• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.13-17
• /
• 2004

The PZT thin films are well-known material that has been widely studied for ferroelectric random access memory (FRAM). We etched the PZT thin films by $CF_4/(Cl_2+Ar)$ plasma and investigated improvement in etching damage by $O_2$ annealing. PZT thin films were etched for 1 min in an ICP using a gas mixture of $Cl_2$(80%)/Ar (20%) with 30% $CF_4$ addition. The etching conditions were fixed at a substrate temperature of $30^{\circ}C$, an rf power of 700 W, a dc-bias voltage of -200 V and a chamber pressure of 2 Pa. To improve the ferroelectric properties of PZT thin films after etching, the samples were annealed for 10 min at various temperatures in $O_2$ atmosphere. After $O_2$ annealing, the remanent polarization, fatigue, and the leakage current were gradually recovered to the characteristics of the as-deposited film, according as the temperature increased.

• Transactions on Electrical and Electronic Materials
• /
• v.9 no.1
• /
• pp.1-5
• /
• 2008

ZnS is an attractive material for future optical and electrical devices since it has a direct and wide band gap to provide blue emission at room temperature. In this study, inductively coupled $BCl_3/Ar$ plasma was used to etch ZnS:Mn thin films. The maximum etch rate of 164.2 nm/min for ZnS:Mn was obtained at a $BCl_3(20)/Ar(80)$ gas mixing ratio, an rf power of 700 W, a dc bias voltage of -200V, a total gas flow of 20 sccm, and a chamber pressure of 1Pa. The etch behaviors of ZnS:Mn thin films under various plasma parameters showed that the ZnS:Mn were effectively removed by the chemically assisted physical etching mechanism. The surface reaction of the ZnS:Mn thin films was investigated by X-ray photoelectron spectroscopy. The XPS analysis revealed that Mn had detected on the surface ZnS:Mn etched in $BCl_3/Ar$ plasma.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.3
• /
• pp.185-189
• /
• 2001

In this paper, since the research on the etching of SrBi$_2$Ta$_2$$O_{9}$(SBT) thin film was few (specially Cl$_2$-base) we had studied the surface reaction of SBT thin films. We have used the OES(optical emission spectroscopy) in high density plasma etching as a function of RF power, dc bias voltage, and Cl$_2$/(Cl$_2$+Ar) gas mixing ratio. It had been found that the etch rate of SBT thin films appeared to be more affected by the physical sputtering between Ar ions and surface of the SBT compared to the chemical reaction. The change of Cl radical density that was measured by the OES as a function of gas combination showed the change of the etch rate of SBT thin films. Therefore, the chemical reactions between Cl radical in plasma and components of the SBT enhanced to increase the etch rates SBT thin films. These results were confirmed by XPS(x-ray photoelectron spectroscopy) analysis.s.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.400-403
• /
• 2003

Etching characteristics of (Pb,Sr)$TiO_3$(PST) thin films were investigated using inductively coupled chlorine based plasma system as functions of gas mixing ratio, RF power and DC bias voltage. It was found that increasing of Ar content in gas mixture lead to sufficient increasing of etch rate and selectivity of PST to Pt. The maximum etch rate of PST film is $562\;{\AA}$/min and the selectivity of PST film to Pt is 0.8 at $Cl_2/(Cl_2+Ar)$ of 20 %. It was proposed that sputter etching is dominant etching mechanism while the contribution of chemical reaction is relatively low due to low volatility of etching products.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.6
• /
• pp.287-291
• /
• 2012

We investigated the etching characteristics of TaN thin films in an $O_2/BCl_3/Cl_2/Ar$ gas using a high density plasma (HDP) system. A maximum etch rate of the TaN thin films and the selectivity of TaN to $SiO_2$ were obtained as 172.7 nm/min and 6.27 in the $O_2/BCl_3/Cl_2/Ar$ (3:2:18:10 sccm) gas mixture, respectively. At the same time, the etch rate was measured as a function of the etching parameters, such as the RF power, DC-bias voltage, and process pressure. The chemical states on the surface of the etched TaN thin films were investigated using X-ray photoelectron spectroscopy. Auger electron spectroscopy was used for elemental analysis on the surface of the etched TaN thin films. These surface analyses confirm that the surface of the etched TaN thin film is formed with the nonvolatile by-product.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.8 no.3
• /
• pp.232-238
• /
• 2008

