• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.10
• /
• pp.504-508
• /
• 2001

The$(Sr_{1-x}Ca_x)TiO_3$(SCT) thin films are deposited on Pt-coated electrode $(Pt-TiN /SiO_2Si)$ using RF sputtering method at various deposition temperature. The crystallinity of thin films was increased with increased of deposition temperature n the temperature range of 200~500 $[^{\circ}C]$. The capacitance changes almost linearly in temperature ranges of -80~+90$[^{\circ}C]$. All SCT thin films used in the study the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200[kHz]. V-I characteristics of SCT thin films show the increasing leakage current with the increases of deposition temperature.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.3C no.2
• /
• pp.43-47
• /
• 2003

Lead zirconate titanate (PZT) thin films were fabricated by the pulsed laser ablation deposition (PLAD) method onto Pt/Ti/SiO$_2$/Si substrates. Crystalline phases as well as preferred orientations in PZT films were investigated by X-ray diffraction analysis (XRD). The well-crystallized perovskite phase and the (101) preferred orientation were obtained by two-step annealing at the conditions of $650^{\circ}C$, 1 hour. It was found that the temperature for the pulsed laser ablated PZT films annealed via a two-step annealing process can be reduced 20$0^{\circ}C$ compared to that of the conventional three-step annealing temperature profile for enhancing the transformation of the perovskite phase. The remanent polarization and the coercive field of this film were about 20 $\mu$C/$\textrm{cm}^2$ and 46 kV/cm, while the dielectric constant and loss values measured at 1 KHz were approximately 860 and 0.04, respectively. The interesting phenomena of this film, such as vertical shift in hysteresis curve, are also discussed.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.4
• /
• pp.178-183
• /
• 2002

The PLZT (x/50/50, x = 1, 2, 5, 7) thin films have been prepared by a sol-gel method using polypropanediol as a solvent, and their dielectric properties have been investigated. The prepared sol was coated 10 times on $Pt/Ti/SiO2_2$/Si wafer. After post-annealing at 560~$600^{\circ}C$ for 10 min, the 600 nm-thick PLZT (x/50/50) thin films were formed with pure perovskite phase. Grain size of the PLZT (x/50/50) thin films was increased with increasing the amount of La. For all the compositions, dielectric properties such as dielectric constant and remnant polarization were enhanced with increasing annealing temperatures. As the amount of La was increased, the remnant polarization, coercive field and dielectric constant of the PLZT (x/50/50) thin films fired at $600^{\circ}C$ were decreased.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.12
• /
• pp.59-64
• /
• 1996

InSb MIS devices prepared by remote PECVD SiO$_{2}$ were fabricated. The SiO$_{2}$ films on InSb were deposited at atemperature range of 67~190$^{\circ}$C. The effects of deposition temperature on the structural characteristics of the SiO$_{2}$ films evaluated Auger electron spectroscopy showed that atomic raito of silicon to oxygen was 0.5 and composition toms were distributed uniformaly throuout the oxide film. The transition region is about 100$\AA$ for SiO$_{2}$/InSb interface. The leakage current density at 1MV/cm and the breakdownelectric field of the MiS device using SiO$_{2}$ film deposited at 105$^{\circ}$C were about 22 nA/cm$^{2}$ and 3.5MV/cm, respectively. The interface-state density at mid-bandgap extracted from 1 MHz high frequency C-V measurement was about 2X10$^{11}$ cm$^{-2}$eV$^{-1}$.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.665-672
• /
• 2000

The ferroelectric YMnO3 thin films were prepared by MOD(metal-organic decomposition) method with Y- and Mn-acetylacetonate as starting materials. Thin films were grown on various substrates by spin-coating technique. The crystalline phases of the thin films were identified by X-ray diffractometer as a function of heat-treatment temperature, pH of coating solution and substrate. In addition, the effect of Mn/Y molar ratio(0.8~1.2) on the formation of hexagonal-YMnO3 phase was investigated. In forming highly c-axisoriented hexagonal-YMnO3 single phase, the Pt coated Si substrate was more effective than the bare Si substrate, and the optimum heat-treatment condition was at 82$0^{\circ}C$ for 30 min. Higher Mn/Y molar ratio within 0.8~1.2 and pH of YMnO3 precursor solution within 0.5~2.5 favored formation of ferroelectric hexagonal phase rather than orthorhombic phase. Leakage current density of the hexagonal-YMnO3 thin film formed on Pt(111)/TiO2/SiO2/Si substrate was low enough as 0.4~4.0$\times$10-8(A/$\textrm{cm}^2$) at 5 V and its remanent polarization(Pr), calculated from the P-E hysteresis loop, was 3 nC/$\textrm{cm}^2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.7
• /
• pp.458-461
• /
• 2014

