Ag8Bi5In solder in BGA were investigated to solve for what kind of problem. Zero cross time, wetting time, and equilibrium force of Sn3Ag8Bi5In solder for Cu and plated Cu such as Sn, Ni, and Au/Ni-plated on Cu were estimated. Plated Sn on Cu showed best wettability for zero cross time, wetting time and equilibrium farce. Shear strength of the reflowed joint with Sn3Ag8Bi5In ball in BGA was investigated. Diameter of the ball was 0.5mm, UBM(under bump metallurgy) was $Au(0.5\mu\textrm{m})Ni(5\mu\textrm{m})/Cu(18\mu\textrm{m})$ and flux was RMA type. For the reflow soldering, the peak reflow temperature was changed in the range of $220~250^{\circ}C$, and conveyor speed was 0.6m/min.. The shear strength of Sn3Ag8Bi5In ball showed similar level as those of Sn37Pb. The soldered balls are aged at $110^{\circ}C$ for 36days and their shear strengths were evaluated. The shear strength of Sn3Ag8Bi5In ball was increased from 480gf to 580gf by aging for 5 days.

• 마이크로전자및패키징학회지
• /
• 제12권2호
• /
• pp.95-103
• /
• 2005

42Sn-58Bi 솔더(이하 wt.$\%$에 의한 표기)와 무전해 Ni-P/치환 Au under bump metallurgy (UBM) 간의 계면 반응을 intermetallic compound (IMC)의 형성과 성장, UBM의 감소, 그리고 범프 전단강도의 영향 관점에서 시효 처리 전 후에 어떠한 변화가 생기는 지를 알아보고자 하였다. 치환 Au 층을 $5{\mu}m$ 두께의 무전해 Ni-P ($14{\~}15 at.\%$ P)위에 세 가지 각기 다른 두께, 즉 $0{\mu}m$(순수한 무전해 Ni-P UBM), $0.1{\mu}m$, $1{\mu}m$로 도금하였다. 그 후 42Sn-58Bi 솔더 범프를 세 가지 다른 UBM 구조에 스크린프린팅 방식으로 형성하였다. 범프 형성 직후에는 세 가지 다른 UBM구조에서 솔더와 UBM 사이에 공통적으로 $Ni_3Sn_4$ IMC (IMC1) 만이 형성됐다. 하지만, 이를 $125^{\circ}C$에서 시효 처리를 할 경우 특이하게 Au를 함유한 UBM 구조에서는 $Ni_3Sn_4$ 위로 또 다른 4원계 화합물 (IMC2)이 관찰되었다. 원자 비로 $Sn_{77}Ni{15}Bi_6Au_2$인 4원계 화합물로 확인되었다. $Sn_{77}Ni{15}Bi_6Au_2$ 층은 솔더 조인트의 접합성에 매우 치명적인 영향을 미쳤다. 시효 처리를 거친 Au를 함유한 UBM 구조에서 솔더 범프의 전단 강도 값은 시효 처리 전에 비해 $40\%$ 이상의 감소를 보였다.

• Journal of Welding and Joining
• /
• 제31권3호
• /
• pp.4-10
• /
• 2013

In electronic industry, the trend of future electronics will be flexible, bendable, wearable electronics. Until now, there is few study on bonding technology and reliability of bonding joint between chip with micro solder bump and flexible substrate. In this study, we investigated joint properties of Si chip with eutectic Sn-58Bi solder bump on Cu pillar bump bonded on flexible substrate finished with ENIG by flip chip process. After flip chip bonding, we observed microstructure of bump joint by SEM and then evaluated properties of bump joint by die shear test, thermal shock test, and bending test. After thermal shock test, we observed that crack initiated between $Cu_6Sn_5IMC$ and Sn-Bi solder and then propagated within Sn-Bi solder and/or interface between IMC and solder. On the other hands, We observed that fracture propated at interface between Ni3Sn4 IMC and solder and/or in solder matrix after bending test.

• 한국주조공학회지
• /
• 제17권3호
• /
• pp.245-251
• /
• 1997

Solderability, interfacial reaction and mechanical properties of joint between Sn-Bi-Ag base solder and Cu-substrate were studied. Solders were subjected to aging treatments to see the change of mechanical properties for up to 30 days at $100^{\circ}C$, and then also examined the changes of microstructure and morphology of interfacial compound. Sn-Bi-Ag base solder showed about double tensile strength comparing to Pb-Sn eutectic solder. Addition of 0.7wt%Al in the Sn-Bi-Ag alloy increase spread area on Cu substrate under R-flux and helps to reduce the growth of intermetallic compound during heat-treatment. According to the aging experiments of Cu/solder joint, interfacial intermetallic compound layer was exhibited a parabolic growth to aging time. The result of EDS, it is supposed that the soldered interfacial zone was composed of $Cu_6Sn_5$.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2007년 추계학술발표대회 개요집
• /
• pp.168-170
• /
• 2007

Sn-Bi eutectic solder alloy have is good wetting and physical properties. The results of solder paste properties test, melting point is about $139^{\circ}C$ and spread test is represent spread properties of $7{\sim}16%$. The results of shear strength after as reflowed, thermal shock test, high temperature storage test of 500hr and 1000hr at $100^{\circ}C$. The shear strength value range is from 6000 to 11000gf, pull strength value range is from 2200 to 3300gf.

• 한국재료학회지
• /
• 제8권9호
• /
• pp.807-812
• /
• 1998

Sn-Bi-X(X:2Cu, 2Sb, 5In) 계 땜납과 Cu 기판과의 계면반응 및 기계적성질에 대하여 고찰하였다. Cu판과 땜납의 접합부는 $100^{\circ}C$에서 60일까지 열처리하여 광학현미경, SEM, EDS,분석을 통하여 시효처리에 따른 미세조직과 계면반응을 분석하였으며, 인장강도 및 연신율은 제조된 시편을 30일까지 열처리 한 후 0.3mm $\textrm{min}^{-1}$로 인장하여 시험하였다. 미세조직 분석결과 Cu의 첨가로 미세조직이 미세화 됨을 알 수 있으며, 계면에 형성된 화합물은 첨가원소에 따라 다르게 나타났다. 인장시험 결과 열처리 초기에는 땜납쪽에서의 파괴가 발생하였으나 열처리 시간이 증가하면서 계면반응층고 땜납의 계면에서 파괴가 발생하였다. 열처리에 따른 인장강도는 Cu를 첨가한 경우에 가장 높은 값을 나타냈다.

• 마이크로전자및패키징학회지
• /
• 제19권3호
• /
• pp.71-76
• /
• 2012

SnBi 저온솔더의 플립칩 공정을 이용한 스마트 의류용 칩 접속공정에 대해 연구하였다. 캐리어 필름에 형성한 Cu 리드프레임을 $130^{\circ}C$에서 직물에 열압착 시킴으로써 Cu 리드프레임이 전사된 직물 기판을 형성하였다. 칩 시편에 SnBi 페이스트를 도포하여 솔더범프를 형성한 후 직물 기판의 Cu 리드프레임에 배열하고 $180^{\circ}C$에서 60초 동안 유지시켜 플립칩 본딩하였다. SnBi 저온솔더를 사용하여 형성된 스마트 의류용 플립칩 접속부의 평균 접속저항은 $9m{\Omega}$이었다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1996년도 재료학회 춘계학술발표회
• /
• pp.25-26
• /
• 1996