• 한국전기전자재료학회논문지
• /
• 제14권10호
• /
• pp.779-784
• /
• 2001

In this work, we studied the characteristics of nitride films for the optimization of PMD(pro-metal dielectric) linear process, which can be applied to the recent semiconductor manufacturing process. We split the deposit condition of nitride films into four parts such as PO(protect overcoat) nitride, baseline, low hydrogen and high stress and low hydrogen, respectively. We tried to find out correlation between BPSG deposition and densification. In order to analyze the changes of Si-H and Si-NH-Si bonding density, we used FTIR area method. We also investigated the crack generation on wafer edge after BPSG densification, and the changes of nitride film stress as a function of RF power variation to judge whether the deposited films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 춘계학술대회 논문집 반도체재료
• /
• pp.38-41
• /
• 2001

In this work, we have been studied the characteristics of each nitride film for the optimization of PMD(pre-metal dielectric) liner nitride process, which can applicable in the recent semiconductor manufacturing process. The deposition conditions of nitride film were splited by PO (protect overcoat) nitride, baseline, low hydrogen, high stress and low hydrogen, respectively. And also we tried to catch hold of correlation between BPSG(boro-phospho silicate glass) deposition and densification. Especially, we used FTIR area method for the analysis of density change of Si-H bonding and Si-NH-Si bonding, which decides the characteristics of nitride film. To judge whether the deposited films were safe or not, we investigated the crack generation of wafer edge after BPSG densification, and the changes of nitride film stress as a function of RF power variation.

• 한국전기전자재료학회논문지
• /
• 제30권8호
• /
• pp.479-483
• /
• 2017

The effect of $NH_3$ plasma treatment on device characteristics was confirmed for an optimized thin film transistor of poly-Si formed by ELA. When C-V curve was checked for MIS (metal-insulator-silicon), Dit of $NH_3$ plasma treated and MIS was $2.7{\times}10^{10}cm^{-2}eV^{-1}$. Also in the TFT device case, it was decreased to the sub-threshold slope of 0.5 V/decade, 1.9 V of threshold voltage and improved in $26cm^2V^{-1}S^{-1}$ of mobility. Si-N and Si-H bonding reduced dangling bonding to each interface. When gate bias stress was applied, the threshold voltage's shift value of $NH_3$ plasma treated device was 0.58 V for 1,000s, 1.14 V for 3,600s, 1.12 V for 7,200s. As we observe from this quality, electrical stability was also improved and $NH_3$ plasma treatment was considered effective for passivation.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.247-250
• /
• 2001

We studied optical properties of SiON thin-film in the applications of optical waveguide. SiON thin-film was grown in $300^{\circ}C$ by PECVD(plasma enhanced chemical vapor deposition) system. The change of SiON thin-film composition and refractive Index was studied as a function of varying $NH_3$ gas flow rate. As $NH_3$ gas flow rate was increased, Quantity of N and refractive index were increased at the same time. By the results, we could form the SiON thin-film to use of a waveguide with refractive index of 1.6. We analyzed the conditions of the thin-film with FTIR(fourier transform infrared) and OES (optical emission spectroscopy). N-H bonding($3390cm^{-1}$ ) can be removed by thermal annealing. And we could observe the SiH bonding state and quantity by OES analysis in $SiH_4$

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.247-250
• /
• 2001

We studied optical properties of SiON thin-film in the applications of optical waveguide. SiON thin-film was grown in 300$^{\circ}C$ by PECVD(plasma enhanced chemical vapor deposition) system. The change of SiON thin-film composition and refractive Index was studied as a function of varying NH$_3$ gas flow rate. As NH$_3$ gas flow rate was increased, Quantity of N and refractive index were increased at the same time. By the results, we could form the SiON thin-film to use of a waveguide with refractive index of 1.6. We analyzed the conditions of the thin-film with FTIR(fourier transform infrared) and OES(optical emission spectroscopy). N-H bonding(3390cm$\^$-1/) can be removed by thermal annealing. And we could observe the SiH bonding state and quantity by OES analysis in SiH$_4$

• 한국전기전자재료학회논문지
• /
• 제15권6호
• /
• pp.479-485
• /
• 2002

We have investigated the effects of various wafers cleaning on glass/Si bonding using 4 inch Pyrex glass wafers and 4 inch silicon wafers. The various wafer cleaning methods were examined; SPM(sulfuric-peroxide mixture, $H_2SO_4:H_2O_2$ = 4 : 1, $120^{\circ}C$), RCA(company name, $NH_4OH:H_2O_2:H_2O$ = 1 : 1 : 5, $80^{\circ}C$), and combinations of those. The best room temperature bonding result was achieved when wafers were cleaned by SPM followed by RCA cleaning. The minimum increase in surface roughness measured by AFM(atomic force microscope) confirmed such results. During successive heat treatments, the bonding strength was improved with increased annealing temperatures up to $400^{\circ}C$, but debonding was observed at $450^{\circ}C$. The difference in thermal expansion coefficients between glass and Si wafer led debonding. When annealed at fixed temperatures(300 and $400^{\circ}C$), bonding strength was enhanced until 28 hours, but then decreased for further anneal. To find the cause of decrease in bonding strength in excessively long annealing time, the ion distribution at Si surface was investigated using SIMS(secondary ion mass spectrometry). tons such as sodium, which had been existed only in glass before annealing, were found at Si surface for long annealed samples. Decrease in bonding strength can be caused by the diffused sodium ions to pass the glass/si interface. Therefore, maximum bonding strength can be achieved when the cleaning procedure and the ion concentrations at interface are optimized in glass/Si wafer direct bonding.

