• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.11
• /
• pp.690-695
• /
• 2016

Induction cooktop has a great attention due to its safety, quick heating and cleanness compared to gas oven. However, the materials for induction cookware is limited to steel or stainless-steel which has the magnetic property. Recently, it has been tried to apply various porcelain to induction cookware after printing the silver layer on the bottom of cookware plates and co-firing at high temperature. Glass frits are added in the silver paste to improve an adhesion force between porcelain materials containers and transferred silver layer. The hybrid silver pastes for induction cookware requires the proper electrical resistance and the thermal conductivity with base plates. After sintering process at $800^{\circ}C$, a part of melted glass migrated to the porcelain and the rest of the glass frit was exposed to the surface. It was confirmed that most of the glass frit formed an adhesion layer between the porcelain and transferred silver layer that enhances the adhesion force.

• Korean Journal of Metals and Materials
• /
• v.46 no.8
• /
• pp.516-523
• /
• 2008

The effect of glass-frit size on microstructural evolution and electrical resistance of conductive silver paste was investigated. Silver paste was prepared by mixing 70 wt% commercial silver powder with $1.6{\mu}m$, 3 wt% Bi based glass-frit and 27 wt% organic vehicle. Two different sizes of glass-frit were obtained by ball-milling of commercial glass-frit ($3{\mu}m$) for 3 and 5 days, which had an average particle size of 1.0 and $0.5{\mu}m$. The smaller glass-frit was melt at low sintered temperature and rapidly spread between the silver particles, which is induced the dense networking among silver particles and strong adhesiveness to $Al_2O_3$ substrate. The silver film with smaller glass-frit sintered at $500^{\circ}C$ showed the small pore size and low porosity resulting in low electrical resistivity of $4{\mu}{\Omega}cm$.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2005.11a
• /
• pp.82-83
• /
• 2005

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.155-155
• /
• 2003

• Archives of design research
• /
• v.18 no.4 s.62
• /
• pp.35-44
• /
• 2005

In the world, most of the metal technologists were as called as adornment artists than other field of industrial arts strongly industrial characters functional materials and manufacturing technology many used in the present age. In the study, one of adornments researched and material character analyzed about Art Clay Silver. The shrinkage rate of shape was about 0.24%. A shrinking phenomenon drying time thought of evaporation of water linking bonding agents and powders. After calcination of Art Clay Silver, the EDX used that just Ag 100% analyzed a result from the surface assay in the room temperature. A binder with powder in the room temperature considered to disappear, because it was been fume and smoke at high calcined temperature. A study showed when handicrafted necklaces make by these characteristic as using in difficult and delicated operations rather than naturally and beautifully expressive products.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.33 no.8
• /
• pp.1273-1279
• /
• 2009

This study examined the difference in the mechanical properties of cotton fabrics treated with nano silver. Nano silver powder, UV-absorber, and DMDHEU are applied to cotton fabrics. The reagents added in a finishing solution were Triton X-100 and $MgCl_2$ $6H_2O$. The mechanical properties of the fabrics were measured by KES-FB system. From these, the primary hand values were evaluated by the conversion equation (KN-202-DS). The results of this study are summarized as follows. The fabric tensile properties and bending properties are increased by the application of nano silver, DMDHEU, and UV-absorber mixed. The values of tensile properties in the warp direction were significantly lower than those in the weft direction. However, the values of bending properties in the warp direction were higher than those in the weft direction. The differences in the values of compression parameters by nano silver coating were unnoticeable. However, the compression energy and resilience of compression in each fabric was increased by DMDHEU treatment. The SMD values of cotton fabrics are decreased by nano silver, DMDHEU, and UV-absorber mixed treatment.

