• Journal of the Korean Applied Science and Technology
• /
• v.25 no.2
• /
• pp.130-136
• /
• 2008

$xTiO_2$-$ySiO_2$ system photocatalysts were developed by sol-gel method based on the change of production parameters, and their structure of crystallization and the specific surface area were measured. Considering the efficiency of the ethanol and phenol degradation using the catalyst, the conclusions were obtained as follows: By means of X-ray analysis of $xTiO_2$-$ySiO_2$ powder that is obtained from Titanium and Silicon alkoxide by sol-gel process, it is shown that crystal structure of anatase type is a dominating structure and, on the other hand, the structure of rutile also partly exists. The increase of $SiO_2$ contents causes the decrease of the degree of crystallization of the gel, whereas the specific surface area preferentially increases. It is shown that more than 90% of ethanol and phenol are degraded when reaction time is about three and an hours, and the maximum degradation rate of ethanol and phenol is shown in $60TiO_2$-$40SiO_2$ catalyst.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.543-550
• /
• 2010

This paper investigated the synthesis conditions of nano-sized $TiO_2$ powder in a hydrothermal process at a temperature range of $100{\sim}180^{\circ}C$ considering the precipitation agent, precipitation pH, reaction temperature and time. Titanium hydroxide formed by $NH_4OH$ exhibited a lower crystallization temperature than that by NaOH and formed less aggregated $TiO_2$ particles. As the precipitation pH increased above 8, the shape of the particles changed from spherical to needle form, which appeared to be caused by dissolution and re-precipitation of the titanium hydroxide in an alkali environment.

• Advances in nano research
• /
• v.14 no.4
• /
• pp.355-362
• /
• 2023

Physical exercise, especially intense exercise and high intensity interval training (HIIT) by trampoline, can lead to muscle injuries. These effects can be reduced with intelligent products made of nanocomposite materials. Most of these nanocomposites are polymers reinforced with silicon dioxide, alumina, and titanium dioxide nanoparticles. This study presents a polymer nanocomposite reinforced with silica. As a result of the rapid reaction between tetraethyl orthosilicate and ammonia in the presence of citric acid and other agents, silica nanostructures were synthesized. By substituting bis (4-amino phenoxy) phenyl-triptycene in N, N-dimethylformamide with potassium carbonate, followed by catalytic reduction with hydrazine and Pd/C, the diamine monomer bis (4-amino phenoxy) phenyl-triptycene is prepared. We synthesized a new polyaromatic (imide) with triptycene unit by sol-gel method from aromatic diamines and dianhydride using pyridine as a condensation reagent in NMP. PI readily dissolves in solvents and forms robust and tough polymer films in situ. The FTIR and NMR techniques were used to determine the effects of SiO₂ on the sol-gel process and the structure of the synthesized nanocomposites. By using a simultaneous thermal analysis (DTA-TG) method, the appropriate thermal operation temperature was also determined. Through SEM analysis, the structure, shape, size, and specific surface area of pores were determined. Analysis of XRD results is used to determine how SiO₂ affects the crystallization of phases and the activation energy of crystallization.

• Fibers and Polymers
• /
• v.4 no.1
• /
• pp.20-26
• /
• 2003

The thermal behavior, morphology, ester-interchange reaction of Poly(trimethylene terephthalate) (PTT)/poly(ethylene terephthalate) (PET) melt blends were investigated over the whole composition range(xPTT/(1-x)PET) using a twinscrew Brabender. The melt blends were analyzed by differential scanning calorimetry (DSC), nuclear magnetic resonance spectroscopy ($^{13}{C-NMR}$), and scanning electron microscopy (SEM). Single glass transition temperature ($T_g$) and cold crystallization temperature ($T_cc$) were observed in all melt blends. Melt blends were found to be due to the ester-interchange reaction in PTT/PET blend. Also the randomness of copolymer increases because transesterification between PT and PET increases with increasing blending time This reaction increases homogeneity of the blends and decreases the degree of crystallinity of the melt blends. In PTT-rich blends, mechanical properties decrease with increase of PET content compared with that of pure PTT. And, in PET-rich blends, tensile modulus decreases with increase of PTT content, but tensile strength and elongation is similar to that of pure PET.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1999.06a
• /
• pp.351-360
• /
• 1999

A large NaX type zeolite crystal of a uniform particle size of 20${\mu}{\textrm}{m}$ are grown with various H2O content by hydrothermal reaction and added seed crystal (2~3 ${\mu}{\textrm}{m}$) to reactant solution as a function of different adding seed levels from 3 to 15 %. The result that increased purity of NaX zeolite above 95% and homogeneity of crystal size by increasing adding seed levels, also decreased crystallization time. It was explained that adding seed to synthesis solution leaded out increase of surface area of physical contact reaction and directed growth of seed crystal, so more rapid consumption of reaction gel as increase seeding levels.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.4
• /
• pp.371-376
• /
• 1999

A large NaX type zeolite crystal of a uniform particle size of 20$\mu\textrm{m}$ are grown with various {{{{{H}_{2}O}}}} content by hydrothermal reaction and added seed crystal (2~3$\mu\textrm{m}$) to reactant solution as a function of different adding seed levels from 3 to 15%. The result that increased purity of NaX zeolite above 95% and homogeneity of crystal size by increasing adding seed levels, also decreased crystallization time. It was explained that adding seed to synthesis solution leaded out increase of surface area for physical contact reaction and directed growth of seed crystal, so more rapid consumption of reaction gel as increase seeding levels.

