• The Journal of Advanced Prosthodontics
• /
• 제6권4호
• /
• pp.309-316
• /
• 2014

PURPOSE. The color of the ceramic restorations is affected by various factors such as brand, thickness of the layered the ceramic, condensation techniques, smoothness of surface, number of firings, firing temperature and thickness of dentin. The aim of this study was to evaluate the color change and surface roughness in dental porcelain with different thicknesses during repeated firings. MATERIALS AND METHODS. Disc-shaped (N=21) metal-ceramic samples (IPS Classic; Ivoclar Vivadent; Shaar, Liechtenstein) with different thickness were exposed to repeated firings. Color measurement of the samples was made using a colorimeter and profilometer was used to determine surface roughness. ANOVA and Tukey tests with repeated measurements were used for statistical analysis. RESULTS. The total thickness of the ceramics which is less than 2 mm significantly have detrimental effect on the surface properties and color of porcelains during firings (P<.05). CONCLUSION. Repeated firings have effects on the color change and surface roughness of the dental ceramics and should be avoided.

• 대한치과기공학회지
• /
• 제4권1호
• /
• pp.5-7
• /
• 1982

This study was performed to examine the effect of repeated firing on porcelain color stability. Sixty sepcimens of generally uniform size and shape(9.7 12mm)were prepared using the manufactorer's specifications and among them 50 specimens that showed no defect after firing procedure were selected. All samples, abraded with sandpaper disc, ultrasonically cleaned, and air fired to amedium glaze were devided into 10 groups according to the number of repeated firing and, upon completion, mounted on a 13 by 16cm board. 30 persons(five dentists, ten dental techanicians, and fiftheen students) were asked to compare the samples for variations, in hue, chroma and value under natural and artificial light. The results were as follows:(1) There were no color change detected in the first four firings.(2) Slight color change were noticed in subsequent firings(ie: greater decreases in value with slight increases In chroam)(3) However, the hue remained constant in all 10 groups after repeated firings.

• The Journal of Advanced Prosthodontics
• /
• 제6권6호
• /
• pp.427-433
• /
• 2014

PURPOSE. Surface color is one of the main criteria to obtain an ideal esthetic. Many factors such as the type of the material, surface specifications, number of firings, firing temperature and thickness of the porcelain are all important to provide an unchanged surface color in dental ceramics. The aim of this study was to evaluate the color changes in dental ceramics according to the material type and glazing methods, during the multiple firings. MATERIALS AND METHODS. Three different types of dental ceramics (IPS Classical metal ceramic, Empress Esthetic and Empress 2 ceramics) were used in the study. Porcelains were evaluated under five main groups according to glaze and natural glaze methods. Color changes (${\Delta}E$) and changes in color parameters (${\Delta}L$, ${\Delta}a$, ${\Delta}b$) were determined using colorimeter during the control, the first, third, fifth, and seventh firings. The statistical analysis of the results was performed using ANOVA and Tukey test. RESULTS. The color changes which occurred upon material-method-firing interaction were statistically significant (P<.05). ${\Delta}E$, ${\Delta}L$, ${\Delta}a$ and ${\Delta}b$ values also demonstrated a negative trend. The MC-G group was less affected in terms of color changes compared to other groups. In all-ceramic specimens, the surface color was significantly affected by multiple firings. CONCLUSION. Firing detrimentally affected the structure of the porcelain surface and hence caused fading of the color and prominence of yellow and red characters. Compressible all-ceramics were remarkably affected by repeated firings due to their crystalline structure.

• 대한치과보철학회지
• /
• 제25권1호
• /
• pp.95-118
• /
• 1987

This study was undertaken to observe the elemental transition of Interface depending on different pretreatment methods, the number of filings, the kinds of porcelain powders and the various alloys in ceramo-metal restoration. The materials used in this study were Pors-on $4^{(R)}$ and Ceramco porcelain powder to compare the differences depending on the pretreatement methods and the number of firings. Ceramco porcelain powder and Vita porcelain powder were used to compare the differences of elemental transition depending on the porcelain powders. The $Parasil^{(R)},\;PGV^{(R)}$ and Pors-on $4^{(R)}$ as Pd-Ag alloy were used to compare the difference of elemental transition depending on the various alloys. The pretreatment methods were : no treatment, treatment under vacuum and air, treatment with 50 % hydrofluoric acid and double heat tretament. The number of firings were 3, 5 and 7 repeated firings All specimens were observed by SEM and concentration of elements were analyzed quantitatively with EPMA The results of this study were obtained as follows : 1. In the groups of air-treatment, concentration of Sn were the highest and widest. A high concentration of In were in the groups of vacuum and air treatment. 2. There were no significant differences in concentration of Sn between the group of vacuum, 5 minutes hydrofluoric acid and double heat treatment. (p>0.05) 3. As the period of time of hydrofluoric acid treatment increased, not only were the trace elements reduced but the main components such as Pd and Ag were also reduced. 4. Concentration of Sn and In increased and diffused with repeated firings but 5 repeated and 7 repeated firings groups had no significant differences. (p>0.05) 5. Sn were more concentrated in the group of Ceramco porcelaion powder than Vita porcelain powder. 6. The higher concentration of trace elements in the alloy, the more increasing concentration of Sn and In in the interface.

