• Transactions on Electrical and Electronic Materials
• /
• v.5 no.4
• /
• pp.153-157
• /
• 2004

ITO thin films were deposited on PET and soda-lime glass substrates by a dc reactive magnetron sputtering of In-Sn alloy metal target without substrate heater and post-deposition thermal treatment. The dependency of rf-bias voltage and substrate power during deposition processing was investigated to control the electrical and optical properties of ITO films. The range of rf bias voltage is from 0 to -80 V and the substrate power is applied from 10 to 50 W. The minimum resistivity of ITO film is 5.4${\times}$10$^{-4}$ $\Omega$cm at 50 W power and rf-bias voltage of -20 V. The best transmittance of ITO films at 550 nm wavelength is 91 % in the substrate power of 30 W and rf-bias voltage of -80 V.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.6
• /
• pp.342-349
• /
• 2019

Titanium nitride(TiN) thin films have been deposited on PEN(Polyethylene naphthalate) substrate by reactive RF(13.56 MHz) magnetron sputtering in a 25% N₂/Ar mixed gas atmosphere. The pulsed DC bias voltage of -50V on substrates was applied with a frequency of 350 kHz, and duty ratio of 40%(1.1 ㎲). The effects of pulsed DC substrate bias voltage on the crystallinity, color, electrical properties of TiN_x films have been investigated using XRD, SEM, XPS and measurement of the electrical properties such as electrical conductivity, carrier concentration, mobility. The deposition rates of TiN_x films was decreased with application of the pulsed DC substrate bias voltage. The TiN_x films deposited without and with pulsed bias of -50V to substrate exhibits gray and gold colors, respectively. XPS depth profiling revealed that the introduction of the substrate bias voltage resulted in decreasing oxygen concentration in TiN_x films, and increasing the electrical conductivities, carrier concentration, and mobility to about 10 times, 5 times, and 2 times degree, respectively.

• Transactions on Electrical and Electronic Materials
• /
• v.5 no.3
• /
• pp.122-125
• /
• 2004

ITO films were deposited on polyethylene terephthalate substrate by a dc reactive magnetron sputtering using rf bias without substrate heater and post-deposition thermal treatment. The dependency of rf substrate bias on plasma sputter processing was investigated to control energetic particles and improve ITO film properties. The substrate was applied negative rf bias voltage from 0 to -80 V. The composition of indium, tin, and oxygen atoms is strongly depended on the rf substrate bias. Oxygen deficiency is the highest at rf bias of -20 V. The electrical and optical properties of ITO films also are dominated obviously by negative rf bias.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1999.10a
• /
• pp.73-75
• /
• 1999

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.6
• /
• pp.493-498
• /
• 2005

Al doped Zinc Oxide, which is widely used as a transparent conductor in opto-electronic devices. In this paper, we find that the lateral variations of the parameters of the ZnO:Al films prepared by the rf magnetron sputtering can be reduced to acceptable levels by optimising the deposition parameters. The effect of bias voltage on the electrical, optical and morphological properties were investigated experimentally. we investigated sample properties of Bias Voltage change in 0 to 50 V.

• Korean Journal of Materials Research
• /
• v.8 no.10
• /
• pp.961-968
• /
• 1998

In order to investigate the effects of substrate bias voltage on the formation of$ZnS-SiO_2$ protective film in phase change optical disk by R.F. magnetron sputtering method, thin dielectric film was formed on Si wafer and Corning glass by using ZnS(80mol%)-$SiO_2$(20mol%)t arget under argon gas. In this study, the Taguchi experimental method was applied in order to obtain optimum conditions with reduced number of experiments and to control numerous variables effectively. At the same time this method can assure the reproducibility of experiments. Optimum conditions for film formation obtained by above method were target RF power of 200 W. substrate RF power of 20 W, Ar pressure of 5 mTorr. sputtering time of 20 min.. respectively. The phase of specimen was determined by using XRD and TEM. The compositional analysis of specimen was performed by XPS test. In order to measure the thermal resistivity of deposited specimen, annealing test was carried out at $300^{\circ}C$ and $600^{\circ}C$. For the account of void fraction in thin film, the Bruggeman EMA(Effective Medium Approximation) method was applied using the optical data obtained by Spectroscopic Ellipsometry. According to the results of this work, the existence of strong interaction between bias voltage and sputtering time was confirmed for refractive index value. According to XRD and TEM analysis of specimen, the film structure formed in bias voltage resulted in more refined structures than that formed without bias voltage. But excess bias voltage resulted in grain growth in thin film. It was confirmed that the application of optimum bias voltage increased film density by reduction of void fraction of about 3.7%.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.2
• /
• pp.93-99
• /
• 1996

