• 반도체디스플레이기술학회지
• /
• 제16권1호
• /
• pp.45-51
• /
• 2017

Poly(urethane acrylate) siloxane oligomers with Interpenetrating polymer netwoked nanoparticles were prepared to synthesize hard coating solution by reaction with diisocyanates. The diisocyanate combined siloxane hard coating solution showed more flexibility than the siloxane solution. In addition, diisocyanate resulted in improvement of curl property and surface hardness in the siloxane solution. Of the used diisocyanates, isophorone diisocyanate and acryloyloxy ethyl diisocyanate were good for UV hard coating solution. This effect will decrease brittleness in the siloxane solution using for plastic display plate.

• 반도체디스플레이기술학회지
• /
• 제16권3호
• /
• pp.87-92
• /
• 2017

Poly(urethane acrylate) siloxane oligomers with Interpenetrating polymer networked nanoparticles were prepared to synthesize hard coating solution by reaction with isophorone diisocyanate(IPDI) of 1, 2, 3, 4 phr. The structures and molecular weights of the synthesized solutions were characterized by IR spectroscopy and gel permeation chromatography, respectively. In the cross-cut test for the adhesion, all the solutions showed good adhesion of 5B regardless of the content of IPDI and film thickness. The addition of 1 phr IPDI resulted in the best pencil hardness. The IPDI combined siloxane hard coating solution showed more flexibility than the siloxane solution. These results will yield the improvement in the siloxane solution using for plastic display plate.

• Bulletin of the Korean Chemical Society
• /
• 제35권6호
• /
• pp.1665-1669
• /
• 2014

Four multialkoxy-functionalized siloxane base-polymers (BP-1~4) were synthesized through either hydrosilylation or condensation reactions in order to prepare multi-networked siloxane polymers having appropriate physical properties for protective coating in fabrications of electronics. Formulations of 4 base-polymers gave coating materials A and B. Product A showed well-controlled flowing and leveling properties, and product A-2 was successfully applied to protective insulating coating for junction areas of connectors and chips in PDP controller. Tack free time, extrusion rate, dielectric breakdown voltage, hardness, thermal stability, water resistance and flame resistance of products A and B were examined.

• 분석과학
• /
• 제25권2호
• /
• pp.127-132
• /
• 2012

반도체와 전자부품의 코팅제로 사용되는, 특히 LCD와 PDP 커넥터주위의 보호를 위해 사용되는 폴리실록산(시편)의 흐름성(flow) 및 퍼짐성(self-leveling)을 측정할 수 있는 시험 장치가 고안되었고, 점도가 각기 다른 실록산 폴리머 견본들을 이용하여 고안된 시험장치를 시험하였다. 이 장치를 사용하여 시편의 흐름성 및 퍼짐성을 측정한 결과, 이 장치가 점도를 통해 흐름성 및 퍼짐성을 예측하던 것을 대신 할 수 있다고 판단되었다. 특히, 흐름성이 적절히 조절되어야만 하는 LCD, PDP 및 반도체 커넥션 보호 코팅제의 특성 평가에 유용하게 활용될 것으로 기대된다.

• 한국표면공학회지
• /
• 제34권3호
• /
• pp.258-263
• /
• 2001

Siloxane thin films were fabricated on a silicon wafer by spin-coating using a siloxane solution made by the sol-gel process. Fluorine was doped using$ CF_4$ plasma treatment. The film was then annealed in-situ state in the nitrogen atmosphere. In order to examine the influence of annealing and fluorine doping on the siloxane thin film, thermogravimetric-differential thermal analysis (TG-DTA), Fourier transform-infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS) were used and the dielectric constant was determined by the high-frequency capacitance-voltage method. Stable siloxane films could be obtained by in-situ annealing in a nitrogen atmosphere after $CF_4$ plasma treatment, and the dielectric value of the film was $\varepsilon$ 2.5.

• Elastomers and Composites
• /
• 제55권2호
• /
• pp.103-107
• /
• 2020

Herein, resin-formed polysilsesquioxanes (PSSQs) were synthesized using monomolecular fluoro silane as a precursor. The synthesized PSSQs exhibited anti-smudge performance and were used as coating liquid. Two structures were acquired by controlling the amount of the silane precursor and the K₂CO₃ catalyst; these materials were used to prepare the anti-smudge coating liquid solution. The synthesized product was analyzed by various methods such as nuclear magnetic resonance spectroscopy, X-ray diffraction analysis, gel permeation chromatography, and water contact angle measurement. The results confirmed that the as-synthesized PSSQs exhibited the ladder structure and had a molecular weight of 5,117 g/mol and water contact angle of 102.31°.