• The Journal of Advanced Prosthodontics
• /
• 제5권1호
• /
• pp.44-50
• /
• 2013

PURPOSE. The aim of this study was to evaluate the effects of repeated porcelain firing process on the corrosion rates of the dental alloys. MATERIALS AND METHODS. Cr-Co, Cr-Ni and Pd-Ag alloys were used for this study. Each metal supported porcelain consisted of 30 specimens of 10 for 7, 9 and 11 firing each. Disc-shaped specimens 10 mm diameter and 3 mm thickness were formed by melting alloys with a propane-oxygen flame and casted with a centrifuge casting machine and then with the porcelain veneer fired onto the metal alloys. Corrosion tests were performed in quintuplicate for each alloy (after repeated porcelain firing) in Fusayama artificial saliva solution (pH = 5) in a low thermal-expansion borosilicate glass cell. Tamhane and Sheffe test was used to compare corrosion differences in the results after repeated firings and among 7, 9 and 11 firing for each alloy. The probability level for statistical significance was set at ${\alpha}$=0.05. RESULTS. The corrosion resistance was higher (30 mV), in case of 7 times firing (Commercial). On the other hand, it was lower in case of 11 times firing (5 mV) (P<.05). Conclusion. Repeated firings decreased corrosion resistance of Pd-Ag, Cr-Co and Cr-Ni alloys. The Pd-Ag alloy exhibited little corrosion in in vitro tests. The Cr-Ni alloy exhibited higher corrosion resistance than Cr-Co alloys in in vitro tests.

• 대한치과보철학회지
• /
• 제49권1호
• /
• pp.73-79
• /
• 2011

연구 목적: 각각 다른 방법으로 색조를 부여한 세 가지 지르코니아 전부도재관에서 반복소성이 전부도재관의 색조에 미치는 영향을 비교, 관찰하였다. 연구 재료 및 방법: 지르코니아 코어를 세가지 방법으로 착색(KW군: Masking liner를 사용하여 하부 코어색 차단, KI군: 지르코니아 코어를 금속 산화물 용액에 침전시켜 착색, NM군: 지르코니아 코어를 고온에서 소결하기 전에 금속산화물과 혼합하여 착색)하여 원반형 시편을 제작하였다. 지르코니아 코어 상방에 A3 색조의 상아질 도재를 소성하고 3, 5, 7회 반복소성 후 $L^*a^*b^*$ 값을 측정하여 비교하고 다른 두 가지 색의 3차원 공간에서의 거리를 나타내는 색차방정식을 이용하여 분석하였다. 측정된 결과는 반복측정 (repeated-measures ANOVA) 분석법과 Tukey 다중범위 검증법을 사용하여 소성횟수에 따른 색조변화를 유의수준 5%에서 검정하였다. 결과: 1. 모든 실험군에서 반복소성에 따른 $L^*a^*b^*$값의 변화가 관찰되었다 (P< .001). 2. 반복소성으로 $L^*$값과 $a^*$값 (KI군제외)은 감소하고 $b^*$값은 증가하는 경향을 보였다. 3. ${\Delta}E$값이 1이상 나타난 반복소성횟수는 KW군과 KI군은 3회 그리고NM군은 7회였다. 4. 7회 반복소성 후 ${\Delta}E$값은 KI군 (${\Delta}E$ = 2.26), KW군 (${\Delta}E$ = 1.47) 그리고 NM군 (${\Delta}E$ = 1.08) 순으로 높게 나타났다 (P< .001). 결론: 반복소성이 지르코니아 코어 색조를 부여방법에 따라 전부도재관의 색조에 미치는 영향을 끼쳤다.

