• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.529-530
• /
• 2006

This paper concerned with SPS (spark plasma sintering), hot pressing of sinter nanometer WC-Co powder and discussed the density, hardness, microstructures and grain sizes of the alloys sintered. The results showed that the two sintered techniques could produce high density alloys and play well on the grain growth, but SPS could lower the sintering temperature and shorten sintering time. Besides, the hardness of the sintered cemented alloys that was dependent on the grain size and densification could also be improved.

• Journal of Advanced Marine Engineering and Technology
• /
• 제26권6호
• /
• pp.661-669
• /
• 2002

Rapid tooling technique enables us to make dies and molds that produce prototype parts with the correct material at a substantially reduced cost and time. In this study, experiments on selective laser sintering of tungsten carbide-cobalt mixture were carried out to find optimal sintering conditions that will be applied to rapid metal tooling. The experiments were carried out within an air, an argon and a nitrogen atmosphere. Coupons of single layer were sintered at various laser powers, scanning speeds and scan spacings. Very severe oxidation took place within an air atmosphere. The oxidation is reduced significantly within an argon and a nitrogen atmosphere. The thickness of the sintered coupons is increased as the energy density, the laser energy Per unit scanned area, is increased. Several multi-layer sintering experiments were also carried out.

• Metals and materials international
• /
• 제24권6호
• /
• pp.1303-1308
• /
• 2018

A new sintering technique for enhancing a densification and hardness of sintered titanium body by supplying hydrogen was developed (Hydrogen Sintering Process, HSP). The HSP was developed by only injecting hydrogen into an argon atmosphere during the core time. As a result, sound titanium sintered bodies with high density and hardness were obtained by the HSP. In addition, a pore size and number of the HSP specimens were smaller than those of the argon atmosphere specimen. It was found that the injecting hydrogen into the argon atmosphere by HSP can prevent the formation of oxide layers, resulting in enhanced densification and hardness.

• 한국세라믹학회지
• /
• 제29권4호
• /
• pp.305-311
• /
• 1992

As compared with conventional sintering, rapid heating in microwave system could enhance sinterability and final properties of alumina with a very short sintering time. In this study microwave sintering was performed using zirconia brick as a reaction chamber which was positioned in a 2.45 GHz(700 W) multimode microwave cavity. Microwave-sintered alumina showed high density and smaller grain size than conventionally sintered alumina because the ratio of densification rate/grain growth rate was increased by rapid heating.

• 한국세라믹학회지
• /
• 제31권11호
• /
• pp.1265-1270
• /
• 1994

Ultra-fine hydroxyapatite powder were synthesized by the hydrothermal reaction at 10 atm, 3 hrs of Ca(OH)2 suspension with (NH4)2HPO4 solution, and were characterized sintering behavior. Sintered bodies of hydroxyapatite powders which synthesized by hydrothermal reaction method has less weight loss, less sintering shrinkage and superior mechanical property, and was more dense than sintered bodies of hydroxyapatite powder which synthesized by wet method. Sintered bodies were hydroxyapatite single phase. When soack in Ringer's solution for 2 weeks, hydroxyapatite powders preserved hydroxyapatite and sintered body absorbed trace of Ca2+ ion with soaked time.

• 한국재료학회지
• /
• 제22권6호
• /
• pp.280-284
• /
• 2012

Bismuth antimony telluride (BiSbTe) thermoelectric materials were successfully prepared by a spark plasma sintering process. Crystalline BiSbTe ingots were crushed into small pieces and then attrition milled into fine powders of about 300 nm ~ 2${\mu}m$ size under argon gas. Spark plasma sintering was applied on the BiSbTe powders at 240, 320, and $380^{\circ}C$, respectively, under a pressure of 40 MPa in vacuum. The heating rate was $50^{\circ}C$/min and the holding time at the sintering temperature was 10 min. At all sintering temperatures, high density bulk BiSbTe was successfully obtained. The XRD patterns verify that all samples were well matched with the $Bi_{0.5}Sb_{1.5}Te_{3}$. Seebeck coefficient (S), electric conductivity (${\sigma}$) and thermal conductivity (k) were evaluated in a temperature range of $25{\sim}300^{\circ}C$. The thermoelectric properties of BiSbTe were evaluated by the thermoelectric figure of merit, ZT (ZT = $S^2{\sigma}T$/k). The grain size and electric conductivity of sintered BiSbTe increased as the sintering temperature increased but the thermal conductivity was similar at all sintering temperatures. Grain growth reduced the carrier concentration, because grain growth reduced the grain boundaries, which serve as acceptors. Meanwhile, the carrier mobility was greatly increased and the electric conductivity was also improved. Consequentially, the grains grew with increasing sintering temperature and the figure of merit was improved.