TiC thin films were deposited on Si wafer by unbalanced magnetron sputtering (UBMS) system with two targets of graphite and titanium. During the TiC sputtering, the RF power was varied from 100 W to 175 W and the physical and electrical properties of TiC films were investigated. The hardness and rms surface roughness of TiC films were improved with increasing RF power and the maximum hardness about 24 GPa and the minimum rms surface roughness about 1.2 nm were obtained. The resistivity of TiC films was decreased with increasing RF power. Consequently, the physical and electrical properties of TiC film wewe improved with increasing RF power.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.5
• /
• pp.237-241
• /
• 2004

Amorphous silicon (a-Si) films are used in a broad range of solar cell, flat panel display, and sensor. Because of the greater ease of deposition and lower processing temperature, thin films are widely used for thin film transistors (TFTs). However, they have lower stability under the exposure of visible light and because of their low field effect mobility ($\mu$$_{FE}$ ) , less than 1 c $m^2$/Vs, they require a driving IC in the external circuits. On the other hand, polycrystalline silicon (poly-Si) thin films have superiority in $\mu$$_{FE}$ and optical stability in comparison to a-Si film. Many researches have been done to obtain high performance poly-Si because conventional methods such as excimer laser annealing, solid phase crystallization and metal induced crystallization have several difficulties to crystallize. In this paper, a new crystallization process using a molybdenum substrate has been proposed. As we use a flexible substrate, high temperature treatment and roll-to-roll process are possible. We have used a high temperature process above 75$0^{\circ}C$ to obtain poly-Si films on molybdenum substrates by a rapid thermal annealing (RTA) of the amorphous silicon (a-Si) layers. The properties of high temperature crystallized poly-Si studied, and poly-Si has been used for the fabrication of TFT. By this method, we are able to achieve high crystal volume fraction as well as high field effect mobility.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.3
• /
• pp.90-94
• /
• 2004

The variation of electrical properties of (Ba,Sr)$TiO_3$ [BST] thin films for Metal-Insulator-Semiconductor (MIS) capacitors was investigated. BST thin films were deposited on p-Si(100) substrates by the RF magnetron sputtering with temperature range of 500~$600^{\circ}C$. The dielectric properties of MIS capacitors consisting of AUBST/$SiO_2$/Si sandwich structure were measured for various conditions. We examined the characteristics of MIS capacitor with various oxygen pressure, substrate temperature and (Ba+Sr)/Ti ratio. It was found that the leakage current was reduced in MIS capacitor with high quality $SiO_2$ layer was grown on bare p-Si substrate by thermal oxidation. The BST MIS structure showed relatively high capacitance even though it is the combination of high-dielectric BST thin films and $SiO_2$ layer. The charge state densities of the MIS capacitors and Current-voltage characteristics of the MIS capacitor were investigated. By applying $SiO_2$ layer between BST thin films and Si substrate, low leakage current of $10^{-10}$ order was observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.151-154
• /
• 2003

AlN/Al/SiO$_2$/Si thin films for application to FBAR(Film Bulk Acoustic Resonator) devices were prepared by FTS(Facing Targets sputtering system) apparatus which provides a stable discharge at low gas pressures and can deposit high quality thin films because of the substrate located apart from the plasma. The AlN thin films were deposited on a $SiO_2(1{\mu}m)/Si(100)$ substrate using an Al bottom electrode. The process parameters were fixed such as sputering power of 200W, working pressures of 1mTorr and AlN thin film thickness of 800nm, respectively and crytallographic characteristics of AlN thin films were investigated as a function of $N_2$ gas flow rate$[N_2/(N_2+Ar)]$. Thickness of AlN thin films were measured by $\alpha$-step, the crystallographic characteristics and c-axis preferred orientation were evaluated by XRD.

• Journal of Korea Foundry Society
• /
• v.15 no.4
• /
• pp.360-367
• /
• 1995

Effects of metal coating treatment on SiC particle on wetting behavior and interfacial strength were studied. Experimental variables are included types of coated metallic films such as Cu and Ni-P, and temperatures of heat-treatment under vacuum. The experimental results concerning wetting phenomena of liquid Al on SiC, showed that coating treatment of metallic film on SiC particles remarkably improves the wetting behavior of liquid Al on SiC, especially in the case of Ni-P coating. The interfacial strength of Al/SiC composites made of coated SiC plate was higher than that of the composite with non-coated SiC plate although the coating treatment was not perfect.