• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.215-218
• /
• 2003

To analyze a bond stress-slip behavior between a reinforcing bar and concrete under repeated loading, pull-out fatigue test was performed. Major variables were repeated stress levels and cycle numbers. Test specimen was taken repeated constant amplitude loading before it was fractured by pull-out test. Increments of bond strength and slip according to repeated stress level and cycle numbers were analyzed. On the basis of test results, Local bond stress-slip relationship under repeated loading were formulated

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.8 no.2
• /
• pp.231-238
• /
• 2004

The deterioration of the flexural capacity by progressive crack and over deflection in R/C bridges is developed actually from the dynamic repeated loading due to vehicle traffics. Such a fact suggest a necessities of confirmation and estimation of the data acquired from monotonic incremental loading test. Therefore, this study carry out the monotonic incremental loading test and dynamic repeated loading test in R/C beams strengthened with CFS. By dynamic repeated loading test, the experiments confirmed the validities and fittness of the results acquired from monotonic incremental loading test and estimated the characteristics of the moment-curvature, degradation of the flexural rigidity, crack and failure.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.4
• /
• pp.183-193
• /
• 2006

This study deals with the response of reinforced concrete beams strengthened with carbon fiber sheets. Test beams are subjected to static loading and repeated loading. Based on the static test results of the RC beams strengthened with carbon fiber sheets, repeated loading tests are performed. The variables of repeated loading test are composed of the number of carbon fiber sheets, the existence of U-shaped band at the end for anchoring, and loading rate of repeated loading, etc. Test results show the flexural behavior, the characteristics of strength, the characteristics of ductility, the change of flexural rigidity, and the amount of energy loss of RC beams under monotonic incremental loading and repeated loading. The failure strain of carbon fiber sheets is also estimated under repeated loading. From the experimental results, this work presents a basis of the data needed to analyze and design the static and dynamic flexural response of RC beams strengthened with carbon fiber sheets.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.627-630
• /
• 2004

This paper investigates a study on the bending behavior of beam strengthened with CFS under repeated loading. The test specimen consisted of 20cm in width, 40cm in depth, and 15cm in CFS width. We find the strength decrease under repeated loading test comparing with the monotonic incremental loading test.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.104-107
• /
• 2004

The crack widths of reinforced concrete flexural members are influenced by repetitive fatigue loadings. The bond stress-slip relation is necessary to estimate these crack widths realistically. The purpose of the present study is, therefore, to propose a realistic model for bond stress-slip relation under repeated loading. To this end, several series of tests were conducted to explore the bond-slip behavior under repeated loadings. Three different bond stress levels with various number of load cycles were considered in the tests. The present tests indicate that the bond strength and the slip at peak bond stress are not influenced much by repeated loading if bond failure does not occur. However, the values of loaded slip and residual slip increase with the increase of load cycles. The bond stress after repeated loading approaches the ultimate bond stress under monotonic loading and the increase of bond stress after repeated loading becomes sharper as the number of repeated loads increases. The bond stress-slip relation after repeated loading was derived as a function of residual slip, bond stress level, and the number of load cycles. The models for slip and residual slip were also derived from the present test data. The number of cycles to bond slip failure was derived on the basis of safe fatigue criterion, i.e. maximum slip criterion at ultimate bond stress.

• Structural Engineering and Mechanics
• /
• v.47 no.6
• /
• pp.773-790
• /
• 2013

Bending behaviors of corroded reinforced concrete (RC) beams under repeated loading were investigated experimentally. A total of twenty test specimens, including four non-corrosion and sixteen corrosion reinforced concrete beams, were prepared and tested. A numerical model for flexural and cracking behaviors of the beam under repeated loading was also developed. Effects of steel corrosion on reinforced concrete beams regarding cracking, mid-span deflection, stiffness and bearing capacity of corroded beams were studied. The impact of corrosion on bond strength as the key factor was investigated to develop the computational model of flexural capacity. It was shown from the experimental results that the bond strength between reinforcement and concrete had increased for specimen of low corrosion levels, while this effect was changed when the corrosion level was higher. It was indicated that the bearing capacity of corrosion beam increased even at a corrosion level of about 5%.

• Structural Monitoring and Maintenance
• /
• v.6 no.4
• /
• pp.269-289
• /
• 2019

This study investigated experimentally the response of thick reinforced concrete specimens having hollow cores with critical parameters. The investigation includes testing of twelve specimens that are solid and hollow-core slab models. Each specimen consists of two pieces, the piece dimensions are (1.2 m) length, (0.3 m) width and (20 cm) thickness tested under both monotonic and repeated loading. The test program is carried out to study the effects of load type, core diameters, core shape, number of cores, and steel fiber existence. Load versus deflection at mid span, failure modes, and crack patterns were obtained during the test. The test results showed that core shape and core number has remarkable influenced on cracking pattern, ultimate load, and failure mode. Also, when considering repeated loading protocol, the ultimate load capacity, load at yielding, and ductility is reduced.

• Structural Engineering and Mechanics
• /
• v.37 no.1
• /
• pp.1-15
• /
• 2011

The response of concrete to transient dynamic loading has received extensive attention for both civil and military applications. Accordingly, thoroughly understanding the response and failure modes of concrete subjected to impact or explosive loading is vital to the protection provided by fortifications. Reactive powder concrete (RPC), as developed by Richard and Cheyrezy (1995) in recent years, is a unique mixture that is cured such that it has an ultra-high compressive strength. In this work, the concrete cylinders with different steel fiber volume fractions were subjected to repeated impact loading by a split Hopkinson Pressure Bar (SHPB) device. Experimental results indicate that the ability of repeated impact resistance of ultra-high-strength concrete was markedly superior to that of other specimens. Additionally, the rate of damage was decelerated and the energy absorption of ultra-high-strength concrete improved as the steel fiber volume fraction increased.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.41 no.2
• /
• pp.61-69
• /
• 1999

When the repeated loading, such as vehicel etc, acts on soft ground, consolidation behaviors due to repeated loading wil show different from standard one. A series of tests was performed to investigate the characteristics of consolidation of lowly organic soil subjected to repeated loadings. Lowly organic soil with Lig. 23.5% was sampeld in Chonbuk Province and tested using a partially and a fully repeated loadings. From test results it was found that void ration, volume change, consolidation coefficient, permeability and secondary consolidation coefficient were greatly affected according to the repetition number and the load weight. The secondary consolidation coefficient was decreased with increase of the repetition number. The results obtained from this research can be used as basic for the improvement of soft ground.

• Structural Engineering and Mechanics
• /
• v.11 no.3
• /
• pp.301-314
• /
• 2001

The purpose of this experimental study is to investigate the damage mechanism due to shear-fatigue behavior of high-strength reinforced concrete beams under repeated loading. The relationship between the number of cycles and the deflection or strain, the crack growths and modes of failure with the increase of number of cycles, fatigue strength, and S-N curve were observed through a fatigue test. Based on the fatigue test results, high-strength reinforced concrete beams failed at 57-66 percent of static ultimate strength for 2 million cycles. The fatigue strength at 2 million cycles from S-N curves was shown as about 60 percent of static ultimate strength. Compared to normal-strength reinforced concrete beams, fatigue capacity of high-strength reinforced concrete beams was similar to or lower than fatigue capacity of normal-strength reinforced concrete beams. Fatigue capacity of normal-strength reinforced concrete beams improved by over 60 percent.