In this work BN thin films were deposited on Si substrate by R. F. sputtering method at $200^{\circ}C$ and in Ar + $N_2$ mixed gas atmosphere. In order to investigate the effect of ion bombardment on substrate for c-BN bonding, substrate bias voltage was applied. The optimum substrate bias voltage for c-BN bonding was determined by FTIR analysis on specimens which were deposited with various bias voltages. Then BN thin film was deposited with this optimum condition and its phase, morphology, chemical composition, and refractive index were compared with those of BN film which was deposited without bias voltage. FTIR results showed that BN films deposited with substrate bias voltage were composed of mixed phases of c-BN and h-BN, while those deposited without bias voltage were h-BN only. When pure Ar gas was used for sputtering gas, BN films were delaminated easily from substrate in air, while when 10% $N_2$ gas was added to the sputtering gas, although c-BN specific infrared peak was reduced, delamination did not occur. GXRD and TEM results showed that BN films were amorphous phases regardless of substrate bias voltage, and AES results showed that the chemical compositions of B/N were about 1.7~1.8. The refractive index of BN film deposited with bias voltage was higher than that without bias voltage. The reason is believed to be the existence of c-BN bonding in BN film and the higher density of film that deposited with the substrate bias voltage.

• Korean Journal of Materials Research
• /
• v.33 no.9
• /
• pp.372-376
• /
• 2023

Transparent conductive tungsten (W) doped indium oxide (In₂O₃; IWO) films were deposited at different substrate bias voltage (-V_b) conditions at room temperature on glass substrates by radio frequency (RF) magnetron sputtering and the influence of the substrate bias voltage on the optical and electrical properties was investigated. As the substrate bias voltage increased to -350 V_b, the IWO films showed a lower resistivity of 2.06 × 10^-4 Ωcm. The lowest resistivity observed for the film deposited at -350 V_b could be attributed to its higher mobility, of 31.8 cm²/Vs compared with that (6.2 cm²/Vs) of the films deposited without a substrate bias voltage (0 V_b). The highest visible transmittance of 84.1 % was also observed for the films deposited at the -350 V_b condition. The X-ray diffraction observation indicated the IWO films deposited without substrate bias voltage were amorphous phase without any diffraction peaks, while the films deposited with bias voltage were polycrystalline with a low In₂O₃ (222) diffraction peak and relatively high intensity (431) and (046) diffraction peaks. From the observed visible transmittance and electrical properties, it is concluded that the opto-electrical performance of the polycrystalline IWO film deposited by RF magnetron sputtering can be enhanced with effective substrate bias voltage conditions.

• Proceedings of the KIEE Conference
• /
• 1996.11a
• /
• pp.206-208
• /
• 1996

Thin films of magnesium oxide(MgO) were deposited on glass substrates by RF magnetron sputtering method. The characteristics of MgO thin films were analyzed as a function of various deposition conditions such as substrate temperature, substrate self-bias, input power and pressure. As the substrate temperature and bias voltage were increased, the grain size of MgO thin film increased. XRD peaks of (111) and (222) direction became dominant, as the substrate bias voltage increases and temperature decreases.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.1
• /
• pp.27-32
• /
• 2004

The diamond-like carbon (DLC) films were deposited on the Si (100) wafer by a rf-PECVD method as a function of the mixture rate of methane-hydrogen gas and bias voltage. The bonding structure and mechanical properties of these deposited DLC films were investigated using FT-IR, Raman, and nano-indenter. The deposition rates of DLC films increased with increased flow rate of methane in the gas mixtures and increased bias voltage. The $sp^3/sp^2$ bonding ratio of carbon in thin film and the hardness increased with increasing flow rate of hydrogen in the gas mixtures and increasing bias voltage.