• Journal of the Korea Institute of Building Construction
• /
• v.20 no.5
• /
• pp.391-397
• /
• 2020

This study is to compare and analyze the strength, drying shrinkage and carbonation properties of lightweight aggregate mortar using recycling water as prewetting water and mixing water. The flow, compressive strength, split tensile strength, drying shrinkage and carbonation depth of lightweight aggregate mortar with recycling water were measured. As test results, the mortar flow was similar in all mixes regardless of the recycling water content. The compresseive strength of the RW5 mix with 5% recycling water as prewetting water and mixing water was the highest value, about 53.9 MPa after 28 days. In addition, the tensile strength of lightweight mortar was about 3.4 to 3.8 MPa, indicating 7 to 9% of the compressive strength value regardless of recycling water content. In the case of drying shrinkage, the RW2.5 mix using 2.5% recycling water showed the lowest shrinkage rate as about 0.107% at 56 days. The drying shrinkage of the plain mix without recycling water was relatively higher than the RW2.5 and RW5 mix. The RW5 mix showed lowest carbonation depth compared to other mixes. In this study, the RW5 lightweight aggregate mortar with 5% recycling water exhibits excellent compressive strength and carbonation resistance. Therefore, it is considered that if the recycling water, a by-product of the concrete industry, is properly used as prewetting water and mixing water of lightweight mortar and concrete, it will be possible to increase the recycling rate of the by-product and contribute to improve the property of lightweitht aggregate mortar and concrete.

• Journal of Conservation Science
• /
• v.24
• /
• pp.57-66
• /
• 2008

It is reported that excavated carbonized wooden objects tend to have more peeling and deformation stemming from the coexisting of different types of parts of objects. However, there is little research results on this. In this experiment, the sugar alcohol method was used and then compared with the results of the PEG4000 method which widely uses. This research targets: prediction of strength by weight increase, investigation of the dimensional stabilization effects by measuring the rate of shrinkage change, condition of drug penetration and change of wood texture by using a scanning electron microscope. As the results, the PEG4000 method needs a phased approach over 80% impregnation. On the other hand, the S A method remains steady from over 40% impregnation. The Deformation of carbonized wooden objects used in this experiment is considered as the phenomenon by shrinkage of non-carbonized parts. The PEG4000 method is verified the shrinkage in the samples treated with 20%, 40% and 60%; the S A method is verified the shrinkage in the samples treated with 20%.

• Polymer(Korea)
• /
• v.37 no.2
• /
• pp.249-253
• /
• 2013

From poly(lactic acid) (PLA) and poly(propylene carbonate) (PPC) synthesized using $CO_2$, a PLA/PPC/PLA layered film is prepared by coextrusion and then stretched to uniaxial orientation. The mechanical, optical, and barrier properties and shrinkage of the prepared film were investigated in detail. The maximum shrinkage of PLA/PPC/PLA film reached to 60% at $75^{\circ}C$. With increasing PPC content, the ratio of shrinkage of the film was increased and its shrinkagerate was increased. The ratio of shrinkage of the film decreased with increasing stretching temperature. The prepared film has oxygen and vapor transmission barrier properties. In this study, the PLA/PPC/PLA film is expected to be commercialized as a environmentally friendly shrinkable film.

• The Research Journal of the Costume Culture
• /
• v.25 no.6
• /
• pp.880-892
• /
• 2017

In this study, the appearance change and the heat moisture transfer properties of knitted fabric by yarn shrinkage were examined to obtain useful data on the development of thermo-sensitive functional materials. Eleven types of knitted fabric were knitted using highly bulky acrylic-blended yarn. After shrinking the specimens using dry heat treatment, the appearance change and thickness were measured. An HEC simulator was adopted for measuring the heat moisture transfer properties of specimens by yarn shrinkage. When holes were arranged vertically in the mesh structure, the specimens with 2,500 and 5,000 holes showed high percent change of hole area, appearance, and thickness. When holes were diagonally arranged in the mesh structure, the percent change of hole area in the specimen with 1,250 holes was larger than the one with 2,500 holes. However, the dimensional stability of the specimen with 2,500 holes was better because of its smaller appearance and thickness change. In the tuck structure, the percent change of hole area in the specimen with 625 and 416 holes was relatively large compared with the appearance and thickness change. Furthermore, the hole size in the tuck structure was smaller than that in the mesh structure but the percent change of hole area was larger. Therefore, it was proved that the tuck structure is more suitable than the mesh structure for developing thermo-sensitive functional materials. Heat moisture transfer property test verified that the change of hole area by yarn shrinkage enabled obtaining the thermal effect due to the distinct temperature difference in the inner layer.

• International Journal of Highway Engineering
• /
• v.11 no.4
• /
• pp.87-94
• /
• 2009

Volume of concrete slab changes by variations of temperature and moisture after its placement. Shrinkage due to evaporation causes tensile stress in the slab when contraction of the slab is restrained by its self weight, friction with subbase, and etc. Actual tensile stress caused by the shrinkage was less than theoretically predicted stress according to previous studies. It was the stress reduction due to visco-elastic property of the early-age concrete slab partially restrained. In this study, strains of restrained circumferential, unrestrained circumferential, and unrestrained square pillar concrete specimens were measured to investigate stress reduction of the specimens with age of concrete. Elastic modulus of the concrete was measured at the age of 1, 3, 7, 14, 28 days and penetration test was performed. The stress reduction was calculated by input the test results into theoretical equations suggested by previous researchers. The stress reduction of the restrained concrete specimens will be applied to design of concrete pavements based on results of the study.

