• 한국표면공학회지
• /
• 제49권2호
• /
• pp.141-146
• /
• 2016

In this study, electrophoretic paint (E-paint) was deposited on the knife-abraded surface of AZ31 magnesium alloy (AZ31), and its adhesion and corrosion resistance were examined by tape peel-test and salt spray test, respectively. E-paint started to deposit on AZ31 Mg alloy after an inductance time and pores were found in the E-paint layer which is ascribed to hydrogen bubbles generated on the surface during the painting process. The pores disappeared after curing for 15 min at $160^{\circ}C$. The E-paint on AZ31 exhibited good adhesion after immersion in deionized water for 500 h at $40^{\circ}C$. The E-paint sample without scratch showed no corrosion after 1500 h of salt spray test. However, on the scratched sample, blisters were visible adjacent to the scratched sites after 500 h of salt spray test.

• 생물환경조절학회지
• /
• 제28권4호
• /
• pp.454-460
• /
• 2019

이 연구에서는 염수를 증발냉각법을 이용하여 담수를 생산할 목적으로 회전형 미세입자 분무장치를 설계 제작하여 회전체의 표면조도, BLDC 시로코 팬의 회전수 그리고 염수 공급량의 변화에 따른 분무입자의 크기와 분포 특성을 실험적으로 분석하고자 하였다. 회전체의 표면조도 $Ra=0.27{\sim}7.65{\mu}m$인 경우 분무입자 크기는 $0.117{\sim}1.360{\mu}m$ 였고, 분무입자의 90% 가 $0.50{\mu}m$ 이하인 것으로 나타났다. $Ra=12.70{\sim}22.84{\mu}m$인 경우에는 분무입자 크기가 $2.51{\sim}184.79{\mu}m$의 범위에 분포하였고, 분무입자의 98%가 $13.59{\mu}m$ 이하인 것으로 나타났다. BLDC 시로코 팬의 회전수가 분무입자의 크기와 분포에 미치는 영향을 분석하기 위하여 표면조도 $Ra=0.27{\mu}m$로 고정한 상태에서 염수 공급량을 일정하게 유지하면서 팬의 회전수를 3,800~5,600rpm 로 변화시켜가며 실험을 수행한 결과 염수 공급량이 2.77~8.28mL/min 인 경우에는 분무입자의 크기가 $0.314{\sim}0.541{\mu}m$의 범위에 분포하였다. 또한 염수공급량이 9.74mL/min 이고 회전수가 5,600rpm인 경우에는 분무입자의 98.23% 이상이 $2.51{\sim}13.59{\mu}m$의 범위에 분포하였다.

• 농약과학회지
• /
• 제9권4호
• /
• pp.411-421
• /
• 2005

환경오염을 최소화하고 병해충 방제효과를 증진시킬 수 있는 희석제농약의 적정사용기술을 확립하기 위하여, 희석용수의 수질이 살포액의 물리성과 약효에 미치는 영향 등을 검토한 결과, 국내 6대강의 하천수와 52지점의 지하수에 대한 경도는 $5{\sim}324$(평균 90) ppm, 전기전도도는 $0.038{\sim}l.078$(평균 0.265) dS/m의 범위로 전반적으로 농약의 희석용수로 양호한 수준이었다. 농약살포액의 pH는 주로 희석용수의 pH 변화에 좌우되었으며, 표면장력은 시간이 지날수록 낮아져 부착면에서는 유리할 것으로 판단되었다. 희석제농약의 유화성, 현수성 등의 물리성은 용수의 경도, 염농도의 영향을 받는 것으로 나타났으며, 농약주성분의 경시적 분해율도 조제 3일 후 대부분 5% 이내로 안정하였다. 유제와 수화제 농약의 혼용순서에 의한 살포액의 물리성은 수화시간을 제외한 모든 면에서 동일하였으며, 단지 수화제(WP>WG>SC)>유제>액제 순으로 희석하는 것이 살포액의 조제작업 측면에서 보다 용이하였다. 조제 3일 후 농약살포액의 각각의 적용병해충에 대한 방제효과는 조제 당일에 비해 95% 이상의 높은 방제효과를 유지하였다.

• 한국터널지하공간학회 논문집
• /
• 제19권2호
• /
• pp.283-299
• /
• 2017

터널의 누수는 콘크리트 라이닝과 같은 구조물의 장기 내구성을 저하시키는 원인이 된다. 내구성 저하 원인은 염화물, 황산염, 물, 가스 등 지하수에 포함되어 있는 여러 가지 물질이 될 수 있다. 본 연구에서는 터널의 지보재로서 또는 방수재로서 사용되는 뿜어붙임멤브레인의 방수성능과 염수에 대한 저항성을 파악하기 위한 기초 시험을 수행하였다. 그 결과, 일부 시험체에서 물의 침투가 발생할 수 있는 것을 파악하였고 그 원인이 액상폴리머와 분말재료의 혼합에 의해 생기는 내부공극과 수압에 의해 내부공극이 연결되어 발생하는 것임을 알 수 있었다. 그리고 증류수와 염수에 침지된 시험체에 대한 인장강도시험을 통해서 인장강도가 기건상태에 비해 절반 이하로 감소될 수 있음을 확인하였다. 또한 신장률은 염수보다 증류수에서 신장률이 더 커지는 결과가 나타났다. 그러나 이 결과는 추가적인 조사가 필요할 것으로 판단된다.