• The Journal of Advanced Prosthodontics
• /
• 제6권6호
• /
• pp.462-467
• /
• 2014

PURPOSE. This study investigated the influence of surface conditioning procedures and repeated firings on monoclinic content and strength of zirconia before cementation. MATERIALS AND METHODS. Sintered bar-shaped zirconia specimens were subjected to no surface treatment (control), air abrasion, or grinding (n=21). Their roughness was evaluated using a profilometer, and microscope analysis was performed on one specimen of each group. Then, 2 or 10 repeated firings (n=10) were executed, the monoclinic content of specimens was analyzed by X-ray diffraction, and a three-point flexural strength test was performed. Surface roughness values were compared using one-way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests, the monoclinic content values were tested using Kruskal-Wallis and Mann-Whitney U tests, and the flexural strength values were tested using two-way ANOVA and Tukey HSD tests (P=.05). Spearman's correlation test was performed to define relationships among measured parameters. RESULTS. Surface-treated specimens were rougher than untreated specimens and had a higher monoclinic content (P<.005), and the relationship between roughness and monoclinic content was significant (P<.000). Neither surface treatment nor firing significantly affected the flexural strength, but Weibull analysis showed that for the air-abraded samples the characteristic strength was significantly lower after the $10^{th}$ firing than after the $2^{nd}$ firing. CONCLUSION. After firing, a negligible amount of monoclinic content remained on the zirconia surfaces, and rougher surfaces had higher monoclinic contents than untreated surfaces. Multiple firings could be performed if necessary, but the fracture probability could increase after multiple firings for rougher surfaces.

• The Journal of Advanced Prosthodontics
• /
• 제3권2호
• /
• pp.57-62
• /
• 2011

MATERIALS AND METHODS. Ceramics have a long history in fixed prosthodontics for achieving optimal esthetics and various materials have been used to improve ceramic core strength. However, there is a lack of information on how color is affected by fabrication procedure. The purpose of this study was to evaluate the effects of various dentin ceramic thicknesses and repeated firings on the color of zirconium oxide all-ceramic system (LavaTM) fabricated using CAD/CAM technology. MATERIALS AND METHODS. Thirty disc-shaped cores, 12 mm in diameter with a 1 mm thickness were fabricated from zirconium oxide based all ceramic systems ($Lava^{TM}$, 3M ESPE, St Paul, MN, USA) and divided into three groups (n = 10) according to veneering with dentin ceramic thicknesses: as 0.5, 1, or 1.5 mm. Repeated firings (3, 5, 7, or 9) were performed, and the color of the specimens was compared with the color after the initial firing. Color differences among ceramic specimens were measured using a spectrophotometer (VITA Easyshade, VITA Zahnfabrik, Bad $S{\ddot{a}}ckingen$, Germany) and data were expressed in CIELAB system coordinates. A repeated measures ANOVA and Bonferroni post hoc test were used to analyze the data (n = 10, ${\alpha}=.05$). RESULTS. $L^{\ast}a^{\ast}b^{\ast}$ values of the ceramic systems were affected by the number of firings (3, 5, 7, or 9 firings) (P<.001) and ceramic thickness (0.5, 1, or 1.5 mm) (P<.001). Significant interactions were present in $L^{\ast}a^{\ast}b^{\ast}$ values between the number of firings and ceramic thickness (P<.001). An increase in number of firings resulted in significant increase in $L^{\ast}$ values for both 0.5 mm and 1.5 mm thicknesses (P<.01, P=.013); however it decreased for 1 mm thickness (P<.01). The $a^{\ast}$ values increased for 1 mm and 1.5 mm thicknesses (P<.01), while it decreased for 0.5 mm specimens. The $b^{\ast}$ values increased significantly for all thicknesses (P<.01, P=.022). As the dentin ceramic thickness increased, significant reductions in $L^{\ast}$ values (P<.01) were recorded. There were significant increases in both $a^{\ast}$ and $b^{\ast}$ values (P<.01) as the dentin ceramic thickness increased. CONCLUSION. The number of firings and dentin ceramic thickness have a definite effect on the final color of all ceramic system tested. The mean ${\Delta}E$ value increased as the dentin ceramic thicknesses increased for zirconium-oxide based all ceramic specimens tested. However, the mean ${\Delta}E$ values were less than 3.7${\Delta}E$ units which is rated as a match in the oral environment.