• Journal of the Korean Ceramic Society
• /
• v.52 no.3
• /
• pp.204-208
• /
• 2015

Synthesis of hydroxyapatite (HA) was attempted through a room-temperature reaction of calcined eggshell with phosphoric acid. Ball-milled, calcined eggshell powder, which has a specific surface area of $31.6m^2/g$, was mixed with various concentrations of phosphoric acid at room temperature. The mixtures showed high reactivity and a vigorous exothermic reaction ; the reacted samples showed both $Ca(OH)_2$ and $CaHPO_4$ crystal phases. After heating at temperatures above $400^{\circ}C$, an HA crystal phase was observed in all samples. The calcined eggshell showed a pure CaO single phase, while the $Ca(OH)_2$ phase was only observed in the wet, ball-milled calcined powder. The degree of formation of the HA crystal phase increased as the phosphoric acid concentration and the heating temperature were increased. A mixture with 50 wt% phosphoric acid concentration showed a well-developed HA crystal phase after heat treatment at $800^{\circ}C$, while the formation of a more intensive amorphous phase was observed in the products of the room-temperature reaction.

• Bulletin of the Korean Chemical Society
• /
• v.19 no.9
• /
• pp.927-933
• /
• 1998

Polycrystalline powder of vanadium-doped forsterite (Vδ $Mg_2SiO_4$) was synthesized by the $H_2O_2$-assisted sol-gel method. The vanadium dopant, which was added as VO$(OMe)_3$ in methanol, went through several redox reactions as the sol-gel reaction proceeded. Upon adding VO$(OMe)_3$ to a mixture of $Mg(OMe)_2$ and Si$(OEt)_4$ in methanol, V(V) reduced to V(IV). As hydrolysis reaction proceeded, the V(IV) oxidized all back to V(V). Apparently, some of the V(V) reduced to V(IV) during subsequent gelation by condensation reaction. The V(IV) remained even after heat treatment of the gel in highly oxidizing atmosphere. The crystallization of the xerogel around 880 ℃ readily produced single phase forsterite without any minor phase. Using the polycrystalline powder as feeding stock, single crystals of vanadium-doped forsterite were grown by the floating zone method in oxidizing or reducing atmosphere. The doping was limited in low level because of the high partitioning of the vanadium in liquid phase during melting. The greenish single crystal absorbed visible light of 700∼1100 nm. But, no emission was obtained in near infrared range.

• Korean Journal of Materials Research
• /
• v.33 no.5
• /
• pp.222-228
• /
• 2023

Transition metal oxides formed by a single or heterogeneous combination of transition metal ions and oxygen ions have various types of crystal structures, which can be classified as layered structures and non-layered structures. With non-layered structures, it is difficult to realize a two-dimensional structure using conventional synthesis methods. In this study, we report the synthesis of cobalt oxide into wafer-scale nanosheets using a surfactant-assisted method. A monolayer of ionized surfactant at the water-air interface acts as a flexible template for direct cobalt oxide crystallization below. The nanosheets synthesized on the water surface can be easily transferred to an arbitrary substrate. In addition, the synthesizing morphological and crystal structures of the nanosheets were analyzed according to the reaction temperatures. The electrochemical properties of the synthesized nanosheets were also measured at each temperature. The nanosheets synthesized at 70 ℃ exhibited higher catalytic properties for the oxygen evolution reaction than those synthesized at other temperatures. This work suggests the possibility of changing material performance by adjusting synthesis temperature when synthesizing 2D nanomaterials using a wide range of functional oxides, resulting in improved physical properties.

• Resources Recycling
• /
• v.16 no.2 s.76
• /
• pp.23-31
• /
• 2007

In this study, the crystallization of neodymium carbonate from neodymium chloride solution by addition of ammonium bicarbonate was investigated. The concentration of reactants such as neodymium chloride and ammonium bicarbonate, and reaction temperature play an important part in order to obtain the crystal of neodymium carbonate. It seemed that amorphous neodymium carbonate was prepared by aggregation of primary particles formed through nucleation. If reaction rate was increased by increasing the concentration of reactants and reaction temperature, then neodymium carbonate crystal could be obtained. Lanthanite-type neodymium carbonate[$Nd_2(CO_3)_3{\cdot}8H_2O$] and tengerite-type neodymium carbonate[$Nd_2(CO_3)_3{\cdot}2.5H_2O$] could be obtained with reaction renditions. Lanthanite-type neodymium carbonate was sensitive to temperature. The thermal decomposition of neodymium carbonate contained the processes or dehydration, decarbonation and crystalization of $Nd_2O_3$. The shape of lanthanite-type neodymium carbonate was irregular lump type, and tengerite-type neodymium carbonate had the shape of needle type. The shape of $Nd_2O_3$ was affected by the shape of neodymium carbonate.