• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.1069-1072
• /
• 2003

Ultraviolet-nanoimprint lithography (UV-NIL) is a promising nanoimprint method for cost-effectively defining nanometer scale structures at room temperature and low pressure. Nanostamp fabrication technology is a key technology for UV-NIL because fabricating a high resolution nanostamp is the first step for defining high resolution nanostructures in a substrate. We used quartz as an UV transparent stamp material for the UVNIL. A $5{\times}5{\times}0.09$ inch stamp was fabricated using the quartz etch process in which Cr film was used as a hard mask for transferring nanostructures into the quartz. In this paper, we describe the quartz etching process and discuss the results including SEM images.

• Journal of Institute of Control, Robotics and Systems
• /
• v.10 no.7
• /
• pp.604-610
• /
• 2004

Ultraviolet-nanoimprint lithography (UV-NIL) is a promising method for cost-effectively defining nanoscale structures at room temperature and low pressure. Since the resolution of transferred nanostructures depends strongly upon that of nanostamps, the nanostamp fabrication technology is a key technology to UV-NIL. In this paper, a $5\times5\times0.09$ in. quartz stamp whose critical dimension is 377 nm was fabricated using the etching process in which a Cr film was employed as a hard mask for transferring nanostructures onto the quartz plate. To effectively apply the fabricated 5-in. stamp to UV-NIL on a 4-in. Si wafer, we have proposed a new UV-NIL process using a multi-dispensing method as a way to supply resist on a wafer. Experiments have shown that the multi-dispensing method can enable UV-NIL using a large-area stamp.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.199-202
• /
• 2003

Ultraviolet-nanoimprint lithography (UV-NIL) is a promising method for cost-effectively defining nanoscale structures at room temperature and low pressure. Since the resolution of nanostructures depends strongly upon that of nanostamps, the nanostamp fabrication technology is a key technology to UV-NIL. In this paper, a 5$\times$5$\times$0.09 in. quartz stamp whose critical dimension is 377 nm was fabricated using the etch process in which a Cr film was employed as a hard mask for transferring nanostructures onto the quartz plate. To effectively apply tile fabricated 5-in. stamp to UV-NIL on a 4-in. Si wafer, we have proposed a new UV-NIL process using a multi-dispensing method as a way to supply resist on a wafer Experiments have shown that the multi-dispensing method can enable UV-NIL rising a large-area stamp.

• Journal of the Korean Vacuum Society
• /
• v.13 no.1
• /
• pp.39-45
• /
• 2004

Ultraviolet-nanoimprint lithography (UV-NIL) is a promising method for cost-effectively defining nanoscale structures at room temperature and low pressure. A 5${\times}$5${\times}$0.09 in. quartz stamp is fabricated using the etch process in which a Cr film was employed as a hard mask for transferring nanostructures onto the quartz plate. FAS(Fluoroalkanesilane) is used as a material for anti-adhesion surface treatment on the stamp and a thin organic film to improve adhesion on a wafer is formed by spin-coating. The low viscosity resin droplets with a nanometer scale volume are dispensed on the whole area of the coated wafer. The UV-NIL experiments have been performed using the EVG620-NIL. 370 nm - 1 m features on the stamp have been transferred to the thin resin layer on the wafer using the multi-dispensing method and UV-NIL process. We have measured the imprinted patterns and residual layer using SEM and AFM to evaluate the potential of the process.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.676-679
• /
• 2005

Nano imprint Lithography (NIL) is regarded as one of the next-generation lithography technologies with EUV lithography, immersion lithography, Laser interference lithography. Because a Si wafer stamp and a quartz stamp, used to imprinting usually are very expensive and easily broken, it is suggested that master stamp is duplicated by PDMS and the PDMS stamp uses to imprint .For using the PDMS stamp, a thermally curable monomer resin was used for the imprinting process to lower pressure and temperature. As a result, NIL patterns were successfully fabricated.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2006.05a
• /
• pp.109-112
• /
• 2006