• Journal of the Korean Ceramic Society
• /
• v.33 no.4
• /
• pp.471-477
• /
• 1996

During Bi(Pb)-Sr-Ca-Cu-O superconductor wire fabrication the effect of the initial packing density on the final characteristics of superconductor wire was systematically studied. To increase the powder packing density with uniform distribution of superconducting core a billet insertion method processed by CIP was applied instead of the commonly used vibration and ramming method of powder insertion into silver sheath. Compared with the vibration and ramming method the billent insertion technique processed by CIP cause the 30% incre-specimen with 130${\mu}{\textrm}{m}$(core thickness : 45 ${\mu}{\textrm}{m}$)and 5.24 mm width processed at 84$0^{\circ}C$for 200hrs. shows specimen with 130${\mu}{\textrm}{m}$ (core thickness ; 45${\mu}{\textrm}{m}$)and 5.24 mm width processed at 84$0^{\circ}C$ for 200 hrs. shows maximum 34A for Ic and 16, 700 A/cm2 for Ic measured at 77K and 0T. Also the sample rolled 3 times shows maximum 7, 2A for Ic and 11, 000 A/cm2 for 77K and 0T. Based on X-ray experimental results the formation of Bi-2223 and texture were significantly well developed at the interface between the superconducting core and silver sheath as compared with those of the interior area of superconducting core.

• Korean Journal of Materials Research
• /
• v.18 no.5
• /
• pp.283-288
• /
• 2008

The effect of sintering aids and glass-frit on the densification and resistivity of silver paste was investigated in an effort to enhance the sintered density and electrical conductivity of the silver electrode. To prepare Pb-free silver paste for use at low sintering temperatures, two commercial silver powders ($0.8\;{\mu}m$ and $1.6\;{\mu}m$ in size) and 5wt.% lab-synthesized nanoparticles (30-50 nm in size) as a sintering aids were mixed with 3 wt.% or 6 wt.% of glass frit ($Bi_2O_3$-based) using a solvent and three roll mills. Thick films from the silver paste were prepared by means of screen printing on an alumina substrate followed by sintering at $450^{\circ}C$ to $550^{\circ}C$ for 15 min. Silver thick films from the paste with bimodal particles showed a high packing density, high densification during sintering and low resistivity compared to films created using monomodal particles. Silver nanoparticles as a sintering aid enhanced the densification of commercial silver powder at a low sintering temperature and induced low resistivity in the silver thick film. The glass frit also enhanced the densification of the films through liquid phase sintering; however, the optimum content of glass frit is necessary to ensure that a dense microstructure and low resistivity are obtained, as excessive glass-frit can provoke low conductivity due to the interconnection of the glass phase with the high resistivity between the silver particles.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.313-322
• /
• 2004

Thick film photolithography is a new technology in that the lithography process such as exposure and development is applied to the conventional thick film process including screen-printing. In this research, low-temperature cofireable silver paste, which enabled the formation of thick film fine-line using photolithographic technology, was developed. The optimum composition for fine-line forming was studied by adjusting the amounts of silver powder, polymer and monomer, and the additional amount of photoinitiator, and then the effect of processing parameter such as exposing dose on the formation of fine-line was also tested. As the result, it was found that the ratio of polymer to monomer, silver powder loading, and the amount of photoinitiator were the main factors affecting the resolution of fine-line. The developed photosensitive silver paste was printed on low-temperature cofireable green sheet, then dried, exposed, developed in aqueous process, laminated, and fired. Results showed that the thick film fine-line under 20$\mu\textrm{m}$ width could be obtained after cofiring.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.559-560
• /
• 2006

Inkjet Printing is very attractive method for direct patterns with no masks, In order to Achieve direct printing with nano metal, It is often necessary to print them with highly concentrated Ink We research the High Concentrated silver nano ink. Formulation which has a good thermal stability and storage stability and jet stability using a ethylene glycol ether. Normally Alcohol-based inks can be sensitive But High boiling point ethylene glycol ether base Ink is creating a stable meniscus and minimum maintenance issues. We are reaching a 50~60wt% high Silver Ink using a Hydrophilic Ag Nano powder. (30~50nm)