• Progress in Superconductivity and Cryogenics
• /
• v.11 no.2
• /
• pp.7-10
• /
• 2009

Effects of $BaCO_3$ purity on the superconducting properties of top seeded melt growth (TSMG) processed $Y_{1+x}Ba_2Cu_3O_{7-y}$ (Y1+x, x=0.1 and 0.2) superconductors were investigated. $YBa_2Cu_3O_{7-y}$ (Y123) powder prepared using $BaCO_3$ with 99.75% purity and commercially available Y123 powder of 99.9% were used for the fabrication of single Y123 grain superconductors. $T_c$ values of the Y1+x samples prepared using low purity Y123 powder were slightly lower than those of the samples prepared using a high purity powder. In addition to the lower $T_c$, an anomalous peak effect in the intermediate magnetic fields was observed in Y1+x samples prepared using the low purity $BaCO_3$ powder. The slight decrease in $T_c$ and the anomalous peak effect are ascribed to the possible incorporation of a Y123 phase with impurity elements such as strontium and calcium included in the $BaCO_3$powder of 99.7%. The result suggests that the low purity $BaCO_3$ powder of a low price can be used as a raw power for the fabrication of single grain YBCO bulk superconductors.

• Journal of Powder Materials
• /
• v.15 no.1
• /
• pp.6-12
• /
• 2008

[ $YBa_2Cu_3O_{7-y}$ ](123) powders were synthesized by the solid state reaction method using two different purity $BaCO_3$ powders (99.75% and 99.7% purity) and $Y_2O_3$ (99.9%) and CuO (99.9%) powders. The effect of $BaCO_3$ purity on the formation of a 123 phase and the superconducting properties were investigated. The mixtures of raw powders were calcined at temperature ranges of $800^{\circ}C-880^{\circ}C$ in air and finally made into a single grain samples by a melt processing with top seeding. It was found that a 123 phase was well formed at temperature above $870^{\circ}C$, but the purity effect on the 123 formation was negligible. The single-grain 123 samples prepared from the different $BaCO_3$ powders showed the same $T_c$ value of 90.5 K and similar $J_c$ values about $10^4\;A/cm^2$ at 0 T and 77 K, and $10^3\;A/cm^2$ at 2 T and 77 K. This result indicates that the low purity, cheap price $BaCO_3$ powder can be used as a raw material for the fabrication of single-grain, high-$J_c$ superconducting levitator.

• Corrosion Science and Technology
• /
• v.5 no.4
• /
• pp.149-152
• /
• 2006

$BaTiO_3$ coatings were prepared by micro arc oxidation (MAO) method. Only $Ba(OH)_2$ was dissolved in the electrolyte and process time was less than 30 min. Commercial purity $Ba(OH)_2$ (97%) containing $BaCO_3$ as impurity was used in preparing the electrolyte. XRD showed that the coating was composed of largely $BaTiO_3$, and in some process conditions, small quantity of impurity, $BaCO_3$, was characterized in the coating layer. The quantity of $BaCO_3$ could be controlled to negligible quantity by regulating the applied voltage and duration time of the MAO process.

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.63-63
• /
• 2008

• Journal of the Korean Ceramic Society
• /
• v.25 no.6
• /
• pp.671-676
• /
• 1988

Preparation of high purity ultrafine Ba2Ti9O20 powder was investigated by coprecipitation method. Formation of Ba2Ti9O20 powder from precipitate of coprecipitation takes place at 120$0^{\circ}C$, which is 20$0^{\circ}C$ lower than that from mechanical mixtures of BaCO3 and TiO2. This is apparently due to the nature of the compounds formed by the reaction of mixtures of aqueous solutions of BaCl2 and TiCl4 with an ammoniacal solution of ammonium carbonate and ammouium hydroxide. In this method, the Ba2Ti9O20 powders show low callcining and sintering temperature and it has good sintering and dielectric constant at room temperature.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.1005-1011
• /
• 1994

The three different composition of BaTi4O9, Ba2Ti9O20 and BaTi5O11 were prepared by coprecipitation process, and then the dielectric properties of these compounds were measured at low microwave frequencies. The powder showing high level of purity was synthesised by the coprecipition reaction of BaCl2 and TiCl4 where (NH4)2CO3 and NH4OH were used as a deflocculent. Followings are the result of this study: 1. The sintering temperature increased with increasing TiO2 content. 2. BaTi4O9 powder were synthesized as a single phase by this processing technique, but the resultant Ba2Ti9O20 and BaTi5O11 phase existed with Ba2Ti9O20 and BaTi5O11 phases. 3. Single phase BaTi4O9 showed high dielectric constant value of 35, high Q value of 8100.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.5
• /
• pp.649-655
• /
• 2011