In this paper, a wideband power efficient 2.2 GHz - 4.9 GHz Medium Power Amplifier (MPA), has been designed and fabricated using $0.8{\mu}m$ SiGe BiCMOS process technology. Passive elements such as parallel-branch spiral inductor, metal-insulator-metal (MIM) capacitor and three types of resistors are all integrated in this process. This MPA is a two stage amplifier with all matching components and bias circuits integrated on-chip. A P1dB of 17.7 dBm has been measured with a power gain of 8.7 dB at 3.4 GHz with a total current consumption of 30 mA from a 3 V supply voltage at $25^{\circ}C$. The measured 3 dB bandwidth is 2.7 GHz and the maximum Power Added Efficiency (PAE) is 41 %, which are very good results for a fully integrated Medium PA. The fabricated circuit occupies a die area of $1.7mm{\times}0.8mm$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.1
• /
• pp.1-5
• /
• 2013

In this paper, we investigated the etching characteristics of the TaN thin films and the surface reaction of TaN thin films after etching process. The etching characteristics of the TaN thin films were carried out using inductively coupled plasma (ICP). The etch rate and the selectivity of TaN to $SiO_2$ and TaN to PR were measured by varying the gas mixing ratio, RF power, DC-bias voltage, and process pressure in CF-based plasma. The surface reaction of TaN thin films were determined by x-ray photoelectron spectroscopy (XPS).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.40-44
• /
• 2000

In this paper, since the research on the etching of SrBi$_2$Ta$_2$O$_{9}$ (SBT) thin film was few (specially Cl$_2$-base ), we had studied the surface reaction of SBT thin films using the OES in high density plasma etching as a function of rf power, dc bias voltage, and Cl$_2$(Cl$_2$+Ar) gas mixing ratio. It had been found that the etch rate of SBT thin films appeared to be more affected by the physical sputtering between Ar ions and surface of the SBT compared to the chemical reaction in our previous papers$^{1.2}$ . The change of Cl radical density that is measured by the OES as a function of gas combination showed the change of the etch rate of SBT thin films. Therefore, the chemical reactions between Cl radical in plasma and components of the SBT enhance to increase the etch rates of SBT thin films and these results were confirmed by XPS analysis.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.213-216
• /
• 2001

Etching behaviors of ferroelectric YMn $O_3$ thin films were studied by an inductively coupled plasma (ICP). Etch characteristic on ferroelectric YMn $O_3$ thin film have been investigated in terms of etch rate, selectivity and etch profile. The maximum etch rate of YMn $O_3$ thin film is 300 $\AA$/min at Ar/C $l_2$ of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of 3$0^{\circ}C$. Addition of C $F_4$ gas decrease the etch rate of YMn $O_3$ thin film. From the results of XPS analysis, Y $F_{X}$ compunds were found on the surface of YMn $O_3$ thin film which is etched in Ar/C1/C $F_4$ plasma. The etch profile of YMn $O_3$ film is improved by addition of C $F_4$ gas into the Ar/C $l_2$ plasma. These results suggest that fluoride yttrium acts as a sidewall passivants which reduce the sticking coefficient of chlorine on YMn $O_3$.>.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.7
• /
• pp.564-568
• /
• 2003

The etching of Au thin films have been performed in an inductively coupled CF$_4$/Cl$_2$/Ar plasma. The etch rates were measured as CF$_4$ contents added from 0 to 30 % to Cl$_2$/Ar plasma, of which gas mixing ratio was fixed at 20%. Other parameters were fixed at an rf power of 700 W, a dc bias voltage of 150 V, a chamber pressure of 15 mTorr, and a substrate temperature of 3$0^{\circ}C$. The highest etch rate of the Au thin film was 3700 $\AA$m/min at a 10% additive CF$_4$ into Cl$_2$/Ar plasma. The surface reaction of the etched Au thin films was investigated using x-ray photoelectron spectroscopy (XPS) analysis. XPS analysis indicated that Au reacted with Cl and formed Au-Cl, which is hard to remove on the surface because of its high melting point. The etching products could be sputtered by Ar ion bombardment.