Abstract
In this work BN thin films were deposited on Si substrate by R. F. sputtering method at $200^{\circ}C$ and in Ar + $N_2$ mixed gas atmosphere. In order to investigate the effect of ion bombardment on substrate for c-BN bonding, substrate bias voltage was applied. The optimum substrate bias voltage for c-BN bonding was determined by FTIR analysis on specimens which were deposited with various bias voltages. Then BN thin film was deposited with this optimum condition and its phase, morphology, chemical composition, and refractive index were compared with those of BN film which was deposited without bias voltage. FTIR results showed that BN films deposited with substrate bias voltage were composed of mixed phases of c-BN and h-BN, while those deposited without bias voltage were h-BN only. When pure Ar gas was used for sputtering gas, BN films were delaminated easily from substrate in air, while when 10% $N_2$ gas was added to the sputtering gas, although c-BN specific infrared peak was reduced, delamination did not occur. GXRD and TEM results showed that BN films were amorphous phases regardless of substrate bias voltage, and AES results showed that the chemical compositions of B/N were about 1.7~1.8. The refractive index of BN film deposited with bias voltage was higher than that without bias voltage. The reason is believed to be the existence of c-BN bonding in BN film and the higher density of film that deposited with the substrate bias voltage.