Methane direct cracking can be utilized to produce $CO_x$ and $NO_x$-free hydrogen for PEM fuel cells, oil refineries, ammonia and methanol production. We present the results of a systematic study of methane direct cracking using a mixed conducting oxide, Y-doped $BaZrO_3$ ($BaZr_{0.85}Y_{0.15}O_3$), membrane. In this paper, dense $BaZr_{0.85}Y_{0.15}O_3$ membrane with disk shape was successfully sintered at $1400^{\circ}C$ with a relative density of more 93% via addition of 1 wt% ZnO. The ($BaZr_{0.85}Y_{0.15}O_3$) membrane is covered with Pd as catalyst for methane decomposition with an DC magnetron sputtering method. Reaction temperature was $800^{\circ}C$ and high purity methane as reactant was employed to membrane side with 1.5 bar pressure. The $H_2$ produced by the reaction was transported through mixed conducting oxide membrane to the outer side. In addition, it was observed that the carbon, by-product, after methane direct cracking was deposited on the Pd/ZnO-$BaZr_{0.85}Y_{0.15}O_3$ membrane. The produced carbon has a shape of sphere and nanosheet, and a particle size of 80 to 100 nm.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2004.05a
• /
• pp.97-100
• /
• 2004

We report $EU^{2+}$ activated green phosphor $Ba_{2}CaMgSi_{2}O_{8}:Eu^{2+}$. The phosphor absorbs ultroviolet radation and emits a green visible light. The phosphors were synthesized by conventional solid state reaction method. The high purity $BaCO_3$, $CaCO_3$, MgO, $SiO_2$, $Eu_{2}O_{3}$ were used as raw materials. The raw materials were mixed thoroughly with an appropriate amount of ethanol in an agate mortar and then dried at $90^{\circ}C$ for 2 hours. The mixture was sintered at $900^{\circ}C$ for 2 hours and reheated at the mild reducing atmosphere 5% $H_2$ gas mixed with 95% $N_2$ gas at about $900^{\circ}C$ to $1200^{\circ}C$ for 2 hours. The photoluminescence spectra of the phosphor powders were measured by a fluorescent spectrophotometer. The crystal structure of phosphor powders were investigated by X -ray diffractometer.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1275-1276
• /
• 2007

For fabrication of $BaTiO_3$ system Ferroelectric thick films, (Ba,Sr,Ca)$TiO_3$ (BSCT) powders, prepared by using the alkoxide-based sol-gel method, were doped $MnCO_3$ as acceptor and $Dy_{2}O_{3}$ as donor. $MnCO_3$ and $Dy_{2}O_{3}$-doped (Ba,Sr,Ca)$TiO_3$ thick films were fabricated by screen printing techniques on high purity alumina substrates. The structure and dielectric properties were investigated with variation of $Dy_{2}O_{3}$ amount. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All the BSCT thick films, sintered at $1420^{\circ}C$ for 2h, showed the typical XRD patterns of perovskite polycrystalline structure and no pyrochlore phase was observed. The average grain size and thickness of specimens no doped with $Dy_{2}O_{3}$ was 1.32mm, 52mm, respectively. The relative dielectric constant decreased and dielectric loss increased with increasing amount of $Dy_{2}O_{3}$ dopant, the values of the BSCT thick films no doped with $Dy_{2}O_{3}$ were 4043 and 0.4% at 1 kHz, respectively. The relative dielectric constant gradually decreased in the measured frequency range from 0.1 to 100 kHz

• Applied Chemistry for Engineering
• /
• v.9 no.2
• /
• pp.165-171
• /
• 1998

The $Y_1Ba_2Cu_3O_{7-x}$(123) superconductor powders were prepared by pyrophoric synthesis method(PSM) using $Y_2O_3$(99.9%), $BaCO_3$(99.9%), and CuO(99.9%) powders. The phase formation and reaction kinetics of 123 superconductor manufactured with powders prepared in various pHs of pyrophoric synthetic solution have been studied through the experiments at various heat treatment temperatures and times. Inductively coupled plasma(ICP) spectroscopy and scanning electron microscopy(SEM) measurements were performed to examine the composition and morphology of the sample. X-ray diffraction(XRD) analysis was done to determine phase formation and conversion ratio of Y-Ba-Cu-O systems. The 123 powder prepared at pH 7(${\pm}0.3$) yields the best result in terms of purity, homogeneity, and reactivity. The activation energies(${\Delta}E_a$) of 123 phase formation were found to be 191 kJ/mol and 230kJ/mol in solid state reaction method and pyrophoric synthesis method, respectively.