• 한국진공학회지
• /
• 제17권3호
• /
• pp.215-219
• /
• 2008

실리콘 웨이퍼 위에 Plasma Enhanced Chemical Vapor Deposition (PECVD) 방법으로 증착 된 SiNx 박막의 수소 함량을 측정하였다. 제작된 SiNx 박막은 Fourier Transform Infrared Spectroscopy (FT-IR) 사용하여 박막의 수소함량과 결합상태를 확인하였으며, Atomic Force Microscopy (AFM) 측정을 통하여 박막의 표면 거칠기를 비교, 시료의 조성비 평가를 위하여 Rutherford Backscattering Spectrometry (RBS)을 사용하였다. 또한 SiNx박막의 조성확인을 위하여 Photoluminescence(PL)를 이용하여 FT-IR spectrum의 결과와 비교 해석하였다. FT-IR에서 NH의 수소함량(at%)이 0.92 %에서 0.64 %로 낮아질 수록 AFM을 이용한 표면 거칠기는 12.8 $\AA$에서 10.8 $\AA$로 낮아지고, Si양이 상대적으로 많아지는 것을 PL에서 확인하였으며, RBS에서도 시뮬레이션을 통해 비슷한 결과를 얻을 수 있었는데, 이는 FT-IR을 사용함으로써 SiNx 박막의 수소 함량의 측정이 가능하다는 것을 보여주므로 단위공정에서 신속하게 SiNx 박막 분석이 가능함을 알 수 있었다.

• Korean Chemical Engineering Research
• /
• 제44권5호
• /
• pp.513-519
• /
• 2006

본 연구에서는 유리(glass)와 석영(quartz)을 재질로 사용하여 MEMS(micro-electro mechanical systems) 공정을 통해 전기영동(electrophoresis)을 위한 microchip을 제작하였다. UV 광이 실리콘(silicon)을 투과하지 못하는 점에 착안하여, 다결정 실리콘(polycrystalline Si, poly-Si) 층을 채널 이외의 부분에 증착시킨 광 차단판(optical slit)에 의해 채널에만 집중된 UV 광의 신호/잡음비(signal-to-noise ratio: S/N ratio)를 크게 향상시켰다. Glass chip에서는 증착된 poly-Si 층이 식각 마스크(etch mask)의 역할을 하는 동시에 접합표면을 적절히 형성하여 양극 접합(anodic bonding)을 가능케 하 였다. Quartz 웨이퍼에 비해 불순물을 많이 포함하는 glass 웨이퍼에서는 표면이 거친 채널 내부를 형성하게 되어 시료용액의 미세한 흐름에 영향을 미치게 된다. 이에 따라, HF와 $NH_4F$ 용액에 의한 혼합 식각액(etchant)을 도입하여 표면 거칠기를 감소시켰다. 두 종류의 재질로 제작된 채널의 형태와 크기를 관찰하였고, microchip electrophoresis에 적용한 결과, quartz과 glass chip의 전기삼투 흐름속도(electroosmotic flow velocity)가 0.5와 0.36 mm/s로 측정되었다. Poly-Si 층에 의한 광 차단판의 존재에 의해, peak의 S/N ratio는 quartz chip이 약 2배 수준, glass chip이 약 3배 수준으로 향상되었고, UV 최대흡광 감도는 각각 약 1.6배 및 1.7배 정도 증가하였다.

• 마이크로전자및패키징학회지
• /
• 제20권2호
• /
• pp.11-15
• /
• 2013

The wafer bonding process becomes a flexible approach to material and device integration. The bonding strength in 3-dimensional process is crucial factor in various interface bonding process such as silicon to silicon, silicon to metals such as oxides to adhesive intermediates. A measurement method of bonding strength was proposed by utilizing AFM applied CNT probe tip which indicated the relative simplicity in preparation of sample and to have merit capable to measure regardless type of films. Also, New Tool was utilized to measure of tip radius. The cleaned $SiO_2$-Si bonding strength of SPFM indicated 0.089 $J/m^2$, and the cleaning result by RCA 1($NH_4OH:H_2O:H_2O_2$) measured 0.044 $J/m^2$, indicated negligible tolerance which verified the possibility capable to measure accurate bonding strength. And it could be confirmed the effective bonding is possible through SPFM cleaning.

• 한국재료학회지
• /
• 제21권4호
• /
• pp.236-241
• /
• 2011

Polysilazane and silazane-based precursor films were deposited on stacked TiN/Ti/TEOS/Si-substrate by spin-coating, then annealed at $150{\sim}400^{\circ}C$, integrated further to form the top electrode and pad, and finally characterized. The precursor solutions were composed of 20% perhydro-polysilazane ($SiH_2NH$)n, and 20% hydropolymethyl silazane ($SiHCH_3NH$)n in dibutyl ether. Annealing of the precursor films led to the compositional change of the two chemicals into silicon (di)oxides, which was confirmed by Fourier transform infrared spectroscopy (FTIR) spectra. It is thought that the different results that were obtained originated from the fact that the two precursors, despite having the same synthetic route and annealing conditions, had different chemical properties. Electrical measurement indicated that under 0.6MV/cm, a larger capacitance of $2.776{\times}10^{-11}$ F and a lower leakage current of 0.4 pA were obtained from the polysilazane-based dielectric films, as compared to $9.457{\times}10^{-12}$ F and 2.4 pA from the silazane-based film, thus producing a higher dielectric constant of 5.48 compared to 3.96. FTIR indicated that these superior electrical properties are directly correlated to the amount of Si-O bonds and the improved chemical bonding structures of the spin-on dielectric films, which were derived from a precursor without C. The chemical properties of the precursor films affected both the formation and the electrical properties of the spin-on dielectric film.