• The Journal of Advanced Prosthodontics
• /
• 제12권4호
• /
• pp.197-203
• /
• 2020

PURPOSE. The aim of this study was to evaluate the effect of multiple firings on the bond strength between yttriatetragonal zirconia polycrystals (Y-TZP) and 2 types of resin cements. MATERIALS AND METHODS. Sixty 3Y-TZP specimens (LAVA Frame Multi) were divided into 3 groups depending on the following firing procedures: (1) 2-firing cycles, (2) 5-firing cycles, (3) 10-firing cycles. Two samples from each group were investigated by using SEM to determine the morphological changes. All specimens were treated with 125 ㎛ airborne-particle abrasion and the surface roughness of each specimen was measured. The specimens from each firing group were then further divided into 2 subgroups (n = 9) to apply 2 types of resin cement (MDP-free resin cement: RelyX Unicem-RU, and MDP containing resin cement: Panavia F 2.0-PA). The shear bond strength (SBS) test was performed and failure types of all the debonded specimens were classified by using a stereomicroscope as adhesive, cohesive, and mixed. The statistical analysis of surface roughness and SBS data were performed by using 1-way ANOVA and 2-way ANOVA followed by Tukey-HSD tests (α=.05). Failure modes were calculated as a percentage for each group. RESULTS. The bond strength of RU and PA to the specimens obtained with 2 firings were not statistically different from each other (P=.1). However, the SBS values of PA were found to be significantly higher than RU for the specimens obtained with 5 and 10 firing cycles (P=.001 and P=.02, respectively). Surface roughness analysis revealed no statistical difference between groups (P=.2). The SEM analysis of samples fired 5- and 10- times showed irregularities and boundary loss in zirconia grains, and empty spaces between zirconia grains. CONCLUSION. The bond strength of PA cement was higher than that of RU to the zirconia subjected to repeated firings (5 and 10 firing cycles). When zirconia is subjected to multiple firings, using MDP-containing resin cement can be recommended.

• 대한치과기공학회지
• /
• 제31권1호
• /
• pp.23-36
• /
• 2009

The goal of esthetic restoration is to achieve morphologic, optical, and biologic acceptance. Creation of a natural looking ceramic restoration, which blends harmoniously with surrounding dentition, is not always achieved. A successful color match is an important aspect of any esthetic dental restoration. Since natural enamel has inherent translucency, it is important that ceramic restorations reproduce the translucency and color of the natural teeth. However, the final color match of porcelain crowns to adjacent natural dentition remains some problem. Difficulties related to color matching arise from the structural differences that exist between metal ceramic crowns and natural teeth, the limited range of available ceramic shades, inadequate shade guides, different types of metal alloys, repeated firing, the condensation technique, and varying compositions of ceramic materials. Many factors contribute to the esthetic success of dental restoration: optical properties such as color and its elements of hue, value, and chroma; translucency and opacity; light transmission and scattering; and metamerism and fluorescence. The purpose of this study was to determine the color changes of metal-ceramic system with different veneering porcelain powder after repeated firing. The objectives of this in vitro study were to measure the lightness($L^*$), chromaticity($a^*$), chromaticity($b^*$), chroma($C^*$), hue(h), reflectance(%), color difference(${\Delta}E$). The following conclusions were obtained: 1. An increase in the number of firings resulted in decrease in lightness($L^*$) but increase in chromacticity($a^*$) with all porcelain. After the second sintering resulted in decrease in chromacticity($b^*$) with opaque-dentin porcelain and dentin porcelain but in increase with enamel porcelain and translucency porcelain. And after the second sintering resulted in decrease in chroma($C^*$) with opaque-dentin porcelain and dentin porcelain, but on the whole side in decrease with enamel porcelain and translucency porcelain. 2. After the second firing, a increase in the number of firings resulted in decrease reflectance(%) in all wavelength. 3. There were noticeable color differences(${\Delta}E$) between first sintering and multiple firings(dentin porcelain: 5.29~8.15, opaque-dentin porcelain: 4.83~8.2, enamel porcelain: 8.93~13.15, translucency porcelain: 9.37~12.91), but the color difference(${\Delta}E$) after second sintering were down to 4.87 in all porcelain. 4. Given the NBS Criteria, a 'trace' was not found this study but a 'slight' was found 2-3, 3-5 in dentin porcelain, 2-3 in opaque-dentin porcelain, 3-5, 5-10 in enamel porcelain and translucency porcelain, a 'noticeable' was 2-5, 3-10, 5-10 in dentin porcelain and opaque-dentin porcelain, 2-3, 2-5, 3-10 in enamel porcelain 2-3, 3-10 in translucency porcelain, an 'appreciable' was 1-2, 1-3, 2-10 in dentin porcelain 1-2, 1-3, 2-10, 3-10 in opaque-dentin porcelain, 2-10 in enamel porcelain, 2-5, 2-10 in translucency porcelain, a 'much' was 1-5, 1-10 in dentin porcelain and opaque-dentin porcelain, 1-2, 1-3, 1-5 in enamel porcelain 1-2, 1-3, 1-5, 1-10 in translucency porcelain, a 'very much' was 1-10 in enamel porcelain.