• 방사선산업학회지
• /
• 제2권3호
• /
• pp.149-154
• /
• 2008

The present study described an antimicrobial spray composition comprising nanosized silica-silver particles, in which nano-silver is bound to silica molecules and a water-soluble polymer, the nanosized silica-silver particles prepared by irradiating a solution comprising a silver salt, silicate and the water-soluble polymer with radiation rays. According to a surfactant addition, the compositions were not turbid and were colorless. Also samples (cotton fabrics and wallpaper) were treated with the compositions also did not cause any stains even after drying under sunshine and at $80^{\circ}C$. Our results suggested that the spray formulation product was of practical use to control indoor fungi.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2006년도 전기학술대회논문집
• /
• pp.265-266
• /
• 2006

The chemical conversion coating formed on magnesium alloy investigated for low cost and harmless in environment by using the colloidal silica as the main component. The film formed in 298 K is thick, the film, which was thought combination of Si-O, was formed. The film formed in 313 K is thinner than that in 298 K. The quantity of film formed at high temperature such as 333 K and 353 K is smaller than dissolved quantity. At the anodic polarization experiment, corrosion resistance in sealing by hot water after chemical conversion treatment in basic solution condition get worse than that in comparison with basic solution condition. In salt spray test, the ratio of black rust on specimen that did not conducted chemical conversion treatment was five times or more compared with those of chemical conversion treated specimen. The film thickness of chemical conversion coating produced by alkali treatment process is thinner than in comparison with that of specimen produced in basic chemical conversion treatment solution condition. It is thought, however, that it showed good corrosion resistance during salt spray test because the area of microcracks is small.

• 한국철도학회논문집
• /
• 제11권4호
• /
• pp.357-363
• /
• 2008

본 연구에서는 염수분무환경에 노출된 철도차량 차체용 탄소섬유/에폭시 복합재의 내구성을 조사하였다. 염수환경시험을 위해서는 해수와 가장 유사하도록 5% 염화나트륨 염수용액을 제조하여 사용하였다. 본 연구에 적용된 시편은 T700 탄소섬유직물을 에폭시 수지에 함침시킨 형태의 복합재 평판에서 채취하였다. 기계적 특성 시험을 통해 인장특성, 굽힘특성, 전단특성을 평가하였으며 동역학 측정장치를 통해 저장탄성계수, 손실탄성계수, 그리고 tan $\delta$ 등의 열분석 특성을 평가하였다. 또한 적외선 분광분석을 통해 노출기간에 따른 화학구조 변화도 조사하였다. 연구결과에 따르면 강화섬유가 지배적인 역할을 하는 기계적 특성은 염수환경에 영향을 받지 않지만 수지가 지배적인 역할을 하는 기계적 특성은 노출기간이 길어짐에 따라 점차 감소하는 양상을 나타낸다. 저장탄성계수는 노출기간에 큰 영향을 받지는 않지만 유리전이온도는 염수환경에 영향을 받으며 노출기간이 길어지면 감소하는 양상을 나타낸다. FT/IR 선도에서 관찰된 피크의 세기는 노출기간에 다소 영향을 받지만 피크의 형상과 위치는 노출 기간에 따른 변화가 관찰되지 않는다. 이로 미루어 볼 때 본 연구에 적용된 탄소섬유/에폭시 복합재는 염수환경에 비교적 안정함을 알 수 있다.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2003년도 추계학술발표대회 논문집
• /
• pp.211-216
• /
• 2003

Coated bars are protecting reinforcing bars from corrosion and enhancing durabilities of reinforced concrete structures are tested to evaluate corrosion protection properties. Tests are performed based on the relevant standards of ACI and ASTM, such as chemical resistance, salt water spray, salt crack test and chloride permeability test with the main variable of the coating thickness. Three type materials are tested by Polyethylene, epoxy and bare bar. Test results show good chemical protection property and chloride permeability. Polyethylene coated bar is good coating material than any other materials.

• 한국해양공학회지
• /
• 제10권4호
• /
• pp.103-108
• /
• 1996

To syudy the change of prtential in the mortar-embedded precorroded rebar, a half cell method was adapted. The rebar was corroded by the salt spray and then the rebar embedded in the mortar. A saturated copper sulfate feference electrode was used. The corrosion potential of the rebar in the mortar specimen cured in air was increased, whereas that of the rebar cured in water was decreased with aging. The corrosion potential of the rebar in the mortar was decreased with corroded time by the salt spray. As the mortar thickness covered the rebar was increased, the corrosion potential of the rebar in the mortar was increased.

• 한국표면공학회지
• /
• 제49권5호
• /
• pp.395-400
• /
• 2016

This article reports improved corrosion resistance and adhesion of electro-paint (E-paint) with fluoride conversion coating (FCC) on AZ31 Mg alloy for the first time. These improvements were observed in comparison to chemically polished samples with no chemical conversion coating and samples with cerium conversion coatings (CeCC). FCCs were prepared in a hydrofluoric acid (HF) solution for four different times; 10, 30, 60, and 120 s. The colour of the samples changed from light gold to brown with increasing immersion time, indicating the formation of thicker FCC coatings with increasing immersion time. The adhesion of the E-paint on FCC-coated AZ31 Mg alloy was tested after 500 h of immersion in deionized (DI) water. Salt spray test (SST) results revealed delamination of E-paint on the chemically polished sample, severe blistering on the samples with CeCC, but no delamination and no blistering on the samples with FCC.