• Science of Emotion and Sensibility
• /
• v.14 no.1
• /
• pp.117-126
• /
• 2011

This study investigates the physical properties and manufacturing method of shape memory fabric for emotional garment made by polypropylene. For this purpose, polypropylene(PP) POY and SDY were texturized using low temperature and constant length heat treatment texturing technologies, respectively. The shape memory fabrics made using these texturized PP yarns were woven with two kinds of PET and PTT shape memory yarns on the air-jet loom and the various physical properties of four kinds of shape memory fabrics were measured and discussed. The tenacity and breaking strain of PP texturized yarns treated by low temperature and constant length heat treatment showed high weaving efficiency and the wet thermal shrinkage of PP textured yarns was shown less than 1.5%, dry thermal shrinkage was ranged between 3% and 5%, which means thermal stability compared to the PTT textured yarn with high thermal shrinkage, 5~8%. The shape memory characteristics of PP shape memory fabrics measured by Toray method showed five grade as same value as PTT shape memory fabric. The heat keeping property of the PP shape memory fabric showed 56% higher value than that of PTT shape memory fabric. The water repellency of PP shape memory fabric measured by spray method showed five grade as same value as PTT shape memory fabric treated with water repellent agent. Especially, shape memory properties of PP shape memory fabric measured by 3-D image and camera measurement methods showed similar characteristics to the PTT shape memory fabric.

• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.805-811
• /
• 2004

In this paper, effects of mixture proportion and material condition on both fundamental properties, drying and autogenous shrinkage of high performance concrete are discussed. According to the results, for the effect of mixture proportion on the fundamental properties, decrease in W/B and unit water content results in reduction of fluidity, while air content has no variation. Compressive strength exhibits an decreasing tendency with an increase in W/B and unit water content do not remarkable affect the compressive strength. For the effect of materials on the fluidity, the fluidity of low heat portland cement(LPC) is smaller than that of ordinary portland cement(OPC). The use of Polycarbonic acid based superplasticizer(PS) has more favorable effect on enhancing fluidity than Naphtalene based superplasticlzer(NS) and Melamine based superplasticizer(MS). Air content of concrete using LPC is larger than that using OPC. The effects of superplasticizer type on the air content is larger in order of MS, PS and NS. The use of LPC exhibited lower strength development at early age than OPC, whereas after 91days, similar level of compressive strength is achieved regardless of cement type. Compressive strength of concrete is not affected by SP type. For the effect of mixture proportion and materials on drying and autogenous shrinkage, an increase in W/B results in reduction of drying shrinkage and an decrease in water content leads to reduce drying shrinkage. Autogenous shrinkage is not observed until 49 days with the concrete mixture with $35\%$ of W/B and $145 kg/m^3$ of water content. This is due to the combination effects of expansion admixture and shrinkage reducing admixture, which causes an offset of autogenous shrinkage. The use of LPC results in a reduction in autogenous shrinkage compared with OPC. SP type has little influence on the autogenous shrinkage. It is found from the results that mixture proportioning of high performance concrete incorporating fly ash, silica fume, expansion admixture and shrinkage reducing admixture is need to focus on the increase in W/B and the reduction in water content and the use of LPC and MS is also required to use to secure the stability against shrinkage properties.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.753-756
• /
• 2005

Recently, the alkali activation of Fly-ash has become a significant field of research because it is possible to use these materials having highly chemical reaction property. Also, the product does not generate CO2 gas, unlike ordinary Portland cement(O.P.C). Therefore, the purpose of this paper is to design for improving mechanical and chemical properties using Fly-ash and Meta-kaolin. And additive(CaO) affected to control the strength behaviors and shrinkage rate.

• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1265-1270
• /
• 1994

Ultra-fine hydroxyapatite powder were synthesized by the hydrothermal reaction at 10 atm, 3 hrs of Ca(OH)2 suspension with (NH4)2HPO4 solution, and were characterized sintering behavior. Sintered bodies of hydroxyapatite powders which synthesized by hydrothermal reaction method has less weight loss, less sintering shrinkage and superior mechanical property, and was more dense than sintered bodies of hydroxyapatite powder which synthesized by wet method. Sintered bodies were hydroxyapatite single phase. When soack in Ringer's solution for 2 weeks, hydroxyapatite powders preserved hydroxyapatite and sintered body absorbed trace of Ca2+ ion with soaked time.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.169-172
• /
• 2002

Silver pastes for inner conductor in the Low Temperature Co-fired Ceramics (LTCC) are composed of silver powder, binder, solvent and additives. The composition of the chemicals have influence on rheology, printability, shrinkage rate, etc. In this study, commercial Ag pastes and Ag pastes made in KETI were investigated to find the relationship between characteristics of Ag paste and solid contents. Ag pastes with 68~90 wt% Solid Contents were tested. Substrate/paste matching property and conductivity of the conductor lines showed large dependence on solid contents of Ag paste.