• Korean Chemical Engineering Research
• /
• 제57권6호
• /
• pp.749-757
• /
• 2019

Methyltrimethoxysilane (MTMS)과 trimethylethoxysilane (TMES)을 출발물질로 사용하여 여러 종류의 용매에 용해시킨 후 다양한 종류의 촉매를 사용해 물과의 가수분해 및 중축합반응을 진행시켜 비불소계 발수 코팅 용액을 제조하였다. 또한 이 코팅 용액을 냉연 강판 위에 스핀 코팅하고 열 경화시켜 발수 코팅 도막을 제조 하였다. 이 과정 중 촉매와 용매의 종류 변화가 생성된 코팅 도막의 발수성에 미치는 영향을 연구하였다. 강산인 염산과 질산을 촉매로 사용한 경우에는 용액 내에 siloxane polymer들의 응집이 발생한 흰색의 불투명 상태를 나타냈다. 반면에 약산인 아세트산, 인산과 옥살산을 사용한 경우에는 투명하고 침전이 없는 안정한 용액 상태를 보였다. 이로 인해 강산인 염산과 질산을 사용한 경우의 코팅 도막의 접촉각은 각각 $58^{\circ}$와 $92^{\circ}$로 낮은 발수성을 보인 반면에 약산인 아세트산, 인산과 옥살산으로 제조된 경우에는 각각 $101^{\circ}$, $103^{\circ}$, $116^{\circ}$의 접촉각을 보여 높은 발수성을 나타내었다. 또한 이소프로판올과 에탄올을 용매로 사용한 경우에는 용액 내에서 siloxane polymer들의 응집이 일어나 불투명한 침전이 발생한 상분리 현상을 보인 반면 메탄올, 에틸아세테이트와 메틸에틸케톤을 용매로 사용한 경우에는 투명하고 침전이 없는 안정된 상태를 나타내었다.

• Macromolecular Research
• /
• 제10권2호
• /
• pp.67-74
• /
• 2002

New immunoprotecting membranes were prepared by spin coating the amphiphilic random multiblock copolymers of poly(ethylene glycol) (PEG) and poly(tetramethylene ether glycol) (PTMEG) or poly(dimethyl siloxane) (PDMS) on porous Durapore(R) membrane. The copolymer coating was intended to make a biocompatible, immunoprotecting diffusional barrier and the supporting porous substrate was for mechanical stability and processability. By filling Durapore(R) membrane pores with water, the penetration of coating solution into the pores was minimized during the spin coating process. A single coating process produced a completely covered thin surface layer (~1 ${\mu}{\textrm}{m}$ in thickness) on the porous substrate membrane. The permselectivity of the coated layer was influenced by PEG block length, polymer composition, and thickness of the coating layer. A composite membrane with the coating layer prepared with PEG 2 K/PTMEG 2 K block copolymer showed that its molecular weight cut-of fat any 40 based on dextran was close to the molecular size of IgG (Mw = 150 kDa). However, IgG permeation was detected from protein permeation test, while glucose oxidase (Mw = 186 kDa) was not permeable through the coated membrane.

• 폴리머
• /
• 제39권3호
• /
• pp.499-505
• /
• 2015

Dimethyldimethoxysilane(DMDMS), methyltrimethoxysilane(MTMS)과 phenyltrimethoxysilane(PTMS)을 이용하여 폴리유기실록산 열 경화성 코팅액을 제조하고 가교도와 페닐기 함량이 코팅액과 도막 물성에 미치는 영향을 살펴보았다. Si-NMR 측정에서 얻어진 D $T^{Me}$ $T^{Ph}$ 구조 코팅액 조성비가 사용된 DMDMS, MTMS, PTMS의 몰 비로부터 얻어진 이론치와 일치함을 확인할 수 있었다. 가교밀도가 높을수록 그리고 페닐 함량이 낮을수록 실록산 결합의 증가에 의하여 코팅액 분자량이 증가됨을 알 수 있으며 페닐기 증가는 코팅액 굴절률 증가에 매우 큰 영향을 미침을 알 수 있었다. 가교밀도가 높을수록, 페닐기 함량이 감소할수록 코팅도막 경도는 증가되었으며 내열특성 또한 우수해짐을 확인할 수 있었다. 이상의 결과로부터 같은 실록산 결합을 갖는 폴리유기실록산 코팅제라도 치환도에 따른 가교도 조절과 페닐기 함량에 따라 코팅액 물성이 달라짐을 확인할 수 있었다.

• 멤브레인
• /
• 제20권4호
• /
• pp.297-303
• /
• 2010

폴리올레핀 중합공정에서 발생되는 미반응 올레핀 모노머를 회수하기 위한 분리막/냉각응축 공정에 적용할 복합막을 용액 코팅공정과 플라즈마 중합공정의 두가지 방법으로 제조하였다. Polysulfone (PSF) 지지체 위에 poly(dimethylsiloxane) (PDMS) 용액을 코팅하였고 코팅 용액에서 prepolymer의 함량이 높을수록 올레핀 모노머의 선택도는 증가하였으나 막이 치밀하여지는 관계로 절대 투과량은 감소하는 경향을 보였다. 유기물의 복합막 투과는 용액확산 메커니즘에 의한 것으로서 임계온도가 높을수록 분리효율은 향상되고 molar volume이 증가할수록 투과도가 향상되었다. 또한 가교시간에 siloxane 계열의 물질을 plasma 종합하여 복합막을 제조하였는데 PSF 및 polypropylene (PP) 지지체를 사용하였다. 특히 지지체로 기존의 용액코팅 공정에서 사용되기 어렵던 PP 지지체 위에도 복합막을 코팅할 수 있었으며 용액코팅 공정으로 제조된 복합막과 유사한 성능을 나타내었다.