• 한국세라믹학회지
• /
• 제34권6호
• /
• pp.629-635
• /
• 1997

The effects of the annealing atmospheres(O2, N2) and sintering additives that Bi2O3 is a major composition on the microwave dielectric and sintering propertie of (1-x)CaTiO3-xLaAlO3 system were investigated. The annealing atmospheres and the increase of annealing time after sintering did not affect the relative dielectric constant($\varepsilon$r) and temperature coefficient of resonant frequency($\tau$f) of (1-x)CaTiO3-xLaAlO3 system. However, the Q.f0 values of (1-x)CaTiO3-xLaAlO3 were very sensitive to annealing atmospheres. As the annealing time increased under O2 atmosphere the Q.f0 values of (1-x)CaTiO3-xLaAlO3 enhanced untill 10 hrs in 0.3$\leq$x$\leq$0.6 region, but degraded over that time. The increasing rate of Q.f0 value increased wth increasing x. On the other hand, as the annealing time increased under N2 atmosphere the Q.f0 values were constant in x$\leq$0.6 region, increased gradually in x$\geq$0.7 region. When 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% as sintering additives were added to (Ca0.5La0.5) (Ti0.5Al0.5)O3 (x=0.5) the sintering temperature of 1$600^{\circ}C$ was lowered to 140$0^{\circ}C$, and the relative dielectric constant($\varepsilon$r) and temperature coefficient of resonant frequency($\tau$f) were not nearly changed. The addition of 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% to (Ca0.5La0.5)(Ti0.5Al0.5)O3 made the Q.f0 values to be lower about 15% and 34%, respectively.

• 열처리공학회지
• /
• 제17권1호
• /
• pp.17-22
• /
• 2004

In the present study, newly developed spark plasma sintering(SPS) technique was introduced to refine the grain size of ${\gamma}$-based TiAl intermetallic compounds. Ti-46Al-1.5Mo and Ti-46Al-1.5Mo-0.2C(at%) prealloyed powders were produced by mechanical milling(MM) in high-energy attritor. The mechanically milled powders were characterized by XRD and SEM for the microstructural evolution as a function of milling time. And then, the MMed powders were sintered by both spark plasma sintering and hot pressing in vacuum (HP). After the sintering process, MM-SPSed specimens were heat-treated in a vacuum furnace (SPS-VHT) and in the SPS equipment(MM-SPS) for microstructural control. It was found from microstrutural observation that the microstructure consisting of equiaxed ${\gamma}$-TiAl with a few hundred nanometer in average size and ${\alpha}_2-Ti_3Al$ particles were formed after both sintering processes. It was also revealed from hardness test and three-point bending test that the effect of grain refinement on the hardness and bending strength is much higher than that of carbon addition. The fully lamellar microstructures, which is less than $80{\mu}m$ in average grain size was obtained by SPS-VHT process, and the fully lamellar microstructure which is less than $100{\mu}m$ in average grain size was obtained by MM-SPS for a relatively shorter heat-treatment time.

• 한국세라믹학회지
• /
• 제48권5호
• /
• pp.418-425
• /
• 2011

In this study, a high energy ball milling process was introduced in order to improve the densification of direct nitrided AlN powder. The sintering behavior and thermal conductivity of the AlN milled powder was investigated. The mixture of AlN powder and 5 wt% $Y_2O_3$ as a sintering additive was pulverized and dispersed by a bead mill with very small $ZrO_2$ bead media. The milled powders were sintered at $1700^{\circ}C-1800^{\circ}C$ for 4 h under $N_2$ atmosphere. The results showed that the sintered density was enhanced with increasing milling time due to the particle refinement as well as the increase in oxygen contents. Appropriate milling time was effective for the improvement of thermal conductivity, but the extensive millied powder formed more fractions of secondary phase during sintering, resulted in the decrease in thermal conductivity. The AlN powder milled for 10min after sintering at $1800^{\circ}C$ revealed the highest thermal conductivity, of 164W/$m{\cdot}K$ in tne densified AlN sintered at $1800^{\circ}C$.

• 자원리싸이클링
• /
• 제16권4호
• /
• pp.10-16
• /
• 2007

전로슬래그를 완효성 칼리비료로 활용하기 위한 기초연구로, 전로슬래그 분말에 시약급 $SiO_2$와 $K_2CO_3$를 첨가하여 염기도를 각각 0.7, 1.0및 1.4로 조절하고, $K_2O$의 함량은 22mass%로 고정한 후 볼밀에서 24시간 이상 혼합하여 $900^{\circ}C{\sim}1000^{\circ}C$ 사이의 온도에서 10분${\sim}$60분 동안 소결하였다. 소결 후 X-선 회절과 ICP분석을 이용하여 제조된 칼리비료의 특성을 조사하고 또한 염기도, 소결온도 및 소결시간이 완효성 칼리비료의 제조 조건에 미치는 영향을 검토하였다. 소결체의 수용성 $K_2O$의 용출특성은 소결시간이 길어질수록, 소결온도가 높아질수록, 염기도가 감소할수록 용출율이 감소하였다. 한편 구용성 $K_2O$의 용출특성은 염기도가 증가할수록 증가하는 경향이 뚜렷하였으며, 소결온도가 높을수록 용출율은 완만하게 감소하였다.