A fluorine-doped diamond-like carbon (F-DLC) stamp which has high contact angle, high UV-transmittance and sufficient hardness, was fabricated using the following direct etching method: F-DLC is deposited on a quartz substrate using DC and RF magnetron sputtering, PMMA is spin coated and patterned using e-beam lithography and finally, $O_2$ plasma etching is performed to transfer the line patterns having 100 nm line width, 100 nm line space and 70 nm line depth on F-DLC. The optimum fluorine concentration was determined after performing several pre-experiments. The stamp was applied successfully to UV-NIL without being coated with an anti-adhesion layer.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.05a
• /
• pp.145-146
• /
• 2006

A fluorine-doped diamond-like carbon (F-DLC) stamp which has high contact angle, high UV-transmittance and sufficient hardness, was fabricated using the following direct etching method: F-DLC is deposited on a quartz substrate using DC and RF magnetron sputtering, PMMA is spin coated and patterned using e-beam lithography and finally, O2 plasma etching is performed to transfer the line patterns having 100 nm line width, 100 nm line space and 70 nm line depth on F-DLC. The optimum fluorine concentration was determined after performing several pre-experiments. The stamp was applied successfully to UV-NIL without being coated with an anti-adhesion layer.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.672-675
• /
• 2005

To imprint 70-nm wide line-patterns, we used a newly developed ultraviolet nanoimprint lithography (UV-NIL) process in which an elementwise patterned stamp (EPS), a large-area stamp, and pressurized air are used to imprint a wafer in a single step. For a single-step UV-NIL of a 4' wafer, we fabricated two identical $5'\times5'\times0.09'(W{\times}L{\times}H)$ quartz EPSs, except that one is with nanopatterns and the other without nanopatterns. Both of them consist of 16 small-area stamps, called elements, each of which is $10\;mm\;\times\;10\;mm$. UV-curable low-viscosity resin droplets were dispensed directly on each element of the EPSs. The volume and viscosity of each droplet are 3.7 nl and 7 cps. Droplets were dispensed in such a way that no air entrapment between elements and wafer occurs. When the droplets were fully pressed between ESP and wafer, some incompletely filled elements were observed because of the topology mismatch between EPS and wafer. To complete those incomplete fillings, pressurized air of 2 bar was applied to the bottom of the wafer for 2 min. Experimental results have shown that nanopatterns of the EPS were successfully transferred to the resin layer on the wafer.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.126-126
• /
• 2004

1996년 Chou 등이 개발한 가열방식의 나노임프린트 리소그래피(nanoimprint lithography, NIL)은 선폭 100nm 이하의 나노구조물을 경제적으로 제작할 수 있는 대표적인 나노패턴닝(nano-patterning) 공정으로 많은 기대가 모아지고 있으나, 열변형에 의해 다층정렬이 어렵다는 점과, 점도가 큰 레지스트(resist)를 임프린트하기 위해서는 고압(∼30 bar)이 필요하다 점 등의 문제점이 있다. 이를 해결할 수 있는 방법으로 UV 나노임프린트 리소그래피(ultraviolet nanoimprint lithography, UV-NIL)를 들 수 있다.(중략)

• Korean Journal of Optics and Photonics
• /
• v.17 no.4
• /
• pp.317-322
• /
• 2006

A polymeric arrayed waveguide grating (AWG) has been proposed and demonstrated by exploiting the nanoimprint method. A PDMS(polydimethylsiloxane) stamp with device patterns engraved was developed out of a master mold made of quartz glass. The device was fabricated by transferring the pattern in the PDMS stamp to a spin-coated polymer film without using any etching process. The device had 8 output channels, while the center wavelengths of each output channel were positioned from 1543.7 nm to 1548.3 nm with the spacing of 0.8 nm. The achieved average channel crosstalk and the 3-dB bandwidth were about 10 dB and 0.8 nm respectively.